CN108795220A - A kind of sterilization and anticorrosion emulsion paint - Google Patents
A kind of sterilization and anticorrosion emulsion paint Download PDFInfo
- Publication number
- CN108795220A CN108795220A CN201810757071.4A CN201810757071A CN108795220A CN 108795220 A CN108795220 A CN 108795220A CN 201810757071 A CN201810757071 A CN 201810757071A CN 108795220 A CN108795220 A CN 108795220A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion
- sterilization
- anticorrosion
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sterilization and anticorrosion emulsion paints, including polyvinyl acetate emulsion, kaolinite mountain flour, nano carbon black, nano silicon dioxide, phenolic resin, pyrovinic acid, chlorine partial emulsion and epoxy resin.The beneficial effects of the invention are as follows：Formula is reasonable, add mixed plant slurry, safety and environmental protection is nontoxic, the volatile quantity of organic compound can be reduced, antibacterial, antiviral, raising index with fresh air, interiro wall latex paint have excellent adhesive force, covering power, water-alkali resistance and anti-corrosive properties, it is simple for process, it is particularly suitable for the decorations such as medical institutions, gymnasium and uses.
Description
Technical field
The present invention relates to a kind of building coating more particularly to a kind of sterilization and anticorrosion emulsion paints.
Background technology
With the development of economy, people's environmental consciousness is continuously improved, and the product feature of environmental protection causes consumer to pay close attention to, and emulsion paint is made
For common coating in Modern Decorative, volatile organic compounds (VOC) content contained by it becomes focus of people's attention
One of.Coating material production manufacturer is usually to set about from auxiliary agent, lotion selection etc. to reduce emulsion paint VOC contents.Emulsion paint passes through
The development of decades is crossed, it has many advantages compared with other coating, and easy for construction, dried coating film is fast, good permeability, water-fast
Property is good.Due to emulsion paint these advantages people indoors in exterior decoration generally using so that emulsion paint obtain in recent years it is considerable
Development.
With the continuous development of the continuous improvement and emulsion paint technology of living standards of the people, body of the indoor environment to people
Health is particularly important, and the environment of especially public place receives people's concern, as movements of population such as hospital, school, hotels and
Bacteria breed is reduced, it is necessary to carry out disinfection in regular multicell to ensure that the air of people is that health is pure and fresh in intensive place
's.
Therefore, to solve the above problems, providing a kind of new technical solution.
Invention content
The present invention provides a kind of sterilization and anticorrosion emulsion paint.
The technical solution adopted by the present invention is：
A kind of sterilization and anticorrosion emulsion paint, including polyvinyl acetate emulsion, kaolinite mountain flour, nano carbon black, nano silicon dioxide, phenolic aldehyde
Resin, pyrovinic acid, chlorine partial emulsion and epoxy resin.
Further, component is respectively by weight：
10-20 parts of polyvinyl acetate emulsion；
20-30 parts of kaolinite mountain flour；
15-20 parts of nano carbon black；
10-15 parts of nano silicon dioxide；
20-25 parts of phenolic resin；
5-10 parts of pyrovinic acid；
8-12 parts of chlorine partial emulsion；
18-25 parts of epoxy resin.
Further, preparation process includes the following steps：
A, kaolinite mountain flour, nano carbon black and nano silicon dioxide are added to successively in ball grinder, it is that 5-10 is micro- to be milled to grain size
Rice takes out ball milling material, is placed in centrifugal blender, obtains batch mixing；
B, polyvinyl acetate emulsion, phenolic resin and epoxy resin are added sequentially in deionized water, are stirred and then add
Then heat adds pyrovinic acid and chlorine partial emulsion is stirred, be heated to 80 DEG C while stirring, be eventually adding step a to 70 DEG C
In batch mixing be stirred mixing, obtain coating.
Further, the speed of centrifugal blender is 300 turns/min in step a.
Further, the mixing time of centrifugal blender is 15-20 minutes in step a.
The beneficial effects of the invention are as follows：Formula is reasonable, adds mixed plant slurry, safety and environmental protection is nontoxic, can reduce organic
The volatile quantity of compound, antibacterial, antiviral, raising index with fresh air, interiro wall latex paint have excellent adhesive force, cover
Power, water-alkali resistance and anti-corrosive properties, it is simple for process, it is particularly suitable for the decorations such as medical institutions, gymnasium and uses.
Specific implementation mode
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, not restrict the protection scope of the present invention.
Embodiment 1
A kind of sterilization and anticorrosion emulsion paint, including polyvinyl acetate emulsion, kaolinite mountain flour, nano carbon black, nano silicon dioxide, Hai Pao
Stone, phenolic resin, pyrovinic acid, chlorine partial emulsion and epoxy resin, component are respectively by weight：
10 parts of polyvinyl acetate emulsion；
20 parts of kaolinite mountain flour；
15 parts of nano carbon black；
10 parts of nano silicon dioxide；
20 parts of phenolic resin；
5 parts of pyrovinic acid；
8 parts of chlorine partial emulsion；
18 parts of epoxy resin；
Further, preparation process includes the following steps：
A, kaolinite mountain flour, nano carbon black and nano silicon dioxide are added to successively in ball grinder, it is 5 microns to be milled to grain size,
Ball milling material is taken out, is placed in centrifugal blender, the speed of centrifugal blender is 300 turns/min, and mixing time is 15 minutes, is obtained
Batch mixing；
B, polyvinyl acetate emulsion, phenolic resin and epoxy resin are added sequentially in deionized water, are stirred and then add
Then heat adds pyrovinic acid and chlorine partial emulsion is stirred, be heated to 80 DEG C while stirring, be eventually adding step a to 70 DEG C
In batch mixing be stirred mixing, obtain coating.
Embodiment 2
A kind of sterilization and anticorrosion emulsion paint, including polyvinyl acetate emulsion, kaolinite mountain flour, nano carbon black, nano silicon dioxide, phenolic aldehyde
Resin, pyrovinic acid, chlorine partial emulsion and epoxy resin, component are respectively by weight：
15 parts of polyvinyl acetate emulsion；
25 parts of kaolinite mountain flour；
17 parts of nano carbon black；
13 parts of nano silicon dioxide；
23 parts of phenolic resin；
7 parts of pyrovinic acid；
10 parts of chlorine partial emulsion；
21 parts of epoxy resin；
Further, preparation process includes the following steps：
A, kaolinite mountain flour, nano carbon black and nano silicon dioxide are added to successively in ball grinder, it is 7 microns to be milled to grain size,
Ball milling material is taken out, is placed in centrifugal blender, the speed of centrifugal blender is 300 turns/min, and mixing time is 17 minutes, is obtained
Batch mixing；
B, polyvinyl acetate emulsion, phenolic resin and epoxy resin are added sequentially in deionized water, are stirred and then add
Then heat adds pyrovinic acid and chlorine partial emulsion is stirred, be heated to 80 DEG C while stirring, be eventually adding step a to 70 DEG C
In batch mixing be stirred mixing, obtain coating.
Embodiment 3
A kind of sterilization and anticorrosion emulsion paint, including polyvinyl acetate emulsion, kaolinite mountain flour, nano carbon black, nano silicon dioxide, phenolic aldehyde
Resin, pyrovinic acid, chlorine partial emulsion and epoxy resin, component are respectively by weight：
20 parts of polyvinyl acetate emulsion；
30 parts of kaolinite mountain flour；
20 parts of nano carbon black；
15 parts of nano silicon dioxide；
25 parts of phenolic resin；
10 parts of pyrovinic acid；
12 parts of chlorine partial emulsion；
25 parts of epoxy resin；
Further, preparation process includes the following steps：
A, kaolinite mountain flour, nano carbon black and nano silicon dioxide are added to successively in ball grinder, it is 10 microns to be milled to grain size,
Ball milling material is taken out, is placed in centrifugal blender, the speed of centrifugal blender is 300 turns/min, and mixing time is 20 minutes, is obtained
Batch mixing；
B, polyvinyl acetate emulsion, phenolic resin and epoxy resin are added sequentially in deionized water, are stirred and then add
Then heat adds pyrovinic acid and chlorine partial emulsion is stirred, be heated to 80 DEG C while stirring, be eventually adding step a to 70 DEG C
In batch mixing be stirred mixing, obtain coating.
The beneficial effects of the invention are as follows：Formula is reasonable, adds mixed plant slurry, safety and environmental protection is nontoxic, can reduce organic
The volatile quantity of compound, antibacterial, antiviral, raising index with fresh air, interiro wall latex paint have excellent adhesive force, cover
Power, water-alkali resistance and anti-corrosive properties, it is simple for process, it is particularly suitable for the decorations such as medical institutions, gymnasium and uses.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and according to the technical essence of the invention made by any modification or equivalent variations, still fall within present invention model claimed
It encloses.
Claims (5)
1. a kind of sterilization and anticorrosion emulsion paint, it is characterised in that：Including polyvinyl acetate emulsion, kaolinite mountain flour, nano carbon black, nanometer
Silica, phenolic resin, pyrovinic acid, chlorine partial emulsion and epoxy resin.
2. a kind of sterilization and anticorrosion emulsion paint according to claim 1, it is characterised in that：Its component is distinguished by weight
For：
10-20 parts of polyvinyl acetate emulsion；
20-30 parts of kaolinite mountain flour；
15-20 parts of nano carbon black；
10-15 parts of nano silicon dioxide；
20-25 parts of phenolic resin；
5-10 parts of pyrovinic acid；
8-12 parts of chlorine partial emulsion；
18-25 parts of epoxy resin.
3. a kind of sterilization and anticorrosion emulsion paint according to claim 2, it is characterised in that：Preparation process includes the following steps：
A, kaolinite mountain flour, nano carbon black and nano silicon dioxide are added to successively in ball grinder, it is that 5-10 is micro- to be milled to grain size
Rice takes out ball milling material, is placed in centrifugal blender, obtains batch mixing；
B, polyvinyl acetate emulsion, phenolic resin and epoxy resin are added sequentially in deionized water, are stirred and then add
Then heat adds pyrovinic acid and chlorine partial emulsion is stirred, be heated to 80 DEG C while stirring, be eventually adding step a to 70 DEG C
In batch mixing be stirred mixing, obtain coating.
4. a kind of sterilization and anticorrosion emulsion paint according to claim 3, it is characterised in that：The speed of centrifugal blender in step a
Degree is 300 turns/min.
5. a kind of sterilization and anticorrosion emulsion paint according to claim 3, it is characterised in that：Centrifugal blender stirs in step a
It is 15-20 minutes to mix the time.