CN108708119A - Based on the elastic polyurethane fiber cloth production process for evaporating shrinking process - Google Patents
Based on the elastic polyurethane fiber cloth production process for evaporating shrinking process Download PDFInfo
- Publication number
- CN108708119A CN108708119A CN201810640458.1A CN201810640458A CN108708119A CN 108708119 A CN108708119 A CN 108708119A CN 201810640458 A CN201810640458 A CN 201810640458A CN 108708119 A CN108708119 A CN 108708119A
- Authority
- CN
- China
- Prior art keywords
- clothes
- obtains
- carries out
- evaporating
- polyurethane fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, includes the following steps：The first step makees desizing processing to elastic polyurethane fiber fabric, obtains A clothes；Second step carries out processing of singing to A clothes, obtains B clothes；Third walks, and carries out boiling drift processing to B clothes, obtains C clothes；4th step carries out C clothes to evaporate shrink process, obtains D clothes；5th step carries out mercerization finish to D clothes, obtains E clothes；6th step carries out long vehicle dyeing processing to E clothes, obtains F clothes；7th step carries out final finishing to F clothes, obtains finished product cloth.The present invention has the characteristics that the door width shrinkage that can effectively improve elastic polyurethane fiber cloth.
Description
Technical field
It is especially a kind of based on the spandex bullet for evaporating shrinking process the present invention relates to a kind for the treatment of process of elastic polyurethane fiber cloth
Power cloth production process.
Background technology
Common elastic polyurethane fiber fabric is made by spandex yarn, such fabric is needed when carrying out long vehicle dyeing by preceding
Processing, part stretch fabric can lead to the door width of the elastic force fabric after pre-treatment is bleached because of weaving itself and spandex thread problem
Super large, and door width can also be widened during subsequent mercerization finish, but door width shrinkage amplitude is not during final finishing
Greatly, to which the door width for influencing finished product is more than very much customer requirement door width greatly.Therefore, there is elastic polyurethane fiber cloth door width for existing technology
The undesirable problem of contractive effect.
Invention content
The object of the present invention is to provide a kind of based on the elastic polyurethane fiber cloth production process for evaporating shrinking process.The present invention
Has the characteristics that the door width shrinkage that can effectively improve elastic polyurethane fiber cloth.
Technical scheme of the present invention：Based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, include the following steps：
The first step makees desizing processing to elastic polyurethane fiber fabric, obtains A clothes；
Second step carries out processing of singing to A clothes, obtains B clothes；
Third walks, and carries out boiling drift processing to B clothes, obtains C clothes；
4th step carries out C clothes to evaporate shrink process, obtains D clothes；
5th step carries out mercerization finish to D clothes, obtains E clothes；
6th step carries out long vehicle dyeing processing to E clothes, obtains F clothes；
7th step carries out final finishing to F clothes, obtains finished product cloth.
It is above-mentioned based in the elastic polyurethane fiber cloth production process for evaporating shrinking process, C clothes carry out evaporating receipts in the 4th step
Contracting processing detailed process be：C clothes are put into rapid steamer and carry out evaporating shrink process, it is 3-8min to evaporate the time, is evaporated
Temperature is 95-105 DEG C；The speed of rapid steamer is 20-30m/min.
It is above-mentioned based in the elastic polyurethane fiber cloth production process for evaporating shrinking process, the time of evaporating of the rapid steamer is
5min。
It is above-mentioned based in the elastic polyurethane fiber cloth production process for evaporating shrinking process, the temperature of evaporating of the rapid steamer is
100℃。
It is above-mentioned based in the elastic polyurethane fiber cloth production process for evaporating shrinking process, the speed of the rapid steamer is 25m/
min。
Compared with prior art, the present invention first carries out evaporating shrink process before elastic polyurethane fiber cloth carries out mercerization finish, leads to
Cross the effect of evaporating so that half-bleached shirting C clothes can be shunk in advance, in the process yarn also can abundant backtwisting so that
Elastic polyurethane fiber cloth can further shrink a width when carrying out mercerization finish.It can effectively be carried in conclusion the present invention has
The characteristics of door width shrinkage of high elastic polyurethane fiber cloth.
Specific implementation mode
With reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1.Based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, include the following steps：
The first step makees desizing processing to elastic polyurethane fiber fabric, obtains A clothes；
Second step carries out processing of singing to A clothes, obtains B clothes；
Third walks, and carries out boiling drift processing to B clothes, obtains C clothes；
4th step carries out C clothes to evaporate shrink process, obtains D clothes；
5th step carries out mercerization finish to D clothes, obtains E clothes；
6th step carries out long vehicle dyeing processing to E clothes, obtains F clothes；
7th step carries out final finishing to F clothes, obtains finished product cloth.
The detailed process that C clothes evaporate shrink process in 4th step is：C clothes are put into rapid steamer and are evaporated
Shrink process, it is 3-8min to evaporate the time, and it is 95-105 DEG C to evaporate temperature；The speed of rapid steamer is 20-30m/min.
The time of evaporating of the rapid steamer is 5min.
The temperature of evaporating of the rapid steamer is 100 DEG C.
The speed of the rapid steamer is 25m/min.
Embodiment 2.Based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, include the following steps：The first step, to ammonia
Synthetic fibre elastic force fabric makees desizing processing, obtains A clothes；
Second step carries out processing of singing to A clothes, obtains B clothes；
Third walks, and carries out boiling drift processing to B clothes, obtains C clothes；
4th step carries out C clothes to evaporate shrink process, obtains D clothes；
5th step carries out mercerization finish to D clothes, obtains E clothes；
6th step carries out long vehicle dyeing processing to E clothes, obtains F clothes；
7th step carries out final finishing to F clothes, obtains finished product cloth.
C clothes are not by weft tension in rapid steamer.
The detailed process that C clothes evaporate shrink process in 4th step is：C clothes are put into rapid steamer and are evaporated
Shrink process；It is 3-8min to evaporate the time.It evaporates temperature and is divided into 2 temperature stages, a temperature stage is 85-95 DEG C, another
A temperature stage is 105-110 DEG C, alternately primary at intervals of two minutes between two temperature stages；The speed of rapid steamer is 20-30m/
min.So as to increase the stability of yarn backtwisting so that yarn being capable of further abundant backtwisting.
The time of evaporating of the rapid steamer is 5min.
The speed of the rapid steamer is 25m/min.
It is additionally provided with carbon dioxide gas in the rapid steamer, for neutralizing the lye on C clothes, is carried out convenient for C clothes
It shrinks and yarn backtwisting.
The concrete model of rapid steamer is Ali's sharp (ARIOLI) loop steamer difficult to understand.
Claims (5)
1. based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, which is characterized in that include the following steps：
The first step makees desizing processing to elastic polyurethane fiber fabric, obtains A clothes；
Second step carries out processing of singing to A clothes, obtains B clothes；
Third walks, and carries out boiling drift processing to B clothes, obtains C clothes；
4th step carries out C clothes to evaporate shrink process, obtains D clothes；
5th step carries out mercerization finish to D clothes, obtains E clothes；
6th step carries out long vehicle dyeing processing to E clothes, obtains F clothes；
7th step carries out final finishing to F clothes, obtains finished product cloth.
2. according to claim 1 based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, it is characterised in that：4th
The detailed process that C clothes evaporate shrink process in step is：C clothes are put into rapid steamer and carry out evaporating shrink process, are steamed
The change time is 3-8min, and it is 95-105 DEG C to evaporate temperature；The speed of rapid steamer is 20-30m/min.
3. according to claim 2 based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, it is characterised in that：It is described
The time of evaporating of rapid steamer is 5min.
4. according to claim 2 based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, it is characterised in that：It is described
The temperature of evaporating of rapid steamer is 100 DEG C.
5. according to claim 2 based on the elastic polyurethane fiber cloth production process for evaporating shrinking process, it is characterised in that：It is described
The speed of rapid steamer is 25m/min.