CN108706911A - A method of producing Footpath brick with resin and papermaking black mud - Google Patents
A method of producing Footpath brick with resin and papermaking black mud Download PDFInfo
- Publication number
- CN108706911A CN108706911A CN201810400783.0A CN201810400783A CN108706911A CN 108706911 A CN108706911 A CN 108706911A CN 201810400783 A CN201810400783 A CN 201810400783A CN 108706911 A CN108706911 A CN 108706911A
- Authority
- CN
- China
- Prior art keywords
- black mud
- brick
- resin
- synthetic resin
- quartz sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method producing Footpath brick with resin and papermaking black mud, the method for the resin and papermaking black mud production Footpath brick is as follows：S1：Choose suitable quartz sand, select suitable synthetic resin and collect remaining blocky black mud after paper production stay do it is spare；S2：The quartz sand collected in step S1 is put into ultrasonic cleaning pond, the present invention carries out Combination heating production using remaining black mud after synthetic resin and papermaking as raw material, wherein synthetic resin and black mud source is wide, it is cheap, after being heated by synthetic resin Hybrid Heating stirring is carried out with the quartz sand after powdered black mud and cleaning, it is dried again after injection molding, so that after the moisture of Footpath brick is oven-dried evaporation, it is cut again, so that the Footpath brick finally has excellent toughness and plasticity, laying is not likely to produce rupture on pavement, damaged situation, because having used synthetic resin, lighter in weight.
Description
Technical field
The present invention relates to Footpath brick technical field, specially a kind of method producing Footpath brick with resin and papermaking black mud.
Background technology
Footpath brick generally uses lithotome or cement concrete to manufacture at present, and unit weight is bigger, for accessible roof,
The application sites such as indoor landscape increase the load of building；And lithotome or cement concrete Footpath brick are in order to reach
To the requirement of thickness, material therefor is more, thus cost is higher；On the other hand, lithotome or cement concrete material
Water penetration is poor, is unfavorable for draining recharge when rainfall in soil.
Existing Footpath brick includes fired brick, cement brick and Ceramic Tiles, is made mostly by inorganic non-metallic material.It is existing
There is the Footpath brick quality weight made of inorganic non-metallic material system of technology, density is big, and transport is inconvenient, load-bearing capacity is strong,
It is not easily repaired after broken, damage, impaired material cannot recycle.As application number 201610224458.4 discloses one
Kind discloses using the method for magnesia and blast-furnace cinder synthetic silicate building material and utilizes magnesia and blast-furnace cinder synthesis
Silicate pavement Footpath brick, Footpath brick made of the material have the shortcomings that density is big, frangible, and discarded brick slag can become
Building waste pollutes environment.
For this purpose, we release a kind of method producing Footpath brick with resin and papermaking black mud.
Invention content
The purpose of the present invention is to provide a kind of methods producing Footpath brick with resin and papermaking black mud, to solve the above-mentioned back of the body
The problem of being proposed in scape technology.
To achieve the above object, the present invention provides the following technical solutions：It is a kind of to produce Footpath brick with resin and papermaking black mud
Method, the resin and papermaking black mud production Footpath brick method be as follows：
S1：Suitable quartz sand is chosen, remaining bulk is black after selecting suitable synthetic resin and collecting paper production
Mud stay do it is spare；
S2：The quartz sand collected in step S1 is put into ultrasonic cleaning pond, pure water, stone are added in quartz sand
The water temperature of sand service sink is set as 40 DEG C, cleans 1-2 hours；
S3：The quartz sand strainer filtering that will be cleaned in step S2, and be put into 1-2 hours in baking oven and remove moisture removal, it dries
Box temperature degree is set as 60-100 DEG C, stayed after drying do it is spare；
S4：The blocky black mud collected in step S1 is smashed with crusher, it is 15-20 minutes to smash the time, is then taken
Go out spare.
S5：The synthetic resin being collected into step S1 is put into and carries out heating hot melt in hot melting furnace, wherein control hot melt
The hot melting temperature of stove is 120 DEG C -170 DEG C, controls the hot molten time 70min-80min of hot melting furnace, the synthetic resin that will have been heated
Stay do it is spare；
S6：Black mud by step S5 and the S4 synthetic resin heated obtained and after smashing is put into heating stirring machine,
And pure water and hydrogen peroxide are added into heating stirring machine, wherein the weight ratio of black mud, pure water and hydrogen peroxide is 15:8:3
Heating stirring 100-120min, heating temperature are set as 60 DEG C, stay do it is spare；
S7：The mixture of the black mud, pure water and the hydrogen peroxide that are obtained in step S6 is added in injection molding machine, and uses note
Molding machine is molded into brick die, and wherein the injection temperature of injection molding machine is controlled at 155 DEG C -165 DEG C；
S8：The brick taking-up of injection formed in step S7 is put into baking oven, the temperature for controlling baking oven is 50 DEG C -55 DEG C, control
The time of drying room drying processed is 24-48 hours, is given over to after drying spare；
S9：The Footpath brick that brick after being dried in step S8 is cut into fritter with cutting machine is sold.
Preferably, synthetic resin is PE- polyethylene, PP- polypropylene, one kind in PVC- polyvinyl chloride in the step S1
Or multiple material composition.
Preferably, the specification of quartz sand is 4-8mm in the step S1.
Preferably, the filtered quartz sand diameter in the step S3 is not more than greatly 8mm.
Preferably, the length, width and height of the step S7 brick dies are respectively 100cm, 60cm, 7cm.
Preferably, the length, width and height of the Footpath brick after the step S9 cuttings are respectively 20cm, 20cm, 7cm.
Compared with prior art, the beneficial effects of the invention are as follows：The present invention is using remaining black after synthetic resin and papermaking
Mud carries out Combination heating production as raw material, and wherein synthetic resin and black mud source is wide, cheap, passes through synthetic resin heat
Hybrid Heating stirring is carried out with the quartz sand after powdered black mud and cleaning after molten, is dried again after injection molding so that
It after the moisture of Footpath brick is oven-dried evaporation, then is cut so that the Footpath brick finally has excellent toughness and plasticity, is laid with
It is not likely to produce rupture, damaged situation on pavement, because having used synthetic resin, lighter in weight is foaming with hydrogen peroxide
The production method of agent, Footpath brick obtained is at low cost, good water permeability.
Specific implementation mode
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Based on the embodiments of the present invention, those of ordinary skill in the art are obtained without making creative work
The every other embodiment obtained, shall fall within the protection scope of the present invention.
Embodiment 1
A method of producing Footpath brick, the method for the resin and papermaking black mud production Footpath brick with resin and papermaking black mud
It is as follows：
S1：Suitable quartz sand is chosen, remaining bulk is black after selecting suitable synthetic resin and collecting paper production
Mud stay do it is spare；
S2：The quartz sand collected in step S1 is put into ultrasonic cleaning pond, pure water, stone are added in quartz sand
The water temperature of sand service sink is set as 40 DEG C, cleans 1 hour；
S3：The quartz sand strainer filtering that will be cleaned in step S2, and be put into 1 hour in baking oven and remove moisture removal, baking oven
Temperature setting be 100 DEG C, stayed after drying do it is spare；
S4：The blocky black mud collected in step S1 is smashed with crusher, it is 15 minutes to smash the time, is then taken out standby
With.
S5：The synthetic resin being collected into step S1 is put into and carries out heating hot melt in hot melting furnace, wherein control hot melt
The hot melting temperature of stove be 120 DEG C, control the hot molten time 70min of hot melting furnace, the synthetic resin heated is stayed do it is spare；
S6：Black mud by step S5 and the S4 synthetic resin heated obtained and after smashing is put into heating stirring machine,
And pure water and hydrogen peroxide are added into heating stirring machine, wherein the weight ratio of black mud, pure water and hydrogen peroxide is 15:8:3
Heating stirring 100min, heating temperature are set as 60 DEG C, stay do it is spare；
S7：The mixture of the black mud, pure water and the hydrogen peroxide that are obtained in step S6 is added in injection molding machine, and uses note
Molding machine is molded into brick die, and wherein the injection temperature of injection molding machine is controlled at 155 DEG C；
S8：The brick taking-up of injection formed in step S7 is put into baking oven, the temperature for controlling baking oven is 50 DEG C, control drying
The time of room drying is 24 hours, is given over to after drying spare；
S9：The Footpath brick that brick after being dried in step S8 is cut into fritter with cutting machine is sold.
Synthetic resin is PE- polyethylene in the step S1, and the specification of quartz sand is 7mm, the step in the step S1
The a diameter of 7mm of filtered quartz sand in rapid S3, the length, width and height of the step S7 brick dies be respectively 100cm, 60cm,
The length, width and height of 7cm, the Footpath brick after the step S9 cuttings are respectively 20cm, 20cm, 7cm.
Embodiment 2
A method of producing Footpath brick, the method for the resin and papermaking black mud production Footpath brick with resin and papermaking black mud
It is as follows：
S1：Suitable quartz sand is chosen, remaining bulk is black after selecting suitable synthetic resin and collecting paper production
Mud stay do it is spare；
S2：The quartz sand collected in step S1 is put into ultrasonic cleaning pond, pure water, stone are added in quartz sand
The water temperature of sand service sink is set as 40 DEG C, cleans 1.5 hours；
S3：The quartz sand strainer filtering that will be cleaned in step S2, and be put into 1.5 hours in baking oven and remove moisture removal, it dries
Box temperature degree is set as 73 DEG C, stayed after drying do it is spare；
S4：The blocky black mud collected in step S1 is smashed with crusher, it is 16 minutes to smash the time, is then taken out standby
With.
S5：The synthetic resin being collected into step S1 is put into and carries out heating hot melt in hot melting furnace, wherein control hot melt
The hot melting temperature of stove be 127 DEG C, control the hot molten time 72min of hot melting furnace, the synthetic resin heated is stayed do it is spare；
S6：Black mud by step S5 and the S4 synthetic resin heated obtained and after smashing is put into heating stirring machine,
And pure water and hydrogen peroxide are added into heating stirring machine, wherein the weight ratio of black mud, pure water and hydrogen peroxide is 15:8:3
Heating stirring 111min, heating temperature are set as 60 DEG C, stay do it is spare；
S7：The mixture of the black mud, pure water and the hydrogen peroxide that are obtained in step S6 is added in injection molding machine, and uses note
Molding machine is molded into brick die, and wherein the injection temperature of injection molding machine is controlled at 156 DEG C；
S8：The brick taking-up of injection formed in step S7 is put into baking oven, the temperature for controlling baking oven is 50 DEG C, control drying
The time of room drying is 24-48 hours, is given over to after drying spare；
S9：The Footpath brick that brick after being dried in step S8 is cut into fritter with cutting machine is sold.
Synthetic resin is PP- polypropylene in the step S1, and the specification of quartz sand is 6mm, the step in the step S1
The a diameter of 6mm of filtered quartz sand in rapid S3, the length, width and height of the step S7 brick dies be respectively 100cm, 60cm,
The length, width and height of 7cm, the Footpath brick after the step S9 cuttings are respectively 20cm, 20cm, 7cm.
Embodiment 3
A method of producing Footpath brick, the method for the resin and papermaking black mud production Footpath brick with resin and papermaking black mud
It is as follows：
S1：Suitable quartz sand is chosen, remaining bulk is black after selecting suitable synthetic resin and collecting paper production
Mud stay do it is spare；
S2：The quartz sand collected in step S1 is put into ultrasonic cleaning pond, pure water, stone are added in quartz sand
The water temperature of sand service sink is set as 40 DEG C, cleans 2 hours；
S3：The quartz sand strainer filtering that will be cleaned in step S2, and be put into 1.5 hours in baking oven and remove moisture removal, it dries
Box temperature degree is set as 68 DEG C, stayed after drying do it is spare；
S4：The blocky black mud collected in step S1 is smashed with crusher, it is 19 minutes to smash the time, is then taken out standby
With.
S5：The synthetic resin being collected into step S1 is put into and carries out heating hot melt in hot melting furnace, wherein control hot melt
The hot melting temperature of stove be 124 DEG C, control the hot molten time 70min of hot melting furnace, the synthetic resin heated is stayed do it is spare；
S6：Black mud by step S5 and the S4 synthetic resin heated obtained and after smashing is put into heating stirring machine,
And pure water and hydrogen peroxide are added into heating stirring machine, wherein the weight ratio of black mud, pure water and hydrogen peroxide is 15:8:3
Heating stirring 100min, heating temperature are set as 60 DEG C, stay do it is spare；
S7：The mixture of the black mud, pure water and the hydrogen peroxide that are obtained in step S6 is added in injection molding machine, and uses note
Molding machine is molded into brick die, and wherein the injection temperature of injection molding machine is controlled at 165 DEG C；
S8：The brick taking-up of injection formed in step S7 is put into baking oven, the temperature for controlling baking oven is 50 DEG C, control drying
The time of room drying is 24-48 hours, is given over to after drying spare；
S9：The Footpath brick that brick after being dried in step S8 is cut into fritter with cutting machine is sold.
Synthetic resin is PVC- polyvinyl chloride in the step S1, and the specification of quartz sand is 8mm in the step S1, described
The a diameter of 8mm of filtered quartz sand in step S3, the length, width and height of the step S7 brick dies be respectively 100cm, 60cm,
The length, width and height of 7cm, the Footpath brick after the step S9 cuttings are respectively 20cm, 20cm, 7cm.
A kind of method producing Footpath brick with resin and papermaking black mud provided by the invention, after synthetic resin and papermaking
Remaining black mud carries out Combination heating production as raw material, and wherein synthetic resin and black mud source is wide, cheap, passes through conjunction
Hybrid Heating stirring is carried out with the quartz sand after powdered black mud and cleaning after being heated at resin, is dried again after injection molding
It is dry so that after the moisture of Footpath brick is oven-dried evaporation, then to be cut so that the Footpath brick finally has excellent toughness and modeling
Property, it is laid with and is not likely to produce rupture, damaged situation on pavement, because having used synthetic resin, lighter in weight.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of method producing Footpath brick with resin and papermaking black mud, it is characterised in that：The resin and papermaking black mud production step
The method of road brick is as follows：
S1：Suitable quartz sand is chosen, remaining blocky black mud stays after selecting suitable synthetic resin and collecting paper production
It does spare；
S2：The quartz sand collected in step S1 is put into ultrasonic cleaning pond, pure water, quartz sand are added in quartz sand
The water temperature of service sink is set as 40 DEG C, cleans 1-2 hours；
S3：The quartz sand strainer filtering that will be cleaned in step S2, and be put into 1-2 hours in baking oven and go moisture removal, baking oven temperature
Degree be set as 60-100 DEG C, stayed after drying do it is spare；
S4：The blocky black mud collected in step S1 is smashed with crusher, it is 15-20 minutes to smash the time, is then taken out standby
With.
S5：The synthetic resin being collected into step S1 is put into and carries out heating hot melt in hot melting furnace, wherein control hot melting furnace
Hot melting temperature is 120 DEG C -170 DEG C, controls the hot molten time 70min-80min of hot melting furnace, the synthetic resin heated is stayed and is done
It is spare；
S6：Black mud by step S5 and the S4 synthetic resin heated obtained and after smashing is put into heating stirring machine, and to
Pure water and hydrogen peroxide are added in heating stirring machine, the wherein weight ratio of black mud, pure water and hydrogen peroxide is 15:8:3 heating
Stir 100-120min, heating temperature is set as 60 DEG C, stay do it is spare；
S7：The mixture of the black mud, pure water and the hydrogen peroxide that are obtained in step S6 is added in injection molding machine, and uses injection molding machine
It is molded into brick die, wherein the injection temperature of injection molding machine is controlled at 155 DEG C -165 DEG C；
S8：The brick taking-up of injection formed in step S7 is put into baking oven, the temperature for controlling baking oven is 50 DEG C -55 DEG C, and control is dried
The time of dry chamber drying is 24-48 hours, is given over to after drying spare；
S9：The Footpath brick that brick after being dried in step S8 is cut into fritter with cutting machine is sold.
2. a kind of method producing Footpath brick with resin and papermaking black mud according to claim 1, it is characterised in that：It is described
Synthetic resin is one or more of PE- polyethylene, PP- polypropylene, PVC- polyvinyl chloride material composition in step S1.
3. a kind of method producing Footpath brick with resin and papermaking black mud according to claim 1, it is characterised in that：It is described
The specification of quartz sand is 4-8mm in step S1.
4. a kind of method producing Footpath brick with resin and papermaking black mud according to claim 1, it is characterised in that：It is described
Filtered quartz sand diameter in step S3 is not more than greatly 8mm.
5. a kind of method producing Footpath brick with resin and papermaking black mud according to claim 1, it is characterised in that：It is described
The length, width and height of step S7 brick dies are respectively 100cm, 60cm, 7cm.
6. a kind of method producing Footpath brick with resin and papermaking black mud according to claim 1, it is characterised in that：It is described
The length, width and height of Footpath brick after step S9 cuttings are respectively 20cm, 20cm, 7cm.