CN108775031A - 自粘防水卷材及制备方法 - Google Patents

自粘防水卷材及制备方法 Download PDF

Info

Publication number
CN108775031A
CN108775031A CN201810668779.2A CN201810668779A CN108775031A CN 108775031 A CN108775031 A CN 108775031A CN 201810668779 A CN201810668779 A CN 201810668779A CN 108775031 A CN108775031 A CN 108775031A
Authority
CN
China
Prior art keywords
dosage
parts
agent
adhesive
self
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810668779.2A
Other languages
English (en)
Inventor
黄万香
丁露
季军鹏
徐国兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Xinglong Waterproof And Thermal Insulation Material Co Ltd
Original Assignee
Wuhu Xinglong Waterproof And Thermal Insulation Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Xinglong Waterproof And Thermal Insulation Material Co Ltd filed Critical Wuhu Xinglong Waterproof And Thermal Insulation Material Co Ltd
Priority to CN201810668779.2A priority Critical patent/CN108775031A/zh
Publication of CN108775031A publication Critical patent/CN108775031A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供了一种自粘防水卷材及制备方法，该自粘橡胶沥青防水卷材包括依次包括聚四氟乙烯薄膜、自粘橡胶沥青防水层、隔离层；其中，制备所述自粘橡胶沥青防水层的原料包括苯乙烯‑丁二烯‑苯乙烯橡胶改性沥青、软化剂、填充剂及消泡剂；其中，制备所述隔离层的原料包括三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂；其中，所述助剂包括促进剂及补强剂；其中，以质量份数计，所述三元乙丙橡胶的用量为60‑80份，所述聚异丁烯橡胶的用量为40‑60份，所述超细碳酸钙的用量为10‑20份，所述抗氧剂的用量为1‑2份，所述促进剂的用量为0.5‑1.5份，所述补强剂的用量为0.5‑1.5份。该自粘防水卷材抗腐蚀抗氧化能力强。

Description

自粘防水卷材及制备方法
技术领域
本发明属于防水领域，更具体地，涉及一种自粘防水卷材及制备方法。
背景技术
防水卷材主要是用于建筑墙体、屋面、以及隧道、公路、垃圾填埋场等处，起到抵御外界雨水、地下水渗漏的一种可卷曲成卷状的柔性建材产品，作为工程基础与建筑物之间无渗漏连接，是整个工程防水的第一道屏障，对整个工程起着至关重要的作用。产品主要有沥青防水卷材和高分子防水卷材，但是目前市面上的这些种类的防水卷材在实际的使用中会出现耐热性、耐候性、耐臭氧性、耐化学腐蚀性、耐低温柔性和弹塑性能都比较弱，抗撕裂的性能也比较弱，因此使用的寿命很短，虽然拥有如此多的弱点，但是由于目前防水卷材的技术医乏，因此可选度很低。
因此有必要研发一种抗腐蚀、抗氧化能力强的自粘防水卷材及制备方法。
发明内容
本发明的目的是提供一种自粘防水卷材及制备方法，该自粘防水卷材抗腐蚀能力强。
为了实现上述目的，根据本发明的一方面提供了一种自粘防水卷材，该自粘橡胶沥青防水卷材包括依次包括聚四氟乙烯薄膜、自粘橡胶沥青防水层、隔离层；
其中，制备所述自粘橡胶沥青防水层的原料包括苯乙烯-丁二烯-苯乙烯橡胶改性沥青、软化剂、填充剂及消泡剂；
其中，制备所述隔离层的原料包括三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂；
其中，所述助剂包括促进剂及补强剂；
其中，以质量份数计，所述三元乙丙橡胶的用量为60-80份，所述聚异丁烯橡胶的用量为40-60份，所述超细碳酸钙的用量为10-20份，所述抗氧剂的用量为1-2份，所述促进剂的用量为0.5-1.5份，所述补强剂的用量为0.5-1.5份。。
优选地，所述软化剂为邻苯二甲酸二丁酯，所述填充剂为滑石粉，所述消泡剂为炭黑。
优选地，以质量分数计，所述苯乙烯-丁二烯-苯乙烯橡胶改性沥青的用量为100份，所述邻苯二甲酸二丁酯的用量为0-5份，所述滑石粉的用量为20-30份，所述炭黑的用量为3-7份。
优选地，制备所述聚四氟乙烯薄膜的原料包括环氧树脂、固化剂、光稳剂及增塑剂。
优选地，所述固化剂为聚酰胺固化剂和/或聚醚胺固化剂。
优选地，以质量分数计，所述环氧树脂的用量为90-100份，所述聚酰胺固化剂的用量为20-30份，所述光稳剂用量为2-5份，所述增塑剂用量为30-45份。
优选地，以质量分数计，所述环氧树脂的用量为90-100份，所述聚酰胺固化剂的用量为10-20份，所述聚醚胺固化剂的用量为10-20份，所述光稳剂用量为2-5份，所述增塑剂用量为30-45份。
根据本发明的另一方面提供了一种自粘防水卷材制备方法，包括：
将苯乙烯-丁二烯-苯乙烯橡胶改性沥青加热，依次加入软化剂、消泡剂搅拌后经二次氧化处理，加入填充剂搅拌，制备获取自粘橡胶沥青防水层；
在自粘橡胶沥青防水层下表面铺设隔离层；
在自粘橡胶沥青防水层上表面铺设聚四氟乙烯薄膜，制备获取自粘防水卷材。
优选地，在自粘橡胶沥青防水层下表面铺设隔离层包括：
将三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂经混炼、压延、挤出制备隔离层；
将隔离层设置在自粘橡胶沥青防水层的下表面。
优选地，在自粘橡胶沥青防水层上表面铺设聚四氟乙烯薄膜包括：
将环氧树脂、固化剂、光稳剂及增塑剂共混搅拌，涂覆在自粘橡胶沥青防水层上表面，在60℃-70℃的条件下，固化形成聚四氟乙烯薄膜。
本发明的其它特征和优点将在随后具体实施方式部分予以详细说明。
具体实施方式
下面将更详细地描述本发明的优选实施方式。虽然以下描述了本发明的优选实施方式，然而应该理解，可以以各种形式实现本发明而不应被这里阐述的实施方式所限制。相反，提供这些实施方式是为了使本发明更加透彻和完整，并且能够将本发明的范围完整地传达给本领域的技术人员。
根据本发明的一方面提供了一种自粘防水卷材，该自粘橡胶沥青防水卷材包括依次包括聚四氟乙烯薄膜、自粘橡胶沥青防水层、隔离层；
其中，制备所述自粘橡胶沥青防水层的原料包括苯乙烯-丁二烯-苯乙烯橡胶改性沥青、软化剂、填充剂及消泡剂；
其中，制备所述隔离层的原料包括三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂；
其中，所述助剂包括促进剂及补强剂；
其中，以质量份数计，所述三元乙丙橡胶的用量为60-80份，所述聚异丁烯橡胶的用量为40-60份，所述超细碳酸钙的用量为10-20份，所述抗氧剂的用量为1-2份，所述促进剂的用量为0.5-1.5份，所述补强剂的用量为0.5-1.5份。。
作为优选方案，所述软化剂为邻苯二甲酸二丁酯，所述填充剂为滑石粉，所述消泡剂为炭黑。
作为优选方案，以质量分数计，所述苯乙烯-丁二烯-苯乙烯橡胶改性沥青的用量为100份，所述邻苯二甲酸二丁酯的用量为0-5份，所述滑石粉的用量为20-30份，所述炭黑的用量为3-7份。
作为优选方案，制备所述聚四氟乙烯薄膜的原料包括环氧树脂、固化剂、光稳剂及增塑剂。
作为优选方案，所述固化剂为聚酰胺固化剂和/或聚醚胺固化剂。
作为优选方案，以质量分数计，所述环氧树脂的用量为90-100份，所述聚酰胺固化剂的用量为20-30份，所述光稳剂用量为2-5份，所述增塑剂用量为30-45份。
作为优选方案，以质量分数计，所述环氧树脂的用量为90-100份，所述聚酰胺固化剂的用量为10-20份，所述聚醚胺固化剂的用量为10-20份，所述光稳剂用量为2-5份，所述增塑剂用量为30-45份。
根据本发明的另一方面提供了一种自粘防水卷材制备方法，包括：
将苯乙烯-丁二烯-苯乙烯橡胶改性沥青加热，依次加入软化剂、消泡剂搅拌后经二次氧化处理，加入填充剂搅拌，制备获取自粘橡胶沥青防水层；
在自粘橡胶沥青防水层下表面铺设隔离层；
在自粘橡胶沥青防水层上表面铺设聚四氟乙烯薄膜，制备获取自粘防水卷材。
作为优选方案，在自粘橡胶沥青防水层下表面铺设隔离层包括：
将三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂经混炼、压延、挤出制备隔离层；
将隔离层设置在自粘橡胶沥青防水层的下表面。
作为优选方案，在自粘橡胶沥青防水层上表面铺设聚四氟乙烯薄膜包括：
将环氧树脂、固化剂、光稳剂及增塑剂共混搅拌，涂覆在自粘橡胶沥青防水层上表面，在60℃-70℃的条件下，固化形成聚四氟乙烯薄膜。】
实施例1
一种自粘防水卷材，该自粘橡胶沥青防水卷材包括依次包括聚四氟乙烯薄膜、自粘橡胶沥青防水层、隔离层。
其中，制备聚四氟乙烯薄膜，以质量分数计，所述环氧树脂的用量为90份，所述聚酰胺固化剂的用量为30份，所述光稳剂用量为2份，所述增塑剂用量为45份。
其中，制备自粘橡胶沥青防水层，以质量分数计，所述苯乙烯-丁二烯-苯乙烯橡胶改性沥青的用量为100份，所述邻苯二甲酸二丁酯的用量为0份，所述滑石粉的用量为20份，所述炭黑的用量为7份。
其中，制备隔离层，以质量份数计，所述三元乙丙橡胶的用量为60份，所述聚异丁烯橡胶的用量为60份，所述超细碳酸钙的用量为10份，所述抗氧剂的用量为2份，所述促进剂的用量为0.5份，所述补强剂的用量为1.5份。
实施例2
一种自粘防水卷材，该自粘橡胶沥青防水卷材包括依次包括聚四氟乙烯薄膜、自粘橡胶沥青防水层、隔离层。
其中，制备聚四氟乙烯薄膜，，以质量分数计，所述环氧树脂的用量为100份，所述聚酰胺固化剂的用量为20份，所述光稳剂用量为5份，所述增塑剂用量为30份。
其中，制备自粘橡胶沥青防水层，以质量分数计，所述苯乙烯-丁二烯-苯乙烯橡胶改性沥青的用量为100份，所述邻苯二甲酸二丁酯的用量为0份，所述滑石粉的用量为30份，所述炭黑的用量为3份。
其中，制备隔离层，以质量份数计，所述三元乙丙橡胶的用量为80份，所述聚异丁烯橡胶的用量为40份，所述超细碳酸钙的用量为20份，所述抗氧剂的用量为1份，所述促进剂的用量为1.5份，所述补强剂的用量为0.5份。
实施例3
一种自粘防水卷材，该自粘橡胶沥青防水卷材包括依次包括聚四氟乙烯薄膜、自粘橡胶沥青防水层、隔离层。
其中，制备聚四氟乙烯薄膜，以质量分数计，所述环氧树脂的用量为95份，所述聚酰胺固化剂的用量为25份，所述光稳剂用量为3份，所述增塑剂用量为40份。
其中，制备自粘橡胶沥青防水层，以质量分数计，所述苯乙烯-丁二烯-苯乙烯橡胶改性沥青的用量为100份，所述邻苯二甲酸二丁酯的用量为3份，所述滑石粉的用量为5份，所述炭黑的用量为4份。
其中，制备隔离层，以质量份数计，所述三元乙丙橡胶的用量为70份，所述聚异丁烯橡胶的用量为50份，所述超细碳酸钙的用量为15份，所述抗氧剂的用量为1份，所述促进剂的用量为1份，所述补强剂的用量为1份。
测试例
将传动防水卷材及实施例1-实施例3的耐候性改性沥青防水卷材切取20*20cm方形块，至于PH值为1-3、氧气浓度50％、潮湿条件下24h，而后测量防水卷材性能。测量结果见表1
表1卷材性能测试结果
以上已经描述了本发明的各实施例，上述说明是示例性的，并非穷尽性的，并且也不限于所披露的各实施例。在不偏离所说明的各实施例的范围和精神的情况下，对于本技术领域的普通技术人员来说许多修改和变更都是显而易见的。

Claims (10)

1.一种自粘防水卷材，其特征在于，该自粘橡胶沥青防水卷材包括依次包括聚四氟乙烯薄膜、自粘橡胶沥青防水层、隔离层；
其中，制备所述自粘橡胶沥青防水层的原料包括苯乙烯-丁二烯-苯乙烯橡胶改性沥青、软化剂、填充剂及消泡剂；
其中，制备所述隔离层的原料包括三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂；
其中，所述助剂包括促进剂及补强剂；
其中，以质量份数计，所述三元乙丙橡胶的用量为60-80份，所述聚异丁烯橡胶的用量为40-60份，所述超细碳酸钙的用量为10-20份，所述抗氧剂的用量为1-2份，所述促进剂的用量为0.5-1.5份，所述补强剂的用量为0.5-1.5份。
2.根据权利要求1所述的自粘防水卷材，其特征在于，所述软化剂为邻苯二甲酸二丁酯，所述填充剂为滑石粉，所述消泡剂为炭黑。
3.根据权利要求1所述的自粘防水卷材，其特征在于，以质量分数计，所述苯乙烯-丁二烯-苯乙烯橡胶改性沥青的用量为100份，所述邻苯二甲酸二丁酯的用量为0-5份，所述滑石粉的用量为20-30份，所述炭黑的用量为3-7份。
4.根据权利要求1所述的自粘防水卷材，其特征在于，制备所述聚四氟乙烯薄膜的原料包括环氧树脂、固化剂、光稳剂及增塑剂。
5.根据权利要求4所述的自粘防水卷材，其特征在于，所述固化剂为聚酰胺固化剂和/或聚醚胺固化剂。
6.根据权利要求5所述的自粘防水卷材，其特征在于，以质量分数计，所述环氧树脂的用量为90-100份，所述聚酰胺固化剂的用量为20-30份，所述光稳剂用量为2-5份，所述增塑剂用量为30-45份。
7.根据权利要求5所述的自粘防水卷材，其特征在于，以质量分数计，所述环氧树脂的用量为90-100份，所述聚酰胺固化剂的用量为10-20份，所述聚醚胺固化剂的用量为10-20份，所述光稳剂用量为2-5份，所述增塑剂用量为30-45份。
8.一种自粘防水卷材制备方法，其特征在于，包括：
将苯乙烯-丁二烯-苯乙烯橡胶改性沥青加热，依次加入软化剂、消泡剂搅拌后经二次氧化处理，加入填充剂搅拌，制备获取自粘橡胶沥青防水层；
在自粘橡胶沥青防水层下表面铺设隔离层；
在自粘橡胶沥青防水层上表面铺设聚四氟乙烯薄膜，制备获取自粘防水卷材。
9.根据权利要求8所述的自粘防水卷材制备方法，其特征在于，在自粘橡胶沥青防水层下表面铺设隔离层包括：
将三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂经混炼、压延、挤出制备隔离层；
将隔离层设置在自粘橡胶沥青防水层的下表面。
10.根据权利要求9所述的自粘防水卷材制备方法，其特征在于，在自粘橡胶沥青防水层上表面铺设聚四氟乙烯薄膜包括：
将环氧树脂、固化剂、光稳剂及增塑剂共混搅拌，涂覆在自粘橡胶沥青防水层上表面，在60℃-70℃的条件下，固化形成聚四氟乙烯薄膜。
CN201810668779.2A 2018-06-26 2018-06-26 自粘防水卷材及制备方法 Withdrawn CN108775031A (zh)