CN108611927A - A kind of waterproof and dampproof corrugated paper and preparation method thereof - Google Patents
A kind of waterproof and dampproof corrugated paper and preparation method thereof Download PDFInfo
- Publication number
- CN108611927A CN108611927A CN201810297571.4A CN201810297571A CN108611927A CN 108611927 A CN108611927 A CN 108611927A CN 201810297571 A CN201810297571 A CN 201810297571A CN 108611927 A CN108611927 A CN 108611927A
- Authority
- CN
- China
- Prior art keywords
- waterproof
- layer
- corrugated paper
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of papermaking, a kind of waterproof and dampproof corrugated paper and preparation method thereof is specifically disclosed.A kind of waterproof and dampproof corrugated paper includes waterproof layer, high intensity cardboard, filled layer, waterproof layer, and drier is filled in the filled layer.Preparation method is:By waterproof layer, high intensity cardboard, filled layer and waterproof layer is compound successively forms, specifically, the high intensity cardboard, by wood pulp, starch and sugarcane fasciated fiber and by weight 10:4:2:1 is mixed;It is manufactured paper with pulp as the slurry by obtained by after size degradation, purification, flotation and defibrination process, obtains high intensity cardboard;By two high intensity cardboards and drier therein is placed by high pressure, forms filled layer;After high intensity cardboard and filled layer pressing, in top sizing, corrugated paper is formed.A kind of waterproof and dampproof corrugated paper of the present invention and preparation method thereof has been obviously improved the waterproof and dampproof ability of corrugated paper, to improve the safety of corrugation paper wrapper.
Description
Technical field
The present invention relates to field of papermaking, a kind of waterproof and dampproof corrugated paper and preparation method thereof is specifically disclosed.
Background technology
Packaging material is to one of the major function that the protectiveness of built-in amount of substance is packaging, and inner packing is even more to be protected to commodity
Shield property plays the role of vital.
Corrugated board is the adherend of a multilayer, it is at least made of one layer of waveform refill layer and a layer paperboard.Corrugation
Cardboard has very high mechanical strength, can fall to the collision and falling in by cargo handling process, mainly for the manufacture of carton and
The outer packing of delicate articles.
Currently, corrugated board is mainly made of fibrous web, it is easy the shadow by external environmental factors such as humidity, temperature
It rings.In the higher environment of some humidity, corrugated board is easy to conduct the moisture of absorption to packaging article, indirectly
Reduce the quality of article;And when corrugated board directly meets with water, then it is easy directly to soak packaging article, gives people
Bring economic loss.
Invention content
In order to overcome shortcoming and defect existing in the prior art, the purpose of the present invention is to provide waterproof and dampproof watt a kind of
Stupefied paper and preparation method thereof.
To achieve the above object, the present invention uses following scheme.
There is a kind of waterproof and dampproof corrugated paper lamination layer structure, composite layer to be followed successively by waterproof layer, high intensity cardboard, fill
Layer, waterproof layer are filled with drier in the filled layer.Drier is calcium chloride.
Wherein, waterproof layer is formed by top sizing.Waterproof layer is by 24-31 parts by weight epoxy-polyurethane adhesive, 6-13 weight
Part melamine, 13-17 parts by weight of lemon acid sodium, 3-5 parts by weight dimethylethanolamine, 2-5 parts by weight magnesium hydroxide, 6-8 weights
Measure part alundum (Al2O3), 3-10 parts by weight of silica, 15-22 parts by weight hydroxypropyls PASELLI EASYGEL, 6-11 parts by weight silicon
Sour calcium composition.
Waterproof and dampproof corrugated paper can be by waterproof layer, high intensity cardboard, filled layer and waterproof layer is compound successively forms, specifically
For by wood pulp, starch and sugarcane fasciated fiber by weight 10:4:2:1 is mixed, and passes through size degradation, purification, flotation and defibrination
Gained slurry is manufactured paper with pulp after processing, obtains high intensity cardboard;By two high intensity cardboards and drier therein is placed through overvoltage
It closes, forms filled layer;After high intensity cardboard and filled layer pressing, waterproof layer is formed in top sizing, it is anti-to obtain waterproof
Damp corrugated paper.
Wherein, the sugarcane fasciated fiber in high intensity cardboard can improve the tearing toughness of cardboard, with filled with drying
After the filled layer of agent is compound, paper can be prevented to be torn because of external stress in all directions.
Surface sizing method is:
(1) melamine, sodium citrate, dimethylethanolamine are mixed first, are added in reaction kettle, deionized water is added,
Then magnesium hydroxide and alundum (Al2O3), silica are added, is heated to 160-180 DEG C, soaking time 1-1.5 hours;
(2) hydroxypropyl PASELLI EASYGEL, calcium silicates, 65-85 DEG C of temperature, reaction time 2-3 hour is secondly added;It is eventually adding
Epoxy-polyurethane glue stirs, and forms glue;
(3) it is stirred evenly after water repellent agent being added in glue, mixed glue solution is then transported to holding vessel, then will be in holding vessel
Glue is delivered directly in sizing applicator, is carried out top sizing, is then dried, and top sizing layer is formed.
The spray pressure of the sizing agent of the sizing applicator is 0.2-0.24Mpa, spraying rate 130-150m/min.
Beneficial effects of the present invention:It is anti-that the waterproof and dampproof corrugated paper and preparation method thereof of the present invention has been obviously improved corrugated paper
The moisture-proof ability of water, to improve the safety of corrugation paper wrapper.
Description of the drawings
Fig. 1 is the structural schematic diagram of size applicator of the present invention.
Specific implementation mode
For the ease of the understanding of those skilled in the art, the present invention is made further with reference to embodiment and attached drawing
Bright, the content that embodiment refers to not is limitation of the invention.
The preparation method of waterproof and dampproof corrugated paper is:It is compound successively by waterproof layer, high intensity cardboard, filled layer and waterproof layer
Composition, specifically, the high intensity cardboard, by wood pulp, starch and sugarcane fasciated fiber and by weight 10:4:2:1 mixing system
At;It is manufactured paper with pulp as the slurry by obtained by after size degradation, purification, flotation and defibrination process, obtains high intensity cardboard;By two high intensity
Cardboard and placement drier therein pass through high pressure, form filled layer;After high intensity cardboard and filled layer pressing, applied on surface
Glue forms corrugated paper.
Surface sizing method is:
Embodiment one:
(1) 6 parts of melamines, 13 parts of sodium citrates, 5 parts of dimethylethanolamines are mixed by weight first, is added to reaction
In kettle, deionized water is added, then adds the 2 parts of magnesium hydroxides, 6 parts of alundum (Al2O3)s, 10 parts of silica of proportional quantity, adds
Heat is to 180 DEG C, soaking time 1.5 hours;
(2) said mixture is added in hydro-thermal tank, and sequentially adds 15 parts by weight hydroxypropyl PASELLI EASYGELs, 11 weight
Part calcium silicates, 85 DEG C of temperature, 2 hours reaction time;Then the stirring of 31 parts by weight epoxy-polyurethane adhesive is added, forms glue;
(3) it is stirred evenly after water repellent agent being added in glue, mixed glue solution is then transported to holding vessel, the glue in holding vessel
It is delivered directly to sizing applicator, top sizing is carried out, then dries.
Embodiment two:
(1) 13 parts of melamines, 17 parts of sodium citrates, 3 parts of dimethylethanolamines are mixed by weight first, is added to reaction
In kettle, deionized water is added, then adds the 5 parts of magnesium hydroxides, 8 parts of alundum (Al2O3)s, 3 parts of silica of proportional quantity, adds
Heat is to 160 DEG C, soaking time 1 hour;
(2) said mixture is added in hydro-thermal tank, and sequentially adds 22 parts by weight hydroxypropyl PASELLI EASYGELs, 6 weight
Part calcium silicates, 65 DEG C of temperature, 3 hours reaction time;Then the stirring of 24 parts by weight epoxy-polyurethane adhesive is added, forms glue;
(3) it is stirred evenly after water repellent agent being added in glue, mixed glue solution is then transported to holding vessel, the glue in holding vessel
It is delivered directly to sizing applicator, top sizing is carried out, then dries.
As shown in Fig. 1, the size applicator of waterproof and dampproof corrugated paper includes:Reaction kettle 1, hydro-thermal tank 2, fluid reservoir 3, sizing
Machine, baking oven 9, sizing applicator include rack 8, upper application roll 4, lower application roll 5, upper glue spraying pipe 6, lower glue spraying pipe 7.
Reaction kettle connects hydro-thermal tank, and hydro-thermal tank is connect with fluid reservoir, and glue is stored in fluid reservoir, is applied in fluid reservoir connection
Sebific duct and lower sizing pipe, rack are located between upper sizing pipe and lower sizing pipe, the position setting being located in rack beside sizing pipe
It, can be by being glued roller compaction after thering is application roll, sizing pipe to spray glue on paper, and be transported in baking oven by rack
Drying forms glue application layer.
The above content is only presently preferred embodiments of the present invention, for those of ordinary skill in the art, according to the present invention
Thought, there will be changes in the specific implementation manner and application range, and the content of the present specification should not be construed as to the present invention
Limitation.
Claims (7)
1. a kind of waterproof and dampproof corrugated paper, it is characterised in that:With lamination layer structure, composite layer is followed successively by waterproof layer, high intensity
Cardboard, filled layer, waterproof layer are filled with drier in the filled layer.
2. waterproof and dampproof corrugated paper according to claim 1, it is characterised in that:Waterproof layer is formed by top sizing.
3. waterproof and dampproof corrugated paper according to claim 1, it is characterised in that:Waterproof layer is poly- by 24-31 parts by weight epoxy-
Urethane glue, 6-13 parts by weight melamine, 13-17 parts by weight of lemon acid sodium, 3-5 parts by weight dimethylethanolamine, 2-5 parts by weight
Magnesium hydroxide, 6-8 parts by weight alundum (Al2O3), 3-10 parts by weight of silica, two starch phosphate of 15-22 parts by weight hydroxypropyl
Ester, 6-11 parts by weight calcium silicates composition.
4. waterproof and dampproof corrugated paper according to claim 1, it is characterised in that:Drier is calcium chloride.
5. a kind of waterproof and dampproof corrugated paper and preparation method thereof, it is characterised in that:By waterproof layer, high intensity cardboard, filled layer and
Waterproof layer compound composition successively, specifically, by wood pulp, starch and sugarcane fasciated fiber by weight 10:4:2:1 is mixed;It is logical
Gained slurry is manufactured paper with pulp after crossing size degradation, purification, flotation and defibrination process, obtains high intensity cardboard;
By two high intensity cardboards and drier therein is placed by pressing, forms filled layer;
After high intensity cardboard and filled layer pressing, waterproof layer is formed in top sizing, to obtain waterproof and dampproof corrugated paper;
Surface sizing method is:
(1) melamine, sodium citrate, dimethylethanolamine are mixed first, are added in reaction kettle, deionized water is added,
Then magnesium hydroxide and alundum (Al2O3), silica are added, is heated to 160-180 DEG C, soaking time 1-1.5 hours;
(2) hydroxypropyl PASELLI EASYGEL, calcium silicates, 65-85 DEG C of temperature, reaction time 2-3 hour is secondly added;It is eventually adding
Epoxy-polyurethane glue stirs, and forms glue;
(3) it is stirred evenly after water repellent agent being added in glue, mixed glue solution is then transported to holding vessel, then will be in holding vessel
Glue is delivered directly in sizing applicator, is carried out top sizing, is then dried, and top sizing layer is formed.
6. a kind of waterproof and dampproof corrugated paper according to claim 5 and preparation method thereof, it is characterised in that:Drier is chlorine
Change calcium.
7. a kind of waterproof and dampproof corrugated paper according to claim 5 and preparation method thereof, it is characterised in that:The sizing applicator
Sizing agent spray pressure be 0.2-0.24Mpa, spraying rate 130-150m/min.