CN108793826A - A kind of building and ornament materials of good flame resistance and preparation method thereof - Google Patents
A kind of building and ornament materials of good flame resistance and preparation method thereof Download PDFInfo
- Publication number
- CN108793826A CN108793826A CN201810799948.6A CN201810799948A CN108793826A CN 108793826 A CN108793826 A CN 108793826A CN 201810799948 A CN201810799948 A CN 201810799948A CN 108793826 A CN108793826 A CN 108793826A
- Authority
- CN
- China
- Prior art keywords
- parts
- building
- flame resistance
- ornament materials
- good flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of building and ornament materials of good flame resistance and preparation method thereof, is related to building material field, the building and ornament materials of good flame resistance include following raw material：Waste plastic, flyash, stone powder, Corvic, bamboo fibre, boron carbide, calcium oxide, nickel oxide, peanut shell, furnace slag, fire retardant, light stabilizer, heat stabilizer and compatilizer；Preparation method includes the following steps：（1）Weigh raw material,（2）Prepare plastic grain,（3）Crush,（4）Stirring,（5）Heating and extrusion forming；The building and ornament materials of good flame resistance produced by the present invention have the advantages that energy conservation and environmental protection and good flame resistance.
Description
Technical field
The invention belongs to building material fields, and in particular to a kind of building and ornament materials of good flame resistance and its preparation side
Method.
Background technology
With the raising of social progress and living standards of the people, requirement of the people to construction material is higher and higher, especially
Building and ornament materials in construction material, existing building and ornament materials have it is the modeling of wooden, metal, steel and gypsum, but
It is that the building and ornament materials of the type are unfavorable for the sustainable use of resource generally using non-renewable resources as former material, in addition,
There is also inflammable problems for existing building and ornament materials, seriously threaten the life security of people.
Therefore, it is necessary to develop the building and ornament materials of a kind of energy conservation and environmental protection and the good flame resistance of good flame resistance.
Invention content
In order to solve the above technical problem, the present invention provides a kind of building and ornament materials of good flame resistance and its preparation sides
The building and ornament materials of method, good flame resistance obtained have the advantages that energy conservation and environmental protection and good flame resistance.
The present invention provides the following technical solutions：
A kind of building and ornament materials of good flame resistance, include the raw material of following parts by weight：28-34 parts of waste plastic, flyash 30-
42 parts, 17-21 parts of stone powder, 7-13 parts of Corvic, 4-6 parts of bamboo fibre, 11-15 parts of boron carbide, 7-11 parts of calcium oxide,
8-12 parts of nickel oxide, 4-6 parts of peanut shell, 13-17 parts of furnace slag, 0.4-0.6 parts of fire retardant, 0.2-0.4 parts of light stabilizer, heat are steady
Determine 0.1-0.3 parts of 0.1-0.3 parts of agent and compatilizer.
Boron carbide is added in raw material, boron carbide is with fire resistance is good, intensity is high, thermal stability is good and chemical stability is good
The characteristics of.
Calcium oxide is added in raw material, calcium oxide has the advantages that fire resistance is good and stability is good.
Nickel oxide is added in raw material, nickel oxide has excellent fire resistance.
Peanut shell and furnace slag are added in raw material, the waste material of peanut shell and furnace slag as agricultural and industry is present to obtain
To cycling and reutilization, achieve the purpose that energy-saving and environment-friendly.
Preferably, include the raw material of following parts by weight：31 parts of waste plastic, 36 parts of flyash, 19 parts of stone powder, polychlorostyrene second
10 parts of olefine resin, 5 parts of bamboo fibre, 13 parts of boron carbide, 9 parts of calcium oxide, 10 parts of nickel oxide, 5 parts of peanut shell, 15 parts of furnace slag, resistance
Fire 0.2 part of 0.5 part of agent, 0.3 part of light stabilizer, 0.2 part of heat stabilizer and compatilizer.
Preferably, the waste plastic is waste polyurethane foamed plastics.
Preferably, the fire retardant is aluminium hydroxide.
Preferably, the light stabilizer is carbon black.
Preferably, the heat stabilizer is aluminum stearate.
Preferably, the compatilizer is maleic anhydride graft compatilizer.
A kind of preparation method of the building and ornament materials of good flame resistance, includes the following steps：
（1）Raw material is weighed according to the parts by weight of the building and ornament materials raw material of good flame resistance；
（2）Waste plastic is added in plastic regenerator to get plastic grain；
（3）Peanut shell is added in pulverizer to get crushed material；
（4）By step（2）In plastic grain, step（3）In crushed material and other raw materials be added blender in, stir 30-
40min is to get mixture；
（5）By step（4）In mixed material heating to 280-300 DEG C, then be placed in the extruder of 4-5 atmospheric pressure and be squeezed into
Type, at normal temperatures timeliness 5-6 days.
The beneficial effects of the invention are as follows：
1, boron carbide is added in the raw material in the present invention, boron carbide is with fire resistance is good, intensity is high, thermal stability is good and chemical
The good feature of stability.
2, it is added to calcium oxide in the raw material in the present invention, calcium oxide has the advantages that fire resistance is good and stability is good.
3, nickel oxide is added in the raw material in the present invention, nickel oxide has excellent fire resistance.
4, peanut shell and furnace slag are added in the raw material in the present invention, peanut shell and furnace slag are as agricultural and industry
Waste material obtains cycling and reutilization now, has achieved the purpose that energy-saving and environment-friendly.
5, heretofore described waste plastic is waste polyurethane foamed plastics, has reached the mesh of waste recovery recycling
's.
6, heretofore described fire retardant is aluminium hydroxide, is conducive to the flame retardant property for improving the building and ornament materials.
7, heretofore described light stabilizer is carbon black, can cover or reflect the substance of ultraviolet light.
8, heretofore described heat stabilizer is aluminum stearate, is conducive to the thermal stability for improving the building and ornament materials.
9, heretofore described compatilizer is maleic anhydride graft compatilizer, can improve inorganic filler and organic resin phase
Capacitive improves the intensity of the building and ornament materials, improves rheological performance.
10, the building and ornament materials of good flame resistance produced by the present invention have the advantages that energy conservation and environmental protection and good flame resistance.
Specific implementation mode
Embodiment 1
A kind of building and ornament materials of good flame resistance, include the raw material of following weight：Waste plastic 28kg, flyash 30kg, stone
Feed powder 17kg, Corvic 7kg, bamboo fibre 4kg, boron carbide 11kg, calcium oxide 7kg, nickel oxide 8kg, peanut shell 4kg,
Furnace slag 13kg, fire retardant 0.4kg, light stabilizer 0.2kg, heat stabilizer 0.1kg and compatilizer 0.1kg.
A kind of preparation method of the building and ornament materials of good flame resistance, includes the following steps：
（1）Raw material is weighed according to the weight of the building and ornament materials raw material of good flame resistance；
（2）Waste plastic is added in plastic regenerator to get plastic grain；
（3）Peanut shell is added in pulverizer to get crushed material；
（4）By step（2）In plastic grain, step（3）In crushed material and other raw materials be added blender in, stir 30-
40min is to get mixture；
（5）By step（4）In mixed material heating to 280-300 DEG C, then be placed in the extruder of 4-5 atmospheric pressure and be squeezed into
Type, at normal temperatures timeliness 5-6 days.
Boron carbide is added in raw material, boron carbide is with fire resistance is good, intensity is high, thermal stability is good and chemical stability is good
The characteristics of.
Calcium oxide is added in raw material, calcium oxide has the advantages that fire resistance is good and stability is good.
Nickel oxide is added in raw material, nickel oxide has excellent fire resistance.
Peanut shell and furnace slag are added in raw material, the waste material of peanut shell and furnace slag as agricultural and industry is present to obtain
To cycling and reutilization, achieve the purpose that energy-saving and environment-friendly.
Waste plastic is waste polyurethane foamed plastics, has achieved the purpose that waste recovery recycles.
Fire retardant is aluminium hydroxide, is conducive to the flame retardant property for improving the building and ornament materials.
Light stabilizer is carbon black, can cover or reflect the substance of ultraviolet light.
Heat stabilizer is aluminum stearate, is conducive to the thermal stability for improving the building and ornament materials.
Compatilizer is maleic anhydride graft compatilizer, can improve inorganic filler and organic resin compatibility, improves this and builds
The intensity of ornament materials is built, rheological performance is improved.
The building and ornament materials of good flame resistance produced by the present invention have the advantages that energy conservation and environmental protection and good flame resistance.
Embodiment 2
A kind of building and ornament materials of good flame resistance, include the raw material of following weight：Waste plastic 34kg, flyash 42kg, stone
Feed powder 21kg, Corvic 13kg, bamboo fibre 6kg, boron carbide 15kg, calcium oxide 11kg, nickel oxide 12kg, peanut shell
6kg, furnace slag 17kg, fire retardant 0.6kg, light stabilizer 0.4kg, heat stabilizer 0.3kg and compatilizer 0.3kg.
A kind of preparation method of the building and ornament materials of good flame resistance, includes the following steps：
（1）Raw material is weighed according to the weight of the building and ornament materials raw material of good flame resistance；
（2）Waste plastic is added in plastic regenerator to get plastic grain；
（3）Peanut shell is added in pulverizer to get crushed material；
（4）By step（2）In plastic grain, step（3）In crushed material and other raw materials be added blender in, stir 30-
40min is to get mixture；
（5）By step（4）In mixed material heating to 280-300 DEG C, then be placed in the extruder of 4-5 atmospheric pressure and be squeezed into
Type, at normal temperatures timeliness 5-6 days.
Boron carbide is added in raw material, boron carbide is with fire resistance is good, intensity is high, thermal stability is good and chemical stability is good
The characteristics of.
Calcium oxide is added in raw material, calcium oxide has the advantages that fire resistance is good and stability is good.
Nickel oxide is added in raw material, nickel oxide has excellent fire resistance.
Peanut shell and furnace slag are added in raw material, the waste material of peanut shell and furnace slag as agricultural and industry is present to obtain
To cycling and reutilization, achieve the purpose that energy-saving and environment-friendly.
Waste plastic is waste polyurethane foamed plastics, has achieved the purpose that waste recovery recycles.
Fire retardant is aluminium hydroxide, is conducive to the flame retardant property for improving the building and ornament materials.
Light stabilizer is carbon black, can cover or reflect the substance of ultraviolet light.
Heat stabilizer is aluminum stearate, is conducive to the thermal stability for improving the building and ornament materials.
Compatilizer is maleic anhydride graft compatilizer, can improve inorganic filler and organic resin compatibility, improves this and builds
The intensity of ornament materials is built, rheological performance is improved.
The building and ornament materials of good flame resistance produced by the present invention have the advantages that energy conservation and environmental protection and good flame resistance.
Embodiment 3
A kind of building and ornament materials of good flame resistance, include the raw material of following weight：Waste plastic 31kg, flyash 36kg, stone
Feed powder 19kg, Corvic 10kg, bamboo fibre 5kg, boron carbide 13kg, calcium oxide 9kg, nickel oxide 10kg, peanut shell
5kg, furnace slag 15kg, fire retardant 0.5kg, light stabilizer 0.3kg, heat stabilizer 0.2kg and compatilizer 0.2kg.
A kind of preparation method of the building and ornament materials of good flame resistance, includes the following steps：
（1）Raw material is weighed according to the weight of the building and ornament materials raw material of good flame resistance；
（2）Waste plastic is added in plastic regenerator to get plastic grain；
（3）Peanut shell is added in pulverizer to get crushed material；
（4）By step（2）In plastic grain, step（3）In crushed material and other raw materials be added blender in, stir 30-
40min is to get mixture；
（5）By step（4）In mixed material heating to 280-300 DEG C, then be placed in the extruder of 4-5 atmospheric pressure and be squeezed into
Type, at normal temperatures timeliness 5-6 days.
Boron carbide is added in raw material, boron carbide is with fire resistance is good, intensity is high, thermal stability is good and chemical stability is good
The characteristics of.
Calcium oxide is added in raw material, calcium oxide has the advantages that fire resistance is good and stability is good.
Nickel oxide is added in raw material, nickel oxide has excellent fire resistance.
Peanut shell and furnace slag are added in raw material, the waste material of peanut shell and furnace slag as agricultural and industry is present to obtain
To cycling and reutilization, achieve the purpose that energy-saving and environment-friendly.
Waste plastic is waste polyurethane foamed plastics, has achieved the purpose that waste recovery recycles.
Fire retardant is aluminium hydroxide, is conducive to the flame retardant property for improving the building and ornament materials.
Light stabilizer is carbon black, can cover or reflect the substance of ultraviolet light.
Heat stabilizer is aluminum stearate, is conducive to the thermal stability for improving the building and ornament materials.
Compatilizer is maleic anhydride graft compatilizer, can improve inorganic filler and organic resin compatibility, improves this and builds
The intensity of ornament materials is built, rheological performance is improved.
The building and ornament materials of good flame resistance produced by the present invention have the advantages that energy conservation and environmental protection and good flame resistance.
Comparative example 1
A kind of building and ornament materials of good flame resistance, include the raw material of following weight：Waste plastic 32.5kg, flyash
37.5kg, stone powder 20kg, Corvic 10kg, bamboo fibre 5kg and fire retardant 0.5kg.
A kind of preparation method of the building and ornament materials of good flame resistance, includes the following steps：
（1）Raw material is weighed according to the weight of the building and ornament materials raw material of good flame resistance；
（2）Waste plastic is added in plastic regenerator to get plastic grain；
（3）By step（2）In plastic grain and other raw materials be added blender in, stirring 30-40min to get mixture；
（4）By step（3）In mixed material heating to 260-300 DEG C, then be placed in the extruder of 4-6 atmospheric pressure and be squeezed into
Type, at normal temperatures timeliness 4-6 days.
The building and ornament materials progressive of good flame resistance will be made in embodiment 1, embodiment 2, embodiment 3 and comparative example 1
It can test, test result is as shown in table 1：
| Index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 |
| Flame retardant rating | A grades | A grades | A grades | B1 |
From 1 data of table compare as can be seen that it is an advantage of the invention that：
1, a kind of building and ornament materials of good flame resistance and preparation method thereof, according to national standard《Construction material and product burns
Grading performance》GB862, the flame retardant rating that embodiment 1-3 is can be seen that from the flame retardant rating measured are superior to comparative example 1, explanation
The good flame resistance of the building and ornament materials of good flame resistance of the present invention.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although with reference to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution recorded in example is modified or equivalent replacement of some of the technical features, all essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (8)
1. a kind of building and ornament materials of good flame resistance, which is characterized in that include the raw material of following parts by weight：Waste plastic 28-
34 parts, 30-42 parts of flyash, 17-21 parts of stone powder, 7-13 parts of Corvic, 4-6 parts of bamboo fibre, boron carbide 11-15
Part, 7-11 parts of calcium oxide, 8-12 parts of nickel oxide, 4-6 parts of peanut shell, 13-17 parts of furnace slag, 0.4-0.6 parts of fire retardant, light are stablized
0.1-0.3 parts of 0.2-0.4 parts of agent, 0.1-0.3 parts of heat stabilizer and compatilizer.
2. the building and ornament materials of good flame resistance according to claim 1, which is characterized in that include the original of following parts by weight
Material：31 parts of waste plastic, 36 parts of flyash, 19 parts of stone powder, 10 parts of Corvic, 5 parts of bamboo fibre, 13 parts of boron carbide,
9 parts of calcium oxide, 10 parts of nickel oxide, 5 parts of peanut shell, 15 parts of furnace slag, 0.5 part of fire retardant, 0.3 part of light stabilizer, heat stabilizer
0.2 part and 0.2 part of compatilizer.
3. the building and ornament materials of good flame resistance according to claim 1, it is characterised in that：The waste plastic is discarded
Polyurethane foam plastics.
4. the building and ornament materials of good flame resistance according to claim 1, it is characterised in that：The fire retardant is hydroxide
Aluminium.
5. the building and ornament materials of good flame resistance according to claim 1, it is characterised in that：The light stabilizer is carbon
It is black.
6. the building and ornament materials of good flame resistance according to claim 1, it is characterised in that：The heat stabilizer is tristearin
Sour aluminium.
7. the building and ornament materials of good flame resistance according to claim 1, it is characterised in that：The compatilizer is maleic acid
Acid anhydride is grafted compatilizer.
8. a kind of preparation method of the building and ornament materials of good flame resistance as described in any one of claim 1-7, special
Sign is, includes the following steps：
（1）Raw material is weighed according to the parts by weight of the building and ornament materials raw material of good flame resistance；
（2）Waste plastic is added in plastic regenerator to get plastic grain；
（3）Peanut shell is added in pulverizer to get crushed material；
（4）By step（2）In plastic grain, step（3）In crushed material and other raw materials be added blender in, stir 30-
40min is to get mixture；
（5）By step（4）In mixed material heating to 280-300 DEG C, then be placed in the extruder of 4-5 atmospheric pressure and be squeezed into
Type, at normal temperatures timeliness 5-6 days.