CN108787732B - 一种可分解土壤有机污染物的珍珠岩颗粒的制备方法 - Google Patents
一种可分解土壤有机污染物的珍珠岩颗粒的制备方法 Download PDFInfo
- Publication number
- CN108787732B CN108787732B CN201810426333.9A CN201810426333A CN108787732B CN 108787732 B CN108787732 B CN 108787732B CN 201810426333 A CN201810426333 A CN 201810426333A CN 108787732 B CN108787732 B CN 108787732B
- Authority
- CN
- China
- Prior art keywords
- perlite
- particles
- soil
- organic pollutants
- perlite particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种可分解土壤有机污染物的珍珠岩颗粒的制备方法，属于环境污染净化材料领域，包括下述步骤。珍珠岩覆膜：将无水乙醇、二水乙酸锌、水杨酸和1,4‑丁二醇在76℃回流，加入珍珠岩颗粒后继续回流，过滤后将滤饼恒温干燥，得到珍珠岩覆膜颗粒；水蒸汽处理：将珍珠岩覆膜颗粒经0.1~0.15Mpa水蒸汽处理，并在80℃恒温干燥；晶化成孔：在370~510℃煅烧2~4 h，冷却至室温，即制得珍珠岩颗粒，可用于分解土壤中的有机污染物。
Description
技术领域
本发明属于环境污染净化材料领域，具体涉及一种可分解土壤有机污染物的珍珠岩颗粒的制备方法。
背景技术
工业和民用废物污染的土壤中含有大量有机污染物，天然降解过程并不能完全使之分解并转化为无害物质，针对土壤有机污染的治理方法普遍效率较低。光催化氧化技术是一种新兴的污染治理方法，在水和大气污染中发挥了很大作用，然而在土壤治理中还没有得到有效的应用。这其中主要的问题就是如何向土壤中添加具有光催化活性的材料。常用的粉末光催化剂并不适于直接应用于土壤，因土壤的流动性会使粉末状光催化剂被土壤覆盖而失去活性。珍珠岩是一种天然轻质矿物，可改善土壤的透气和保水性能。珍珠岩质轻并含有大量孔隙，即使被土壤覆盖也会逐渐向土壤上层迁移而露出土壤表面。如果能够使珍珠岩颗粒具备在光照下降解土壤中有机污染物的能力，就会使该种材料得到更为广泛的应用，也很好地解决了治理有机污染土壤的目的。
发明内容
针对现有技术存在的问题，本发明旨在提供一种可分解土壤有机污染物的珍珠岩颗粒的制备方法，可以用于治理有机污染物污染的土壤并改善土壤性能。
采用的技术方案是：
一种可分解土壤有机污染物的珍珠岩颗粒的制备方法，其特征在于，包括以下步骤：
1. 珍珠岩覆膜
1.1在1L圆底烧瓶中加入520~580 mL无水乙醇、60~76 g二水乙酸锌、5~8 g水杨酸和21~25 mL 1,4-丁二醇，上述试剂均为纯料，以恒温电热包加热至76℃，在此温度下回流60 min；
1.2 向烧瓶中加入尺寸8~12mm的珍珠岩颗粒20g，继续在76℃回流60 min，冷却至室温；
1.3 将上述悬浮液过滤，将滤饼在110℃恒温电热箱中放置12h，得到珍珠岩覆膜颗粒。
2. 水蒸汽处理
2.1将珍珠岩覆膜颗粒移入压力蒸汽灭菌器中，保持蒸汽压力0.1~0.15Mpa，处理30~50 min后取出；
2.2 将步骤2.1得到的材料在80℃恒温电热箱中放置12h，得到干燥的珍珠岩颗粒。
3. 晶化成孔
3.1将珍珠岩颗粒置于程控箱式电炉中，在370~510℃煅烧2~4 h，冷却至室温，即制得可分解土壤有机污染物的珍珠岩颗粒。
与现有技术相比，本发明的优点在于：
本发明解决了在珍珠岩颗粒上涂覆具有光催化活性的氧化锌薄膜的技术。通过对原料组成和制备工艺的合理调控，制备的覆膜珍珠岩颗粒不仅保持多孔和轻质特点，而且可以在光照下分解土壤中的有机污染物。本发明制备的珍珠岩颗粒上的氧化锌薄膜与珍珠岩基体结合紧密，性能稳定，可以适用于处理各种有机污染物污染的土壤。
具体实施方式
实施例1
一种可分解土壤有机污染物的珍珠岩颗粒的制备方法，主要包括以下步骤：
1. 珍珠岩覆膜
1.1在1L圆底烧瓶中加入520 mL无水乙醇、60 g二水乙酸锌、5 g水杨酸和21 mL1,4-丁二醇，上述试剂均为纯料，以恒温电热包加热至76℃，在此温度下回流60 min；
1.2 向烧瓶中加入尺寸8~12 mm的珍珠岩颗粒20g，继续在76℃回流60 min，冷却至室温；
1.3 将上述悬浮液过滤，将滤饼在110℃恒温电热箱中放置12h，得到珍珠岩覆膜颗粒。
2. 水蒸汽处理
2.1将珍珠岩覆膜颗粒移入压力蒸汽灭菌器中，保持蒸汽压力0.1Mpa，处理30 min后取出；
2.2 将步骤2.1得到的材料在80℃恒温电热箱中放置12h，得到干燥的珍珠岩颗粒。
3. 晶化成孔
3.1将珍珠岩颗粒置于程控箱式电炉中，在370℃煅烧4 h，冷却至室温，即制得可分解土壤有机污染物的珍珠岩颗粒。
实施例2
一种可分解土壤有机污染物的珍珠岩颗粒的制备方法，主要包括以下步骤：
1. 珍珠岩覆膜
1.1在1L圆底烧瓶中加入550 mL无水乙醇、67 g二水乙酸锌、6 g水杨酸和23 mL1,4-丁二醇，上述试剂均为纯料，以恒温电热包加热至76℃，在此温度下回流60 min；
1.2 向烧瓶中加入尺寸8~12 mm的珍珠岩颗粒20g，继续在76℃回流60 min，冷却至室温；
1.3 将上述悬浮液过滤，将滤饼在110℃恒温电热箱中放置12h，得到珍珠岩覆膜颗粒。
2. 水蒸汽处理
2.1将珍珠岩覆膜颗粒移入压力蒸汽灭菌器中，保持蒸汽压力0.12Mpa，处理40min后取出；
2.2 将步骤2.1得到的材料在80℃恒温电热箱中放置12h，得到干燥的珍珠岩颗粒。
3. 晶化成孔
3.1将珍珠岩颗粒置于程控箱式电炉中，在430℃煅烧3 h，冷却至室温，即制得可分解土壤有机污染物的珍珠岩颗粒。
实施例3
一种可分解土壤有机污染物的珍珠岩颗粒的制备方法，主要包括以下步骤：
1. 珍珠岩覆膜
1.1在1L圆底烧瓶中加入580 mL无水乙醇、76 g二水乙酸锌、8 g水杨酸和25 mL1,4-丁二醇，上述试剂均为纯料，以恒温电热包加热至76℃，在此温度下回流60 min；
1.2 向烧瓶中加入尺寸8~12mm的珍珠岩颗粒20g，继续在76℃回流60 min，冷却至室温；
1.3 将上述悬浮液过滤，将滤饼在110℃恒温电热箱中放置12h，得到珍珠岩覆膜颗粒。
2. 水蒸汽处理
2.1将珍珠岩覆膜颗粒移入压力蒸汽灭菌器中，保持蒸汽压力0.15Mpa，处理50min后取出；
2.2 将步骤2.1得到的材料在80℃恒温电热箱中放置12h，得到干燥的珍珠岩颗粒。
3. 晶化成孔
3.1将珍珠岩颗粒置于程控箱式电炉中，在510℃煅烧2 h，冷却至室温，即制得可分解土壤有机污染物的珍珠岩颗粒。
Claims (1)
1.一种可分解土壤有机污染物的珍珠岩颗粒的制备方法，其特征在于，包括以下步骤：
珍珠岩覆膜
1.1在1L圆底烧瓶中加入520 ~ 580 mL无水乙醇、60 ~ 76 g二水乙酸锌、5 ~ 8 g水杨酸和21~ 25 mL 1,4-丁二醇，上述试剂均为纯料，以恒温电热包加热至76℃，在此温度下回流60min；
1.2 向烧瓶中加入尺寸8 ~ 12mm的珍珠岩颗粒20g，继续在76℃回流60 min，冷却至室
温；
1.3 将悬浮液过滤，将滤饼在110℃恒温电热箱中放置12h，得到珍珠岩覆膜颗粒；
水蒸汽处理
2.1将珍珠岩覆膜颗粒移入压力蒸汽灭菌器中，保持蒸汽压力0.1 ~ 0.15Mpa，处理30~ 50
min后取出；
2.2 将步骤2.1得到的材料在80℃恒温电热箱中放置12h，得到干燥的珍珠岩颗粒；
晶化成孔
3.1将珍珠岩颗粒置于程控箱式电炉中，在370 ~ 510℃煅烧2 ~ 4 h，冷却至室温，即制得
可分解土壤有机污染物的珍珠岩颗粒。