CN108751889A - One kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs - Google Patents
One kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs Download PDFInfo
- Publication number
- CN108751889A CN108751889A CN201810797644.6A CN201810797644A CN108751889A CN 108751889 A CN108751889 A CN 108751889A CN 201810797644 A CN201810797644 A CN 201810797644A CN 108751889 A CN108751889 A CN 108751889A
- Authority
- CN
- China
- Prior art keywords
- parts
- basalt powder
- buildingss
- effect
- paint systems
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, includes the raw material of following parts by weight：Basalt powder, diatomite, preserved egg mountain flour, oyster shell whiting, nano zine oxide, nano-titanium dioxide, aggregate, inorganic gel substance, filler, pigment, boric acid ester coupler, coating dispersant, antioxidant, brightener, Ludox and coalescents, preparation flow are：Stock, heating fusion, stands molding at grinding.The present invention is added to basalt powder, has pressure-resistant, water-fast, high temperature resistant, alkaline-resisting, anti-pollution corrosion-resistant.Preserved egg mountain flour is nontoxic, tasteless, radiationless, and color and luster is abundant, and quality is fine and smooth.Oyster shell whiting formaldehyde adsorption purifies air, prevents fire-retardant etc., and basalt powder and diatomite all have strong adsorption, and sound insulation is heat-insulated, double-deck effect fusion.Therefore the building coating of the present invention has formaldehyde adsorption, purification air, nontoxic, sound insulation, heat-insulated, anti-fire-retardant and service life long, and antiseptic property reaches national advanced level, meets the high-tech regeneration product of environmental requirement.
Description
Technical field
The present invention relates to coating preparation fields, specially a kind of to contain more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs.
Background technology
Diatomite paint is popular now environment-friendly type coating.It is zero formaldehyde, pollution-free, nuisanceless.Most of finishings
Diatom coating will be selected as indoor hardware fitting.Diatom coating finds a good market, and obtains the highly recognition of the common people.But in the later stage
In use, diatom coating metope easily goes out cut, slideway.It is not easily repaired.Metal material is damaged by the effect of surrounding medium, referred to as
Metal erosion.The corrosion of metal is most common etch state.When corrosion, chemistry or electrochemistry have occurred on the interface of metal
Heterogeneous reaction makes metal be transferred to oxidation (ion) state.This can significantly reduce the mechanics such as the intensity, plasticity, toughness of metal material
Performance destroys the geometry of metal component, increases the abrasion between part, deteriorates physical properties, the shortening such as electrical and optical and sets
Standby service life, or even cause the catastrophic failures such as fire, explosion.For metallic surface anti-corrosion, usually in metal watch
Face protective mulch makes metal product be isolated with surrounding corrosive medium, and to prevent corroding, existing anti-corrosion coating materials use
Effect is bad, prepares difficult.
So how to design one kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, becoming us will currently solve
Certainly the problem of.
Invention content
The purpose of the present invention is to provide containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the present invention provides the following technical solutions：One kind is novel containing more effect basalt powder diatoms
Building coating includes the raw material of following parts by weight：20-30 parts of basalt powder, 30-40 parts of diatomite, preserved egg mountain flour 15-20, shellfish
20-22 parts of shell powder, 6-20 parts of nano zine oxide, 6-20 parts of nano-titanium dioxide, 5-35 parts of aggregate, inorganic gel substance 6-18
Part, 20 parts of filler, 20 parts of pigment, 1-3 parts of boric acid ester coupler, 1-2 parts of coating dispersant, 1-2 parts of antioxidant, brightener
0.2-0.4 parts of 0.2-0.8 parts, 0.1-0.3 parts of Ludox and coalescents.
According to above-mentioned technical proposal, it is described by basalt powder breakdown mill be 500 mesh；Diatomite grain size is 6 mesh or less；It is described
Preserved egg mountain flour grain size is 6 mesh or less；The oyster shell whiting grain size is 6 mesh or less；The nano zine oxide is that grain size is that 20-30 receives
Rice；The nano oxidized peptide is that grain size is 20-30 nanometers；The aggregate is quartz sand；The inorganic gel substance is titanium dioxide
Calcium, grain size are 400-1000 mesh；The filler is any one or two kinds of mixing according to arbitrary proportion composition in coarse whiting, fine particle calcium carbonate
Close object；The pigment is titanium oxide serial pigment, and grain size is 500-1200 mesh.
According to above-mentioned technical proposal, the preparation method of the boric acid ester coupler is to mix boric acid, ethanol amine and toluene,
4-7h is reacted at 100-120 DEG C, N hydroxymethyl acrylamide and polymerization inhibitor is added, and is less than 0.1MPa in vacuum degree, temperature is
The reaction was continued under conditions of 50-70 DEG C, and boric acid ester coupler is made.
According to above-mentioned technical proposal, the preparation method of the Ludox is first can be made with the organosilan of rectification and purification
For raw material, it is dissolved in inorganic acid or acidic silicate solution is made in organic acid；Then by can be with the organosilan of rectification and purification
It is dissolved in inorganic base or organic aqueous alkali and the siliceous solution of alkalinity is made, or inorganic base or organic aqueous alkali is directly dilute
It releases and the not siliceous solution of alkalinity is made；Again by acidic silicate solution and the siliceous or not siliceous solution of alkalinity in 105 DEG C of temperature below
Degree reaction, is prepared into Ludox；Ludox is finally heated to boiling under normal pressure or under reduced pressure and excludes the by-products such as methanol/ethanol
The water of product and a part, obtains Ludox of the concentration 20% or more.
One kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, includes the following steps：
1) it stocks up：It is matched by above-mentioned formula material and prepares material, it is spare；
2) it grinds：By homologue abrasive lapping, crush；
3) heating fusion：After mixing tank is warming up to 60-70 DEG C, by basalt powder, diatomite, preserved egg mountain flour, oyster shell whiting,
Nano zine oxide, nano-titanium dioxide, aggregate, inorganic gel substance, filler, pigment, are added sequentially in mixing tank, wait for whole
After thawing, mixing tank is made to be warming up to 90-110 DEG C, sequentially adds boric acid ester coupler, coating dispersant, antioxidant, light
Mixed liquor is made after all mixing in agent, Ludox and coalescents, spare；
4) molding is stood：Mixed liquor is stood into 2-4h, more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs are made；
Compared with prior art, the beneficial effects of the invention are as follows：The present invention is added to basalt powder, have it is water-fast, it is alkaline-resisting,
Anti-pollution, gasproof performance, sound insulation are heat-insulated.Basalt fibre is renewable simultaneously, does not persecute environment；It is added to diatomite, shell
Powder, preserved egg mountain flour have the advantages that moisture-proof, strong adsorption, nontoxic zero formaldehyde and environmental protection, therefore the building coating of the present invention,
Environmentally safe with corrosion-inhibiting coating, service life is long, and antiseptic property reaches national advanced level, meets the height of environmental requirement
Scientific and technological regeneration product.
Description of the drawings
Fig. 1 is more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGS preparation flow block diagrams of the present invention；
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1：Referring to Fig. 1, a kind of containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, including following weight
The raw material of part：30 parts of basalt powder, 40 parts of diatomite, preserved egg mountain flour 20,22 parts of oyster shell whiting, 20 part, nanometer two of nano zine oxide
20 parts of titanium oxide, 35 parts of aggregate, 18 parts of inorganic gel substance, 18 parts of filler, 18 parts of pigment, 3 parts of boric acid ester coupler, coating point
0.3 part of 2 parts of powder, 0.5 part of antioxidant, 0.5 part of brightener, 0.2 part of Ludox and coalescents.
According to above-mentioned technical proposal, it is described by basalt powder breakdown mill be 500 mesh；Diatomite grain size is 6 mesh or less；It is described
Preserved egg mountain flour grain size is 6 mesh or less；The oyster shell whiting grain size is 6 mesh or less；The nano zine oxide is that grain size is that 20-30 receives
Rice；The nano oxidized peptide is that grain size is 20-30 nanometers；The aggregate is quartz sand；The inorganic gel substance is titanium dioxide
Calcium, grain size are 400-1000 mesh；The filler is any one or two kinds of mixing according to arbitrary proportion composition in coarse whiting, fine particle calcium carbonate
Close object；The pigment is titanium oxide serial pigment, and grain size is 500-1200 mesh.
According to above-mentioned technical proposal, the preparation method of the boric acid ester coupler is to mix boric acid, ethanol amine and toluene,
4-7h is reacted at 100-120 DEG C, N hydroxymethyl acrylamide and polymerization inhibitor is added, and is less than 0.1MPa in vacuum degree, temperature is
The reaction was continued under conditions of 50-70 DEG C, and boric acid ester coupler is made.
According to above-mentioned technical proposal, the preparation method of the Ludox is first can be made with the organosilan of rectification and purification
For raw material, it is dissolved in inorganic acid or acidic silicate solution is made in organic acid；Then by can be with the organosilan of rectification and purification
It is dissolved in inorganic base or organic aqueous alkali and the siliceous solution of alkalinity is made, or inorganic base or organic aqueous alkali is directly dilute
It releases and the not siliceous solution of alkalinity is made；Again by acidic silicate solution and the siliceous or not siliceous solution of alkalinity in 105 DEG C of temperature below
Degree reaction, is prepared into Ludox；Ludox is finally heated to boiling under normal pressure or under reduced pressure and excludes the by-products such as methanol/ethanol
The water of product and a part, obtains Ludox of the concentration 20% or more.
One kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, includes the following steps：
1) it stocks up：It is spare by above-mentioned formula material than preparing material；
2) it grinds：By homologue abrasive lapping, crush；
3) heating fusion：After mixing tank is warming up to 60-70 DEG C, by basalt powder, diatomite, preserved egg mountain flour, oyster shell whiting,
Nano zine oxide, nano-titanium dioxide, aggregate, inorganic gel substance, filler, pigment, are added sequentially in mixing tank, wait for whole
After thawing, mixing tank is made to be warming up to 90-110 DEG C, sequentially adds boric acid ester coupler, coating dispersant, antioxidant, light
Mixed liquor is made after all mixing in agent, Ludox and coalescents, spare；
4) molding is stood：Mixed liquor is stood into 2-4h, more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs are made；
Embodiment 2：Referring to Fig. 1, the present invention, which provides kind, contains more effect basalt powder diatom novel building coating materials,
Include the raw material of following parts by weight：20 parts of basalt powder, 30 parts of diatomite, preserved egg mountain flour 15,20 parts of oyster shell whiting, nano zine oxide
10 parts, 10 parts of nano-titanium dioxide, 20 parts of aggregate, 10 parts of inorganic gel substance, 10 parts of filler, 5 parts of pigment, boric acid ester coupler
0.2 part of 1 part, 1 part of coating dispersant, 1 part of antioxidant, 0.3 part of brightener, 0.1 part of Ludox and coalescents.
According to above-mentioned technical proposal, it is described by basalt powder breakdown mill be 500 mesh；Diatomite grain size is 6 mesh or less；It is described
Preserved egg mountain flour grain size is 6 mesh or less；The oyster shell whiting grain size is 6 mesh or less；The nano zine oxide is that grain size is that 20-30 receives
Rice；The nano oxidized peptide is that grain size is 20-30 nanometers；The aggregate is quartz sand；The inorganic gel substance is titanium dioxide
Calcium, grain size are 400-1000 mesh；The filler is any one or two kinds of mixing according to arbitrary proportion composition in coarse whiting, fine particle calcium carbonate
Close object；The pigment is titanium oxide serial pigment, and grain size is 500-1200 mesh.
According to above-mentioned technical proposal, the preparation method of the boric acid ester coupler is to mix boric acid, ethanol amine and toluene,
4-7h is reacted at 100-120 DEG C, N hydroxymethyl acrylamide and polymerization inhibitor is added, and is less than 0.1MPa in vacuum degree, temperature is
The reaction was continued under conditions of 50-70 DEG C, and boric acid ester coupler is made.
According to above-mentioned technical proposal, the preparation method of the Ludox is first can be made with the organosilan of rectification and purification
For raw material, it is dissolved in inorganic acid or acidic silicate solution is made in organic acid；Then by can be with the organosilan of rectification and purification
It is dissolved in inorganic base or organic aqueous alkali and the siliceous solution of alkalinity is made, or inorganic base or organic aqueous alkali is directly dilute
It releases and the not siliceous solution of alkalinity is made；Again by acidic silicate solution and the siliceous or not siliceous solution of alkalinity in 105 DEG C of temperature below
Degree reaction, is prepared into Ludox；Ludox is finally heated to boiling under normal pressure or under reduced pressure and excludes the by-products such as methanol/ethanol
The water of product and a part, obtains Ludox of the concentration 20% or more.
One kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, includes the following steps：
1) it stocks up：It is spare by above-mentioned formula material than preparing material；
2) it grinds：By homologue abrasive lapping, crush；
3) heating fusion：After mixing tank is warming up to 60-70 DEG C, by basalt powder, diatomite, preserved egg mountain flour, oyster shell whiting,
Nano zine oxide, nano-titanium dioxide, aggregate, inorganic gel substance, filler, pigment, are added sequentially in mixing tank, wait for whole
After thawing, mixing tank is made to be warming up to 90-110 DEG C, sequentially adds boric acid ester coupler, coating dispersant, antioxidant, light
Mixed liquor is made after all mixing in agent, Ludox and coalescents, spare；
4) molding is stood：Mixed liquor is stood into 2-4h, more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs are made；
Based on above-mentioned, it is an advantage of the current invention that the present invention is added to basalt powder, tool has pressure resistance, water-fast, resistance to height
Temperature, alkaline-resisting, anti-pollution, corrosion-resistant, sound insulation are heat-insulated.Basalt powder is renewable simultaneously, does not persecute environment；It is added to diatomite, shellfish
Shell powder, preserved egg mountain flour has the advantages that moisture-proof, strong adsorption, nontoxic zero formaldehyde and environmental protection, therefore the building of the present invention applies
Material has formaldehyde adsorption, purification air, nontoxic, sound insulation, heat-insulated, anti-fire-retardant and service life long, and antiseptic property reaches state
Family's advanced level, meets the high-tech regeneration product of environmental requirement.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is by appended claims and its waits.
Claims (5)
1. one kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, it is characterised in that：Include the raw material of following parts by weight：
20-30 parts of basalt powder, preserved egg mountain flour 15-20,20-22 parts of oyster shell whiting, 6-20 parts of nano zine oxide, is received 30-40 parts of diatomite
6-20 parts of titanium dioxide of rice, 5-35 parts of aggregate, 6-18 parts of inorganic gel substance, 20 parts of filler, 20 parts of pigment, boric acid ester coupler
1-3 parts, 1-2 parts of coating dispersant, 1-2 parts of antioxidant, 0.2-0.8 parts of brightener, 0.1-0.3 parts of Ludox and coalescents
0.2-0.4 parts.
2. one kind according to claim 1 contains more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, it is characterised in that：It is described profound
The preparation method of military rock powder is to crush basalt, be ground to 500 mesh；Diatomite grain size is 6 mesh or less；The preserved egg mountain flour grain
Diameter is 6 mesh or less；The oyster shell whiting grain size is 6 mesh or less；The nano zine oxide is that grain size is 20-30 nanometers；The nanometer
It is 20-30 nanometers that oxidation peptide, which is grain size,；The aggregate is quartz sand；The inorganic gel substance is calcium dioxide, and grain size is
400-1000 mesh；The filler is any one or two kinds of mixtures formed according to arbitrary proportion in coarse whiting, fine particle calcium carbonate；It is described
Pigment is titanium oxide serial pigment, and grain size is 500-1200 mesh.
3. one kind according to claim 1 contains more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, it is characterised in that：The boron
The preparation method of acid esters coupling agent is to mix boric acid, ethanol amine and toluene, and 4-7h is reacted at 100-120 DEG C, and N- hydroxyls are added
Methacrylamide and polymerization inhibitor are less than 0.1MPa in vacuum degree, and the reaction was continued under conditions of temperature is 50-70 DEG C, and boron is made
Acid esters coupling agent.
4. one kind according to claim 1 contains more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, it is characterised in that：The silicon
The preparation method of colloidal sol is first can be dissolved in inorganic acid or organic acid using the organosilan of rectification and purification as raw material
Acidic silicate solution is made；Then it will can be dissolved in inorganic base or organic aqueous alkali and be made with the organosilan of rectification and purification
The siliceous solution of alkalinity, or inorganic base or organic aqueous alkali are directly diluted, the not siliceous solution of alkalinity is made；Again by acid silicon
Acid solution, in 105 DEG C of thermotonuses below, is prepared into Ludox with alkaline siliceous or not siliceous solution；Finally by Ludox
It is heated to boiling under normal pressure or under reduced pressure and excludes the byproducts such as methanol/ethanol and the water of a part, obtains concentration 20% or more
Ludox.
5. one kind containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs, it is characterised in that：Include the following steps：
1) it stocks up：It is matched by above-mentioned formula material and prepares material, it is spare；
2) it grinds：By homologue abrasive lapping, crush；
3) heating fusion：After mixing tank is warming up to 60-70 DEG C, by basalt powder, diatomite, preserved egg mountain flour, oyster shell whiting, nanometer
Zinc oxide, nano-titanium dioxide, aggregate, inorganic gel substance, filler pigments, are added sequentially in mixing tank, wait for whole thawings
Afterwards, so that mixing tank is warming up to 90-110 DEG C, sequentially add boric acid ester coupler, coating dispersant, antioxidant, brightener,
Mixed liquor is made after all mixing in Ludox and coalescents, spare；
4) molding is stood：Mixed liquor is stood into 2-4h, is made containing more effect basalt powder diatom NEW PAINT SYSTEMS FOR BUILDINGSs.