CN108610894A - 一种土木建筑路桥施工桥梁连接栏杆表面涂层 - Google Patents
一种土木建筑路桥施工桥梁连接栏杆表面涂层 Download PDFInfo
- Publication number
- CN108610894A CN108610894A CN201611149912.0A CN201611149912A CN108610894A CN 108610894 A CN108610894 A CN 108610894A CN 201611149912 A CN201611149912 A CN 201611149912A CN 108610894 A CN108610894 A CN 108610894A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- bridge
- oil
- mesh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种土木建筑路桥施工桥梁连接栏杆表面涂层，由以下组分组成：邻甲酚醛环氧树脂、聚对苯二甲酰对苯二胺、氟橡胶、氟硅油、三辛酸甘油酯、芳烃油、迷迭香精油、聚甘油蓖麻醇酯、十二烷基二甲基苄基氯化铵、乌洛托品、大蒜油、洗必泰、双十八烷基二甲基氯化铵、活性碳酸钙、异辛酸锌、石英砂粉末、锂辉石粉、二硅化钼粉末、聚六亚甲基双胍盐酸盐、木质纤维素、锑酸钠粉末、三甘醇二异辛酸酯、磷酸三甲酚酯、十溴联苯醚、苯乙烯化苯酚、乙二胺四乙酸四钠、乙酸钾、山梨酸、氟基烷基聚醚改性聚硅氧烷、烷基磺酸钠。本发明产品具有较为优越的阻燃、耐酸碱、防霉变抗菌性能，改善了产品性能。
Description
技术领域
本发明涉及一种土木建筑路桥施工桥梁连接栏杆表面涂层，属于土木桥梁建设技术领域。
背景技术
土木建筑中，经常需要针对路桥进行施工处理，其中，需要针对桥梁进行施工改善处理。这些桥梁都离不开连接栏杆的安装和处理，一般的连接栏杆表面需要采用合适的涂层予以保护，以便能够改善其使用效果，这些涂层材料往往使用效果不好，有必要予以改进。
发明内容
本发明的目的在于提供一种土木建筑路桥施工桥梁连接栏杆表面涂层，以便更好地实现土木建筑路桥施工桥梁连接栏杆表面涂层的使用功能，使产品具有阻燃、耐酸碱、防霉变抗菌性能，改善产品使用性能。
为了实现上述目的，本发明的技术方案如下。
一种土木建筑路桥施工桥梁连接栏杆表面涂层，由以下质量份数的组分组成：邻甲酚醛环氧树脂26～30份、聚对苯二甲酰对苯二胺24～28份、氟橡胶24～28份、氟硅油22～26份、三辛酸甘油酯24～28份、芳烃油24～28份、迷迭香精油22～26份、聚甘油蓖麻醇酯24～28份、十二烷基二甲基苄基氯化铵24～28份、乌洛托品22～26份、大蒜油22～26份、洗必泰22～26份、双十八烷基二甲基氯化铵24～28份、活性碳酸钙22～26份、异辛酸锌20～24份、石英砂粉末24～28份、锂辉石粉22～26份、二硅化钼粉末20～24份、聚六亚甲基双胍盐酸盐22～26份、木质纤维素20～24份、锑酸钠粉末20～24份、三甘醇二异辛酸酯20～24份、磷酸三甲酚酯18～22份、十溴联苯醚14～18份、苯乙烯化苯酚12～16份、乙二胺四乙酸四钠12～16份、乙酸钾12～16份、山梨酸12～16份、氟基烷基聚醚改性聚硅氧烷12～16份、烷基磺酸钠12～16份。
进一步地，上述土木建筑路桥施工桥梁连接栏杆表面涂层，由以下质量份数的组分组成：邻甲酚醛环氧树脂26份、聚对苯二甲酰对苯二胺24份、氟橡胶24份、氟硅油22份、三辛酸甘油酯24份、芳烃油24份、迷迭香精油22份、聚甘油蓖麻醇酯24份、十二烷基二甲基苄基氯化铵24份、乌洛托品22份、大蒜油22份、洗必泰22份、双十八烷基二甲基氯化铵24份、活性碳酸钙22份、异辛酸锌20份、石英砂粉末24份、锂辉石粉22份、二硅化钼粉末20份、聚六亚甲基双胍盐酸盐22份、木质纤维素20份、锑酸钠粉末20份、三甘醇二异辛酸酯20份、磷酸三甲酚酯18份、十溴联苯醚14份、苯乙烯化苯酚12份、乙二胺四乙酸四钠12份、乙酸钾12份、山梨酸12份、氟基烷基聚醚改性聚硅氧烷12份、烷基磺酸钠12份。
进一步地，上述土木建筑路桥施工桥梁连接栏杆表面涂层，由以下质量份数的组分组成：邻甲酚醛环氧树脂28份、聚对苯二甲酰对苯二胺26份、氟橡胶26份、氟硅油24份、三辛酸甘油酯26份、芳烃油26份、迷迭香精油24份、聚甘油蓖麻醇酯26份、十二烷基二甲基苄基氯化铵26份、乌洛托品24份、大蒜油24份、洗必泰24份、双十八烷基二甲基氯化铵26份、活性碳酸钙24份、异辛酸锌22份、石英砂粉末26份、锂辉石粉24份、二硅化钼粉末22份、聚六亚甲基双胍盐酸盐24份、木质纤维素22份、锑酸钠粉末22份、三甘醇二异辛酸酯22份、磷酸三甲酚酯20份、十溴联苯醚16份、苯乙烯化苯酚14份、乙二胺四乙酸四钠14份、乙酸钾14份、山梨酸14份、氟基烷基聚醚改性聚硅氧烷14份、烷基磺酸钠14份。
进一步地，上述土木建筑路桥施工桥梁连接栏杆表面涂层，由以下质量份数的组分组成：邻甲酚醛环氧树脂30份、聚对苯二甲酰对苯二胺28份、氟橡胶28份、氟硅油26份、三辛酸甘油酯28份、芳烃油28份、迷迭香精油26份、聚甘油蓖麻醇酯28份、十二烷基二甲基苄基氯化铵28份、乌洛托品26份、大蒜油26份、洗必泰26份、双十八烷基二甲基氯化铵28份、活性碳酸钙26份、异辛酸锌24份、石英砂粉末28份、锂辉石粉26份、二硅化钼粉末24份、聚六亚甲基双胍盐酸盐26份、木质纤维素24份、锑酸钠粉末24份、三甘醇二异辛酸酯24份、磷酸三甲酚酯22份、十溴联苯醚18份、苯乙烯化苯酚16份、乙二胺四乙酸四钠16份、乙酸钾16份、山梨酸16份、氟基烷基聚醚改性聚硅氧烷16份、烷基磺酸钠16份。
进一步地，所述活性碳酸钙由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～9∶4～8∶1。
进一步地，所述二硅化钼粉末由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～7∶2～8∶1。
进一步地，所述迷迭香精油的粘度在25℃为120～140mpa.s。
进一步地，所述石英砂粉末由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为2～4∶3～5∶1。
进一步地，所述氟硅油的粘度在25℃为80～100mpa.s。
进一步地，上述土木建筑路桥施工桥梁连接栏杆表面涂层制备方法步骤如下：
(1)将所述质量份数的邻甲酚醛环氧树脂、聚对苯二甲酰对苯二胺、氟橡胶、氟硅油、三辛酸甘油酯、芳烃油、迷迭香精油、聚甘油蓖麻醇酯、十二烷基二甲基苄基氯化铵、乌洛托品、大蒜油、洗必泰、双十八烷基二甲基氯化铵、活性碳酸钙、异辛酸锌、石英砂粉末、锂辉石粉、二硅化钼粉末、聚六亚甲基双胍盐酸盐、木质纤维素予以混合，超声高速分散，超声波频率为20～40KHz，分散速度5000～5400r/min左右，分散时间为30～60min；
(2)加入所述质量份数的锑酸钠粉末、三甘醇二异辛酸酯、磷酸三甲酚酯、十溴联苯醚、苯乙烯化苯酚，超声高速分散，超声波频率为20～35KHz，分散速度4800～5200r/min左右，分散时间为30～50min；
(3)加入所述质量份数的乙二胺四乙酸四钠、乙酸钾、山梨酸、氟基烷基聚醚改性聚硅氧烷、烷基磺酸钠，超声高速分散，超声波频率为20～30KHz，分散速度4600～4800r/min左右，分散时间为20～40min；混合均匀后制得本品。
该发明的有益效果在于：本发明中的土木建筑路桥施工桥梁连接栏杆表面涂层，由以下组分组成：邻甲酚醛环氧树脂、聚对苯二甲酰对苯二胺、氟橡胶、氟硅油、三辛酸甘油酯、芳烃油、迷迭香精油、聚甘油蓖麻醇酯、十二烷基二甲基苄基氯化铵、乌洛托品、大蒜油、洗必泰、双十八烷基二甲基氯化铵、活性碳酸钙、异辛酸锌、石英砂粉末、锂辉石粉、二硅化钼粉末、聚六亚甲基双胍盐酸盐、木质纤维素、锑酸钠粉末、三甘醇二异辛酸酯、磷酸三甲酚酯、十溴联苯醚、苯乙烯化苯酚、乙二胺四乙酸四钠、乙酸钾、山梨酸、氟基烷基聚醚改性聚硅氧烷、烷基磺酸钠。本发明产品具有较为优越的阻燃、耐酸碱、防霉变抗菌性能，改善了产品性能。
具体实施方式
下面结合实施例对本发明的具体实施方式进行描述，以便更好的理解本发明。
实施例1
本实施例中的土木建筑路桥施工桥梁连接栏杆表面涂层，由以下质量份数的组分组成：邻甲酚醛环氧树脂26份、聚对苯二甲酰对苯二胺24份、氟橡胶24份、氟硅油22份、三辛酸甘油酯24份、芳烃油24份、迷迭香精油22份、聚甘油蓖麻醇酯24份、十二烷基二甲基苄基氯化铵24份、乌洛托品22份、大蒜油22份、洗必泰22份、双十八烷基二甲基氯化铵24份、活性碳酸钙22份、异辛酸锌20份、石英砂粉末24份、锂辉石粉22份、二硅化钼粉末20份、聚六亚甲基双胍盐酸盐22份、木质纤维素20份、锑酸钠粉末20份、三甘醇二异辛酸酯20份、磷酸三甲酚酯18份、十溴联苯醚14份、苯乙烯化苯酚12份、乙二胺四乙酸四钠12份、乙酸钾12份、山梨酸12份、氟基烷基聚醚改性聚硅氧烷12份、烷基磺酸钠12份。
所述活性碳酸钙由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3∶4∶1。
所述二硅化钼粉末由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3∶2∶1。
所述迷迭香精油的粘度在25℃为120mpa.s。
所述石英砂粉末由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为2∶3∶1。
所述氟硅油的粘度在25℃为80mpa.s。
上述土木建筑路桥施工桥梁连接栏杆表面涂层制备方法步骤如下：
(1)将所述质量份数的邻甲酚醛环氧树脂、聚对苯二甲酰对苯二胺、氟橡胶、氟硅油、三辛酸甘油酯、芳烃油、迷迭香精油、聚甘油蓖麻醇酯、十二烷基二甲基苄基氯化铵、乌洛托品、大蒜油、洗必泰、双十八烷基二甲基氯化铵、活性碳酸钙、异辛酸锌、石英砂粉末、锂辉石粉、二硅化钼粉末、聚六亚甲基双胍盐酸盐、木质纤维素予以混合，超声高速分散，超声波频率为20kHz，分散速度5400r/min左右，分散时间为60min；
(2)加入所述质量份数的锑酸钠粉末、三甘醇二异辛酸酯、磷酸三甲酚酯、十溴联苯醚、苯乙烯化苯酚，超声高速分散，超声波频率为20kHz，分散速度5200r/min左右，分散时间为50min；
(3)加入所述质量份数的乙二胺四乙酸四钠、乙酸钾、山梨酸、氟基烷基聚醚改性聚硅氧烷、烷基磺酸钠，超声高速分散，超声波频率为20kHz，分散速度4800r/min左右，分散时间为40min；混合均匀后制得本品。
实施例2
本实施例中的土木建筑路桥施工桥梁连接栏杆表面涂层，由以下质量份数的组分组成：邻甲酚醛环氧树脂28份、聚对苯二甲酰对苯二胺26份、氟橡胶26份、氟硅油24份、三辛酸甘油酯26份、芳烃油26份、迷迭香精油24份、聚甘油蓖麻醇酯26份、十二烷基二甲基苄基氯化铵26份、乌洛托品24份、大蒜油24份、洗必泰24份、双十八烷基二甲基氯化铵26份、活性碳酸钙24份、异辛酸锌22份、石英砂粉末26份、锂辉石粉24份、二硅化钼粉末22份、聚六亚甲基双胍盐酸盐24份、木质纤维素22份、锑酸钠粉末22份、三甘醇二异辛酸酯22份、磷酸三甲酚酯20份、十溴联苯醚16份、苯乙烯化苯酚14份、乙二胺四乙酸四钠14份、乙酸钾14份、山梨酸14份、氟基烷基聚醚改性聚硅氧烷14份、烷基磺酸钠14份。
所述活性碳酸钙由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为6∶6∶1。
所述二硅化钼粉末由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为5∶5∶1。
所述迷迭香精油的粘度在25℃为130mpa.s。
所述石英砂粉末由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为3∶4∶1。
所述氟硅油的粘度在25℃为90mpa.s。
上述土木建筑路桥施工桥梁连接栏杆表面涂层制备方法步骤如下：
(1)将所述质量份数的邻甲酚醛环氧树脂、聚对苯二甲酰对苯二胺、氟橡胶、氟硅油、三辛酸甘油酯、芳烃油、迷迭香精油、聚甘油蓖麻醇酯、十二烷基二甲基苄基氯化铵、乌洛托品、大蒜油、洗必泰、双十八烷基二甲基氯化铵、活性碳酸钙、异辛酸锌、石英砂粉末、锂辉石粉、二硅化钼粉末、聚六亚甲基双胍盐酸盐、木质纤维素予以混合，超声高速分散，超声波频率为30kHz，分散速度5200r/min左右，分散时间为45min；
(2)加入所述质量份数的锑酸钠粉末、三甘醇二异辛酸酯、磷酸三甲酚酯、十溴联苯醚、苯乙烯化苯酚，超声高速分散，超声波频率为27kHz，分散速度5000r/min左右，分散时间为40min；
(3)加入所述质量份数的乙二胺四乙酸四钠、乙酸钾、山梨酸、氟基烷基聚醚改性聚硅氧烷、烷基磺酸钠，超声高速分散，超声波频率为25kHz，分散速度4700r/min左右，分散时间为30min；混合均匀后制得本品。
实施例3
本实施例中的土木建筑路桥施工桥梁连接栏杆表面涂层，由以下质量份数的组分组成：邻甲酚醛环氧树脂30份、聚对苯二甲酰对苯二胺28份、氟橡胶28份、氟硅油26份、三辛酸甘油酯28份、芳烃油28份、迷迭香精油26份、聚甘油蓖麻醇酯28份、十二烷基二甲基苄基氯化铵28份、乌洛托品26份、大蒜油26份、洗必泰26份、双十八烷基二甲基氯化铵28份、活性碳酸钙26份、异辛酸锌24份、石英砂粉末28份、锂辉石粉26份、二硅化钼粉末24份、聚六亚甲基双胍盐酸盐26份、木质纤维素24份、锑酸钠粉末24份、三甘醇二异辛酸酯24份、磷酸三甲酚酯22份、十溴联苯醚18份、苯乙烯化苯酚16份、乙二胺四乙酸四钠16份、乙酸钾16份、山梨酸16份、氟基烷基聚醚改性聚硅氧烷16份、烷基磺酸钠16份。
所述活性碳酸钙由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为9∶8∶1。
所述二硅化钼粉末由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为7∶8∶1。
所述迷迭香精油的粘度在25℃为140mpa.s。
所述石英砂粉末由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为4∶5∶1。
所述氟硅油的粘度在25℃为100mpa.s。
上述土木建筑路桥施工桥梁连接栏杆表面涂层制备方法步骤如下：
(1)将所述质量份数的邻甲酚醛环氧树脂、聚对苯二甲酰对苯二胺、氟橡胶、氟硅油、三辛酸甘油酯、芳烃油、迷迭香精油、聚甘油蓖麻醇酯、十二烷基二甲基苄基氯化铵、乌洛托品、大蒜油、洗必泰、双十八烷基二甲基氯化铵、活性碳酸钙、异辛酸锌、石英砂粉末、锂辉石粉、二硅化钼粉末、聚六亚甲基双胍盐酸盐、木质纤维素予以混合，超声高速分散，超声波频率为40kHz，分散速度5000r/min，分散时间为30min；
(2)加入所述质量份数的锑酸钠粉末、三甘醇二异辛酸酯、磷酸三甲酚酯、十溴联苯醚、苯乙烯化苯酚，超声高速分散，超声波频率为35kHz，分散速度4800r/min，分散时间为30min；
(3)加入所述质量份数的乙二胺四乙酸四钠、乙酸钾、山梨酸、氟基烷基聚醚改性聚硅氧烷、烷基磺酸钠，超声高速分散，超声波频率为30kHz，分散速度4600r/min左右，分散时间为20min；混合均匀后制得本品。
针对实施例1、实施例2和实施例3中的产品和某市售产品进行性能测量，所测得的数据如表1所示。防火阻燃等级测试采用UL94标准。
表1性能测试结果
可见，本发明产品具有较好的耐腐蚀、防火阻燃、防霉变、抗菌性能。
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围。
Claims (10)
1.一种土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：由以下质量份数的组分组成：邻甲酚醛环氧树脂26～30份、聚对苯二甲酰对苯二胺24～28份、氟橡胶24～28份、氟硅油22～26份、三辛酸甘油酯24～28份、芳烃油24～28份、迷迭香精油22～26份、聚甘油蓖麻醇酯24～28份、十二烷基二甲基苄基氯化铵24～28份、乌洛托品22～26份、大蒜油22～26份、洗必泰22～26份、双十八烷基二甲基氯化铵24～28份、活性碳酸钙22～26份、异辛酸锌20～24份、石英砂粉末24～28份、锂辉石粉22～26份、二硅化钼粉末20～24份、聚六亚甲基双胍盐酸盐22～26份、木质纤维素20～24份、锑酸钠粉末20～24份、三甘醇二异辛酸酯20～24份、磷酸三甲酚酯18～22份、十溴联苯醚14～18份、苯乙烯化苯酚12～16份、乙二胺四乙酸四钠12～16份、乙酸钾12～16份、山梨酸12～16份、氟基烷基聚醚改性聚硅氧烷12～16份、烷基磺酸钠12～16份。
2.根据权利要求1所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述土木建筑路桥施工桥梁连接栏杆表面涂层由以下质量份数的组分组成：邻甲酚醛环氧树脂26份、聚对苯二甲酰对苯二胺24份、氟橡胶24份、氟硅油22份、三辛酸甘油酯24份、芳烃油24份、迷迭香精油22份、聚甘油蓖麻醇酯24份、十二烷基二甲基苄基氯化铵24份、乌洛托品22份、大蒜油22份、洗必泰22份、双十八烷基二甲基氯化铵24份、活性碳酸钙22份、异辛酸锌20份、石英砂粉末24份、锂辉石粉22份、二硅化钼粉末20份、聚六亚甲基双胍盐酸盐22份、木质纤维素20份、锑酸钠粉末20份、三甘醇二异辛酸酯20份、磷酸三甲酚酯18份、十溴联苯醚14份、苯乙烯化苯酚12份、乙二胺四乙酸四钠12份、乙酸钾12份、山梨酸12份、氟基烷基聚醚改性聚硅氧烷12份、烷基磺酸钠12份。
3.根据权利要求1至2所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述土木建筑路桥施工桥梁连接栏杆表面涂层由以下质量份数的组分组成：邻甲酚醛环氧树脂28份、聚对苯二甲酰对苯二胺26份、氟橡胶26份、氟硅油24份、三辛酸甘油酯26份、芳烃油26份、迷迭香精油24份、聚甘油蓖麻醇酯26份、十二烷基二甲基苄基氯化铵26份、乌洛托品24份、大蒜油24份、洗必泰24份、双十八烷基二甲基氯化铵26份、活性碳酸钙24份、异辛酸锌22份、石英砂粉末26份、锂辉石粉24份、二硅化钼粉末22份、聚六亚甲基双胍盐酸盐24份、木质纤维素22份、锑酸钠粉末22份、三甘醇二异辛酸酯22份、磷酸三甲酚酯20份、十溴联苯醚16份、苯乙烯化苯酚14份、乙二胺四乙酸四钠14份、乙酸钾14份、山梨酸14份、氟基烷基聚醚改性聚硅氧烷14份、烷基磺酸钠14份。
4.根据权利要求1至3所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述土木建筑路桥施工桥梁连接栏杆表面涂层由以下质量份数的组分组成：邻甲酚醛环氧树脂30份、聚对苯二甲酰对苯二胺28份、氟橡胶28份、氟硅油26份、三辛酸甘油酯28份、芳烃油28份、迷迭香精油26份、聚甘油蓖麻醇酯28份、十二烷基二甲基苄基氯化铵28份、乌洛托品26份、大蒜油26份、洗必泰26份、双十八烷基二甲基氯化铵28份、活性碳酸钙26份、异辛酸锌24份、石英砂粉末28份、锂辉石粉26份、二硅化钼粉末24份、聚六亚甲基双胍盐酸盐26份、木质纤维素24份、锑酸钠粉末24份、三甘醇二异辛酸酯24份、磷酸三甲酚酯22份、十溴联苯醚18份、苯乙烯化苯酚16份、乙二胺四乙酸四钠16份、乙酸钾16份、山梨酸16份、氟基烷基聚醚改性聚硅氧烷16份、烷基磺酸钠16份。
5.根据权利要求1所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述活性碳酸钙由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～9∶4～8∶1。
6.根据权利要求1所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述二硅化钼粉末由三种粒径目数的粉体组成，其粒径目数分别为30～50目、50～80目、80～100目，上述三种粉体的混合质量比例为3～7∶2～8∶1。
7.根据权利要求1所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述迷迭香精油的粘度在25℃为120～140mpa.s。
8.根据权利要求1所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述石英砂粉末由三种粒径目数的粉体组成，其粒径目数分别为20～50目、50～70目、70～90目，上述三种粉体的混合质量比例为2～4∶3～5∶1。
9.根据权利要求1所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述氟硅油的粘度在25℃为80～100mpa.s。
10.根据权利要求1所述的土木建筑路桥施工桥梁连接栏杆表面涂层，其特征在于：所述土木建筑路桥施工桥梁连接栏杆表面涂层制备方法步骤如下：
(1)将所述质量份数的邻甲酚醛环氧树脂、聚对苯二甲酰对苯二胺、氟橡胶、氟硅油、三辛酸甘油酯、芳烃油、迷迭香精油、聚甘油蓖麻醇酯、十二烷基二甲基苄基氯化铵、乌洛托品、大蒜油、洗必泰、双十八烷基二甲基氯化铵、活性碳酸钙、异辛酸锌、石英砂粉末、锂辉石粉、二硅化钼粉末、聚六亚甲基双胍盐酸盐、木质纤维素予以混合，超声高速分散，超声波频率为20～40KHz，分散速度约5000～5400r/min，分散时间为30～60min左右；
(2)加入所述质量份数的锑酸钠粉末、三甘醇二异辛酸酯、磷酸三甲酚酯、十溴联苯醚、苯乙烯化苯酚，超声高速分散，超声波频率为20～35KHz，分散速度为约4800～5200r/min，分散时间为30～50min左右；
(3)加入所述质量份数的乙二胺四乙酸四钠、乙酸钾、山梨酸、氟基烷基聚醚改性聚硅氧烷、烷基磺酸钠，超声高速分散，超声波频率为20～30KHz，分散速度为约4600～4800r/min，分散时间为20～40min左右；混合均匀后制得本品。