CN108754802A - The weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying - Google Patents
The weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying Download PDFInfo
- Publication number
- CN108754802A CN108754802A CN201810587790.6A CN201810587790A CN108754802A CN 108754802 A CN108754802 A CN 108754802A CN 201810587790 A CN201810587790 A CN 201810587790A CN 108754802 A CN108754802 A CN 108754802A
- Authority
- CN
- China
- Prior art keywords
- fabric
- warming
- needle
- draw textured
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of weaving methods of the warming chamois flannel face fabric of water-absorbing fast-drying, include the following steps：One Double-plate machine is provided, arranges trigonometric sum knitting needle as requested；Yarn is provided, yarn includes island draw textured yarn, terylene draw textured yarn, spandex；Step is woven, is woven using one, three tunnel cycle：The first via is using island draw textured yarn and is lining into spandex braiding fabric internal layer；Second tunnel is lining into spandex using terylene draw textured yarn and weaves fabric outer layer, and latitude flat structure is formed in outer layer；Third road uses terylene draw textured yarn to connect yarn, to connect fabric internal layer and outer layer.The fabric that the present invention is woven has good heat-preserving function, can effectively control human body wet-heat durability.
Description
Technical field
The present invention relates to fields such as textile fabrics, the weaving square of the warming chamois flannel face fabric of specially a kind of water-absorbing fast-drying
Method.
Background technology
Rapid-curing cutback knitting fabric is generally used for rapid-curing cutback clothing.Rapid-curing cutback clothing major function：Rapid-curing cutback clothing answers outdoor use environment
It is required that generate.Under normal circumstances, rapid-curing cutback clothing can be put on when spring and summer replaces, they are compared with thick and heavy charge garment at this time
Facilitate, it is much practical.The major function of rapid-curing cutback clothing is rapid perspiration, that is, the sweat gone out on skin is absorbed rapidly, is expanded
It dissipates, and evaporation rate is accelerated by enlarged-area as far as possible.Ordinary movement dress is worn, takes exercise and is transferred to rest shape at once after perspiring
State, can be sick because of the variation of human body temperature.And can to dissipate wet and warmth retention property good for rapid-curing cutback clothing, is conducive to keep dry skin clear
It is refreshing.It is important to mention when doing outdoor sports, rapid-curing cutback clothing can play better effect at windproof, rain-proof, damp proof aspect.
And most of current season in spring and autumn fabric only has single heat-preserving function, and lack water-absorbing fast-drying function, due to
It is damp and hot to cause manufactured clothes dress experience very poor.Therefore, there is not also a fabric that can be suitable for spring and autumn on the market at present
Section, is allowed to adapt to this cold and hot Changes in weather, also has the effect of water-absorbing fast-drying while making it have warmth retention property, can be effective
The effect of controlling human body wet-heat durability.
Invention content
The purpose of the present invention is：A kind of weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying is provided, it is existing to solve
Rapid-curing cutback face does not adapt to the problem of this cold and hot Changes in weather, also has the work(of water-absorbing fast-drying while to make it have warmth retention property
The effect of imitating, capable of effectively controlling human body wet-heat durability.
Realizing the technical solution of above-mentioned purpose is：A kind of weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying, including
Following steps：One Double-plate machine is provided, arranges trigonometric sum knitting needle as requested；There is provided yarn, yarn include island draw textured yarn,
Terylene draw textured yarn, spandex；Step is woven, is woven using one, three tunnel cycle：The first via uses island stretcher strain
Silk is simultaneously lining into spandex braiding fabric internal layer, dials twice needle flotation line, syringe twice needle lopping；Second tunnel uses terylene stretcher strain
Silk is lining into spandex braiding fabric outer layer, and latitude flat structure, dials twice needle lopping, syringe twice needle flotation line are formed in outer layer；Third
Road uses terylene draw textured yarn to connect yarn, to connect fabric internal layer and outer layer, one needle tuck of dials twice needle, a needle
Flotation line, one needle tuck of syringe twice needle, a needle flotation line.
Further, during the first via braiding, bottom cylinder carries out 1 every 1 drawn needle, between the formation of fabric internal layer
Every equidistant stereo concave-convex groove structure.
Further, after weaving step also include successively preshrunk, fibrillation, predetermined, dyeing, raising, finished product sizing step
Suddenly.
Further, the fibrillation step includes configuration work liquid；Fabric after braiding is put into working solution, bath raio is
1:40-1:60；95 DEG C are warming up to 1 DEG C/min of rate, keeps the temperature 60min.
Further, the working solution includes penetrating agent JFC, a concentration of 1g/L-3g/L；Sodium hydroxide, a concentration of 4g/
L-8g/L。
Further, the island draw textured yarn is the islands 105D/36F draw textured yarn.
Further, the terylene draw textured yarn is 75D/36F terylene draw textured yarns.
Further, the spandex is 40D spandexs.
It is an advantage of the invention that：The weaving method of the warming chamois flannel face fabric of the water-absorbing fast-drying of the present invention, the face woven
Material has good heat-preserving function, can effectively control human body wet-heat durability.Wherein, the stereo concave-convex groove structure of fabric internal layer exists
Human body can be largely discharged due to excessively thermogenetic sweat in skin surface.It is excellent that the latitude flat structure of fabric outer layer ensure that the fabric possesses
Good elasticity, while using the hydrophobicity of terylene, allowing moisture in outer layer rapid evaporation.The face that method through the invention is woven
Material can be widely used for making the clothes of season in spring and autumn.
Description of the drawings
The present invention is further explained with reference to the accompanying drawings and examples.
Fig. 1 is the cam chart of the present invention.
Fig. 2 is the knitting needle arrangement figure of the present invention.
Fig. 3 is the stereo concave-convex groove structure schematic diagram of the present invention.
Specific implementation mode
The explanation of following embodiment is to refer to additional schema, to illustrate the particular implementation that the present invention can be used to implement
Example.Direction term that the present invention is previously mentioned, such as "upper", "lower", "front", "rear", "left", "right", "top", "bottom" etc. are only
With reference to the direction of annexed drawings.Therefore, the direction term used is to illustrate and understand the present invention, rather than to limit this hair
It is bright.
Embodiment：A kind of weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying, includes the following steps.
A Double-plate machine is provided, it is 34 〞 to select the Double-plate machine of profit mountain RS models, machine 28G syringes, barrel dliameter.It arranges as requested
Row trigonometric sum knitting needle；Triangle arrangement method is as shown in Figure 1, knitting needle such as Fig. 2 is arranged." ∪ ∩ " indicates tuck cam in Fig. 1；
" ∨ ∧ " indicates stitch cam；"-" indicates flotation line triangle；Fig. 2 Zhong " ∣ " 1. indicate first of knitting needle；" | " 2. indicates second
Knitting needle,Indicate the drawn needle of bottom cylinder.
Yarn is provided, yarn includes island draw textured yarn, terylene draw textured yarn, spandex；In the present embodiment, the sea
Island draw textured yarn is the islands 105D/36F draw textured yarn.The terylene draw textured yarn is 75D/36F terylene stretcher strains
Silk.The spandex is 40D spandexs.
Step is woven, is woven using one, three tunnel cycle：The first via is using island draw textured yarn and is lining into spandex
Weave fabric internal layer, dials twice needle flotation line, syringe twice needle lopping；It is excellent to ensure that the fabric possesses in internal layer for this step
Elasticity, the islands the 105D/36F draw textured yarn of use makes the fabric after braiding have excellent moisture absorption after fiber opening process
Property, while being easy to rear road raising.During first via braiding, bottom cylinder carries out 1 every 1 drawn needle, between the formation of fabric internal layer
Every equidistant stereo concave-convex groove structure.Stereo concave-convex groove structure is as shown in Figure 3.Stereo concave-convex groove structure can in skin surface
Human body is largely discharged due to excessively thermogenetic sweat.
Second tunnel is lining into spandex using terylene draw textured yarn and weaves fabric outer layer, and latitude flat structure, dials are formed in outer layer
Twice needle lopping, syringe twice needle flotation line；Latitude flat structure ensure that the fabric possesses excellent elasticity, while dredging using terylene
It is aqueous, allow moisture in outer layer rapid evaporation.
Third road uses terylene draw textured yarn to connect yarn, to connect fabric internal layer and outer layer, dials twice needle
One needle tuck, a needle flotation line, one needle tuck of syringe twice needle, a needle flotation line.
Also include preshrunk, fibrillation, predetermined, dyeing, raising, finished product fixating shape step successively after weaving step.
The fibrillation step includes configuration work liquid；Fabric after braiding is put into working solution, bath raio 1:40-1:
60；95 DEG C are warming up to 1 DEG C/min of rate, keeps the temperature 60min.The working solution includes penetrating agent JFC, a concentration of 1g/L-3g/
L, preferably 2g/L；Sodium hydroxide, a concentration of 4g/L-8g/L, preferably 5g/L.After fibrillation step, the skin surface of fabric is (interior
Layer) island draw textured yarn be stripped into superfine fibre, the minim gap between single fiber brings the capillary of geometrical property to imitate
It answers, assigns the good hygroscopicity of fabric and gas permeability, while bringing the feel of soft exquisiteness and comfortable experience.
Sea island yarn skin surface after fibrillation makes using the rational sanding in rear road (including plucking, roughing process)
The surface of fabric generates one layer of exquisiteness, closely knit villus, to assign fabric good warmth retention property.In finished product fixating shape step,
Moisture absorbing and sweat releasing auxiliary agent processing is carried out again, makes the water-absorbing fast-drying function of the fabric more powerful.Moisture absorbing and sweat releasing auxiliary agent steps for Hensel
HSD-S, a concentration of 30g/L.
Measure of merit：
The evaluation of the absorbing fast-drying performance of textile is detected, wherein water absorption rate, diffusion of dripping by standard GB/T 21655.1
Time, measure wicking height characterize hygroscopicity；Rapid-drying properties are indicated with evaporation rate and vapor transfer rate.As a result as shown in table 1 below：
Table 1 is the hygroscopicity and rapid-drying properties test parameter of fabric；
Warm property is evaluated using ISO11092 test methods, the warming chamois flannel face fabric CLO of water-absorbing fast-drying of the invention
Value is 0.56.
It is therefore seen that the fabric has the function of outstanding water-absorbing fast-drying, while the fabric possesses good heat-preserving function, energy
Effectively control human body wet-heat durability.
The above is merely preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
All any modification, equivalent and improvement made by within principle etc., should all be included in the protection scope of the present invention.
Claims (8)
1. a kind of weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying, which is characterized in that include the following steps：
One Double-plate machine is provided, arranges trigonometric sum knitting needle as requested；
Yarn is provided, yarn includes island draw textured yarn, terylene draw textured yarn, spandex；
Step is woven, is woven using one, three tunnel cycle：
The first via is using island draw textured yarn and is lining into spandex braiding fabric internal layer, dials twice needle flotation line, syringe twice needle
Lopping；
Second tunnel is lining into spandex using terylene draw textured yarn and weaves fabric outer layer, and latitude flat structure, dials twice are formed in outer layer
Needle lopping, syringe twice needle flotation line；
Third road uses terylene draw textured yarn to connect yarn, to connect fabric internal layer and outer layer, one needle of dials twice needle
Tuck, a needle flotation line, one needle tuck of syringe twice needle, a needle flotation line.
2. the weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying according to claim 1, which is characterized in that described
During weaving all the way, bottom cylinder carries out 1 every 1 drawn needle, and equidistant stereo concave-convex groove knot is spaced to be formed in fabric internal layer
Structure.
3. the weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying according to claim 1, which is characterized in that weaving
Also include preshrunk, fibrillation, predetermined, dyeing, raising, finished product fixating shape step successively after step.
4. the weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying according to claim 1, which is characterized in that described to open
Fine step includes
Configuration work liquid；
Fabric after braiding is put into working solution, bath raio 1:40-1:60；
95 DEG C are warming up to 1 DEG C/min of rate, keeps the temperature 60min.
5. the weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying according to claim 1, which is characterized in that the work
Making liquid includes
Penetrating agent JFC, a concentration of 1g/L-3g/L；
Sodium hydroxide, a concentration of 4g/L-8g/L.
6. the weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying according to claim 1, which is characterized in that the sea
Island draw textured yarn is the islands 105D/36F draw textured yarn.
7. the weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying according to claim 1, which is characterized in that described to wash
Synthetic fibre draw textured yarn is 75D/36F terylene draw textured yarns.
8. the weaving method of the warming chamois flannel face fabric of water-absorbing fast-drying according to claim 1, which is characterized in that spandex is
40D spandexs.