CN108556447A - A kind of fire-retardant brown paper - Google Patents
A kind of fire-retardant brown paper Download PDFInfo
- Publication number
- CN108556447A CN108556447A CN201810295873.8A CN201810295873A CN108556447A CN 108556447 A CN108556447 A CN 108556447A CN 201810295873 A CN201810295873 A CN 201810295873A CN 108556447 A CN108556447 A CN 108556447A
- Authority
- CN
- China
- Prior art keywords
- retardant
- fire
- layer
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of papermaking, specifically disclose a kind of fire-retardant brown paper.A kind of fire-retardant brown paper includes flame-retardant layer, kraft paper core, filled layer, flame-retardant layer, filled with fire extinguishing material in the filled layer.Preparation method is:It is formed by flame-retardant layer, kraft paper core, filled layer and flame-retardant layer are compound successively, specifically, wood pulp, starch and sugarcane fasciated fiber are manufactured paper with pulp as the slurry by obtained by after size degradation, purification, flotation and defibrination process by a certain percentage, obtains kraft paper core;By two kraft paper cores and fire extinguishing material therein is placed by high pressure, forms filled layer;After kraft paper core and filled layer pressing, in top sizing, brown paper is formed.A kind of fire-retardant brown paper of the present invention has been obviously improved Flame Retardancy, prevents it from being lost because of combustion zone when as packaging material.
Description
Technical field
The present invention relates to field of papermaking, specifically disclose a kind of fire-retardant brown paper.
Background technology
Packaging material is to one of the major function that the protectiveness of built-in amount of substance is packaging, and inner packing is even more to be protected to commodity
Shield property plays the role of vital.
Brown paper is tough and tensile water-fast package paper, is in brown color, has many uses, main quality requirement is flexible knot
Real, bursting strength is high, can bear larger pulling force and pressure does not rupture, and is mainly used for wrapping paper, envelope, paper bag etc. and printing machine rolling
Cylinder cylinder-packing etc..
However, although brown paper has a higher tearing toughness, but the common fault that unavoidable paper is inflammable, for
The storage of brown paper brings limitation with use, therefore the anti-flammability for improving brown paper has application value very much.
Invention content
In order to overcome shortcoming and defect existing in the prior art, the purpose of the present invention is to provide a kind of fire-retardant ox-hides
Paper.
To achieve the above object, the present invention uses following scheme.
There is a kind of fire-retardant brown paper lamination layer structure, composite layer to be followed successively by flame-retardant layer, kraft paper core, and filled layer is fire-retardant
Layer, filled with fire extinguishing material in the filled layer.The group of fire extinguishing material becomes tetrachloro Bromofume, ammonium carbonate and talcum powder, matter
Amount is than being 1:12:10.
Wherein, the fire extinguishing material in filled layer by accidental destruction and when burning, can play resistance in brown paper because of flame-retardant layer
The effect of combustion and fire extinguishing, prevents the burning of brown paper.
Wherein, flame-retardant layer is formed by top sizing.Flame-retardant layer is by 30-45 parts by weight epoxy-polyurethane adhesive, 5-10 weight
Part melamine, 10-12 parts by weight of urea, 3-5 parts by weight of phosphoric acid front threes phenyl ester, 1-3 parts by weight magnesium hydroxide, 2-6 parts by weight
Line borate, 3-10 weight parts of calcium carbonate, 15-22 parts by weight hydroxypropyls PASELLI EASYGEL, 6-11 parts by weight sodium perborate composition.
Fire-retardant brown paper can be formed by flame-retardant layer, kraft paper core, filled layer and flame-retardant layer are compound successively, specifically, will
Wood pulp, starch and sugarcane fasciated fiber are by weight 10:4:2:1 is mixed, and passes through size degradation, purification, flotation and defibrination process
Gained slurry is manufactured paper with pulp afterwards, obtains kraft paper core;By two kraft paper cores and fire extinguishing material therein is placed by pressing, is formed
Filled layer;After kraft paper core and filled layer pressing, flame-retardant layer is formed in top sizing, to obtain fire-retardant brown paper.
Surface sizing method is:
(1) melamine, urea, tricresyl phosphate are mixed first, is added in reaction kettle, alcohol solvent is added, then
Magnesium hydroxide and line borate, calcium carbonate are added, is heated to 160-180 DEG C, soaking time 1-1.5 hours;
(2) hydroxypropyl PASELLI EASYGEL, sodium perborate, 65-85 DEG C of temperature, reaction time 2-3 hour is secondly added;Then plus
Enter the stirring of epoxy-polyurethane glue, forms glue;
(3) it is stirred evenly after water repellent agent being added in glue, mixed glue solution is then transported to holding vessel, then will be in holding vessel
Glue is delivered directly in sizing applicator, is carried out top sizing, is then dried, and top sizing layer is formed.
Beneficial effects of the present invention:Fire-retardant brown paper has been obviously improved Flame Retardancy, prevents it as packaging material
When lose because of combustion zone.
Description of the drawings
Fig. 1 is the structural schematic diagram of size applicator of the present invention.
Specific implementation mode
For the ease of the understanding of those skilled in the art, the present invention is made further with reference to embodiment and attached drawing
Bright, the content that embodiment refers to not is limitation of the invention.
The preparation method of fire-retardant brown paper is:It is formed by flame-retardant layer, kraft paper core, filled layer and flame-retardant layer are compound successively,
Specifically, the kraft paper core, by wood pulp, starch and sugarcane fasciated fiber and by weight 10:4:2:1 is mixed;Pass through
Gained slurry is manufactured paper with pulp after size degradation, purification, flotation and defibrination process, obtains kraft paper core;By two kraft paper cores and placement
Fire extinguishing material therein passes through high pressure, forms filled layer;After kraft paper core and filled layer pressing, in top sizing, ox is formed
Mulberry paper.
Surface sizing method is:
Embodiment one:
(1) 5 parts of melamines, 10 parts of urea, 5 parts of tricresyl phosphates are mixed by weight first, are added in reaction kettle,
Then the 1 part of magnesium hydroxide, 6 parts of line borates, 10 parts of calcium carbonate for adding proportional quantity, are heated to 180 DEG C, soaking time 1.5 is small
When;
(2) said mixture is added in hydro-thermal tank, and sequentially adds 15 parts by weight hydroxypropyl PASELLI EASYGELs, 11 weight
Part sodium perborate, 85 DEG C of temperature, 2 hours reaction time;Then the stirring of 45 parts by weight epoxy-polyurethane adhesive is added, forms glue
(3) it is stirred evenly after water repellent agent being added in glue, mixed glue solution is then transported to holding vessel, the glue in holding vessel
It is delivered directly to sizing applicator, top sizing is carried out, then dries.
Embodiment two:
(1) 10 parts of melamines, 12 parts of urea, 3 parts of tricresyl phosphates are mixed by weight first, is added to reaction kettle
In, the 3 parts of magnesium hydroxides, 2 parts of line borates, 3 parts of calcium carbonate of proportional quantity are then added, are heated to 160 DEG C, soaking time 1 is small
When;
(2) said mixture is added in hydro-thermal tank, and sequentially adds 22 parts by weight hydroxypropyl PASELLI EASYGELs, 6 weight
Part sodium perborate, 65 DEG C of temperature, 3 hours reaction time;Then the stirring of 30 parts by weight epoxy-polyurethane adhesive is added, forms glue
(3) it is stirred evenly after water repellent agent being added in glue, mixed glue solution is then transported to holding vessel, the glue in holding vessel
It is delivered directly to sizing applicator, top sizing is carried out, then dries.
As shown in Fig. 1, the size applicator of fire-retardant brown paper includes:Reaction kettle 1, hydro-thermal tank 2, fluid reservoir 3, sizing applicator,
Baking oven 9, sizing applicator include rack 8, upper application roll 4, lower application roll 5, upper glue spraying pipe 6, lower glue spraying pipe 7.
Reaction kettle connects hydro-thermal tank, and hydro-thermal tank is connect with fluid reservoir, and glue is stored in fluid reservoir, is applied in fluid reservoir connection
Sebific duct and lower sizing pipe, rack are located between upper sizing pipe and lower sizing pipe, the position setting being located in rack beside sizing pipe
It, can be by being glued roller compaction after thering is application roll, sizing pipe to spray glue on paper, and be transported in baking oven by rack
Drying forms glue application layer.
The above content is only presently preferred embodiments of the present invention, for those of ordinary skill in the art, according to the present invention
Thought, there will be changes in the specific implementation manner and application range, and the content of the present specification should not be construed as to the present invention
Limitation.
Claims (6)
1. a kind of fire-retardant brown paper, it is characterised in that:With lamination layer structure, composite layer is followed successively by flame-retardant layer, kraft paper core, fills out
Fill layer, flame-retardant layer, filled with fire extinguishing material in the filled layer.
2. fire-retardant brown paper according to claim 1, it is characterised in that:The flame-retardant layer is formed by top sizing.
3. fire-retardant brown paper according to claim 1, it is characterised in that:The flame-retardant layer is poly- by 30-45 parts by weight epoxy-
Urethane glue, 5-10 parts by weight melamine, 10-12 parts by weight of urea, 3-5 parts by weight of phosphoric acid front threes phenyl ester, 1-3 parts by weight hydrogen-oxygens
Change magnesium, 2-6 part by weight of boric acid calcium, 3-10 weight parts of calcium carbonate, 15-22 parts by weight hydroxypropyls PASELLI EASYGEL, 6-11 weight
Part sodium perborate composition.
4. fire-retardant brown paper according to claim 1, it is characterised in that:The group of the fire extinguishing material becomes tetrachloro dibromo second
Alkane, ammonium carbonate and talcum powder.
5. fire-retardant brown paper according to claim 5, it is characterised in that:The tetrachloro Bromofume, ammonium carbonate and talcum
The mass ratio of powder is 1:12:10.
6. fire-retardant brown paper according to claim 1, it is characterised in that:The filled layer is by two kraft paper cores and setting
Fire extinguishing material therebetween presses.