CN108589124A - A kind of Anti-deformation knitted fabric - Google Patents
A kind of Anti-deformation knitted fabric Download PDFInfo
- Publication number
- CN108589124A CN108589124A CN201810255064.4A CN201810255064A CN108589124A CN 108589124 A CN108589124 A CN 108589124A CN 201810255064 A CN201810255064 A CN 201810255064A CN 108589124 A CN108589124 A CN 108589124A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fiber
- temperature
- surface layer
- outer layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of Anti-deformation knitted fabric, including bottom surface layer and outer layer, the bottom surface layer are made of cotton fiber and cocoon fiber, and the outer layer is made of polyester fiber, and compared with prior art, the present invention has following advantageous effect:Because being provided with outer layer and bottom surface layer, makes the present invention have wearing comfort good, be not easy Folding Deformation, the high advantage of soft touch degree.
Description
Technical field
The present invention is a kind of Anti-deformation knitted fabric, belongs to fabric technical field.
Background technology
Knitting is by yarn bends lopping and mutually string set and the fabric that is formed using knitting needle.It is knitted fabric and tatting face
Material is the difference is that the form of yarn in the fabric is different.Knitting is divided into weft knitting and warp knit, and raw material passes through in weft knitting produces
Crossing doff later can be the directly upper machine production of cheese.Each of weft-knitting machine is placed on along broadwise sequence ground cushion per one thread
On knitting needle, to form weft-knitted fabric.Raw material is by doff, warping in warp knit production, and yarn is arranged in parallel to be wound into warp beam, so
Upper machine production afterwards.Yarn moves back solution from warp beam and gets off, and respectively pad is placed on one of warp knitting machine or extremely to each one thread along longitudinal direction
On more two knitting needles, to form knitted fabric.Also have on certain knitting machines weft knitting and the combined method of warp knit.This
When be configured with two groups of yarns on knitting machine, one group is pressed warp knitting method band yarn, and another group by weft-knitted method band yarn, and knitting needle is two
Group yarn constitutes coil together, forms knitted fabric.The coil formed by same one thread is matched in weft-knitted fabric along broadwise
It sets, and is then configured along warp-wise in warp-knitted fabric
Currently, knitting fabric is widely used in garment material and lining, in the products such as home textile, liked by consumers in general,
Since the 21th century, as the development of world technology, garment material will develop to high-tech functionalization, garment material should have
The comfortable ventilating sexual function of natural fiber, but should with chemical fibre it is not wrinkled, be not easy to shrink, the not function of flexible type.
Pass happy comfortable with the continuous improvement of people's living standards, people pursue life, it is necessarily comfortable and easy to wear to clothes proposition, have
Elasticity, the requirement of not modification.
Knitting fabric in the prior art is knitted fabric wearing comfort not for a long time using easily Folding Deformation
Good, feel is not soft enough, so being badly in need of wanting a kind of Anti-deformation knitted fabric to solve the above-mentioned problem.
Invention content
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of Anti-deformation knitted fabric, it is above-mentioned to solve
The problem of being proposed in background technology.
To achieve the goals above, the present invention is to realize by the following technical solutions:A kind of Anti-deformation knitted fabric,
Including bottom surface layer and outer layer, the bottom surface layer is made of cotton fiber and cocoon fiber;
The outer layer is made of polyester fiber;
The bottom surface layer is made with outer layer of following steps:
Bottom surface layer is prepared, cotton fiber and cocoon fiber are delivered in frame, while ream is adjusted to 160mm, selects the sides 137cm
Long ryce, while 6 hank ties are used, with the strand frame production rotating speed of 120~160r/min, to cotton fiber and cocoon fiber
Skeining is carried out, skeining is at complete fabric;
Then 8~l0kg fabrics are delivered in the mercerized yarn frame that length is 137cm, are oozed using the alkaline-resisting of a concentration of 3g/L
Saturating agent carries out mercerization finish to fabric, then uses water temperature to carry out hot water wash to fabric in 70~80 DEG C of hot water, reuses 50
DEG C warm water to fabric carry out warm water wash;
Fabric after mercerization finish is delivered to the dye vat in injecting type hank-dyeing machine, high temperature modification activity dye is added to dye vat
Material, makes fabric soaking and dyeing 10min at room temperature, and dye vat temperature is then increased to 80 DEG C, and after impregnating 15min, it is bright that member is added
Powder, then 30min is impregnated, soda ash is then added and impregnates 30~65min;
Then fabric is dehydrated using rubber roller pressure bundle mode;
Drying equipment is reused to dry fabric;
Then the fabric after drying is delivered in open width gas flame gassing frame, using the double burners of a positive and a negative, machine door width
600mm is handled with the loose thread that the speed of 80m/min is exposed to fabric, bottom surface layer is made;
Outer layer is prepared, polyester is subjected to slicing treatment, 0.3%~0.5% titanium dioxide is then added in polyester slice, to poly-
Ester slice carries out delustring;
Then ebullated bed is used to carry out pre-crystallized, crystallization temperature is 160~180 DEG C, and crystallization time is 8~15min, then uses and stir
Formula filling pre-crystallizer is mixed, temperature is 120~140 DEG C, and the time is 1~1.5h;
Polyester slice is processed by screw extruder again, processing temperature is 285~290 DEG C, and Screw Extrusion pressure is 6.6
~7.5MPa, then 20~30 DEG C of temperature is used to the polyester fiber of extrusion, the cold wind of humidity 70% is cooled down;
Then polyester fiber after cooling is compiled into complete polyester fabric by establishment machine again, outer layer is made.
Further, the cotton fiber content accounts for 50~70%, and the cocoon fiber accounts for 30~50%.
Further, the outer layer connect by calender high-temperature laminating with bottom surface layer and is combined into one.
Beneficial effects of the present invention:A kind of Anti-deformation knitted fabric of the present invention makes because being provided with outer layer and bottom surface layer
The present invention has wearing comfort good, is not easy Folding Deformation, the high advantage of soft touch degree.
Specific implementation mode
To make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, with reference to
Specific implementation mode, the present invention is further explained.
The present invention provides a kind of technical solution:A kind of Anti-deformation knitted fabric, including bottom surface layer and outer layer, bottom surface layer by
Cotton fiber is constituted with cocoon fiber.
Outer layer is made of polyester fiber.
Cotton fiber content accounts for 50~70%, and cocoon fiber accounts for 30~50%.
Outer layer connect by calender high-temperature laminating with bottom surface layer and is combined into one.
As an embodiment of the present invention:Bottom surface layer is made with outer layer of following steps:
(1)Bottom surface layer is prepared, cotton fiber and cocoon fiber are delivered in frame, while ream is adjusted to 160mm, is selected
The ryce of the 137cm length of sides, while using 6 hank ties, with the strand frame production rotating speed of 120~160r/min, to cotton fiber with
Cocoon fiber carries out skeining, and skeining is at complete fabric;
Then 8~l0kg fabrics are delivered in the mercerized yarn frame that length is 137cm, are oozed using the alkaline-resisting of a concentration of 3g/L
Saturating agent carries out mercerization finish to fabric, then uses water temperature to carry out hot water wash to fabric in 70~80 DEG C of hot water, reuses 50
DEG C warm water to fabric carry out warm water wash;
Fabric after mercerization finish is delivered to the dye vat in injecting type hank-dyeing machine, high temperature modification activity dye is added to dye vat
Material, makes fabric soaking and dyeing 10min at room temperature, and dye vat temperature is then increased to 80 DEG C, and after impregnating 15min, it is bright that member is added
Powder, then 30min is impregnated, soda ash is then added and impregnates 30~65min;
Then fabric is dehydrated using rubber roller pressure bundle mode;
Drying equipment is reused to dry fabric;
Then the fabric after drying is delivered in open width gas flame gassing frame, using the double burners of a positive and a negative, machine door width
600mm is handled with the loose thread that the speed of 80m/min is exposed to fabric, bottom surface layer is made;
(2)Outer layer is prepared, polyester is subjected to slicing treatment, 0.3%~0.5% titanium dioxide is then added in polyester slice,
Delustring is carried out to polyester slice;
Then ebullated bed is used to carry out pre-crystallized, crystallization temperature is 160~180 DEG C, and crystallization time is 8~15min, then uses and stir
Formula filling pre-crystallizer is mixed, temperature is 120~140 DEG C, and the time is 1~1.5h;
Polyester slice is processed by screw extruder again, processing temperature is 285~290 DEG C, and Screw Extrusion pressure is 6.6
~7.5MPa, then 20~30 DEG C of temperature is used to the polyester fiber of extrusion, the cold wind of humidity 70% is cooled down;
Then polyester fiber after cooling is compiled into complete polyester fabric by establishment machine again, outer layer is made.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from the present invention spirit or
In the case of essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that come within the meaning and range of equivalency of the claims in the present invention
It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (3)
1. a kind of Anti-deformation knitted fabric, including bottom surface layer and outer layer, it is characterised in that:The bottom surface layer is by cotton fiber and very
Silk fiber is constituted;
The outer layer is made of polyester fiber;
The bottom surface layer is made with outer layer of following steps:
Bottom surface layer is prepared, cotton fiber and cocoon fiber are delivered in frame, while ream is adjusted to 160mm, selects the sides 137cm
Long ryce, while 6 hank ties are used, with the strand frame production rotating speed of 120~160r/min, to cotton fiber and cocoon fiber
Skeining is carried out, skeining is at complete fabric;
Then 8~l0kg fabrics are delivered in the mercerized yarn frame that length is 137cm, are oozed using the alkaline-resisting of a concentration of 3g/L
Saturating agent carries out mercerization finish to fabric, then uses water temperature to carry out hot water wash to fabric in 70~80 DEG C of hot water, reuses 50
DEG C warm water to fabric carry out warm water wash;
Fabric after mercerization finish is delivered to the dye vat in injecting type hank-dyeing machine, high temperature modification activity dye is added to dye vat
Material, makes fabric soaking and dyeing 10min at room temperature, and dye vat temperature is then increased to 80 DEG C, and after impregnating 15min, it is bright that member is added
Powder, then 30min is impregnated, soda ash is then added and impregnates 30~65min;
Then fabric is dehydrated using rubber roller pressure bundle mode;
Drying equipment is reused to dry fabric;
Then the fabric after drying is delivered in open width gas flame gassing frame, using the double burners of a positive and a negative, machine door width
600mm is handled with the loose thread that the speed of 80m/min is exposed to fabric, bottom surface layer is made;
Outer layer is prepared, polyester is subjected to slicing treatment, 0.3%~0.5% titanium dioxide is then added in polyester slice, to poly-
Ester slice carries out delustring;
Then ebullated bed is used to carry out pre-crystallized, crystallization temperature is 160~180 DEG C, and crystallization time is 8~15min, then uses and stir
Formula filling pre-crystallizer is mixed, temperature is 120~140 DEG C, and the time is 1~1.5h;
Polyester slice is processed by screw extruder again, processing temperature is 285~290 DEG C, and Screw Extrusion pressure is 6.6
~7.5MPa, then 20~30 DEG C of temperature is used to the polyester fiber of extrusion, the cold wind of humidity 70% is cooled down;
Then polyester fiber after cooling is compiled into complete polyester fabric by establishment machine again, outer layer is made.
2. a kind of Anti-deformation knitted fabric according to claim 1, it is characterised in that:The cotton fiber content accounts for 50~
70%, the cocoon fiber accounts for 30~50%.
3. a kind of Anti-deformation knitted fabric according to claim 1, it is characterised in that:The outer layer is with bottom surface layer through overvoltage
Prolong the connection of machine high-temperature laminating to be combined into one.