CN108729295A - A kind of breakage-proof air purification filter paper and preparation method - Google Patents
A kind of breakage-proof air purification filter paper and preparation method Download PDFInfo
- Publication number
- CN108729295A CN108729295A CN201810577037.9A CN201810577037A CN108729295A CN 108729295 A CN108729295 A CN 108729295A CN 201810577037 A CN201810577037 A CN 201810577037A CN 108729295 A CN108729295 A CN 108729295A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- isopropyl ester
- breakage
- filter paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to air purification filter material processing technique fields, provide a kind of breakage-proof air purification filter paper and preparation method, the filter paper includes alkali-free glass microfibre, organic fiber, acrylic adhesive, the breakage-proof air purification filter paper further includes polyester enhancer, and the polyester enhancer includes the raw material of following parts by weight:7 parts of 47 parts of polyacrylic resin, 9 parts of epoxy resin, 8 parts of three isopropyl ester of aluminic acid, 18 parts of polyethersulfone resin, 5 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturated polyester resin.By adjusting the ingredient of filter paper and the ingredients such as binder, reinforcing agent are added in the present invention, so that air-filtering membrane is had and preferably put damaged performance;Preparation method, simple for process, prepared product quality is high.
Description
Technical field
The invention belongs to air purification filter material processing technique fields, and in particular, to a kind of breakage-proof air purification
Filter paper and preparation method.
Background technology
Glass fibre air filter paper has filter efficiency high, and good chemical stability is widely used.But it is general
Logical glass filter material is influenced by ingredient and preparation process, is easy breakage in use, is caused filter effect impacted, because
This, it is necessary to develop a kind of glass fibre air filter paper of breakage-proof.
Publication No. is that the Chinese patent of CN 102505554A discloses " high-strength glass fiber air filter paper ", this is specially
Glass fibre air filter paper made from profit has good high temperature resistance, but mechanical performance is relatively low, and breakage-proof ability is not
Foot.
Invention content
For the defects in the prior art, on the one hand the purpose of the present invention is to provide a kind of breakage-proof air purification filter
On the one hand paper also provides a kind of method preparing the breakage-proof air purification filter paper.
By adjusting the ingredient of air filter paper and bonding is added in breakage-proof air purification filter paper provided by the invention
The ingredients such as agent, reinforcing agent make air-filtering membrane have and preferably put damaged performance.
The method provided by the invention for preparing the breakage-proof air purification filter paper, product matter simple for process, prepared
Amount is high.
A kind of breakage-proof air purification filter paper provided according to an aspect of the present invention, including alkali-free glass microfibre, have
Machine fiber, acrylic adhesive, the breakage-proof air purification filter paper further includes polyester enhancer.
The polyester enhancer includes the raw material of following parts by weight:44-60 parts of polyacrylic resin, epoxy resin 7-11
Part, 5-10 parts of three isopropyl ester of aluminic acid, 17-25 parts of polyethersulfone resin, 4-7 parts of diisooctyl phthalate, malonic acid ring isopropyl
5-12 parts of 6-11 parts of ester and unsaturated polyester resin.
The polyester enhancer includes the raw material of following parts by weight:45-59 parts of polyacrylic resin, epoxy resin 8-10
Part, 6-9 parts of three isopropyl ester of aluminic acid, 16-20 parts of polyethersulfone resin, 5-6 parts of diisooctyl phthalate, malonic acid ring isopropyl ester
8-9 parts and 5-11 parts of unsaturated polyester resin.
The polyester enhancer includes the raw material of following parts by weight:47 parts of polyacrylic resin, 9 parts of epoxy resin, aluminium
Sour 8 parts of three isopropyl ester, 18 parts of polyethersulfone resin, 5 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturation
7 parts of polyester resin.
The unsaturated polyester resin is through further including:Bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxide
Change diisopropylbenzene (DIPB), hydroquinone.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:15-20:3-5:2-4:2-6:2-8:1:1-5.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:17:4:3:5:6:1:4.
The preparation method of the polyester enhancer is as follows:
Step(1):Polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid are taken by weight
Diisodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin, mechanical mixture is uniform again after above-mentioned each ingredient is heated;
Step(2):By step(1)The mixture being uniformly mixed after middle heating carries out twin-screw extruder, at 150-160 DEG C after extrusion
Lower heat preservation 20min, is cooled to room temperature.
On the one hand a kind of preparation method of the breakage-proof air purification filter paper provided, the breakage-proof air purification filter
The preparation method of paper is as follows:
Step(1):Take 14-20 parts of 45-55 parts of alkali-free glass microfibre, organic fiber mixing;
Step(2):To step(1)Aqueous sulfuric acid is added in mixture to be beaten, obtains slurry, controls stock quality concentration
For 2.9-3.1%, pH value 2.5-2.9;
Step(3):It is diluted with water step(2)Gained slurry to mass concentration is 0.28-0.31%;
Step(4):With centrifugation slag remover to step(3)Slurry after dilution removes the gred, and enterprising in inclined-wire form paper machine
Row wet moulding obtains glass fibre l Water Paper;
Step(5):To step(4)Gained l Water Paper is carried out dehydrating, and makes the moisture percentage < 35% of l Water Paper, dewatering vacuum degree be
0.05-0.1MPa;
Step(6):By being uniformly mixed for acrylic adhesive, polyester enhancer and suitable quantity of water, it is sprayed on step step(5)Institute
Obtain wet paper surface;
Step(7):By step step(6)L Water Paper processing is dried under the conditions of 180-250 DEG C.
Compared with prior art, the present invention has following advantageous effect:
(1)Polyethersulfone resin in inventive formulation is a kind of thermoplastic macromolecule material of excellent combination property, is to be answered
One of special engineering plastics few in number.It has excellent heat resistance, physical mechanical property, insulation performance etc.,
Retention property stabilization etc. can be used continuously and be remained in temperature environment jumpy at high temperature by, which especially having, protrudes
Advantage has been used widely in many fields.Breakage-proof air purification filter paper can therefore had more excellent resistance to
High-temperature behavior can use under 500-600 DEG C of hot environment;
(2)The diisooctyl phthalate being added in inventive formulation is the excellent primary plasticizer of high temperature resistant, ageing-resistant performance.
Its resistance to volatilization, resistance to migration, resistance to extraction, electrical insulating property are good, and products machinery performance is good, flexibility varies with temperature smaller, is suitable for
The wide product of use temperature range.This product is alternatively arranged as plasticizer, on the vulcanization of sizing material without influence.Therefore it can make breakage-proof
Air purification filter paper has more excellent high temperature resistant, high-intensity performance;
(3)In inventive formulation be added unsaturated polyester (UP) be mainly used for fiberglass is made with glass fiber reinforcement, be enhancing
One of principal item in plastics.It has excellent tensile strength and impact flexibility, and relative density is small, heat and electrical insulation capability
Well, the characteristics such as also good light transmission, weather-proof, acidproof and sound insulation, price are low.Filter paper is carried as the reinforcing agent of filter membrane
Draftability and mechanical strength;
(4)Unsaturated polyester resin cohesive force that the present invention is modified is strong, heat resistance and good insulation preformance, high mechanical strength, anti-
Damp fungicidal properties is good, and has excellent refrigerant performance;
(5)Present invention adds polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acids two
Isodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin etc., the stretching for further improving the filter paper being prepared is strong
Degree and impact strength, especially when 47 parts of polyacrylic resin, 9 parts of epoxy resin, 8 parts of three isopropyl ester of aluminic acid, polyethersulfone resin 18
When part, 5 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturated polyester resin, what twin-screw extruder obtained
The performance of filter paper is best, and resisting breakage performance is best.
Specific implementation mode
Present invention will be further explained below with reference to specific examples.It should be understood that these embodiments are merely to illustrate the present invention
Rather than it limits the scope of the invention.
A kind of breakage-proof air purification filter paper that one aspect of the present invention provides, including alkali-free glass microfibre, organic fibre
Dimension, acrylic adhesive, the breakage-proof air purification filter paper further includes polyester enhancer.
Preferably, the polyester enhancer includes the raw material of following parts by weight:44-60 parts of polyacrylic resin, epoxy
7-11 parts of resin, 5-10 parts of three isopropyl ester of aluminic acid, 17-25 parts of polyethersulfone resin, 4-7 parts of diisooctyl phthalate, the third two
5-12 parts of 6-11 parts of sour ring isopropyl ester and unsaturated polyester resin.
Polyethersulfone resin in inventive formulation is a kind of thermoplastic macromolecule material of excellent combination property, is to be answered
One of special engineering plastics few in number.It has excellent heat resistance, physical mechanical property, insulation performance etc.,
Retention property stabilization etc. can be used continuously and be remained in temperature environment jumpy at high temperature by, which especially having, protrudes
Advantage has been used widely in many fields.Breakage-proof air purification filter paper can therefore had more excellent resistance to
High-temperature behavior can use under 500-600 DEG C of hot environment;
The diisooctyl phthalate being added in inventive formulation is the excellent primary plasticizer of high temperature resistant, ageing-resistant performance.Its
It is resistance to volatilization, it is resistance to migration, it is resistance to extraction, electrical insulating property it is good, products machinery performance is good, flexibility vary with temperature it is smaller, suitable for making
With the wide product of temperature range.This product is alternatively arranged as plasticizer, on the vulcanization of sizing material without influence.Therefore breakage-proof can be made empty
The cleaned filter paper of gas has more excellent high temperature resistant, high-intensity performance;
In inventive formulation be added unsaturated polyester (UP) be mainly used for fiberglass is made with glass fiber reinforcement, be reinforced plastics
In one of principal item.It has excellent tensile strength and impact flexibility, and relative density is small, and heat and electrical insulation capability are good,
Characteristics, the prices such as also good light transmission, weather-proof, acidproof and sound insulation are low.Filter paper is carried as the reinforcing agent of filter membrane
Draftability and mechanical strength;
Unsaturated polyester resin cohesive force that the present invention is modified is strong, heat resistance and good insulation preformance, high mechanical strength, moisture resistance are anti-
Mouldiness can be good, and has excellent refrigerant performance;
Present invention adds polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid two are different
Last of the ten Heavenly stems ester, malonic acid ring isopropyl ester and unsaturated polyester resin etc., further improve the tensile strength for the filter paper being prepared
And impact strength, especially when 47 parts of polyacrylic resin, 9 parts of epoxy resin, 8 parts of three isopropyl ester of aluminic acid, 18 parts of polyethersulfone resin,
When 5 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturated polyester resin, mistake that twin-screw extruder obtains
The performance of filter paper is best, and resisting breakage performance is best.
The polyester enhancer includes the raw material of following parts by weight:45-59 parts of polyacrylic resin, epoxy resin 8-10
Part, 6-9 parts of three isopropyl ester of aluminic acid, 16-20 parts of polyethersulfone resin, 5-6 parts of diisooctyl phthalate, malonic acid ring isopropyl ester
8-9 parts and 5-11 parts of unsaturated polyester resin.
The polyester enhancer includes the raw material of following parts by weight:47 parts of polyacrylic resin, 9 parts of epoxy resin, aluminium
Sour 8 parts of three isopropyl ester, 18 parts of polyethersulfone resin, 5 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturation
7 parts of polyester resin.
The unsaturated polyester resin is through further including:Bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxide
Change diisopropylbenzene (DIPB), hydroquinone.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:15-20:3-5:2-4:2-6:2-8:1:1-5.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:17:4:3:5:6:1:4.
The preparation method of the polyester enhancer is as follows:
Step(1):Polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid are taken by weight
Diisodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin, mechanical mixture is uniform again after above-mentioned each ingredient is heated;
Step(2):By step(1)The mixture being uniformly mixed after middle heating carries out twin-screw extruder, at 150-160 DEG C after extrusion
Lower heat preservation 20min, is cooled to room temperature.
On the one hand a kind of preparation method of the breakage-proof air purification filter paper provided, the breakage-proof air purification filter
The preparation method of paper is as follows:
Step(1):Take 14-20 parts of 45-55 parts of alkali-free glass microfibre, organic fiber mixing;
Step(2):To step(1)Aqueous sulfuric acid is added in mixture to be beaten, obtains slurry, controls stock quality concentration
For 2.9-3.1%, pH value 2.5-2.9;
Step(3):It is diluted with water step(2)Gained slurry to mass concentration is 0.28-0.31%;
Step(4):With centrifugation slag remover to step(3)Slurry after dilution removes the gred, and enterprising in inclined-wire form paper machine
Row wet moulding obtains glass fibre l Water Paper;
Step(5):To step(4)Gained l Water Paper is carried out dehydrating, and makes the moisture percentage < 35% of l Water Paper, dewatering vacuum degree be
0.05-0.1MPa;
Step(6):By being uniformly mixed for acrylic adhesive, polyester enhancer and suitable quantity of water, it is sprayed on step step(5)Institute
Obtain wet paper surface;
Step(7):By step step(6)L Water Paper processing is dried under the conditions of 180-250 DEG C.
Embodiment 1
On the one hand a kind of breakage-proof air purification filter paper that the present embodiment provides, including alkali-free glass microfibre, organic fiber,
Acrylic adhesive, the breakage-proof air purification filter paper further includes polyester enhancer.
The polyester enhancer includes the raw material of following parts by weight:60 parts of polyacrylic resin, 7 parts of epoxy resin, aluminium
Sour 10 parts of three isopropyl ester, 17 parts of polyethersulfone resin, 7 parts of diisooctyl phthalate, 6 parts of malonic acid ring isopropyl ester and unsaturation
12 parts of polyester resin.
The unsaturated polyester resin is through further including:Bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxide
Change diisopropylbenzene (DIPB), hydroquinone.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:20:3:4:2:8:1:1.
The preparation method of the polyester enhancer is as follows:
Step(1):Polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid are taken by weight
Diisodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin, mechanical mixture is uniform again after above-mentioned each ingredient is heated;
Step(2):By step(1)The mixture being uniformly mixed after middle heating carries out twin-screw extruder, is protected at 160 DEG C after extrusion
Warm 20min, is cooled to room temperature.
On the one hand a kind of preparation method of the breakage-proof air purification filter paper provided, the breakage-proof air purification filter
The preparation method of paper is as follows:
Step(1):Take 14 parts of 55 parts of alkali-free glass microfibre, organic fiber mixing;
Step(2):To step(1)Aqueous sulfuric acid is added in mixture to be beaten, obtains slurry, controls stock quality concentration
It is 3.1%, pH value 2.5;
Step(3):It is diluted with water step(2)Gained slurry to mass concentration is 0.31%;
Step(4):With centrifugation slag remover to step(3)Slurry after dilution removes the gred, and enterprising in inclined-wire form paper machine
Row wet moulding obtains glass fibre l Water Paper;
Step(5):To step(4)Gained l Water Paper is carried out dehydrating, and makes the moisture percentage < 35% of l Water Paper, dewatering vacuum degree be
0.05MPa;
Step(6):By being uniformly mixed for acrylic adhesive, polyester enhancer and suitable quantity of water, it is sprayed on step step(5)Institute
Obtain wet paper surface;
Step(7):By step step(6)L Water Paper processing is dried under the conditions of 250 DEG C.
Embodiment 2
On the one hand a kind of breakage-proof air purification filter paper that the present embodiment provides, including alkali-free glass microfibre, organic fiber,
Acrylic adhesive, the breakage-proof air purification filter paper further includes polyester enhancer.
The polyester enhancer includes the raw material of following parts by weight:44 parts of polyacrylic resin, 11 parts of epoxy resin, aluminium
Sour 5 parts of three isopropyl ester, 25 parts of polyethersulfone resin, 4 parts of diisooctyl phthalate, 11 parts of malonic acid ring isopropyl ester and unsaturation
5 parts of polyester resin.
The unsaturated polyester resin is through further including:Bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxide
Change diisopropylbenzene (DIPB), hydroquinone.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:20:3:4:2:8:1:1.
The preparation method of the polyester enhancer is as follows:
Step(1):Polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid are taken by weight
Diisodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin, mechanical mixture is uniform again after above-mentioned each ingredient is heated;
Step(2):By step(1)The mixture being uniformly mixed after middle heating carries out twin-screw extruder, is protected at 150 DEG C after extrusion
Warm 20min, is cooled to room temperature.
On the one hand a kind of preparation method of the breakage-proof air purification filter paper provided, the breakage-proof air purification filter
The preparation method of paper is as follows:
Step(1):Take 14 parts of 55 parts of alkali-free glass microfibre, organic fiber mixing;
Step(2):To step(1)Aqueous sulfuric acid is added in mixture to be beaten, obtains slurry, controls stock quality concentration
It is 3.1%, pH value 2.5;
Step(3):It is diluted with water step(2)Gained slurry to mass concentration is 0.31%;
Step(4):With centrifugation slag remover to step(3)Slurry after dilution removes the gred, and enterprising in inclined-wire form paper machine
Row wet moulding obtains glass fibre l Water Paper;
Step(5):To step(4)Gained l Water Paper is carried out dehydrating, and makes the moisture percentage < 35% of l Water Paper, dewatering vacuum degree be
0.1MPa;
Step(6):By being uniformly mixed for acrylic adhesive, polyester enhancer and suitable quantity of water, it is sprayed on step step(5)Institute
Obtain wet paper surface;
Step(7):By step step(6)L Water Paper processing is dried under the conditions of 250 DEG C.
Embodiment 3
On the one hand a kind of breakage-proof air purification filter paper that the present embodiment provides, including alkali-free glass microfibre, organic fiber,
Acrylic adhesive, the breakage-proof air purification filter paper further includes polyester enhancer.
The polyester enhancer includes the raw material of following parts by weight:59 parts of polyacrylic resin, 8 parts of epoxy resin, aluminium
Sour 9 parts of three isopropyl ester, 16 parts of polyethersulfone resin, 6 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturation
11 parts of polyester resin.
The unsaturated polyester resin is through further including:Bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxide
Change diisopropylbenzene (DIPB), hydroquinone.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:17:4:3:5:6:1:4.
The preparation method of the polyester enhancer is as follows:
Step(1):Polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid are taken by weight
Diisodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin, mechanical mixture is uniform again after above-mentioned each ingredient is heated;
Step(2):By step(1)The mixture being uniformly mixed after middle heating carries out twin-screw extruder, is protected at 155 DEG C after extrusion
Warm 20min, is cooled to room temperature.
On the one hand a kind of preparation method of the breakage-proof air purification filter paper provided, the breakage-proof air purification filter
The preparation method of paper is as follows:
Step(1):Take 17 parts of 48 parts of alkali-free glass microfibre, organic fiber mixing;
Step(2):To step(1)Aqueous sulfuric acid is added in mixture to be beaten, obtains slurry, controls stock quality concentration
It is 3.0%, pH value 2.7;
Step(3):It is diluted with water step(2)Gained slurry to mass concentration is 0.29%;
Step(4):With centrifugation slag remover to step(3)Slurry after dilution removes the gred, and enterprising in inclined-wire form paper machine
Row wet moulding obtains glass fibre l Water Paper;
Step(5):To step(4)Gained l Water Paper is carried out dehydrating, and makes the moisture percentage < 35% of l Water Paper, dewatering vacuum degree be
0.05-0.1MPa;
Step(6):By being uniformly mixed for acrylic adhesive, polyester enhancer and suitable quantity of water, it is sprayed on step step(5)Institute
Obtain wet paper surface;
Step(7):By step step(6)L Water Paper processing is dried under the conditions of 140 DEG C.
Embodiment 4
On the one hand a kind of breakage-proof air purification filter paper that the present embodiment provides, including alkali-free glass microfibre, organic fiber,
Acrylic adhesive, the breakage-proof air purification filter paper further includes polyester enhancer.
The polyester enhancer includes the raw material of following parts by weight:59 parts of polyacrylic resin, 8 parts of epoxy resin, aluminium
Sour 9 parts of three isopropyl ester, 16 parts of polyethersulfone resin, 6 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturation
11 parts of polyester resin.
The unsaturated polyester resin is through further including:Bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxide
Change diisopropylbenzene (DIPB), hydroquinone.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:17:4:3:5:6:1:4.
The preparation method of the polyester enhancer is as follows:
Step(1):Polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid are taken by weight
Diisodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin, mechanical mixture is uniform again after above-mentioned each ingredient is heated;
Step(2):By step(1)The mixture being uniformly mixed after middle heating carries out twin-screw extruder, is protected at 156 DEG C after extrusion
Warm 20min, is cooled to room temperature.
On the one hand a kind of preparation method of the breakage-proof air purification filter paper provided, the breakage-proof air purification filter
The preparation method of paper is as follows:
Step(1):Take 18 parts of 48 parts of alkali-free glass microfibre, organic fiber mixing;
Step(2):To step(1)Aqueous sulfuric acid is added in mixture to be beaten, obtains slurry, controls stock quality concentration
It is 3.1%, pH value 2.7;
Step(3):It is diluted with water step(2)Gained slurry to mass concentration is 0.28%;
Step(4):With centrifugation slag remover to step(3)Slurry after dilution removes the gred, and enterprising in inclined-wire form paper machine
Row wet moulding obtains glass fibre l Water Paper;
Step(5):To step(4)Gained l Water Paper is carried out dehydrating, and makes the moisture percentage < 35% of l Water Paper, dewatering vacuum degree be
0.09MPa;
Step(6):By being uniformly mixed for acrylic adhesive, polyester enhancer and suitable quantity of water, it is sprayed on step step(5)Institute
Obtain wet paper surface;
Step(7):By step step(6)L Water Paper processing is dried under the conditions of 190 DEG C.
Embodiment 5
On the one hand a kind of breakage-proof air purification filter paper that the present embodiment provides, including alkali-free glass microfibre, organic fiber,
Acrylic adhesive, the breakage-proof air purification filter paper further includes polyester enhancer.
The polyester enhancer includes the raw material of following parts by weight:47 parts of polyacrylic resin, 9 parts of epoxy resin, aluminium
Sour 8 parts of three isopropyl ester, 18 parts of polyethersulfone resin, 5 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturation
7 parts of polyester resin.
The unsaturated polyester resin is through further including:Bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxide
Change diisopropylbenzene (DIPB), hydroquinone.
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating diisopropyl
Benzene, hydroquinone mass ratio are:17:4:3:5:6:1:4.
The preparation method of the polyester enhancer is as follows:
Step(1):Polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid are taken by weight
Diisodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin, mechanical mixture is uniform again after above-mentioned each ingredient is heated;
Step(2):By step(1)The mixture being uniformly mixed after middle heating carries out twin-screw extruder, is protected at 160 DEG C after extrusion
Warm 20min, is cooled to room temperature.
On the one hand a kind of preparation method of the breakage-proof air purification filter paper provided, the breakage-proof air purification filter
The preparation method of paper is as follows:
Step(1):Take 16 parts of 49 parts of alkali-free glass microfibre, organic fiber mixing;
Step(2):To step(1)Aqueous sulfuric acid is added in mixture to be beaten, obtains slurry, controls stock quality concentration
It is 3.1%, pH value 2.9;
Step(3):It is diluted with water step(2)Gained slurry to mass concentration is 0.31%;
Step(4):With centrifugation slag remover to step(3)Slurry after dilution removes the gred, and enterprising in inclined-wire form paper machine
Row wet moulding obtains glass fibre l Water Paper;
Step(5):To step(4)Gained l Water Paper is carried out dehydrating, and makes the moisture percentage < 35% of l Water Paper, dewatering vacuum degree be
0.1MPa;
Step(6):By being uniformly mixed for acrylic adhesive, polyester enhancer and suitable quantity of water, it is sprayed on step step(5)Institute
Obtain wet paper surface;
Step(7):By step step(6)L Water Paper processing is dried under the conditions of 210 DEG C.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (2)
1. a kind of breakage-proof air purification filter paper, including alkali-free glass microfibre, organic fiber, acrylic adhesive,
It is characterized in that, the breakage-proof air purification filter paper further includes polyester enhancer;
The polyester enhancer includes the raw material of following parts by weight:44-60 parts of polyacrylic resin, 7-11 parts of epoxy resin,
5-10 parts of three isopropyl ester of aluminic acid, 17-25 parts of polyethersulfone resin, 4-7 parts of diisooctyl phthalate, malonic acid ring isopropyl ester 6-
11 parts and 5-12 parts of unsaturated polyester resin;
The polyester enhancer includes the raw material of following parts by weight:45-59 parts of polyacrylic resin, 8-10 parts of epoxy resin,
6-9 parts of three isopropyl ester of aluminic acid, 16-20 parts of polyethersulfone resin, 5-6 parts of diisooctyl phthalate, malonic acid ring isopropyl ester 8-9
5-11 parts of part and unsaturated polyester resin;
The polyester enhancer includes the raw material of following parts by weight:47 parts of polyacrylic resin, 9 parts of epoxy resin, aluminic acid three
8 parts of isopropyl ester, 18 parts of polyethersulfone resin, 5 parts of diisooctyl phthalate, 8 parts of malonic acid ring isopropyl ester and unsaturated polyester (UP)
7 parts of resin;
The unsaturated polyester resin further includes:Bismaleimide, epoxy resin, tung oil acid anhydride, styrene, peroxidating two are different
Propyl benzene, hydroquinone;
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, cumyl peroxide,
Hydroquinone mass ratio is:15-20:3-5:2-4:2-6:2-8:1:1-5;
The unsaturated polyester resin, bismaleimide, epoxy resin, tung oil acid anhydride, styrene, cumyl peroxide,
Hydroquinone mass ratio is:17:4:3:5:6:1:4;
The preparation method of the polyester enhancer is as follows:
Step(1):Polyacrylic resin, epoxy resin, three isopropyl ester of aluminic acid, polyethersulfone resin, phthalic acid are taken by weight
Diisodecyl ester, malonic acid ring isopropyl ester and unsaturated polyester resin, mechanical mixture is uniform again after above-mentioned each ingredient is heated;
Step(2):By step(1)The mixture being uniformly mixed after middle heating carries out twin-screw extruder, at 150-160 DEG C after extrusion
Lower heat preservation 20min, is cooled to room temperature.
2. the preparation method of breakage-proof air purification filter paper according to claim 1, it is characterised in that:The breakage-proof
The preparation method of air purification filter paper is as follows:
Step(1):Take 14-20 parts of 45-55 parts of alkali-free glass microfibre, organic fiber mixing;
Step(2):To step(1)Aqueous sulfuric acid is added in mixture to be beaten, obtains slurry, controls stock quality concentration
For 2.9-3.1%, pH value 2.5-2.9;
Step(3):It is diluted with water step(2)Gained slurry to mass concentration is 0.28-0.31%;
Step(4):With centrifugation slag remover to step(3)Slurry after dilution removes the gred, and enterprising in inclined-wire form paper machine
Row wet moulding obtains glass fibre l Water Paper;
Step(5):To step(4)Gained l Water Paper is carried out dehydrating, and makes the moisture percentage < 35% of l Water Paper, dewatering vacuum degree be
0.05-0.1MPa;
Step(6):By being uniformly mixed for acrylic adhesive, polyester enhancer and suitable quantity of water, it is sprayed on step step(5)Institute
Obtain wet paper surface;
Step(7):By step step(6)L Water Paper processing is dried under the conditions of 180-250 DEG C.