CN108582956A - A kind of anti slip glass processing technology - Google Patents
A kind of anti slip glass processing technology Download PDFInfo
- Publication number
- CN108582956A CN108582956A CN201810397041.7A CN201810397041A CN108582956A CN 108582956 A CN108582956 A CN 108582956A CN 201810397041 A CN201810397041 A CN 201810397041A CN 108582956 A CN108582956 A CN 108582956A
- Authority
- CN
- China
- Prior art keywords
- glass
- slip
- slip material
- processing technology
- plastic foil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti slip glass processing technologys, and discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus；Glass powder, fluorescent powder, silicon particle are mixed into composition anti-slip material, are thoroughly mixed；By the side surface clean of glass, drying, clean surface is formed；In cover board of the clean surface lid last layer with pierced pattern of glass, one layer of plastic foil for carrying identical pierced pattern of corresponding paving on the cover board with pierced pattern；The position of pierced pattern spray equipment sprays last layer glue in step (5), and glue is contacted with the clean surface of glass；Plastic foil is removed, then, the anti-slip material in the position of hollow out sprinkles step (2)；It takes cover board away, the glass with anti-slip material in step (7) is heated, plastic foil is removed before spreading anti-slip material, anti-slip material can be avoided to be sticked to the surface of plastic foil, avoids the waste of anti-slip material.
Description
Technical field
The present invention relates to glass machining technique technical field, especially a kind of anti slip glass processing technology.
Background technology
With protecting resource, protecting the cry of environment for human survival higher and higher, modern glass industry is faced with recycling
Utilize the severe challenge of glass production waste material.It will produce a series of waste materials in Improving Glass Manufacturing Processes, including waste water, exhaust gas and solid
Body waste material, and waste water, exhaust gas can recycle generation solid waste again.Some solid wastes contain noxious material, factory
Family carries out specially treated, considerably increases production cost in this way.And it is toxic waste is buried nor final solution.For
For producer, ensure the long-term burial of toxic waste, it is a kind of responsibility and a stubborn problem to be not excavated, because of glass
Glass produces waste material and comes from production process, so containing there are many advantageous elements and compound with value, but often they compare again
Certain other materials pollutions, are not easy to so dealing with.At abroad, many research institutions are all to be dedicated to glass production useless
The processing of material and the research utilized.Resource has been saved in the recycling of glass production waste material, protects environment, has certain warp
Benefit of helping and social benefit.
In the prior art, for glass production processing enterprise, glass waste must be will produce during processing, for
The price that the processing mode of these glass wastes, which is usually used lower price and is sold to recovery plant, to be recycled, and recycled
It is not high, great raising is had no to the business efficiency of enterprise.And for some functional glass, such as anti-skidding, ambetti
Product, in order to enhance the design sense of product, enterprise also needs to the various new materials of foreign acquisition and applies on glass product, for
The production cost of product constantly improves.In light of this situation, how the realization environmental protection of these glass wastes is recycled, is
The direction that processing enterprise constantly brings forth new ideas.
Invention content
The purpose of the present invention is to solve the above problems, devise a kind of anti slip glass processing technology, which is characterized in that
Including processing step below：
(1) discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus；
(2) glass powder, fluorescent powder, silicon particle are mixed into composition anti-slip material, are thoroughly mixed, according to following mass fraction
Mixing, wherein glass powder is 20-30 parts, and fluorescent powder is 6-8 parts, and silicon particle is 2-5 parts；
(3) by the side surface clean of glass, drying, clean surface is formed；
(4) in cover board of the clean surface lid last layer with pierced pattern of glass, the bottom of cover board is to be bonded with glass surface
Level is rubber layer；
(5) one layer of plastic foil for carrying identical pierced pattern of corresponding paving on the cover board with pierced pattern；
(6) last layer glue is sprayed in the position of pierced pattern with spray equipment in step (5), and the clean surface of glue and glass connects
It touches；
(7) plastic foil is removed, then, the anti-slip material in the position of hollow out sprinkles step (2)；
(8) it takes cover board away, the glass with anti-slip material in step (7) is heated, glue is dried, then Temperature fall, is obtained
To anti slip glass；
Glass powder average grain diameter in the step (1) is less than 8nm.
The average grain diameter of silicon particle is less than 20nm in the step (2).
Glass in the step (3) uses tempered glass.
Plastic foil in the step (5) is recyclable plastic foil, and the thickness of the glued membrane is 0 .6-1 .8mm.
Pierced pattern in the step (4) is any one in irregular geometric figures, decorative pattern, human-like head portrait, cartoon
Kind design pattern.
Drying time in the step (8) is 15-20 minutes, and drying temperature is 60-70 DEG C.
The fragrant particle of 4 parts of 2- is added in the step (2), the fragrance particle is fresh flower fragrance particle.
Advantageous effect：
Discarded ultrawhite glass is ground into glass powder by 1 by glass disintegrating apparatus, then using glass powder as anti-slip material it
One, it realizes the cycling and reutilization to glass waste, reduces production loss；
2 glass powders, fluorescent powder, silicon particle mixing composition anti-slip material stick in the surface of glass in the form of designing, and are formed
The different shape of protrusion surface increases the frictional force of glass product, to realize antiskid function；
The bottom of 3 cover boards of the present invention is rubber layer, and there is rubber layer itself leakproofness, rubber layer to be close to seal with glass surface,
It can prevent after glass surface sprays glue, glue flows out around from pierced pattern edge；
4 is very uniform in the glue of pierced pattern position spray in the way of spraying, and anti-slip material can be uniformly stained with for the later stage
Premise is provided；
5 in spraying, and the surrounding of plastic film, pierced pattern inevitably sprays glue, before spreading anti-slip material
Plastic foil is removed, anti-slip material can be avoided to be sticked to the surface of plastic foil, avoids the waste of anti-slip material.
Description of the drawings
Fig. 1 is side schematic view of the present invention.
Fig. 2 is schematic top plan view of the present invention.
Glass -1, cover board -2, rubber layer -3, plastic foil -4, pierced pattern -5.
Specific implementation mode
According to the figure, invention is further explained for root：
Embodiment 1
A kind of anti slip glass processing technology, which is characterized in that including processing step below：
(1) discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus, glass powder average grain diameter is less than 8nm；
(2) glass powder, fluorescent powder, silicon particle are mixed into composition anti-slip material, are thoroughly mixed, according to following mass fraction
Mixing, wherein glass powder is 30 parts, and fluorescent powder is 8 parts, 4 parts of fragrant particle, and silicon particle is 5 parts, and fragrant particle is fresh flower virtue
The average grain diameter of fragrant particle, silicon particle is less than 20nm；
(3) by the side surface clean of glass 1, drying, clean surface is formed, glass uses tempered glass；
(4) in cover board 2 of the clean surface lid last layer of glass with pierced pattern, pierced pattern 5 is irregular geometric figures, flower
Any one design pattern in line, human-like head portrait, cartoon, the bottom of cover board are that the level being bonded with glass surface is rubber
Layer；
(5) one layer of plastic foil 4 for carrying identical pierced pattern of corresponding paving, the plastic foil are on the cover board with pierced pattern
Recyclable plastic foil, thickness are 0 .6mm；
(6) last layer glue is sprayed in the position of pierced pattern with spray equipment in step (5), and the clean surface of glue and glass connects
It touches；
(7) plastic foil is removed, then, the anti-slip material in the position of hollow out sprinkles step (2)；
(8) it takes cover board away, the glass with anti-slip material in step (7) is heated, glue is dried, drying time is 20 points
Clock, drying temperature is 70 DEG C, then Temperature fall, obtains anti slip glass.
Discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus, then using glass powder as anti-slip material
One of, it realizes the cycling and reutilization to glass waste, reduces production loss；Glass powder, fluorescent powder, silicon particle mixing composition
Anti-slip material sticks in the surface of glass in the form of designing, and forms the different shape of protrusion surface, increases glass product
Frictional force, to realize antiskid function；The bottom of cover board of the present invention is rubber layer, and rubber layer itself has leakproofness,
Rubber layer is close to seal with glass surface, can prevent after glass surface sprays glue, and glue is from pierced pattern edge to four
Week outflow；It is very uniform in the glue of pierced pattern position spray in the way of spraying, it can uniformly be stained with ribband for the later stage
Material provides premise；In spraying, the surrounding of plastic film, pierced pattern inevitably sprays glue, is spreading ribband
Plastic foil is removed before material, anti-slip material can be avoided to be sticked to the surface of plastic foil, avoids the waste of anti-slip material.
Embodiment 2
A kind of anti slip glass processing technology, which is characterized in that including processing step below：
(1) discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus, glass powder average grain diameter is less than 8nm；
(2) glass powder, fluorescent powder, silicon particle are mixed into composition anti-slip material, are thoroughly mixed, according to following mass fraction
Mixing, wherein glass powder is 20 parts, and fluorescent powder is 6 parts, 2 parts of fragrant particle, and silicon particle is 2 parts, and fragrant particle is fresh flower virtue
The average grain diameter of fragrant particle, silicon particle is less than 20nm；
(3) by the side surface clean of glass, drying, clean surface is formed, glass uses tempered glass；
(4) in cover board of the clean surface lid last layer with pierced pattern of glass, pierced pattern is irregular geometric figures, flower
Any one design pattern in line, human-like head portrait, cartoon, the bottom of cover board are that the level being bonded with glass surface is rubber
Layer；
(5) one layer of plastic foil for carrying identical pierced pattern of corresponding paving, the plastic foil are on the cover board with pierced pattern
Recyclable plastic foil, thickness 1.8mm；
(6) last layer glue is sprayed in the position of pierced pattern with spray equipment in step (5), and the clean surface of glue and glass connects
It touches；
(7) plastic foil is removed, then, the anti-slip material in the position of hollow out sprinkles step (2)；
(8) it takes cover board away, the glass with anti-slip material in step (7) is heated, glue is dried, drying time is 15 points
Clock, drying temperature is 60 DEG C, then Temperature fall, obtains anti slip glass.
Discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus, then using glass powder as anti-slip material
One of, it realizes the cycling and reutilization to glass waste, reduces production loss；Glass powder, fluorescent powder, silicon particle mixing composition
Anti-slip material sticks in the surface of glass in the form of designing, and forms the different shape of protrusion surface, increases rubbing for glass product
Power is wiped, to realize antiskid function；The bottom of cover board of the present invention be rubber layer, rubber layer itself have leakproofness, rubber layer with
Glass surface is close to seal, and can prevent after glass surface sprays glue, glue from pierced pattern edge to
Surrounding flows out；It is very uniform in the glue of pierced pattern position spray in the way of spraying, it can be uniformly stained with for the later stage
Anti-slip material provides premise；In spraying, the surrounding of plastic film, pierced pattern inevitably sprays glue, is spreading
Plastic foil is removed before anti-slip material, anti-slip material can be avoided to be sticked to the surface of plastic foil, avoid the wave of anti-slip material
Take.
Embodiment 3
A kind of anti slip glass processing technology, which is characterized in that including processing step below：
(1) discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus, glass powder average grain diameter is less than 8nm；
(2) glass powder, fluorescent powder, silicon particle are mixed into composition anti-slip material, are thoroughly mixed, according to following mass fraction
Mixing, wherein glass powder is 25 parts, and fluorescent powder is 7 parts, 3 parts of fragrant particle, and silicon particle is 3 parts, and fragrant particle is fresh flower virtue
The average grain diameter of fragrant particle, silicon particle is less than 20nm；
(3) by the side surface clean of glass, drying, clean surface is formed, glass uses tempered glass；
(4) in cover board of the clean surface lid last layer with pierced pattern of glass, pierced pattern is irregular geometric figures, flower
Any one design pattern in line, human-like head portrait, cartoon, the bottom of cover board are that the level being bonded with glass surface is rubber
Layer；
(5) one layer of plastic foil for carrying identical pierced pattern of corresponding paving, the plastic foil are on the cover board with pierced pattern
Recyclable plastic foil, thickness 1.0mm；
(6) last layer glue is sprayed in the position of pierced pattern with spray equipment in step (5), and the clean surface of glue and glass connects
It touches；
(7) plastic foil is removed, then, the anti-slip material in the position of hollow out sprinkles step (2)；
(8) it takes cover board away, the glass with anti-slip material in step (7) is heated, glue is dried, drying time is 18 points
Clock, drying temperature is 65 DEG C, then Temperature fall, obtains anti slip glass.
Discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus, then using glass powder as anti-slip material
One of, it realizes the cycling and reutilization to glass waste, reduces production loss；Glass powder, fluorescent powder, silicon particle mixing composition
Anti-slip material sticks in the surface of glass in the form of designing, and forms the different shape of protrusion surface, increases rubbing for glass product
Power is wiped, to realize antiskid function；The bottom of cover board of the present invention be rubber layer, rubber layer itself have leakproofness, rubber layer with
Glass surface is close to seal, and can prevent after glass surface sprays glue, and glue flows out around from pierced pattern edge；Profit
The glue sprayed in pierced pattern position with the mode of spraying is very uniform, can be uniformly stained with before anti-slip material provides for the later stage
It carries；In spraying, the surrounding of plastic film, pierced pattern inevitably sprays glue,
Plastic foil is removed before spreading anti-slip material, anti-slip material can be avoided to be sticked to the surface of plastic foil, avoid ribband
The waste of material.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
With technical scheme described in the above embodiments is modified or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in the present invention's
Within protection domain.
Claims (8)
1. a kind of anti slip glass processing technology, which is characterized in that including processing step below：
(1) discarded ultrawhite glass is ground into glass powder by glass disintegrating apparatus；
(2) glass powder, fluorescent powder, silicon particle are mixed into composition anti-slip material, are thoroughly mixed, according to following mass fraction
Mixing, wherein glass powder is 20-30 parts, and fluorescent powder is 6-8 parts, and silicon particle is 2-5 parts；
(3) by the side surface clean of glass, drying, clean surface is formed；
(4) in cover board of the clean surface lid last layer with pierced pattern of glass, the bottom of cover board is to be bonded with glass surface
Level is rubber layer；
(5) one layer of plastic foil for carrying identical pierced pattern of corresponding paving on the cover board with pierced pattern；
(6) last layer glue is sprayed in the position of pierced pattern with spray equipment in step (5), and the clean surface of glue and glass connects
It touches；
(7) plastic foil is removed, then, the anti-slip material in the position of hollow out sprinkles step (2)；
(8) it takes cover board away, the glass with anti-slip material in step (7) is heated, glue is dried, then Temperature fall, is obtained
To anti slip glass.
2. a kind of anti slip glass processing technology according to claim 1, it is characterised in that：Glass in the step (1)
Powder average particle size is less than 8nm.
3. a kind of anti slip glass processing technology according to claim 1, it is characterised in that：Silicon particle in the step (2)
Average grain diameter be less than 20nm.
4. a kind of anti slip glass processing technology according to claim 1, it is characterised in that：Glass in the step (3)
Using tempered glass.
5. a kind of anti slip glass processing technology according to claim 1, it is characterised in that：Plastics in the step (5)
Film is recyclable plastic foil, and the thickness of the glued membrane is 0 .6-1 .8mm.
6. a kind of anti slip glass processing technology according to claim 1, it is characterised in that：Hollow out in the step (4)
Pattern is any one design pattern in irregular geometric figures, decorative pattern, human-like head portrait, cartoon.
7. a kind of anti slip glass processing technology according to claim 1, it is characterised in that：Drying in the step (8)
Time is 15-20 minutes, and drying temperature is 60-70 DEG C.
8. a kind of anti slip glass processing technology according to claim 1, it is characterised in that：The step (2)
The middle fragrant particle that 4 parts of 2- is added, the fragrance particle is fresh flower fragrance particle.