CN110510938A - A kind of environmental and ecological fire resistant doorsets door panel - Google Patents
A kind of environmental and ecological fire resistant doorsets door panel Download PDFInfo
- Publication number
- CN110510938A CN110510938A CN201910862070.0A CN201910862070A CN110510938A CN 110510938 A CN110510938 A CN 110510938A CN 201910862070 A CN201910862070 A CN 201910862070A CN 110510938 A CN110510938 A CN 110510938A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- resistant doorsets
- fire resistant
- environmental
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environmental and ecological fire resistant doorsets door panels, including following raw material according to parts by weight: 42-54 parts of niobium yttrium mine tailing, 16-24 parts of plant fiber powder, 11-16 parts of Portland pozzolana cement, 12-15 parts of oleate, 3-5 parts of ZK-9 rubber powder, 1-2 parts of peregal, 2-3 parts of silicon powder, 3-5 parts of dry powder, 3-5 parts of fire retardant, 3-5 parts of organic short fiber, 10-25 parts of water, the application is with light foaming cement due to light, it is high-strength, energy conservation, benefit is useless, heat preservation, sound insulation, it is ageing-resistant, the performances such as nonflammable, it is mainly used in fire resistant doorsets product, first class fire resistant doorsets (requirement of fire resistant doorsets fire resistance period: first class is not less than 1.5h) requirement can be reached, and energy conservation and environmental protection, it is green non-poisonous harmless, long service life, application Can be good, prepare simple and convenient, raw material sources are extensive.
Description
Technical field
The present invention relates to fire resistant doorsets gate technique field, especially a kind of environmental and ecological fire resistant doorsets door panel.
Background technique
Fire resistant doorsets are by skeleton, and door core packing material and fire prevention hardware are constituted, and the packing material of door panel is fire resistant doorsets
Core material, quality and performance are particularly important.The packing material of existing door panel mostly use greatly rock wool, aluminium silicate wool, mineral wool,
The materials such as pearlite slab, foaming magnesium oxychloride cement plate, cement board.Aluminium silicate wool plate, rock wool, mineral wool or mineral wool class are anti-
Vent plate, although these material light weights, heat-insulated good, energy consumption is high in production process, is formed, was produced using organic adhesive
Pollution is generated in journey and use process, it is difficult to meet the requirement of environmental protection, when existing simultaneously anti-fire door core board globality poor, fire endurance
Between short, poor mechanical property, be easily deformed, the problems such as overall cost is higher, inconvenient to use.
Summary of the invention
Although the purpose of the present invention is to solve fire resistant doorsets door panel light weights in the prior art, heat-insulated good, production
Energy consumption is high in the process, is formed using organic adhesive, pollution is generated in production process and use process, it is difficult to meet the requirement of environmental protection
The defects of, a kind of environmental and ecological fire resistant doorsets door panel is provided.
The present invention is achieved by the following technical solutions:
A kind of environmental and ecological fire resistant doorsets door panel, including following raw material according to parts by weight: niobium yttrium mine tailing 42-54
Part, 16-24 parts of plant fiber powder, 11-16 parts of Portland pozzolana cement, 12-15 parts of oleate, 3-5 parts of ZK-9 rubber powder,
1-2 parts of peregal, 2-3 parts of silicon powder, 3-5 parts of dry powder, 3-5 parts of fire retardant, 3-5 parts of organic short fiber, 10-25 parts of water.
Preferably, a kind of environmental and ecological fire resistant doorsets door panel, including following raw material according to parts by weight: niobium yttrium mine tailing
50 parts, 20 parts of plant fiber powder, 12 parts of Portland pozzolana cement, 14 parts of oleate, 4 parts of ZK-9 rubber powder, peregal 2
Part, 2 parts of silicon powder, 4 parts of dry powder, 4 parts of fire retardant, 4 parts of organic short fiber, 20 parts of water.
Preferably, organic short fiber be polypropylene organic short fiber, 15~20 millimeters of fibre length.
Preferably, it is (20-80) mesh powder that plant fiber powder, which is granular size,.
Preferably, the fire retardant includes following raw material according to parts by weight: 30-40 parts of nano boric acid copper, hydroxide
8-15 parts of magnesium, 6-12 parts of aluminium hydroxide, 5-8 parts of carbon black pellet, 8-13 parts of zinc borate, 8-17 parts of diatomite, tartaric acid 10-20
Part.
Preferably, the fire retardant includes following raw material according to parts by weight: 35 parts of nano boric acid copper, magnesium hydroxide 10
Part, 10 parts of aluminium hydroxide, 6 parts of carbon black pellet, 9 parts of zinc borate, 13 parts of diatomite, 17 parts of tartaric acid.
A kind of manufacture craft of environmental and ecological fire resistant doorsets door panel, includes the following steps:
S1: straw is crushed as (20-80) mesh powder；
S2: niobium yttrium mine tailing, plant fiber powder, silicon powder, dry powder and suitable quantity of water are taken according to weight ratio, pours into stirring
In equipment, it is uniformly mixing to obtain paste；
S3: the oleate and peregal of above-mentioned parts by weight are added in the paste obtained in step s 2, continues to stir；
S4: Portland pozzolana cement is added in the mixture obtained in step s3 and suitable quantity of water is added stirs evenly
After successively fire retardant, organic staple fibers peacekeeping ZK-9 rubber powder be added stir evenly；
S5: modulus tool pours into the mixture that step S4 is obtained and strikes off；
S6: compression moulding, briquetting pressure 34-35MPa, it is 125-135 DEG C, kettle that Men Xin obtained, which is then placed in temperature,
Interior pressure is that steam press maintenance handles 75-85min in 1.05-1.15MPa steam pressure equipment.
The beneficial effect of fire-proof plate of the invention is: the application with light foaming cement due to it is light, high-strength,
The performances such as energy conservation, sharp useless, heat preservation, sound insulation, ageing-resistant, nonflammable, are mainly used in fire resistant doorsets product, can reach first class fire resistant doorsets
(requirement of fire resistant doorsets fire resistance period: first class is not less than 1.5h) requirement, and energy conservation and environmental protection, green non-poisonous harmless, service life
Long, application performance is good, prepares simple and convenient, and raw material sources are extensive.
Specific embodiment
In order to deepen the understanding of the present invention, the present invention will be described in further detail with reference to the examples below, the embodiment
For explaining only the invention, it is not intended to limit the scope of the present invention..
Embodiment 1
A kind of environmental and ecological fire resistant doorsets door panel, including following raw material according to parts by weight: 50 parts of niobium yttrium mine tailing is planted
20 parts of fibres powder, 12 parts of Portland pozzolana cement, 14 parts of oleate, 4 parts of ZK-9 rubber powder, 2 parts of peregal, silicon powder
2 parts, 4 parts of dry powder, 4 parts of fire retardant, 4 parts of organic short fiber, 20 parts of water.
Wherein, organic short fiber be polypropylene organic short fiber, 15~20 millimeters of fibre length.
Plant fiber powder is that granular size is (20-80) mesh powder.
The fire retardant includes following raw material according to parts by weight: 35 parts of nano boric acid copper, 10 parts of magnesium hydroxide, and hydrogen-oxygen
Change 10 parts of aluminium, 6 parts of carbon black pellet, 9 parts of zinc borate, 13 parts of diatomite, 17 parts of tartaric acid.
A kind of manufacture craft of environmental and ecological fire resistant doorsets door panel, includes the following steps:
S1: straw is crushed as (20-80) mesh powder；
S2: niobium yttrium mine tailing, plant fiber powder, silicon powder, dry powder and suitable quantity of water are taken according to weight ratio, pours into stirring
In equipment, it is uniformly mixing to obtain paste；
S3: the oleate and peregal of above-mentioned parts by weight are added in the paste obtained in step s 2, continues to stir；
S4: Portland pozzolana cement is added in the mixture obtained in step s3 and suitable quantity of water is added stirs evenly
After successively fire retardant, organic staple fibers peacekeeping ZK-9 rubber powder be added stir evenly；
S5: modulus tool pours into the mixture that step S4 is obtained and strikes off；
S6: compression moulding, briquetting pressure 34-35MPa, it is 125-135 DEG C, kettle that Men Xin obtained, which is then placed in temperature,
Interior pressure is that steam press maintenance handles 75-85min in 1.05-1.15MPa steam pressure equipment.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (7)
1. a kind of environmental and ecological fire resistant doorsets door panel, it is characterised in that: including following raw material according to parts by weight: niobium yttrium tailing
42-54 parts of powder, 16-24 parts of plant fiber powder, 11-16 parts of Portland pozzolana cement, 12-15 parts of oleate, ZK-9 glue
3-5 parts of powder, 1-2 parts of peregal, 2-3 parts of silicon powder, 3-5 parts of dry powder, 3-5 parts of fire retardant, 3-5 parts of organic short fiber, water 10-
25 parts.
2. a kind of environmental and ecological fire resistant doorsets door panel according to claim 1, it is characterised in that: including it is following by weight
The raw material of number meter: 50 parts of niobium yttrium mine tailing, 20 parts of plant fiber powder, 12 parts of Portland pozzolana cement, 14 parts of oleate,
4 parts of ZK-9 rubber powder, 2 parts of peregal, 2 parts of silicon powder, 4 parts of dry powder, 4 parts of fire retardant, 4 parts of organic short fiber, 20 parts of water.
3. a kind of environmental and ecological fire resistant doorsets door panel according to claim 1, it is characterised in that: organic short fiber is poly- third
Alkene organic short fiber, 15~20 millimeters of fibre length.
4. a kind of environmental and ecological fire resistant doorsets door panel according to claim 1, it is characterised in that: plant fiber powder is
Grain size is (20-80) mesh powder.
5. a kind of environmental and ecological fire resistant doorsets door panel according to claim 1, it is characterised in that: the fire retardant include with
Under raw material according to parts by weight: 30-40 parts of nano boric acid copper, 8-15 parts of magnesium hydroxide, 6-12 parts of aluminium hydroxide, carbon black pellet
5-8 parts, 8-13 parts of zinc borate, 8-17 parts of diatomite, 10-20 parts of tartaric acid.
6. a kind of environmental and ecological fire resistant doorsets door panel according to claim 5, it is characterised in that: the fire retardant include with
Under raw material according to parts by weight: 35 parts of nano boric acid copper, 10 parts of magnesium hydroxide, 10 parts of aluminium hydroxide, 6 parts of carbon black pellet, boron
9 parts of sour zinc, 13 parts of diatomite, 17 parts of tartaric acid.
7. a kind of manufacture craft of environmental and ecological fire resistant doorsets door panel, characterized by the following steps:
S1: straw is crushed as (20-80) mesh powder；
S2: niobium yttrium mine tailing, plant fiber powder, silicon powder, dry powder and suitable quantity of water are taken according to weight ratio, pours into mixing plant
In, it is uniformly mixing to obtain paste；
S3: the oleate and peregal of above-mentioned parts by weight are added in the paste obtained in step s 2, continues to stir；
S4: Portland pozzolana cement is added in the mixture obtained in step s3 and suitable quantity of water is added adds after mixing evenly
Enter successively fire retardant, organic staple fibers peacekeeping ZK-9 rubber powder to stir evenly；
S5: modulus tool pours into the mixture that step S4 is obtained and strikes off；
S6: compression moulding, briquetting pressure 34-35MPa, it is 125-135 DEG C, kettle internal pressure that Men Xin obtained, which is then placed in temperature,
75-85min is handled by force for steam press maintenance in 1.05-1.15MPa steam pressure equipment.