CN109021849A - 耐候性改性沥青防水卷材及制备方法 - Google Patents

耐候性改性沥青防水卷材及制备方法 Download PDF

Info

Publication number
CN109021849A
CN109021849A CN201810668765.0A CN201810668765A CN109021849A CN 109021849 A CN109021849 A CN 109021849A CN 201810668765 A CN201810668765 A CN 201810668765A CN 109021849 A CN109021849 A CN 109021849A
Authority
CN
China
Prior art keywords
dosage
modified
parts
weatherability
app
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810668765.0A
Other languages
English (en)
Inventor
黄万香
丁露
季军鹏
徐国兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Xinglong Waterproof And Thermal Insulation Material Co Ltd
Original Assignee
Wuhu Xinglong Waterproof And Thermal Insulation Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Xinglong Waterproof And Thermal Insulation Material Co Ltd filed Critical Wuhu Xinglong Waterproof And Thermal Insulation Material Co Ltd
Priority to CN201810668765.0A priority Critical patent/CN109021849A/zh
Publication of CN109021849A publication Critical patent/CN109021849A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供了一种耐候性改性沥青防水卷材及制备方法，该耐候性改性沥青防水卷材依次包括隔离层、塑性体改性沥青涂层、胎基层、塑性体改性沥青涂层、隔离层；其中，制备所述塑性体改性沥青涂层的原料包括100#石油沥青、改性胶粉、无规聚丙烯、偶联剂及填充剂；其中，制备所述胎基层的原料包括玻纤增强聚酯毡、玻纤毡、聚酯毡中的至少一种；其中，制备所述隔离层的原料包括三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂。该耐候性改性沥青防水卷材耐候性、耐低温性更佳。

Description

耐候性改性沥青防水卷材及制备方法
技术领域
本发明属于防水领域，更具体地，涉及一种耐候性改性沥青防水卷材及制备方法。
背景技术
防水卷材主要是用于建筑墙体、屋面、以及隧道、公路、垃圾填埋场等处，起到抵御外界雨水、地下水渗漏的一种可卷曲成卷状的柔性建材产品，作为工程基础与建筑物之间无渗漏连接，是整个工程防水的第一道屏障，对整个工程起着至关重要的作用。产品主要有沥青防水卷材和高分子防水卷材，但是目前市面上的这些种类的防水卷材在实际的使用中会出现耐热性、耐候性、耐臭氧性、耐化学腐蚀性、耐低温柔性和弹塑性能都比较弱，抗撕裂的性能也比较弱，因此使用的寿命很短，虽然拥有如此多的弱点，但是由于目前防水卷材的技术医乏，因此可选度很低。
因此有必要研发一种耐候性强、耐低温的耐候性改性沥青防水卷材及制备方法。
发明内容
本发明的目的是提供一种耐候性改性沥青防水卷材及制备方法，该耐候性改性沥青防水卷材耐候性强，耐低温效果佳。
为了实现上述目的，根据本发明的一方面提供了一种耐候性改性沥青防水卷材，该耐候性改性沥青防水卷材依次包括隔离层、塑性体改性沥青涂层、胎基层、塑性体改性沥青涂层、隔离层；
其中，制备所述塑性体改性沥青涂层的原料包括100#石油沥青、改性胶粉、无规聚丙烯、偶联剂及填充剂；
其中，制备所述胎基层的原料包括玻纤增强聚酯毡、玻纤毡、聚酯毡中的至少一种；
其中，制备所述隔离层的原料包括三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂。
优选地，以质量份数计，所述100#石油沥青的用量为90-100份，所述改性胶粉的用量为10-20份，所述无规聚丙烯的用量为10-20份，所述偶联剂的用量为3-5份，所述填充剂的用量为20-30份。
优选地，所述填充剂为滑石粉，所述偶联剂为硅烷偶联剂。
优选地，制备所述改性胶粉的原料包括硅藻土、甲基环氧氯丙烷、环氧丙醇、溶剂、PH调整剂。
优选地，以质量份数计，所述硅藻土的用量为80-90份，所述甲基环氧氯丙烷的用量为25-35份，所述甲基环氧氯丙烷的用量为20-30份。
优选地，所述助剂包括促进剂及补强剂，以质量份数计，所述三元乙丙橡胶的用量为30-50份，所述聚异丁烯橡胶的用量为60-80份，所述超细碳酸钙的用量为10-20份，所述抗氧剂的用量为1-2份，所述促进剂的用量为0.5-1.5份，所述补强剂的用量为0.5-1.5份。
根据本发明的另一方面提供了一种耐候性改性沥青防水卷材的制备方法，其特征在于，包括：
制备胎基层，制备改性胶粉；
将100#石油沥青及偶联剂在150-200℃条件下共混；
加入改性胶粉、无规聚丙烯及填充剂，制备塑性体改性沥青；
将塑性体改性沥青涂覆在胎基层上，形成塑性体改性沥青涂层；
制备隔离层，通过隔离层包覆所述塑性体改性沥青涂层。
优选地，制备改性胶粉包括：
将基环氧氯丙烷、环氧丙醇加入到溶剂中；
加入PH调整剂，调节PH值至2-4；
加入硅藻土搅拌、过滤、烘干制得改性胶粉。
优选地，制备隔离层包括将三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂经混炼、压延、挤出制备隔离层。
本发明的有益效果在于：通过特定的配方制备耐候性改性沥青防水卷材，使其耐候性、耐低温性能能更佳。
本发明的其它特征和优点将在随后具体实施方式部分予以详细说明。
具体实施方式
下面将更详细地描述本发明的优选实施方式。虽然以下描述了本发明的优选实施方式，然而应该理解，可以以各种形式实现本发明而不应被这里阐述的实施方式所限制。相反，提供这些实施方式是为了使本发明更加透彻和完整，并且能够将本发明的范围完整地传达给本领域的技术人员。
根据本发明的一方面提供了一种耐候性改性沥青防水卷材，该耐候性改性沥青防水卷材依次包括隔离层、塑性体改性沥青涂层、胎基层、塑性体改性沥青涂层、隔离层；
其中，制备所述塑性体改性沥青涂层的原料包括100#石油沥青、改性胶粉、无规聚丙烯、偶联剂及填充剂；
其中，制备所述胎基层的原料包括玻纤增强聚酯毡、玻纤毡、聚酯毡中的至少一种；
其中，制备所述隔离层的原料包括三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂。
作为优选方案，以质量份数计，所述100#石油沥青的用量为90-100份，所述改性胶粉的用量为10-20份，所述无规聚丙烯的用量为10-20份，所述偶联剂的用量为3-5份，所述填充剂的用量为20-30份。
作为优选方案，所述填充剂为滑石粉，所述偶联剂为硅烷偶联剂。
作为优选方案，制备所述改性胶粉的原料包括硅藻土、甲基环氧氯丙烷、环氧丙醇、溶剂、PH调整剂。
作为优选方案，以质量份数计，所述硅藻土的用量为80-90份，所述甲基环氧氯丙烷的用量为25-35份，所述甲基环氧氯丙烷的用量为20-30份。
作为优选方案，所述助剂包括促进剂及补强剂，以质量份数计，所述三元乙丙橡胶的用量为30-50份，所述聚异丁烯橡胶的用量为60-80份，所述超细碳酸钙的用量为10-20份，所述抗氧剂的用量为1-2份，所述促进剂的用量为0.5-1.5份，所述补强剂的用量为0.5-1.5份。
根据本发明的另一方面提供了一种耐候性改性沥青防水卷材的制备方法，其特征在于，包括：
制备胎基层，制备改性胶粉；
将100#石油沥青及偶联剂在150-200℃条件下共混；
加入改性胶粉、无规聚丙烯及填充剂，制备塑性体改性沥青；
将塑性体改性沥青涂覆在胎基层上，形成塑性体改性沥青涂层；
制备隔离层，通过隔离层包覆所述塑性体改性沥青涂层。
作为优选方案，制备改性胶粉包括：
将基环氧氯丙烷、环氧丙醇加入到溶剂中；
加入PH调整剂，调节PH值至2-4；
加入硅藻土搅拌、过滤、烘干制得改性胶粉。
作为优选方案，制备隔离层包括将三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂经混炼、压延、挤出制备隔离层。
本发明的有益效果在于：通过特定的配方制备耐候性改性沥青防水卷材，使其耐候性、耐低温性能能更佳。
实施例1
一种耐候性改性沥青防水卷材依次包括隔离层、塑性体改性沥青涂层、胎基层、塑性体改性沥青涂层、隔离层；
其中，塑性体改性沥青涂以质量份数计，所述100#石油沥青的用量为100份，所述改性胶粉的用量为10份，所述无规聚丙烯的用量为20份，所述偶联剂的用量为3份，所述填充剂的用量为30份。
其中，隔离层以质量份数计，所述三元乙丙橡胶的用量为30份，所述聚异丁烯橡胶的用量为80份，所述超细碳酸钙的用量为10份，所述抗氧剂的用量为2份，所述促进剂的用量为0.5份，所述补强剂的用量为1.5份。
实施例2
一种耐候性改性沥青防水卷材依次包括隔离层、塑性体改性沥青涂层、胎基层、塑性体改性沥青涂层、隔离层；
其中，塑性体改性沥青涂以质量份数计，所述100#石油沥青的用量为90份，所述改性胶粉的用量为20份，所述无规聚丙烯的用量为10份，所述偶联剂的用量为3-5份，所述填充剂的用量为30份。
其中，隔离层以质量份数计，所述三元乙丙橡胶的用量为30份，所述聚异丁烯橡胶的用量为80份，所述超细碳酸钙的用量为10份，所述抗氧剂的用量为2份，所述促进剂的用量为0.55份，所述补强剂的用量为0.5份。
实施例3
一种耐候性改性沥青防水卷材依次包括隔离层、塑性体改性沥青涂层、胎基层、塑性体改性沥青涂层、隔离层；
其中，塑性体改性沥青涂以质量份数计，所述100#石油沥青的用量为100份，所述改性胶粉的用量为10份，所述无规聚丙烯的用量为15份，所述偶联剂的用量为4份，所述填充剂的用量为25份。
其中，隔离层以质量份数计，所述三元乙丙橡胶的用量为40份，所述聚异丁烯橡胶的用量为65份，所述超细碳酸钙的用量为15份，所述抗氧剂的用量为1份，所述促进剂的用量为1份，所述补强剂的用量为1份。
测试例
将传动防水卷材及实施例1-实施例3的耐候性改性沥青防水卷材切取20*20cm方形块，至于零下50摄氏度8h，而后测量防水卷材性能。测量结果见表1
表1卷材性能测试结果
以上已经描述了本发明的各实施例，上述说明是示例性的，并非穷尽性的，并且也不限于所披露的各实施例。在不偏离所说明的各实施例的范围和精神的情况下，对于本技术领域的普通技术人员来说许多修改和变更都是显而易见的。

Claims (9)

1.一种耐候性改性沥青防水卷材，其特征在于，该耐候性改性沥青防水卷材依次包括隔离层、塑性体改性沥青涂层、胎基层、塑性体改性沥青涂层、隔离层；
其中，制备所述塑性体改性沥青涂层的原料包括100#石油沥青、改性胶粉、无规聚丙烯、偶联剂及填充剂；
其中，制备所述胎基层的原料包括玻纤增强聚酯毡、玻纤毡、聚酯毡中的至少一种；
其中，制备所述隔离层的原料包括三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂。
2.根据权利要求1所述的耐候性改性沥青防水卷材，其特征在于，以质量份数计，所述100#石油沥青的用量为90-100份，所述改性胶粉的用量为10-20份，所述无规聚丙烯的用量为10-20份，所述偶联剂的用量为3-5份，所述填充剂的用量为20-30份。
3.根据权利要求2所述的耐候性改性沥青防水卷材，其特征在于，所述填充剂为滑石粉，所述偶联剂为硅烷偶联剂。
4.根据权利要求2所述的耐候性改性沥青防水卷材，其特征在于，制备所述改性胶粉的原料包括硅藻土、甲基环氧氯丙烷、环氧丙醇、溶剂、PH调整剂。
5.根据权利要求4所述的耐候性改性沥青防水卷材，其特征在于，以质量份数计，所述硅藻土的用量为80-90份，所述甲基环氧氯丙烷的用量为25-35份，所述甲基环氧氯丙烷的用量为20-30份。
6.根据权利要求1所述的耐候性改性沥青防水卷材，其特征在于，所述助剂包括促进剂及补强剂，以质量份数计，所述三元乙丙橡胶的用量为30-50份，所述聚异丁烯橡胶的用量为60-80份，所述超细碳酸钙的用量为10-20份，所述抗氧剂的用量为1-2份，所述促进剂的用量为0.5-1.5份，所述补强剂的用量为0.5-1.5份。
7.一种基于权利要求1-6中任意一项所述的耐候性改性沥青防水卷材的制备方法，其特征在于，包括：
制备胎基层，制备改性胶粉；
将100#石油沥青及偶联剂在150-200℃条件下共混；
加入改性胶粉、无规聚丙烯及填充剂，制备塑性体改性沥青；
将塑性体改性沥青涂覆在胎基层上，形成塑性体改性沥青涂层；
制备隔离层，通过隔离层包覆所述塑性体改性沥青涂层。
8.根据权利要7所述的制备方法，其特征在于，制备改性胶粉包括：
将基环氧氯丙烷、环氧丙醇加入到溶剂中；
加入PH调整剂，调节PH值至2-4；
加入硅藻土搅拌、过滤、烘干制得改性胶粉。
9.根据权利要7所述的制备方法，其特征在于，制备隔离层包括将三元乙丙橡胶、聚异丁烯橡胶、超细碳酸钙、抗氧剂及助剂经混炼、压延、挤出制备隔离层。
CN201810668765.0A 2018-06-26 2018-06-26 耐候性改性沥青防水卷材及制备方法 Withdrawn CN109021849A (zh)