CN108867074A - A kind of production method of smooth fabric - Google Patents
A kind of production method of smooth fabric Download PDFInfo
- Publication number
- CN108867074A CN108867074A CN201810566501.4A CN201810566501A CN108867074A CN 108867074 A CN108867074 A CN 108867074A CN 201810566501 A CN201810566501 A CN 201810566501A CN 108867074 A CN108867074 A CN 108867074A
- Authority
- CN
- China
- Prior art keywords
- fabric
- warp thread
- fiber
- agent
- weft yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of smooth fabric, it is raw material including cotton, silk broadcloth chemical fibre and thick fabric, described includes warp thread and weft yarn, it is interwoven by warp thread and weft yarn according to institutional framework, the warp thread and weft yarn is the mixed yarn that acrylic fiber, polyester fiber and tencel AlOO fiber are constituted, the composition of raw materials be crude oil, antistatic agent, anti pilling agent, finishing agent and adhesive, its advantage is that：It is mixed by anti pilling agent with finishing agent, so that being formed between effect and fabric that silk broadcloth chemical fibre particle passes through adhesive a kind of functional netted thin, entirety touches up smooth pliable, its anti-pilling property is good, with graceful natural gloss, right warp thread and weft yarn are through face plain weave or through face twill because warp thread is different with the shrinking percentage of weft yarn by interlaced structure structure, it will form natural crepe structure in web surface, this fold has stereovision by fabric, natural crepe structure reduces the area of cloth contact body, and achievees the effect that nice and cool.
Description
Technical field
The present invention relates to field of textile, more particularly, to a kind of production method of smooth fabric.
Background technique
Clothes are made with fabric, and fabric is exactly the material for making clothes, as one of clothes three elements, fabric
The style and characteristic of clothes can be not only annotated, but also directly controls the expression effect of the color of clothes, moulding, it is big in clothes
In the world, the fabric of clothes is multifarious, makes rapid progress, but generally, high-quality, high-grade fabric mostly has
The characteristics of several aspects such as wear is comfortable, sweat-absorbing breathable, pendency is well-pressed, vision is noble, tactile is soft and graceful, it is produced on formal social activity
The clothes of occasion institute wear, preferably select pure cotton, pure wool, pure silk, pure gunny products, the clothes made with these four pure natural quality fabrics
Dress, mostly class is higher, and with the development of the times, the continuous improvement of living standards of the people, textile product is increasingly by people
Like, for being fabricated to a variety of woollens, gym suit etc..
But there is easy pilling fluffing, rough feature in some existing web surfaces, though what fabric can
All kinds of clothes are made, but low-cost abrasion resistance, heat resistance, hygroscopicity, gas permeability are poor, heat is easily deformed, and is easy to produce
Raw electrostatic, bad sale at high cost, overall class is not high, does not appeal to refined taste.
Summary of the invention
The purpose of the present invention is to provide a kind of production methods of smooth fabric.
Technical solution of the present invention is summarized as follows：
A kind of production method of smooth fabric, including cotton, silk broadcloth chemical fibre and thick fabric are raw material, described to include
Warp thread and weft yarn are interwoven by warp thread and weft yarn according to institutional framework, and the warp thread and weft yarn are acrylic fiber, terylene
The mixed yarn that fiber and tencel AlOO fiber are constituted, the composition of raw materials be crude oil, antistatic agent, anti pilling agent, finishing agent and
Adhesive；
Including following steps：
Step 1: first successively pretreatment early period is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in dyeing 70%
Silk broadcloth chemical fibre, 30% thick fabric is by control relative humidity 50%-55%, 25 DEG C -30 DEG C of temperature, add crude oil and
Antistatic agent makes fiber have excellent lubricity, increases coherent, the antistatic property of fiber；
Step 2: successively carrying out anti pilling processing, enzymatic treatment and softness to cotton, silk broadcloth chemical fibre and thick fabric again
Processing, obtains flexible foundation cloth, by preparing coating material, is interwoven and is mixed to be according to institutional framework by warp thread and weft yarn
Finishing agent is added by chemistry reflection in the mixed yarn that acrylic fiber, polyester fiber and tencel AlOO fiber are constituted in fabric
Composition melts cotton fabric, leaves the ingredient washed, drying and processing；
Step 3: being mixed by anti pilling agent with finishing agent, so that the work that silk broadcloth chemical fibre particle passes through adhesive
It is a kind of functional netted thin with being formed between fabric, smooth fabric is obtained in setting treatment with cold rinse.
Preferably, the warp thread and weft yarn by interlaced structure structure be through face plain weave or through face twill or Warp Satin,
Its warp thread and weft quality percentage are 30%-70%.
Preferably, warp thread and weft quality percentage are 50%-60%.
Preferably, the warp count is 19-19.64 root/cm, and valuable yarn density is 27.8-31 root/cm.
Preferably, the anti pilling agent is phosphate antimony oxide mixture, phosphate antimony oxide mixture
Dosage is the 1.5-4% of finishing agent capacity.
Preferably, the phosphate antimony oxide amount of mixture is the 2.5-3.5% of finishing agent capacity.
Preferably, the cotton layer is with a thickness of 0.5cm-0.8cm, and the silk broadcloth chemical fibre layer is with a thickness of 0.6cm-
Lcm, the thick fabric thickness are 0.2cm-0.35cm.
The beneficial effects of the invention are as follows：It is mixed by anti pilling agent with finishing agent, so that silk broadcloth chemical fibre particle is logical
It crosses between the effect of adhesive and fabric and is formed a kind of functional netted thin, integrally touch up smooth pliable, anti-pilling
Can be good, have graceful natural gloss, right warp thread and weft yarn by interlaced structure structure for through face plain weave or through face twill, warp thread
It is 30%-70% with weft quality percentage, because warp thread is different with the shrinking percentage of weft yarn, will form natural wrinkle in web surface
Structure, this fold has stereovision by fabric, and ironing is not required to after washing, and natural crepe structure reduces cloth contact body
Area, to achieve the effect that nice and cool, acrylic fiber and polyester fiber genus polyporus substance, good permeability, hygroscopicity are splendid.
Specific embodiment
The present invention is clearly and completely described below with reference to embodiment, it is clear that described embodiment is only this
Invention a part of the embodiment, instead of all the embodiments, based on the embodiments of the present invention, those of ordinary skill in the art exist
Every other embodiment obtained under the premise of creative work is not made, shall fall within the protection scope of the present invention.
The present invention provides a kind of production methods of smooth fabric, including cotton, silk broadcloth chemical fibre and thick fabric to be
Raw material, described includes warp thread and weft yarn, is interwoven by warp thread and weft yarn according to institutional framework, the warp thread and weft yarn are
The mixed yarn that acrylic fiber, polyester fiber and tencel AlOO fiber are constituted, the composition of raw materials are crude oil, antistatic agent, resist
Globule, finishing agent and adhesive；
Including following steps：
Step 1: first successively pretreatment early period is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in dyeing 70%
Silk broadcloth chemical fibre, 30% thick fabric is by control relative humidity 50%-55%, 25 DEG C -30 DEG C of temperature, add crude oil and
Antistatic agent makes fiber have excellent lubricity, increases coherent, the antistatic property of fiber；
Step 2: successively carrying out anti pilling processing, enzymatic treatment and softness to cotton, silk broadcloth chemical fibre and thick fabric again
Processing, obtains flexible foundation cloth, by preparing coating material, is interwoven and is mixed to be according to institutional framework by warp thread and weft yarn
Finishing agent is added by chemistry reflection in the mixed yarn that acrylic fiber, polyester fiber and tencel AlOO fiber are constituted in fabric
Composition melts cotton fabric, leaves the ingredient washed, drying and processing；
Step 3: being mixed by anti pilling agent with finishing agent, so that the work that silk broadcloth chemical fibre particle passes through adhesive
It is a kind of functional netted thin with being formed between fabric, smooth fabric is obtained in setting treatment with cold rinse.
Wherein warp thread and weft yarn are warp thread and latitude through face plain weave or through face twill or Warp Satin by interlaced structure structure
Yarn quality percentage is 30%-70%.
It is 19-19.64 root/cm by warp count, valuable yarn density is 27.8-31 root/cm.
It is phosphate antimony oxide mixture by anti pilling agent, phosphate antimony oxide amount of mixture is to arrange
The 1.5-4% of agent capacity.
And cotton layer, with a thickness of 0.5cm-0.8cm, the silk broadcloth chemical fibre layer is described with a thickness of 0.6cm-lcm
Thick fabric thickness is 0.2cm-0.35cm.
Embodiment 1：Pretreatment early period successively first is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in dyeing 70%
Silk broadcloth chemical fibre, 30% thick fabric 25 DEG C -30 DEG C of temperature, adds crude oil by control relative humidity 50%-55%
And antistatic agent, make fiber that there is excellent lubricity, increases coherent, the antistatic property of fiber, then successively to cotton, silk
Silk fabric chemical fibre and thick fabric carry out anti pilling processing, enzymatic treatment and soft treatment, obtain flexible foundation cloth, are coated by preparation
Material is interwoven according to institutional framework by warp thread and weft yarn and is mixed to be acrylic fiber, polyester fiber and tencel AlOO fiber
The mixed yarn of composition is added finishing agent composition in fabric and melts cotton fabric, leave the ingredient washed, dry by chemistry reflection
Processing, warp thread and weft yarn are warp thread and weft quality through face plain weave or through face twill or Warp Satin by interlaced structure structure
Percentage is 30%-70%, and warp count is 19-19.64 root/cm, and valuable yarn density is 27.8-31 root/cm, passes through anti pilling agent
It is mixed with finishing agent, so that being formed between effect and fabric that silk broadcloth chemical fibre particle passes through adhesive a kind of functional
It is netted thin, smooth fabric is obtained in setting treatment with cold rinse, the fabric is fine and soft soft, has graceful natural gloss.
Embodiment 2：Pretreatment early period successively first is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in dyeing 80%
Silk broadcloth chemical fibre, 30% thick fabric 25 DEG C -30 DEG C of temperature, adds crude oil by control relative humidity 40%-50%
And antistatic agent, make fiber that there is excellent lubricity, increases coherent, the antistatic property of fiber, then successively to cotton, silk
Silk fabric chemical fibre and thick fabric carry out anti pilling processing, enzymatic treatment and soft treatment, obtain flexible foundation cloth, are coated by preparation
Material is interwoven according to institutional framework by warp thread and weft yarn and is mixed to be acrylic fiber, polyester fiber and tencel AlOO fiber
The mixed yarn of composition is added finishing agent composition in fabric and melts cotton fabric, leave the ingredient washed, dry by chemistry reflection
Processing, warp thread and weft yarn are warp thread and weft quality through face plain weave or through face twill or Warp Satin by interlaced structure structure
Percentage is 30%-70%, and warp count is 19-19.64 root/cm, and valuable yarn density is 27.8-31 root/cm, passes through anti pilling agent
It is mixed with finishing agent, so that being formed between effect and fabric that silk broadcloth chemical fibre particle passes through adhesive a kind of functional
It is netted thin, smooth fabric is obtained in setting treatment with cold rinse, the fabric is fine and soft soft, has graceful natural gloss.
Embodiment 3：Pretreatment early period successively first is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in dyeing 77%
Silk broadcloth chemical fibre, 30% thick fabric 25 DEG C -35 DEG C of temperature, adds crude oil by control relative humidity 52%-58%
And antistatic agent, make fiber that there is excellent lubricity, increases coherent, the antistatic property of fiber, then successively to cotton, silk
Silk fabric chemical fibre and thick fabric carry out anti pilling processing, enzymatic treatment and soft treatment, obtain flexible foundation cloth, are coated by preparation
Material is interwoven according to institutional framework by warp thread and weft yarn and is mixed to be acrylic fiber, polyester fiber and tencel AlOO fiber
The mixed yarn of composition is added finishing agent composition in fabric and melts cotton fabric, leave the ingredient washed, dry by chemistry reflection
Processing, warp thread and weft quality percentage are 30%-70%, and warp count is 19-19.64 root/cm, and valuable yarn density is
27.8-31 root/cm is mixed by anti pilling agent with finishing agent, so that the effect that silk broadcloth chemical fibre particle passes through adhesive
It is functional netted thin that one kind is formed between fabric, obtains smooth fabric in setting treatment with cold rinse, the fabric is fine and soft
It is soft, there is graceful natural gloss.
Embodiment 4：Pretreatment early period successively first is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in dyeing 70%
Silk broadcloth chemical fibre, 30% thick fabric 25 DEG C -30 DEG C of temperature, adds crude oil by control relative humidity 50%-55%
And antistatic agent, make fiber that there is excellent lubricity, increases coherent, the antistatic property of fiber, then successively to cotton, silk
Silk fabric chemical fibre and thick fabric carry out anti pilling processing, enzymatic treatment and soft treatment, obtain flexible foundation cloth, are coated by preparation
Material is interwoven according to institutional framework by warp thread and weft yarn and is mixed to be acrylic fiber, polyester fiber and tencel AlOO fiber
The mixed yarn of composition is added finishing agent composition in fabric and melts cotton fabric, leave the ingredient washed, dry by chemistry reflection
Processing, warp thread and weft yarn are warp thread and weft quality through face plain weave or through face twill or Warp Satin by interlaced structure structure
Percentage is 30%-70%, and warp count is 19-19.64 root/cm, and valuable yarn density is 27.8-31 root/cm, passes through anti pilling agent
It is mixed with finishing agent, so that being formed between effect and fabric that silk broadcloth chemical fibre particle passes through adhesive a kind of functional
It is netted thin, smooth fabric is obtained in setting treatment with cold rinse, the fabric is fine and soft soft, has graceful natural gloss.
Embodiment 5：Pretreatment early period successively first is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in dyeing 70%
Silk broadcloth chemical fibre, 33% thick fabric 25 DEG C -30 DEG C of temperature, adds crude oil by control relative humidity 55%-65%
And antistatic agent, make fiber that there is excellent lubricity, increases coherent, the antistatic property of fiber, then successively to cotton, silk
Silk fabric chemical fibre and thick fabric carry out anti pilling processing, enzymatic treatment and soft treatment, obtain flexible foundation cloth, are coated by preparation
Material is interwoven according to institutional framework by warp thread and weft yarn and is mixed to be acrylic fiber, polyester fiber and tencel AlOO fiber
The mixed yarn of composition is added finishing agent composition in fabric and melts cotton fabric, leave the ingredient washed, dry by chemistry reflection
Processing, warp thread and weft yarn are warp thread and weft quality through face plain weave or through face twill or Warp Satin by interlaced structure structure
Percentage is 30%-70%, and warp count is 19-19.64 root/cm, and valuable yarn density is 27.8-31 root/cm, passes through anti pilling agent
It is mixed with finishing agent, so that being formed between effect and fabric that silk broadcloth chemical fibre particle passes through adhesive a kind of functional
It is netted thin, smooth fabric is obtained in setting treatment with cold rinse, the fabric is fine and soft soft, has graceful natural gloss.
Embodiment 6：Pretreatment early period successively first is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in dyeing 70%
Silk broadcloth chemical fibre, 32% thick fabric 25 DEG C -35 DEG C of temperature, adds crude oil by control relative humidity 52%-55%
And antistatic agent, make fiber that there is excellent lubricity, increases coherent, the antistatic property of fiber, then successively to cotton, silk
Silk fabric chemical fibre and thick fabric carry out anti pilling processing, enzymatic treatment and soft treatment, obtain flexible foundation cloth, are coated by preparation
Material is interwoven according to institutional framework by warp thread and weft yarn and is mixed to be that acrylic fiber, polyester fiber and tencel fiber are constituted
Mixed yarn by chemistry reflection, finishing agent composition is added in fabric and melts cotton fabric, leaves the ingredient washed, at drying
Reason, warp thread and weft yarn are warp thread and weft quality hundred through face plain weave or through face twill or Warp Satin by interlaced structure structure
Point than be 30%-70%, warp count be 19-19.64 root/cm, valuable yarn density be 27.8-31 root/cm, by anti pilling agent with
Finishing agent mixing, so that forming a kind of functional net between effect and fabric that silk broadcloth chemical fibre particle passes through adhesive
Shape is thin, obtains smooth fabric in setting treatment with cold rinse, and the fabric is fine and soft soft, has graceful natural gloss.
| Title | Example 1 | Example 2 | Example 3 | Example 4 | Example 5 | Example 6 |
| Dye levels | 1.04 | 1.11 | 1.08 | 1.28 | 1.21 | 1.33 |
| Fibre weight (g) | 3.60g | 3.88g | 3.45g | 3.47g | 3.54g | 3.61g |
Although the embodiments of the present invention have been disclosed as above, but its is not only in the description and the implementation listed
With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily
Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously unlimited
In specific details and embodiment shown here.
Claims (7)
1. a kind of production method of smooth fabric, which is characterized in that including cotton, silk broadcloth chemical fibre and thick fabric be original
Material, described includes warp thread and weft yarn, is interwoven by warp thread and weft yarn according to institutional framework, the warp thread and weft yarn are nitrile
The mixed yarn that synthetic fibre fiber, polyester fiber and tencel AlOO fiber are constituted, the composition of raw materials are crude oil, antistatic agent, anti pilling
Agent, finishing agent and adhesive；
Including following steps：
Step 1: first successively pretreatment early period is carried out to cotton, silk broadcloth chemical fibre and thick fabric, in the silk of dyeing 70%
Silk fabric chemical fibre, 30% thick fabric 25 DEG C -30 DEG C of temperature, are added crude oil and resisted quiet by control relative humidity 50%-55%
Electric agent makes fiber have excellent lubricity, increases coherent, the antistatic property of fiber；
Step 2: successively being carried out at anti pilling processing, enzymatic treatment and softness to cotton, silk broadcloth chemical fibre and thick fabric again
Reason, obtains flexible foundation cloth, by preparing coating material, is interwoven and is mixed to be nitrile according to institutional framework by warp thread and weft yarn
The mixed yarn that synthetic fibre fiber, polyester fiber and tencel AlOO fiber are constituted by chemistry reflection, be added in fabric finishing agent at
Part melts cotton fabric, leaves the ingredient washed, drying and processing；
Step 3: mix with finishing agent by anti pilling agent so that silk broadcloth chemical fibre particle pass through the effect of adhesive with
It is functional netted thin that one kind is formed between fabric, obtains smooth fabric in setting treatment with cold rinse.
2. a kind of production method of smooth fabric according to claim 1, which is characterized in that the warp thread and weft yarn are pressed
Interlaced structure structure is through face plain weave or through face twill or Warp Satin, and warp thread and weft quality percentage are 30%-70%.
3. a kind of production method of smooth fabric according to claim 2, which is characterized in that warp thread and weft quality hundred
Divide than being 50%-60%.
4. a kind of production method of smooth fabric according to claim 2, which is characterized in that the warp count is
19-19.64 root/cm, valuable yarn density are 27.8-31 root/cm.
5. a kind of production method of smooth fabric according to claim 1, which is characterized in that the anti pilling agent is phosphorus
Acid esters antimony oxide mixture, phosphate antimony oxide amount of mixture are the 1.5-4% of finishing agent capacity.
6. a kind of production method of smooth fabric according to claim 5, which is characterized in that the phosphate three aoxidizes
Two antimony amount of mixture are the 2.5-3.5% of finishing agent capacity.
7. a kind of production method of smooth fabric according to claim 1, which is characterized in that the cotton layer with a thickness of
0.5cm-0.8cm, for the silk broadcloth chemical fibre layer with a thickness of 0.6cm-lcm, the thick fabric thickness is 0.2cm-0.35cm.