KR101882756B1 - Adhesive sheet comprising a surface-coating film layer having antifouling property and scratch-resisting property and Method for producing the same - Google Patents

Adhesive sheet comprising a surface-coating film layer having antifouling property and scratch-resisting property and Method for producing the same Download PDF

Info

Publication number
KR101882756B1
KR101882756B1 KR1020170057832A KR20170057832A KR101882756B1 KR 101882756 B1 KR101882756 B1 KR 101882756B1 KR 1020170057832 A KR1020170057832 A KR 1020170057832A KR 20170057832 A KR20170057832 A KR 20170057832A KR 101882756 B1 KR101882756 B1 KR 101882756B1
Authority
KR
South Korea
Prior art keywords
surface coating
layer
film layer
coating layer
base film
Prior art date
Application number
KR1020170057832A
Other languages
Korean (ko)
Inventor
고영남
Original Assignee
주식회사 크래프트맨
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 크래프트맨 filed Critical 주식회사 크래프트맨
Priority to KR1020170057832A priority Critical patent/KR101882756B1/en
Application granted granted Critical
Publication of KR101882756B1 publication Critical patent/KR101882756B1/en

Abstract

The present invention relates to an adhesive sheet comprising a surface-coating film layer having antifouling properties and scratch restoration performance on one side thereof. The adhesive sheet of the present invention comprises: the surface-coating film layer (10) including a surface coating layer (11) and a thermoplastic polyurethane thin film layer (12) on a surface of which the surface coating layer (11) is formed; and a base film layer (20) including a base film (21) which is made of a transparent or opaque material as a film of synthetic resins, on the surface of which colors, designs, decorations or characters are formed by a printing method, and which has a first adhesive layer (22) formed on a rear side thereof, and the first adhesive layer (22) which is formed on the rear side of the base film (21) to perform functions of temporarily adhering the rear side of the base film (21) to a release paper (23) and adhering the base film (21) to the surface of an object to be adhered after the release paper (23) is removed, and the release paper (23) which is temporarily adhered to the first adhesive layer (22). The surface coating layer (11) is formed by spray-coating a surface coating layer-forming solution on the surface of the thermoplastic polyurethane thin film layer (12) and drying the surface coating layer-forming solution spray-coated on the thermoplastic polyurethane thin film layer (12) at the temperature of 70°C for 1.5 hours, wherein the surface coating layer-forming solution is prepared by uniformly mixing a mixed solvent in which acrylic acid, isopropyl alcohol and distilled water are mixed at a preset ratio with a silicon dioxide mixed composition in which silicon dioxide, sodium fluoride, and toluene diisocyanate are mixed at a preset ratio.

Description

방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지 및 이의 제조방법{Adhesive sheet comprising a surface-coating film layer having antifouling property and scratch-resisting property and Method for producing the same}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to an adhesive sheet comprising a surface-coating film layer having antifouling property and scratch-resisting property, and a process for producing the adhesive sheet.

본 발명은 접착 시트지 및 이의 제조방법에 관한 것으로, 보다 상세하게는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지 및 이의 제조방법에 관한 것이다. The present invention relates to an adhesive sheet and a method for producing the same, and more particularly to an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience, and a method for producing the same.

현재 자동차 내외장, 가전제품, 휴대전화 등 제품의 표면의 오염이나 긁힘을 방지하여, 제품의 특성 및 외관의 수명을 유지하기 위하여, 제품의 표면을 보호하기 위하여, 다양한 코팅제가 사용되고 있으며, 완성된 표면에 보호필름, 접착시트지 등을 추가적으로 부착하여 부가하는 방식이 사용되고 있다.Various coating agents have been used to protect the surface of the product in order to prevent contamination or scratching of the surface of the product such as automobile interior and exterior, home appliance, mobile phone, and to maintain the product characteristics and the life of appearance. A method in which a protective film, an adhesive sheet or the like is additionally attached to the surface is added.

이와 같은 표면 보호 소재로는, 표면이 이물질 등으로 쉽게 오염되지 않고, 오염된 물질의 제거가 용이한 특성인 방오성을 가지면서도, 스크래치 등 외부 손상에 강한 경도를 가지는 내스크래치성을 가지고, 나아가 스크래치 등을 자가로 복원하는 스크래치 복원성을 가질 것이 요구되고 있는 상황이다.Such a surface protecting material has scratch resistance that has a stiffness against external damage such as scratches while having antifouling property that the surface is not easily contaminated with foreign substances and is easy to remove the contaminated material, It is required to have scratch resilience in which the user restores the user's back.

이에 따라, 방오성, 내스크래치성 및 스크래치 복원성을 가지는 표면 보호 소재의 개발하는 것이 절실히 요구되고 있는 상황이며, 하기 특허문헌과 같이 일부 자외선 경화형 조성물과 무기 입자나 불소계 화합물을 첨가한 조성물을 혼합하는 표면 보호 소재를 위한 코팅 재료가 개발되고 있느나, 충분한 표면 경도와 스크래치 복원성을 가지지 못하는 문제가 있다.Accordingly, there is an urgent need to develop a surface protective material having antifouling property, scratch resistance and scratch resilience. In addition, as described in the following Patent Literature, there is a problem in that some of the ultraviolet curing composition and a composition Although coating materials for protective materials have been developed, there is a problem in that they do not have sufficient surface hardness and scratch resilience.

또한, 코팅 조성물 형태로 제작되어 자외선등에 의하여 쉽게 경화됨으로써 취급이 불편하고, 실제 제품의 표면에 시공시 시공성이 떨어지는 문제가 있다. In addition, it is produced in the form of a coating composition and is easily cured by ultraviolet rays or the like, which is inconvenient for handling, and there is a problem that the workability is lowered on the surface of actual products.

이에 따라, 충분한 방오성, 내스크래치성 및 스크래치 복원성을 가지면서도 취급이 편리하고, 실제 제품의 표면에 시공시 시공성을 향상시키는 새로운 형태의 방오성 및 스크래치 복원성을 가지는 보호 필름 및 이를 포함하는 접착 시트지의 제조방법의 개발이 절실히 요구되고 있는 상황이다. Thereby, a protective film having a sufficient antifouling property, scratch resistance and scratch resistance and being easy to handle, and having a new type of antifouling property and scratch resilience which improves the workability on the surface of an actual product, and a process for producing an adhesive sheet The development of methods is urgently required.

특허등록 제10-1407617호(자기 치유 능력이 있는 열경화성 코팅 조성물, 코팅 필름 및 코팅 필름의 제조 방법, 공고일자 2014년06월27일)Patent Registration No. 10-1407617 (Self-Healing Capable Thermosetting Coating Composition, Coating Film and Manufacturing Method of Coating Film, Date of Publication June 27, 2014)

따라서, 본 발명은 상기 종래기술의 문제를 해결하여, 충분한 방오성, 내스크래치성 및 스크래치 복원성을 가지면서도 취급이 편리하고, 실제 제품의 표면에 시공시 시공성을 향상시키는 새로운 형태의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지 및 이의 제조방법을 제공하는 것을 목적으로 한다.SUMMARY OF THE INVENTION Accordingly, it is an object of the present invention to solve the above-mentioned problems of the prior art and to provide a new type of antifouling property and scratch resilience that can be handled easily while having sufficient antifouling property, scratch resistance and scratch resilience, And a method for producing the adhesive sheet.

본 발명은 일측면에서 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지에 관한 것으로, 표면 코팅층(11)과 상기 표면 코팅층(11)이 그 표면에 형성되는 열가소성 폴리우레탄 박막층(12)로 구성되는 표면 코팅 필름층(10), 및 합성수지류의 필름이 투명 또는 불투명 재질로 표면에는 색채, 도안, 장식 또는 문자 등이 인쇄 등의 방법으로 형성되고, 이면에서는 제1 접착층(21)이 형성되는 베이스 필름(21), 베이스 필름(21)의 이면에 형성되어 상기 베이스 필름(21)의 이면을 이형지(23)에 임시 접착하고, 상기 이형지(23)가 제거된 뒤 접착 대상의 표면에 결합시키는 기능을 수행하는 제1 접착층(22), 상기 제1 접착층(22)에 임시 접착되는 이형지(23)을 포함하여 구성되는 베이스 필름층(20)을 포함하여, 상기 표면 코팅층(11)은, 열가소성 폴리우레탄 필름 층(12)의 표면에 아크릴산, 이소 프로필 알코올, 증류수가 사전 설정된 비율로 혼합된 혼합용제에 이산화규소, 플루오린화나트륨, 톨루엔 디 이소시아네이트가 사전설정된 비율로 혼합된 이산화규소 혼합 조성물이 균일하게 혼합된 표면 코팅층 형성용액을 스프레이 도포하여 70℃의 온도로 대략 1.5로 건조하여 형성되는 것을 특징으로 한다.The present invention relates to an adhesive sheet comprising a surface coating film layer having an antifouling property and a scratch resilience in one aspect, comprising a surface coating layer (11) and a thermoplastic polyurethane thin film layer (12) A surface coating film layer 10 made of a synthetic resin film and a synthetic resin film made of transparent or opaque material such as color, The base film 21 is formed on the back surface of the base film 21. The back surface of the base film 21 is temporarily bonded to the release paper 23 and the release paper 23 is removed, And a release film (23) temporarily bonded to the first adhesive layer (22), wherein the surface coating layer (11) comprises a first adhesive layer (22) , Thermoplastic poly A silicon dioxide mixed composition in which silicon dioxide, sodium fluoride, and toluene diisocyanate are mixed at a predetermined ratio in a mixed solvent in which acrylic acid, isopropyl alcohol, and distilled water are mixed at a predetermined ratio on the surface of the urethane film layer 12 is uniformly The mixed surface coating layer forming solution is applied by spraying and dried at a temperature of about 70 캜 to about 1.5.

바람직하게는, 상기 표면 코팅층 형성용액은, 이산화 규소(SiO2) 5~9중량%, 플루오린화나트륨(NaF) 6~10중량%, 톨루엔 디 이소시아네이트(TDI) 7~13중량%, 아크릴산 10~20중량%, 이소 프로필 알코올 35~55중량%, 증류수 10~20중량%의 조성을 가진다.Preferably, the surface coating layer forming solution contains 5 to 9% by weight of silicon dioxide (SiO 2 ), 6 to 10% by weight of sodium fluoride (NaF), 7 to 13% by weight of toluene diisocyanate (TDI) 20% by weight of isopropyl alcohol, 35 to 55% by weight of isopropyl alcohol, and 10 to 20% by weight of distilled water.

바람직하게는, 상기 표면 코팅층(11)은 10㎛ ~ 15㎛ 의 두께를 가지도록 형성된다.Preferably, the surface coating layer 11 is formed to have a thickness of 10 mu m to 15 mu m.

바람직하게는, 상기 표면 코팅층 형성용액은 아크릴산/이소 프로필 알코올/증류수가 1/3/1의 비율인 혼합용제 75중량%에 이산화규소/플루오린화나트륨/톨루엔 디 이소시아네이트가 7/8/10의 비율로 혼합된 이산화규소 혼합 조성물 25중량%이 균일하게 혼합된다.Preferably, the surface coating layer forming solution contains 75% by weight of a mixed solvent having a ratio of acrylic acid / isopropyl alcohol / distilled water of 1/3/1, a ratio of silicon dioxide / sodium fluoride / toluene diisocyanate of 7/8/10 25 wt% of the mixed silicon dioxide composition was uniformly mixed.

바람직하게는, 표면 코팅층 형성용액은 아크릴산 15중량%, 이소 프로필 알코올 45중량%, 증류수 15중량%, 이산화규소 7중량%, 플루오린화나트륨 8중량%, 톨루엔 디 이소시아네이트 10중량%의 조성비를 갖는다.Preferably, the surface coating layer forming solution has a composition ratio of 15 wt% of acrylic acid, 45 wt% of isopropyl alcohol, 15 wt% of distilled water, 7 wt% of silicon dioxide, 8 wt% of fluorinated sodium and 10 wt% of toluene diisocyanate.

다른 측면에서 본 발명은 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제작방법으로, 표면 코팅층 형성용액을 제조하는 표면 코팅층 형성용액 혼합공정(210), 베이스 필름(21)의 표면에 색채, 도안, 장식 또는 문자 등 필요한 색채 또는 도안을 형성하고 이면에 접착제를 도포하여 제1 접착층(22)을 형성하며, 상기 제1 접착층(22)에 임시 접착되는 이형지(23)를 부착하는 공정을 포함하는 베이스 필름층 가공공정(220)을 포함하여, 상기 베이스 필름층 가공공정(220)은 색채 또는 도안이 형성된 표면에 열가소성 폴리우레탄 박막층(12)을 형성하는 공정을 포함하여, 상기 표면 코팅층 형성용액은 아크릴산, 이소 프로필 알코올, 증류수가 사전 설정된 비율로 혼합된 혼합용제에 이산화규소, 플루오린화나트륨, 톨루엔 디 이소시아네이트가 사전설정된 비율로 혼합된 이산화규소 혼합 조성물이 균일하게 혼합하여 제조되며, 베이스 필름층 가공공정(220)에서 가공된 열가소성 폴리우레탄 박막층(12)이 형성된 베이스 필름층(20)의 표면에 표면 코팅층 형성용액 혼합공정(210)에서 혼합된 표면 코팅층 형성용액을 도포하여, 70℃의 온도로 대략 1.5 시간 건조하여 표면 코팅층(11)을 형성하는 표면 코팅층 형성공정(230)을 포함한다.In another aspect, the present invention provides a method for producing an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience, comprising a surface coating layer forming solution mixing process 210 for producing a surface coating layer forming solution, A first adhesive layer 22 is formed by applying an adhesive to the back surface of the substrate 20, and a release paper 23 temporarily adhered to the first adhesive layer 22 is attached to the first adhesive layer 22 Wherein the base film layer processing step (220) includes a step of forming a thermoplastic polyurethane thin film layer (12) on a color or patterned surface, the base film layer processing step (220) The coating layer-forming solution is prepared by mixing silicon dioxide, sodium fluoride, toluene diisocyanate, and the like in a mixed solvent in which acrylic acid, isopropyl alcohol, The surface of the base film layer 20 on which the processed thermoplastic polyurethane thin film layer 12 is formed in the base film layer processing step 220 is formed on the surface of the base film layer 20, And a surface coating layer forming step 230 for coating the surface coating layer forming solution mixed in the coating layer forming solution mixing process 210 and drying the coating solution at a temperature of 70 ° C for about 1.5 hours to form a surface coating layer 11.

또 다른 측면에서, 본 발명은 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제작방법으로, 표면 코팅층 형성용액을 제조하는 표면 코팅층 형성용액 혼합공정(310), 열가소성 폴리우레탄 박막층(12)을 구성하는 열가소성 폴리우레탄 박막 필름을 준비하고, 준비된 열가소성 폴리우레탄 박막 필름의 표면에 코팅층 형성용액을 스프레이 방식으로 도포하여 표면 코팅층(11)이 형성된 열가소성 폴리우레탄 박막층(12)을 제작하는 표면 코팅층 형성공정(320), 베이스 필름(21)의 표면에 색채, 도안, 장식 또는 문자 등 필요한 색채 또는 도안을 형성하고 이면에 접착제를 도포하여 접착층(22)을 형성하며, 상기 접착층(22)에 임시 접착되는 이형지(23)를 부착하는 공정을 포함하여, 베이스 필름층(20)을 가공하는 베이스 필름층 가공공정(330), 및 표면 코팅층 형성공정(320)에서 제작된 표면 코팅층(11)이 형성된 열가소성 폴리우레탄 박막층(12)과 베이스 필름층 가공공정(330)에서 가공된 베이스 필름층(20)을 결합하는 표면 코팅 필름층 결합공정(340)을 포함하여, 상기 표면 코팅층 형성용액은 아크릴산, 이소 프로필 알코올, 증류수가 사전 설정된 비율로 혼합된 혼합용제에 이산화규소, 플루오린화나트륨, 톨루엔 디 이소시아네이트가 사전설정된 비율로 혼합된 이산화규소 혼합 조성물이 균일하게 혼합하여 제조되며, 표면 코팅층 형성공정(320)에서 가공된 열가소성 폴리우레탄 박막층(12)의 표면에 표면 코팅층 형성용액 표면 코팅층 형성용액을 도포하여, 70℃의 온도로 대략 1.5 시간 건조하여 표면 코팅층(11)을 형성한다.According to another aspect of the present invention, there is provided a method for producing an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience, comprising the steps of: a surface coating layer forming solution mixing step (310) for producing a surface coating layer forming solution; a thermoplastic polyurethane thin film layer The thermoplastic polyurethane thin film constituting the thermoplastic polyurethane thin film 12 constituting the surface coating layer 11 is coated on the surface of the prepared thermoplastic polyurethane thin film by a spraying method to form a thermoplastic polyurethane thin film A step of forming a coating layer 320 and a step of forming a necessary color or pattern such as a color, a pattern, a decoration or a character on the surface of the base film 21 and applying an adhesive to the back surface to form an adhesive layer 22, And a base film layer processing step of processing the base film layer (20), including a step of attaching the releasing paper (23) The thermoplastic polyurethane thin film layer 12 on which the surface coating layer 11 formed in the surface coating layer forming step 320 is formed and the base film layer 20 processed in the base film layer processing step 330 are bonded The surface coating layer forming solution including a surface coating film layer bonding step (340) is prepared by mixing silicon dioxide, sodium fluoride, and toluene diisocyanate in a mixed solvent in which acrylic acid, isopropyl alcohol and distilled water are mixed in a predetermined ratio And a surface coating layer forming solution is applied to the surface of the thermoplastic polyurethane thin film layer 12 processed in the surface coating layer forming process 320. The surface coating layer forming solution is heated at 70 ° C And dried at a temperature for about 1.5 hours to form a surface coating layer 11.

바람직하게는, 상기 표면 코팅층(11)은 10㎛ ~ 15㎛ 의 두께를 가지도록 형성된다.Preferably, the surface coating layer 11 is formed to have a thickness of 10 mu m to 15 mu m.

바람직하게는, 상기 표면 코팅층 형성용액은 아크릴산/이소 프로필 알코올/증류수가 1/3/1의 비율인 혼합용제 75중량%에 이산화규소/플루오린화나트륨/톨루엔 디 이소시아네이트가 7/8/10의 비율로 혼합된 이산화규소 혼합 조성물 25중량%이 균일하게 혼합된다.Preferably, the surface coating layer forming solution contains 75% by weight of a mixed solvent having a ratio of acrylic acid / isopropyl alcohol / distilled water of 1/3/1, a ratio of silicon dioxide / sodium fluoride / toluene diisocyanate of 7/8/10 25 wt% of the mixed silicon dioxide composition was uniformly mixed.

바람직하게는, 표면 코팅층 형성용액은 아크릴산 15중량%, 이소 프로필 알코올 45중량%, 증류수 15중량%, 이산화규소 7중량%, 플루오린화나트륨 8중량%, 톨루엔 디 이소시아네이트 10중량%의 조성비를 갖는다.Preferably, the surface coating layer forming solution has a composition ratio of 15 wt% of acrylic acid, 45 wt% of isopropyl alcohol, 15 wt% of distilled water, 7 wt% of silicon dioxide, 8 wt% of fluorinated sodium and 10 wt% of toluene diisocyanate.

상술한 바와 같은 본 발명에 의하면 충분한 방오성, 내스크래치성 및 스크래치 복원성을 가지면서도 취급이 편리하고, 실제 제품의 표면에 시공시 시공성을 향상시키는 새로운 형태의 방오성 및 스크래치 복원성을 가지는 보호 필름을 포함하는 접착 시트지를 제공하는 효과를 갖는다.According to the present invention as described above, it is possible to provide a protective film having a sufficient antifouling property, scratch resistance and scratch resilience, which is easy to handle, and has a new form of antifouling property and scratch resilience And has an effect of providing an adhesive sheet.

도 1은 본 발명에 따른 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 단면을 도시한 도면
도 2는 본 발명의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제조방법의 제1 실시예의 흐름도.
도 3은 본 발명의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제조방법의 제2 실시예의 흐름도.
도 4는 본 발명의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 시공방법의 흐름도.1 is a cross-sectional view of an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience according to the present invention
2 is a flow chart of a first embodiment of a method for producing an adhesive sheet comprising a surface coating film layer having antifouling and scratch-resisting properties according to the present invention.
3 is a flow chart of a second embodiment of a method of producing an adhesive sheet comprising a surface coating film layer having antifouling and scratch-resisting properties according to the present invention.
4 is a flow chart of a method of applying an adhesive sheet comprising a surface coating film layer having antifouling and scratch-resisting properties of the present invention.

아래에서는 첨부한 도면을 참고로 하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나, 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 유사한 부분에 대해서는 유사한 도면 부호를 붙였다. 또한 상세한 설명을 생략하여도 본 기술분야의 당업자가 쉽게 이해할 수 있는 부분의 설명은 생략하였다. 명세서 및 청구범위 전체에서, 어떤 부분이 어떤 구성 요소를 포함한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. In order to clearly illustrate the present invention, parts not related to the description are omitted, and similar parts are denoted by like reference characters throughout the specification. And a detailed description thereof will be omitted to omit descriptions of portions that can be readily understood by those skilled in the art. Throughout the specification and claims, where a section includes a constituent, it does not exclude other elements unless specifically stated otherwise, but may include other elements.

본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. The terms and words used in the present specification and claims should not be construed as limited to ordinary or dictionary terms and the inventor may appropriately define the concept of the term in order to best describe its invention It should be construed as meaning and concept consistent with the technical idea of the present invention.

따라서, 본 명세서에 기재된 실시예와 도면에 도시된 구성에서는 본 발명을 한정하여 설명하고 있으나, 이는 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, It should be understood that there may be various equivalents and variations that may be substituted at the time of filing.

도 1은 본 발명에 따른 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지를 도시한 도면이다.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a view showing an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience according to the present invention. Fig.

도 1을 참조하면, 본 발명에 따른 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지(100)는, 표면 코팅 필름층(10) 및 베이스 필름층(20)을 포함하여 구성된다.Referring to FIG. 1, an adhesive sheet 100 including a surface coating film layer having antifouling property and scratch resilience according to the present invention comprises a surface coating film layer 10 and a base film layer 20.

표면 코팅 필름층(10)은, 표면 코팅층(11)과 상기 표면 코팅층(11)이 그 표면에 형성되는 열가소성 폴리우레탄 박막층(12)로 구성되며, 실시예에 따라서는 제2 접착층(13)을 더 포함하여 구성된다.The surface coating film layer 10 is composed of a surface coating layer 11 and a thermoplastic polyurethane thin film layer 12 on the surface of which the surface coating layer 11 is formed, .

상기 표면 코팅층(11)은, 열가소성 폴리우레탄 필름 층(12)의 표면에 아크릴산, 이소 프로필 알코올, 증류수가 사전 설정된 비율로 혼합된 혼합용제에 이산화규소, 플루오린화나트륨, 톨루엔 디 이소시아네이트가 사전설정된 비율로 혼합된 이산화규소 혼합 조성물이 균일하게 혼합된 표면 코팅층 형성용액을 스프레이 도포하여 70℃의 온도로 대략 1.5로 건조하여 형성된다.The surface coating layer 11 is formed by mixing silicon dioxide, sodium fluoride and toluene diisocyanate in a mixed solvent in which acrylic acid, isopropyl alcohol and distilled water are mixed at a predetermined ratio on the surface of the thermoplastic polyurethane film layer 12 Is formed by spray coating a uniformly mixed surface coating layer forming solution and drying at about 1.5 at a temperature of 70 캜.

상기 표면 코팅층 형성용액은, 이산화 규소(SiO2) 5~9중량%, 플루오린화나트륨(NaF) 6~10중량%, 톨루엔 디 이소시아네이트(TDI) 7~13중량%, 아크릴산 10~20중량%, 이소 프로필 알코올 35~55중량%, 증류수 10~20중량%의 조성을 가질 수 있으며, 바람직하게는 스프레이 양을 조절하여 건조 후 10㎛ ~ 15㎛ 의 두께를 가지도록 형성된다. 이는 접착 시트지가 제작되었을때 표면 코팅층(11)의 연성에 의하여 표면의 균열 내지 크랙을 방지할 수 있는 최적의 두께로 실험적으로 선택되었다.Wherein the surface coating layer forming solution contains 5 to 9% by weight of silicon dioxide (SiO 2 ), 6 to 10% by weight of sodium fluoride (NaF), 7 to 13% by weight of toluene diisocyanate (TDI) 35 to 55% by weight of isopropyl alcohol, 10 to 20% by weight of distilled water, and preferably 10 to 15 占 퐉 after drying by adjusting the amount of spray. It was experimentally selected to have an optimum thickness to prevent cracking or cracking of the surface due to ductility of the surface coating layer 11 when the adhesive sheet was produced.

상기 표면 코팅층 형성용액은 다음과 같은 원료 물질을 교반하여 조제된다.The surface coating layer forming solution is prepared by stirring the following raw materials.

(1) 이산화 규소(SiO2) : 이산화 규소(二酸化硅素)는 규소의 산화물로, 화학식은 SiO2이고, 실리카(silica)라고도 하며, 표면 코팅층 형성용액에 5~9중량%가 준비되어 희석될 수 있다. 본 실시예의 경우 CAS 번호 37631-86-9 의 이산화 규소가 사용된다. 이산화 규소는 플루오린화 수소 기체 또는 플루오린화 수소산 액체와 반응시키면 각각 사플루오린화 규소(silicon tetrafluoride) 또는 플루오린화 규소산(hexafluorosilicic acid)이 얻어진다. (2) 플루오린화나트륨 (NaF) : 플루오린화 나트륨(Sodium fluoride)은 CAS번호 7681-49-4, 화학식 NaF의 화합물로, 표면 코팅층 형성용액에 6~10중량%를 용해하여 사용할 수 있다. (3) 톨루엔 디 이소시아네이트 (TDI) : 톨루엔 디 이소시아네이트 (Toluene Diisocyanate)는 CH3C6H3(NCO)2의 화학식을 갖는 유기화합물로, 가능한 6개의 이성질체 중 2,4-TDI (CAS 번호: 584-84-9) 및 2,6-TDI (CAS 번호 91-08-7)의 2 가지가 상업적으로 중요하며, 본 실시예의 경우 CAS 번호: 584-84-9의 2,4-TDI를 표면 코팅층 형성용액에 7~13중량%를 용해하여 사용할 수 있다. (4) 아크릴산 : 아크릴산 (Propenoic Acid)은 CAS번호 79-10-7, 화학식 CH2 = CHCOOH 의 유기 화합물로, 본 실시예의 표면 코팅층 형성용액에 10~20중량%를 준비하여 희석할 수 있다. (5) 이소 프로필 알코올 : 이소 프로필 알코올(Isopropyl alcohol)은 CAS번호 67-63-0, 화학식 C3H8O 또는 C3H7OH 또는 CH3CHOHCH3 의 화합물로 본 실시예의 표면 코팅층 형성용액에 35~55중량%의 이소 프로필 알코올이 혼합될 수 있다. (6) 증류수 : 증류수(Distiled Water)는 CAS번호 7732-18-5, 화학식 H2O로 본 실시예의 표면 코팅층 형성용액에 10~20중량%의 증류수가 혼합될 수 있다.(1) Silicon dioxide (SiO 2 ): Silicon dioxide (silicon dioxide) is an oxide of silicon, and its chemical formula is SiO 2 and is also referred to as silica, and 5 to 9% by weight is prepared in the surface coating layer forming solution to be diluted . In this embodiment, the silicon dioxide of CAS No. 37631-86-9 is used. Silicon tetrachloride or hexafluorosilicic acid can be obtained by reacting silicon dioxide with a fluorinated hydrogen gas or a fluorinated hydrofluoric acid liquid, respectively. (2) Sodium fluoride (NaF): Sodium fluoride is a compound of the formula NaSF 7681-49-4, which can be used by dissolving 6 to 10 wt% in the surface coating layer forming solution. (3) Toluene diisocyanate (TDI): Toluene diisocyanate is an organic compound having the chemical formula CH 3 C 6 H 3 (NCO) 2 , and 2,4-TDI (CAS number: 584-84-9) and 2,6-TDI (CAS No. 91-08-7) are commercially important, and in this example, 2,4-TDI of CAS number: 7 to 13% by weight may be dissolved in the coating layer forming solution. (4) Acrylic acid: Propenoic Acid is an organic compound having a chemical formula of CAS No. 79-10-7 and CH 2 = CHCOOH, and may be diluted by preparing 10 to 20% by weight of the solution in the surface coating layer forming solution of this embodiment. (5) Isopropyl alcohol: Isopropyl alcohol is a compound of CAS No. 67-63-0, a compound of the formula C 3 H 8 O or C 3 H 7 OH or CH 3 CHOHCH 3 , To 35% by weight to 55% by weight of isopropyl alcohol. (6) Distilled water: Distilled water can be mixed with 10 to 20% by weight of distilled water in the surface coating layer forming solution of this embodiment with CAS No. 7732-18-5 and formula H 2 O.

본 실시예의 경우 상기 표면 코팅층 형성용액은 아크릴산/이소 프로필 알코올/증류수가 1/3/1의 비율인 혼합용제 75중량%에 이산화규소/플루오린화나트륨/톨루엔 디 이소시아네이트가 7/8/10의 비율로 혼합된 이산화규소 혼합 조성물 25중량%이 균일하게 혼합되어 제조된다.In the case of this embodiment, the surface coating layer forming solution is prepared by mixing 75 wt% of a mixed solvent having a ratio of acrylic acid / isopropyl alcohol / distilled water 1/3/1, a ratio of silicon dioxide / sodium fluoride / toluene diisocyanate of 7/8/10 And 25 wt% of the silicon dioxide mixed composition were mixed uniformly.

이에 따라, 표면 코팅층 형성용액은 아크릴산 15중량%, 이소 프로필 알코올 45중량%, 증류수 15중량%, 이산화규소 7중량%, 플루오린화나트륨 8중량%, 톨루엔 디 이소시아네이트 10중량%의 조성비를 갖는다.Thus, the surface coating layer forming solution has a composition ratio of 15 wt% of acrylic acid, 45 wt% of isopropyl alcohol, 15 wt% of distilled water, 7 wt% of silicon dioxide, 8 wt% of fluorinated sodium and 10 wt% of toluene diisocyanate.

열가소성 폴리우레탄 박막층(12)은 사전 제작된 박막 형태의 열가소성 폴리우레탄 필름을 사용할 수 있으며, 표면 코팅 필름층(10)은 제2 접착층(13)을 더 포함하여 구성된다.The thermoplastic polyurethane thin film layer 12 may be a preformed thin film thermoplastic polyurethane film and the surface coating film layer 10 may further comprise a second adhesive layer 13. [

열가소성 폴리우레탄 박막층(12) 후술하는 베이스 필름층(20)의 상면에 접착된 뒤 표면 코팅층(11)이 형성되거나, 표면 코팅층(11)이 형성된 열가소성 폴리우레탄 박막층(12) 후술하는 베이스 필름층(20)의 상면에 접착될 수 있으며, 표면 코팅층(11)의 건조과정에서의 타 구성의 변성을 방지의 측면에서, 표면 코팅층(11)이 형성된 열가소성 폴리우레탄 박막층(12) 베이스 필름층(20)의 상면에 접착하는 방식이 유리하다.The thermoplastic polyurethane thin film layer 12 is adhered to the upper surface of the base film layer 20 to be described later to form the surface coating layer 11 or the thermoplastic polyurethane thin film layer 12 on which the surface coating layer 11 is formed, The thermoplastic polyurethane thin film layer 12 on which the surface coating layer 11 is formed may be adhered to the upper surface of the base film layer 20 in order to prevent denaturation of other constituents in the drying process of the surface coating layer 11. [ Is advantageously used.

또한, 실시예에 따라서는, 열가소성 폴리우레탄 박막층(12)은 베이스 필름층(20)의 상면에 폴리우레탄 수지 용액을 직접 도포 및 건조하여 형성할 수 있으며, 폴리우레탄 수지는 일반적으로 이소시아네이트 화합물과 폴리올 화합물간의 반응생성물로 이루어진 수지를 총칭한다. 요구되는 특징에 따라 선택된 폴리우레탄 수지조성물을 다양한 공지의 방법으로 희석제에 용해해 폴리우레탄 수지 용액을 준비하고, 이를 베이스 필름층(20)의 상면에 스프레이 방식으로 도포한 뒤 건조함으로써, 열가소성 폴리우레탄 박막층(12)은 베이스 필름층(20)의 상면에 직접형성하며, 이 경우 표면 코팅 필름층(10)에는 별도의 제2 접착층(13)이 포함되지 않는다.Further, according to the embodiment, the thermoplastic polyurethane thin film layer 12 can be formed by directly coating a polyurethane resin solution on the upper surface of the base film layer 20 and drying it. The polyurethane resin generally contains an isocyanate compound and a polyol The resin consisting of the reaction product between the compounds is collectively referred to. A polyurethane resin composition is prepared by dissolving a polyurethane resin composition selected according to the required characteristics in a diluting agent by various known methods to prepare a polyurethane resin solution and applying the solution to the top surface of the base film layer 20 by a spraying method and drying the thermoplastic polyurethane resin The thin film layer 12 is formed directly on the upper surface of the base film layer 20, and in this case, the surface coating film layer 10 does not include a separate second adhesive layer 13.

베이스 필름층(20)은 폴리에틸렌(polyethylen) 필름지, 오피피(Oriented Poly Propylene) 필름지, PET(polyethylen terephthalate)필름지 등의 다양한 합성수지류의 필름이 투명 또는 불투명 재질로 가공되어 사용될 수 있으며, 표면에는 색채, 도안, 장식 또는 문자 등이 인쇄 등의 방법으로 형성되고, 이면에서는 제1 접착층(21)이 형성되는 베이스 필름(21), 베이스 필름(21)의 이면에 형성되어 베이스 필름(21)의 이면을 이형지(23)에 임시 접착하고, 이형지(23)가 제거된 뒤 접착 대상의 표면에 결합시키는 기능을 수행하는 제1 접착층(22), 제1 접착층(22)에 임시 접착되는 이형지(23)을 포함하여 구성된다.The base film layer 20 may be formed by using various synthetic resin films such as polyethylene film, Oriented Polypropylene film, and PET (polyethylene terephthalate) film as transparent or opaque materials. A base film 21 on which a first adhesive layer 21 is formed, a base film 21 formed on the back surface of the base film 21 and a rear surface of the base film 21, A first adhesive layer 22 that temporarily adheres to the release paper 23 and performs a function of bonding the release paper 23 to the surface of the object to be adhered after the release paper 23 is removed, a release paper 23 temporarily adhered to the first adhesive layer 22, .

제1 접착층(22)은 접착 대상의 표면 특성, 인쇄면의 특성 등이 고려되어 접착력이 결정되어 선택된 다양한 공지의 점착제 용액을 도포하여 경화시킴으로써 형성된다.The first adhesive layer 22 is formed by applying various known pressure-sensitive adhesive solutions and curing them after the adhesive strength is determined in consideration of the surface characteristics of the object to be adhered, the characteristics of the printed surface, and the like.

이하 도면을 참조하여, 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제조방법의 실시예들을 설명한다.BEST MODE FOR CARRYING OUT THE INVENTION With reference to the drawings, embodiments of a method of manufacturing an adhesive sheet including a surface coating film layer having antifouling property and scratch resilience will be described.

도 2는 본 발명의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제조방법의 제1 실시예의 흐름도이다.2 is a flow chart of a first embodiment of a method for producing an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience according to the present invention.

제1 실시예의 경우 열가소성 폴리우레탄 박막층(12)을 베이스 필름층(20)의 상면에 형성한 뒤 베이스 필름층(20)의 표면에 형성된 열가소성 폴리우레탄 박막층(12)의 표면에 표면 코팅층 형성용액을 스프레이 방식으로 도포하여 표면 코팅층(11)을 실시하는 실시예로서, 열가소성 폴리우레탄 박막층(12)을 구성하는 열가소성 폴리우레탄 박막을 베이스 필름층(20)의 상면에 접착된 뒤 표면 코팅층 형성용액을 스프레이 방식으로 도포하여 표면 코팅층(11)을 형성하거나, 베이스 필름층(20)의 표면에 열가소성 폴리우레탄 수지 용액을 준비하고, 열가소성 폴리우레탄 수지 용액을 베이스 필름층(20)의 상면에 스프레이 방식으로 도포한 뒤 건조함으로써, 열가소성 폴리우레탄 박막층(12)을 베이스 필름층(20)의 상면에 형성한 뒤 표면 코팅층 형성용액을 스프레이 방식으로 도포하여 표면 코팅층(11)을 형성하여 본 발명의 표면 코팅 필름층(10) 및 베이스 필름층(20)을 포함하여 구성되는 방오성과 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지(100)를 제조하는 실시예이다. The thermoplastic polyurethane thin film layer 12 is formed on the upper surface of the base film layer 20 and then the surface coating layer forming solution is formed on the surface of the thermoplastic polyurethane thin film layer 12 formed on the surface of the base film layer 20 A thermoplastic polyurethane thin film constituting the thermoplastic polyurethane thin film layer 12 is adhered to the upper surface of the base film layer 20 and then the surface coating layer forming solution is sprayed Or a thermoplastic polyurethane resin solution is prepared on the surface of the base film layer 20 and the thermoplastic polyurethane resin solution is applied to the upper surface of the base film layer 20 by a spraying method The thermoplastic polyurethane thin film layer 12 is formed on the upper surface of the base film layer 20 and then the surface coating layer forming solution is sprayed (100) comprising a surface coating film layer (10) having antifouling property and scratch resilience, which comprises a surface coating film layer (10) and a base film layer (20) ). ≪ / RTI >

도 2를 참조하면, 제1 실시예의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제조방법은, 표면 코팅층 형성용액 혼합공정(210), 베이스 필름층 가공공정(220), 표면 코팅층 형성공정(230), 및 후가공(240)의 일련의 공정을 포함하여 수행된다.Referring to FIG. 2, the method for manufacturing the adhesive sheet including the surface coating film layer having antifouling property and scratch resilience according to the first embodiment includes a surface coating layer forming solution mixing process 210, a base film layer processing process 220, A coating layer forming step 230, and a post-processing 240. [

표면 코팅층 형성용액 혼합공정(210)은, 혼합용제에 이산화규소 혼합 조성물을 사전 설정된 비율로 균일하게 혼합하여 표면 코팅층 형성용액을 제조한다. In the surface coating layer forming solution mixing step 210, a silicon dioxide mixed composition is uniformly mixed with a mixed solvent at a predetermined ratio to prepare a surface coating layer forming solution.

상기 표면 코팅층 형성용액은, 이산화 규소(SiO2) 5~9중량%, 플루오린화나트륨(NaF) 6~10중량%, 톨루엔 디 이소시아네이트(TDI) 7~13중량%, 아크릴산 10~20중량%, 이소 프로필 알코올 35~55중량%, 증류수 10~20중량%의 조성을 가질 수 있으며, 바람직하게는 스프레이 양을 조절하여 건조 후 10㎛ ~ 15㎛ 의 두께를 가지도록 형성된다. 이는 접착 시트지가 제작되었을때 표면 코팅층(11)의 연성에 의하여 표면의 균열 내지 크랙을 방지할 수 있는 최적의 두께로 실험적으로 선택되었다.Wherein the surface coating layer forming solution contains 5 to 9% by weight of silicon dioxide (SiO 2 ), 6 to 10% by weight of sodium fluoride (NaF), 7 to 13% by weight of toluene diisocyanate (TDI) 35 to 55% by weight of isopropyl alcohol, 10 to 20% by weight of distilled water, and preferably 10 to 15 占 퐉 after drying by adjusting the amount of spray. It was experimentally selected to have an optimum thickness to prevent cracking or cracking of the surface due to ductility of the surface coating layer 11 when the adhesive sheet was produced.

본 실시예의 경우 상기 표면 코팅층 형성용액은 아크릴산/이소 프로필 알코올/증류수가 1/3/1의 비율인 혼합용제 75중량%에 이산화규소/플루오린화나트륨/톨루엔 디 이소시아네이트가 7/8/10의 비율로 혼합된 이산화규소 혼합 조성물 25중량%이 균일하게 혼합되어 제조된다.In the case of this embodiment, the surface coating layer forming solution is prepared by mixing 75 wt% of a mixed solvent having a ratio of acrylic acid / isopropyl alcohol / distilled water 1/3/1, a ratio of silicon dioxide / sodium fluoride / toluene diisocyanate of 7/8/10 And 25 wt% of the silicon dioxide mixed composition were mixed uniformly.

이에 따라, 표면 코팅층 형성용액은 아크릴산 15중량%, 이소 프로필 알코올 45중량%, 증류수 15중량%, 이산화규소 7중량%, 플루오린화나트륨 8중량%, 톨루엔 디 이소시아네이트 10중량%의 조성비를 갖는다.Thus, the surface coating layer forming solution has a composition ratio of 15 wt% of acrylic acid, 45 wt% of isopropyl alcohol, 15 wt% of distilled water, 7 wt% of silicon dioxide, 8 wt% of fluorinated sodium and 10 wt% of toluene diisocyanate.

제1 실시예의 베이스 필름층 가공공정(220)은 베이스 필름(21)의 표면에 색채, 도안, 장식 또는 문자 등 필요한 색채 또는 도안을 인쇄 등의 방법으로 형성하고 이면에 접착제를 도포하여 제1 접착층(22)을 형성하며, 상기 제1 접착층(22)에 임시 접착되는 이형지(23)를 부착하는 공정을 포함한다. 이를 통해 베이스 필름(21), 제1 접착층(22), 이형지(23)로 구성되는 베이스 필름층(20)이 가공된다.In the base film layer processing step 220 of the first embodiment, necessary colors or patterns such as color, pattern, decoration, or characters are formed on the surface of the base film 21 by printing or the like, and an adhesive is applied on the back surface, (22), and attaching a release paper (23) temporarily adhered to the first adhesive layer (22). The base film layer 20 composed of the base film 21, the first adhesive layer 22, and the release paper 23 is processed.

본 실시예의 경우, 베이스 필름층 가공공정(220)은 색채 또는 도안이 형성된 표면에 열가소성 폴리우레탄 박막층(12)을 형성하는 공정을 포함할 수 있다.In the case of the present embodiment, the base film layer processing step 220 may include a step of forming a thermoplastic polyurethane thin film layer 12 on the color or patterned surface.

열가소성 폴리우레탄 박막층(12)을 형성하는 공정은 베이스 필름(21)의 색채 또는 도안이 형성된 표면에 접착제를 도포하여 제2 접착층(13)을 형성하여 미리 준비된 열가소성 폴리우레탄 박막층(12)을 구성하는 열가소성 폴리우레탄 박막을 부착하는 공정을 포함할 수 있다.In the step of forming the thermoplastic polyurethane thin film layer 12, a second adhesive layer 13 is formed by applying an adhesive to the color or patterned surface of the base film 21 to constitute the thermoplastic polyurethane thin film layer 12 previously prepared And adhering a thermoplastic polyurethane thin film.

또한, 실시예에 따라서는 열가소성 폴리우레탄 박막층(12)을 형성하는 공정은 베이스 필름층(20)의 상면에 미리 준비된 열가소성 폴리우레탄 수지 용액을 스프레이 방식으로 도포한 뒤 건조함으로써, 열가소성 폴리우레탄 박막층(12)을 베이스 필름층(20)의 상면에 형성하는 공정을 포함할 수 있다.According to the embodiment, in the step of forming the thermoplastic polyurethane thin film layer 12, a thermoplastic polyurethane resin solution previously prepared on the top surface of the base film layer 20 is applied by a spray method and then dried to form a thermoplastic polyurethane thin film layer 12 may be formed on the upper surface of the base film layer 20.

제1 실시예의 표면 코팅층 형성공정(230)은 베이스 필름층 가공공정(220)에서 가공된 열가소성 폴리우레탄 박막층(12)이 형성된 베이스 필름층(20)의 표면에 표면 코팅층 형성용액 혼합공정(210)에서 혼합된 표면 코팅층 형성용액을 도포하고, 70℃의 온도로 대략 1.5 시간 건조하여 표면 코팅층(11)을 형성하며, 바람직하게는 스프레이 양을 조절하여 건조 후 표면 코팅층(11)이 10㎛ ~ 15㎛ 의 두께를 가지도록 형성한다. The surface coating layer forming process 230 of the first embodiment may include a surface coating layer forming solution mixing process 210 on the surface of the base film layer 20 on which the thermoplastic polyurethane thin film layer 12 processed in the base film layer processing process 220 is formed, And the surface coating layer 11 is formed by drying at a temperature of 70 캜 for about 1.5 hours. Preferably, the surface coating layer 11 is dried to a thickness of 10 탆 to 15 Mu m.

후가공(240)은 상기 표면 코팅 필름층(10) 및 베이스 필름층(20)을 포함하여 구성된 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지(100)의 소요되는 크기 및 형태로 절단하는 공정 및 포장 또는 권취하는 공정을 포함하여 수행된다. The post-processing 240 is cut in a desired size and shape of the adhesive sheet 100 including the surface coating film layer 10 having antifouling property and scratch-resisting property, which is composed of the surface coating film layer 10 and the base film layer 20 And a step of packaging or winding.

이를 통해, 표면 코팅 필름층(10) 및 베이스 필름층(20)을 포함하여 구성되는 본 발명에 따른 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지(100)가 가공된다.Thereby, the adhesive sheet 100 comprising the surface coating film layer 10 having the antifouling property and the scratch resilience according to the present invention comprising the surface coating film layer 10 and the base film layer 20 is processed.

도 3은 본 발명의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제조방법의 제2 실시예의 흐름도이다.3 is a flow chart of a second embodiment of a method for producing an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience according to the present invention.

제2 실시예의 경우 열가소성 폴리우레탄 박막층(12)을 구성하는 열가소성 폴리우레탄 박막 필름을 먼저 준비하고, 준비된 열가소성 폴리우레탄 박막 필름의 표면 코팅층 형성용액을 스프레이 방식으로 도포하여 표면 코팅층(11)이 형성된 열가소성 폴리우레탄 박막층(12)을 베이스 필름층(20)의 상면에 접착하는 실시예로, 표면 코팅층(11)이 형성된 열가소성 폴리우레탄 박막층(12)을 제2 접착층(13)을 통해 베이스 필름층(20)의 상면에 접착하여, 본 발명의 표면 코팅 필름층(10) 및 베이스 필름층(20)을 포함하여 구성되는 방오성과 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지(100)를 제조하는 실시예이다. In the case of the second embodiment, the thermoplastic polyurethane thin film constituting the thermoplastic polyurethane thin film layer 12 is first prepared, and the solution for forming the surface coating layer of the prepared thermoplastic polyurethane thin film is applied by a spray method to form a thermoplastic polyurethane thin film The thermoplastic polyurethane thin film layer 12 on which the surface coating layer 11 is formed is bonded to the base film layer 20 through the second adhesive layer 13 by bonding the polyurethane thin film layer 12 to the upper surface of the base film layer 20, To produce an adhesive sheet 100 comprising a surface coating film layer having antifouling property and scratch resilience, which is composed of the surface coating film layer 10 and the base film layer 20 of the present invention Fig.

상기 제2 접착층(13)은 사전 준비된 접착제를 베이스 필름층(20)의 상면에 도포 및 건조하여 형성할 수 있으며, 실시예에 따라서는 열가소성 폴리우레탄 박막층(12)의 하면에 도포 및 건조하여 형성할 수도 있다.The second adhesive layer 13 may be formed by applying a preliminarily prepared adhesive to the upper surface of the base film layer 20 and drying it. In some embodiments, the second adhesive layer 13 may be applied to the lower surface of the thermoplastic polyurethane thin film layer 12, You may.

도 3을 참조하면, 제2 실시예의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제조방법은, 표면 코팅층 형성용액 혼합공정(310), 표면 코팅층 형성공정(320), 베이스 필름층 가공공정(330), 표면 코팅 필름층 결합공정(340) 및 후가공(350)의 일련의 공정을 포함하여 수행된다.Referring to FIG. 3, a method of manufacturing an adhesive sheet including a surface coating film layer having antifouling property and scratch resilience according to the second embodiment includes a surface coating layer forming solution mixing process 310, a surface coating layer forming process 320, A layer processing step 330, a surface coating film layer bonding step 340, and a post-processing step 350.

표면 코팅층 형성용액 혼합공정(320)은, 혼합용제에 이산화규소 혼합 조성물을 사전 설정된 비율로 균일하게 혼합하여 표면 코팅층 형성용액을 제조하는 공정으로 상술한 제1 실시예의 경우와 동일하게 합용제는 아크릴산/이소 프로필 알코올/증류수가 1/3/1의 비율인 혼합용제이며, 이산화규소 혼합 조성물은 이산화규소/플루오린화나트륨/톨루엔 디 이소시아네이트가 7/8/10의 비율로 혼합된 조성물로, 혼합용제 75중량%와 상기 이산화규소 혼합 조성물 25중량%를 균일하게 혼합하여 표면 코칭 필름 층 형성 용액을 제조하여, 표면 코팅층 형성용액은, 이산화 규소(SiO2) 5~9중량%, 플루오린화나트륨(NaF) 6~10중량%, 톨루엔 디 이소시아네이트(TDI) 7~13중량%, 아크릴산 10~20중량%, 이소 프로필 알코올 35~55중량%, 증류수 10~20중량%의 조성을 가질수 있으며, 바람직하게는, 아크릴산/이소 프로필 알코올/증류수가 1/3/1의 비율인 혼합용제 75중량%에 이산화규소/플루오린화나트륨/톨루엔 디 이소시아네이트가 7/8/10의 비율로 혼합된 이산화규소 혼합 조성물 25중량%(이산화규소 7중량%, 플루오린화나트륨(NaF) 8중량%, 톨루엔 디 이소시아네이트 (TDI) 10중량%)을 균일하게 혼합하여 표면 코칭 필름 층 형성 용액을 제조하여, 표면 코팅층 형성용액은 아크릴산 15중량%, 이소 프로필 알코올 45중량%, 증류수 15중량%, 이산화규소 7중량%, 플루오린화나트륨(NaF) 8중량%, 톨루엔 디 이소시아네이트 (TDI) 10중량%의 조성비를 갖는다.The surface coating layer forming solution mixing process 320 is a process for preparing a surface coating layer forming solution by uniformly mixing a silicon dioxide mixed composition with a mixed solvent at a predetermined ratio. In the same manner as in the first embodiment described above, / Isopropyl alcohol / distilled water in a ratio of 1/3/1, and the silicon dioxide mixed composition is a composition in which silicon dioxide / sodium fluoride / toluene diisocyanate is mixed in a ratio of 7/8/10, The surface coating layer forming solution is prepared by mixing 5 to 9% by weight of silicon dioxide (SiO 2 ), 5 to 9% by weight of sodium fluoride (NaF ) Of 6 to 10% by weight, toluene diisocyanate (TDI) 7 to 13% by weight, acrylic acid 10 to 20% by weight, isopropyl alcohol 35 to 55% by weight and distilled water 10 to 20% Was prepared by mixing a silicon dioxide mixed composition 25 in which silicon dioxide / sodium fluoride / toluene diisocyanate was mixed at a ratio of 7/8/10 to 75% by weight of a mixed solvent having a ratio of acrylic acid / isopropyl alcohol / distilled water of 1/3/1 The surface coating layer forming solution was prepared by uniformly mixing 10 wt% (silicon dioxide 7 wt%, sodium fluoride (NaF) 8 wt%, and toluene diisocyanate (TDI 10 wt%)) 15 weight% of isopropyl alcohol, 15 weight% of distilled water, 7 weight% of silicon dioxide, 8 weight% of sodium fluoride (NaF) and 10 weight% of toluene diisocyanate (TDI).

제2 실시예의 표면 코팅층 형성공정(320)은, 열가소성 폴리우레탄 박막층(12)을 구성하는 열가소성 폴리우레탄 박막 필름을 먼저 준비하고, 준비된 열가소성 폴리우레탄 박막 필름의 표면에 코팅층 형성용액을 스프레이 방식으로 도포하여 표면 코팅층(11)을 형성된 열가소성 폴리우레탄 박막층(12)을 제작한다.In the surface coating layer forming step 320 of the second embodiment, the thermoplastic polyurethane thin film constituting the thermoplastic polyurethane thin film layer 12 is first prepared, and the coating layer forming solution is applied on the surface of the prepared thermoplastic polyurethane thin film by a spraying method Thereby forming a thermoplastic polyurethane thin film layer 12 on which the surface coating layer 11 is formed.

제2 실시예의 표면 코팅층 형성공정(320)은 준비된 열가소성 폴리우레탄 박막 필름의 표면에 표면 코팅층 형성용액 혼합공정(310)에서 혼합된 표면 코팅층 형성용액을 도포하고, 70℃의 온도로 대략 1.5 시간 건조하여 표면 코팅층(11)을 형성하며, 바람직하게는 스프레이 양을 조절하여 건조 후 표면 코팅층(11)이 10㎛ ~ 15㎛ 의 두께를 가지도록 형성한다. In the surface coating layer forming step 320 of the second embodiment, the surface coating layer forming solution mixed in the surface coating layer forming solution mixing step 310 is applied to the surface of the prepared thermoplastic polyurethane thin film and dried at a temperature of 70 캜 for about 1.5 hours And the surface coating layer 11 is formed to have a thickness of 10 탆 to 15 탆 after drying by adjusting the spray amount.

실시예에 따라서는 제2 실시예의 표면 코팅층 형성공정(320)은 표면 코팅층(11)을 형성된 열가소성 폴리우레탄 박막층(12)의 하면에 사전 준비된 접착제를 도포 및 건조하여 제2 접착층(13)을 형성하는 공정을 포함할 수 있다.According to the embodiment, the surface coating layer forming step 320 of the second embodiment forms a second adhesive layer 13 by applying a previously prepared adhesive to the lower surface of the thermoplastic polyurethane thin film layer 12 formed with the surface coating layer 11, . ≪ / RTI >

제2 실시예의 베이스 필름층 가공공정(330)은, 베이스 필름(21)의 표면에 색채, 도안, 장식 또는 문자 등 필요한 색채 또는 도안을 인쇄 등의 방법으로 형성하고 이면에 접착제를 도포하여 제1 접착층(22)을 형성하며, 상기 제1 접착층(22)에 임시 접착되는 이형지(23)를 부착하는 공정을 포함한다. 이를 통해 베이스 필름(21), 제1 접착층(22), 이형지(23)로 구성되는 베이스 필름층(20)이 가공된다.In the base film layer processing step 330 of the second embodiment, a necessary color or pattern such as a color, a pattern, a decoration, or a character is formed on the surface of the base film 21 by printing or the like, And a step of forming an adhesive layer (22) and attaching a release paper (23) temporarily adhered to the first adhesive layer (22). The base film layer 20 composed of the base film 21, the first adhesive layer 22, and the release paper 23 is processed.

실시예에 따라서는 베이스 필름층 가공공정(330)은 상기 베이스 필름층(20)의 상면에 사전 준비된 접착제를 도포 및 건조하여 제2 접착층(13)을 형성하는 공정을 포함할 수 있다. According to an embodiment, the base film layer processing step 330 may include a step of forming a second adhesive layer 13 by applying a previously prepared adhesive to the upper surface of the base film layer 20 and drying the same.

표면 코팅 필름층 결합공정(340)은 표면 코팅층 형성공정(320)에서 제작된 표면 코팅층(11)을 형성된 열가소성 폴리우레탄 박막층(12)과 베이스 필름층 가공공정(330)에서 가공된 베이스 필름층(20)을 결합하는 공정이다.The surface coating film layer bonding process 340 is a process of bonding the surface coating layer 11 formed in the surface coating layer forming process 320 to the thermoplastic polyurethane thin film layer 12 formed in the base film layer processing step 330, 20).

실시예에 따라서는 표면 코팅 필름층 결합공정(340)은 상기 베이스 필름층(20)의 상면에 사전 준비된 접착제를 도포 및 건조하여 제2 접착층(13)을 형성하는 공정을 포함할 수 있다.According to an embodiment, the surface coating film layer bonding step 340 may include a step of forming a second adhesive layer 13 by applying a preliminarily prepared adhesive to the upper surface of the base film layer 20 and drying the same.

후가공(240)은 상기 표면 코팅 필름층(10) 및 베이스 필름층(20)을 포함하여 구성된 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지(100)의 소요되는 크기 및 형태로 절단하는 공정 및 포장 또는 권취하는 공정을 포함하여 수행된다. The post-processing 240 is cut in a desired size and shape of the adhesive sheet 100 including the surface coating film layer 10 having antifouling property and scratch-resisting property, which is composed of the surface coating film layer 10 and the base film layer 20 And a step of packaging or winding.

이를 통해, 본 발명에 따른 표면 코팅 필름층(10) 및 베이스 필름층(20)을 포함하여 구성되는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지(100)가 가공된다.Thereby, the adhesive sheet 100 including the surface coating film layer having the antifouling property and the scratch resilience, which is composed of the surface coating film layer 10 and the base film layer 20 according to the present invention, is processed.

도 4는 본 발명의 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 시공방법의 흐름도이다.4 is a flow chart of a method of applying an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience according to the present invention.

도 4를 참조하면, 상술한 바와 같이 제작된 표면 코팅 필름층(10) 및 베이스 필름층(20)을 포함하여 구성되는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지(100)는, 접착 대상표면 세척 과정(410), 이형지 제거 과정(420), 스퀴징 공정(430), 필름 커팅 및 열처리 공정(440)을 포함하여 접착 대상 표면에 접착된다.Referring to FIG. 4, the adhesive sheet 100 including the surface coating film layer having antifouling property and scratch resilience, which comprises the surface coating film layer 10 and the base film layer 20 manufactured as described above, The bonding surface cleaning process 410, the release paper removing process 420, the squeezing process 430, the film cutting process, and the heat treatment process 440, as shown in FIG.

접착 대상표면 세척 과정(410)은, 접착 대상인 자동차 내외장, 가전제품, 휴대전화 등 제품의 표면의 부착면을 세척하는 공정으로, 부착면을 탈지제와 부드러운 천을 이용하여 탈지하며, 본 실시예의 경우 탈지제로 이소 프로필렌 알콜(isopropyl alcohol)　80%를 희석하지 않고 원액그대로 사용한다. The bonding object surface cleaning process 410 is a process of cleaning the attachment surface of a product such as an automobile interior / exterior, a home appliance, a mobile phone, etc., and the attachment surface is degreased using a degreasing agent and a soft cloth. As the degreasing agent, 80% of isopropyl alcohol is not diluted but used as the undiluted solution.

이형지 제거/시트지 접착 과정(420)은, 상술한 접착 시트지(100)의 이면에 임시 부착된 이형지를 제거하고, 제품의 표면의 부착면에 시트지를 접착하는 공정이다. The release paper removing / paper sheet adhering process 420 is a process of removing the release paper temporarily attached to the back surface of the above-described adhesive paper sheet 100 and adhering the sheet paper to the attachment surface of the product surface.

스퀴징 공정(430)은, 부착된 시트지의 표면 코팅 필름층(10)의 표면 코팅층(11)의 표면에 계면활성제 용액을 충분히 도포 후 우레탄 스퀴지를 이용하여 표면에 밀착시켜 가압상태로 미는 스퀴징을 수행하는 공정이다. 본 실시예의 경우 물/계면활성제는 1/99의 비율로 혼합한 계면활성제 용액을 도포하며, 계면활성제 용액을 도포한 후 스퀴징함으로써, 부드러운 스퀴징과 표면손상이 방지되어 표면 코팅층(11)으로 인한 스퀴징 작업의 작업성 저하 및 표면 코팅층(11)의 표면 손상으로 인한 미관 저하를 방지할 수 있다.The surface of the surface coating layer 11 of the surface coating film layer 10 of the attached sheet is sufficiently coated with the surfactant solution, and then the surface of the surface coating layer 11 is closely contacted with the surface of the surface layer using a urethane squeegee, . In this embodiment, the surfactant solution mixed with the water / surfactant in a ratio of 1/99 is applied, and after the surfactant solution is applied and then squeezed, soft spiking and surface damage are prevented and the surface coating layer 11 It is possible to prevent deterioration in the workability of the squeegeeing operation and deterioration of the appearance due to surface damage of the surface coating layer 11. [

필름 커팅 및 열처리 공정(440)은, 제품의 표면의 부착면이외의 부분에 불필요하게 부착된 시트지 부분을 커팅에 의하여 제거하고, 시트지의 절단된 끝부분을 압력을 주며 열을 가하는 열처리 공정이다. 열처리 공정에는 핫건 또는 드라이어기를 이용한다.The film cutting and heat treatment process 440 is a heat treatment process in which a sheet portion unnecessarily attached to a portion other than the attachment surface of the product is removed by cutting and heat is applied to the cut end of the sheet under pressure. A hot gun or a dryer is used for the heat treatment process.

[방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 물성 실험][Test of physical properties of an adhesive sheet containing a surface coating film layer having antifouling property and scratch resilience]

아크릴산/이소 프로필 알코올/증류수가 1/3/1의 비율인 혼합용제 75중량%(아크릴산 15중량%, 이소 프로필 알코올 45중량%, 증류수 15중량%)에 이산화규소/플루오린화나트륨/톨루엔 디 이소시아네이트가 7/8/10의 비율로 혼합된 이산화규소 혼합 조성물 25중량%(이산화규소 7중량%, 플루오린화나트륨(NaF) 8중량%, 톨루엔 디 이소시아네이트 (TDI) 10중량%)을 균일하게 혼합하여 표면 코칭 필름 층 형성 용액을 상기 실시예에 적용하여 제작된 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지에 대하여 1) 헤이즈미터(haze meter)를 이용하여 광투과율과 반사율을 오염전후 측정하여 오염전후의 변화량을 측정하여 하기 표1과 같은 실험결과를 얻었으며, 2) 헤이즈미터(haze meter)를 이용하여 헤이즈값의 변화를 100g/㎠의 하중으로 철솔로 스크래치를 진행하기전 직후 일정시간 경과후 측정하여 그 최종 변화량을 측정하여 하기 표2와 같은 실험결과를 얻었다.To the mixed solvent of acrylic acid / isopropyl alcohol / distilled water at a ratio of 1/3/1 was added 75 wt% (acrylic acid 15 wt%, isopropyl alcohol 45 wt%, distilled water 15 wt%), silicon dioxide / sodium fluoride / toluene diisocyanate (7% by weight of silicon dioxide, 8% by weight of sodium fluoride (NaF) and 10% by weight of toluene diisocyanate (TDI)) mixed in a ratio of 7/8/10 were mixed uniformly The adhesive sheet comprising the surface coating film layer having antifouling property and scratch resilience, which was prepared by applying the surface coaching film layer forming solution to the above embodiment, was subjected to 1) measurement of light transmittance and reflectance using a haze meter And the change amount before and after the contamination was measured to obtain the experimental results shown in Table 1. 2) The change of the haze value was measured using a haze meter with a steel brush with a load of 100 g / And the final change amount was measured to obtain the results as shown in Table 2 below.

표1의 실험결과를 통해 오염 전후 광투과율의 변화량은 1%, 반사율의 변화량은 0.1%로 변화량이 매우 적어 오염에 강한 우수한 방오성을 가짐이 확인되었으며, 표2의 실험결과를 통해 스크래치 직후(1분 이내) 해이즈값의 변화량은 2.0%로 일반적인 변화량으로 상승하나 일정 시간이후(10분 이후) 해이즈값의 최종 변화량이 0.4%로 매우 낮아 스크래치에 대한 우수한 특성을 가지며 자가 복원성을 가짐을 확인할 수 있다. From the results of Table 1, it was confirmed that the variation of the light transmittance before and after the contamination was 1% and the variation of the reflectance was 0.1% Min.) The change in the haze value is 2.0%, which is increased to a general change amount. However, after a certain time (after 10 minutes), the final change amount of the haze value is as very low as 0.4% .

광투과율(%)Light transmittance (%) 반사율(%)reflectivity(%) 오염 전Before contamination 2020 2.02.0 오염 후After pollution 1919 1.91.9 변화량Variation 1One 0.10.1

헤이즈값(%)Haze value (%) 스크래치 전Scratch before 4.04.0 스크래치 직후(1분 이내)Immediately after scratching (within 1 minute) 6.06.0 스크래치 후(10분 이후) After scratching (after 10 minutes) 4.44.4 최종 변화량Final variation 0.40.4

Haze(%)= Is / (Is+Ir) *100, 여기서, Is = 2.5° 이상에서 투과된 빛의 세기 (=확산 투과율 광), Ir = 2.5° 내에서 투과된 빛의 세기 (=평행 투과율 광)(= Diffuse transmittance light), Ir = transmitted light intensity (= parallel transmittance) at Ir = 2.5 °, Haze (%) = Is / (Is + Ir) ore)

100 : 접착 시트지 10 : 표면 코팅 필름층
20 : 베이스 필름층 100: Adhesive sheet 10: Surface coating film layer
20: base film layer

Claims (10)

방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지에 있어서,
표면 코팅층(11)과 상기 표면 코팅층(11)이 그 표면에 형성되는 열가소성 폴리우레탄 박막층(12)로 구성되는 표면 코팅 필름층(10), 및
합성수지류의 필름이 투명 또는 불투명 재질로 표면에는 색채, 도안, 장식 또는 문자가 인쇄의 방법으로 형성되고, 이면에서는 제1 접착층(21)이 형성되는 베이스 필름(21), 베이스 필름(21)의 이면에 형성되어 상기 베이스 필름(21)의 이면을 이형지(23)에 임시 접착하고, 상기 이형지(23)가 제거된 뒤 접착 대상의 표면에 결합시키는 기능을 수행하는 제1 접착층(22), 상기 제1 접착층(22)에 임시 접착되는 이형지(23)을 포함하여 구성되는 베이스 필름층(20)을 포함하여,
상기 표면 코팅층(11)은, 열가소성 폴리우레탄 필름 층(12)의 표면에 아크릴산, 이소 프로필 알코올, 증류수가 사전 설정된 비율로 혼합된 혼합용제에 이산화규소, 플루오린화나트륨, 톨루엔 디 이소시아네이트가 사전설정된 비율로 혼합된 이산화규소 혼합 조성물이 균일하게 혼합된 표면 코팅층 형성용액을 스프레이 도포하여 70℃의 온도로 1.5시간으로 건조하여 형성되는 것을 특징으로 하는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지.
An adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience,
A surface coating film layer 10 composed of a surface coating layer 11 and a thermoplastic polyurethane thin film layer 12 on which the surface coating layer 11 is formed,
The base film 21 on which the first adhesive layer 21 is formed, the base film 21 on which the first adhesive layer 21 is formed, and the base film 21 on which the first adhesive layer 21 is formed. A first adhesive layer 22 formed on the back surface of the base film 21 to temporarily bond the back surface of the base film 21 to the release paper 23 and to bond the release paper 23 to the surface of the object to be bonded after the release paper 23 is removed, And a release film (23) temporarily adhered to the first adhesive layer (22). The base film layer (20)
The surface coating layer 11 is formed by mixing silicon dioxide, sodium fluoride and toluene diisocyanate in a mixed solvent in which acrylic acid, isopropyl alcohol and distilled water are mixed at a predetermined ratio on the surface of the thermoplastic polyurethane film layer 12 Is coated by spraying a uniformly mixed surface coating layer forming solution and dried at a temperature of 70 ° C for 1.5 hours to form a surface coating film layer having antifouling property and scratch resistance, Sheet.
청구항 1에 있어서,
상기 표면 코팅층 형성용액은, 이산화 규소(SiO2) 5~9중량%, 플루오린화나트륨(NaF) 6~10중량%, 톨루엔 디 이소시아네이트(TDI) 7~13중량%, 아크릴산 10~20중량%, 이소 프로필 알코올 35~55중량%, 증류수 10~20중량%의 조성을 가지는 것을 특징으로 하는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지.
The method according to claim 1,
Wherein the surface coating layer forming solution contains 5 to 9% by weight of silicon dioxide (SiO 2 ), 6 to 10% by weight of sodium fluoride (NaF), 7 to 13% by weight of toluene diisocyanate (TDI) A surface coating film layer having antifouling property and scratch resilience, wherein the adhesive layer has a composition of 35 to 55% by weight of isopropyl alcohol and 10 to 20% by weight of distilled water.
청구항 1에 있어서,
상기 표면 코팅층(11)은 10㎛ ~ 15㎛ 의 두께를 가지도록 형성된 것을 특징으로하는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지.
The method according to claim 1,
Wherein the surface coating layer (11) is formed to have a thickness of 10 탆 to 15 탆, and a surface coating film layer having antifouling property and scratch resilience.
삭제delete 청구항 1 내지 청구항 3 중 어느 한 항에 있어서,
표면 코팅층 형성용액은 아크릴산 15중량%, 이소 프로필 알코올 45중량%, 증류수 15중량%, 이산화규소 7중량%, 플루오린화나트륨 8중량%, 톨루엔 디 이소시아네이트 10중량%의 조성비를 갖는 것을 특징으로 하는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지.
The method according to any one of claims 1 to 3,
The surface coating layer forming solution has a composition ratio of 15 wt% of acrylic acid, 45 wt% of isopropyl alcohol, 15 wt% of distilled water, 7 wt% of silicon dioxide, 8 wt% of sodium fluoride and 10 wt% of toluene diisocyanate And a surface coating film layer having scratch resilience.
방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제작방법에 있어서,
표면 코팅층 형성용액을 제조하는 표면 코팅층 형성용액 혼합공정(210),
베이스 필름(21)의 표면에 색채, 도안, 장식 또는 문자를 형성하고 이면에 접착제를 도포하여 제1 접착층(22)을 형성하며, 상기 제1 접착층(22)에 임시 접착되는 이형지(23)를 부착하는 공정을 포함하는 베이스 필름층 가공공정(220)을 포함하여,
상기 베이스 필름층 가공공정(220)은 색채 또는 도안이 형성된 표면에 열가소성 폴리우레탄 박막층(12)을 형성하는 공정을 포함하여,
상기 표면 코팅층 형성용액은 아크릴산, 이소 프로필 알코올, 증류수가 사전 설정된 비율로 혼합된 혼합용제에 이산화규소, 플루오린화나트륨, 톨루엔 디 이소시아네이트가 사전설정된 비율로 혼합된 이산화규소 혼합 조성물이 균일하게 혼합하여 제조되며,
베이스 필름층 가공공정(220)에서 가공된 열가소성 폴리우레탄 박막층(12)이 형성된 베이스 필름층(20)의 표면에 표면 코팅층 형성용액 혼합공정(210)에서 혼합된 표면 코팅층 형성용액을 도포하여, 70℃의 온도로 1.5 시간 건조하여 표면 코팅층(11)을 형성하는 표면 코팅층 형성공정(230)을 포함하는 것을 특징으로 하는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제작방법.
A method of producing an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience,
A surface coating layer forming solution mixing process 210 for preparing a surface coating layer forming solution,
A first adhesive layer 22 is formed by applying a glue to the back surface of the base film 21 and a release paper 23 temporarily adhered to the first adhesive layer 22 And a base film layer processing step (220)
The base film layer processing step 220 includes a step of forming a thermoplastic polyurethane thin film layer 12 on the color or patterned surface,
The surface coating layer forming solution is prepared by uniformly mixing a silicone dioxide mixed composition in which silicon dioxide, sodium fluoride, and toluene diisocyanate are mixed in a predetermined ratio in a mixed solvent in which acrylic acid, isopropyl alcohol, and distilled water are mixed in a predetermined ratio And,
The surface coating layer forming solution mixed in the surface coating layer forming solution mixing process 210 is applied to the surface of the base film layer 20 formed with the thermoplastic polyurethane thin film layer 12 processed in the base film layer processing step 220, And a surface coating layer forming step (230) of forming a surface coating layer (11) by drying at a temperature of 100C for 1.5 hours.
방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제작방법에 있어서,
표면 코팅층 형성용액을 제조하는 표면 코팅층 형성용액 혼합공정(310),
열가소성 폴리우레탄 박막층(12)을 구성하는 열가소성 폴리우레탄 박막 필름을 준비하고, 준비된 열가소성 폴리우레탄 박막 필름의 표면에 코팅층 형성용액을 스프레이 방식으로 도포하여 표면 코팅층(11)이 형성된 열가소성 폴리우레탄 박막층(12)을 제작하는 표면 코팅층 형성공정(320),
베이스 필름(21)의 표면에 색채, 도안, 장식 또는 문자를 형성하고 이면에 접착제를 도포하여 접착층(22)을 형성하며, 상기 접착층(22)에 임시 접착되는 이형지(23)를 부착하는 공정을 포함하여, 베이스 필름층(20)을 가공하는 베이스 필름층 가공공정(330), 및
표면 코팅층 형성공정(320)에서 제작된 표면 코팅층(11)이 형성된 열가소성 폴리우레탄 박막층(12)과 베이스 필름층 가공공정(330)에서 가공된 베이스 필름층(20)을 결합하는 표면 코팅 필름층 결합공정(340)을 포함하여,
상기 표면 코팅층 형성용액은 아크릴산, 이소 프로필 알코올, 증류수가 사전 설정된 비율로 혼합된 혼합용제에 이산화규소, 플루오린화나트륨, 톨루엔 디 이소시아네이트가 사전설정된 비율로 혼합된 이산화규소 혼합 조성물이 균일하게 혼합하여 제조되며,
표면 코팅층 형성공정(320)에서 가공된 열가소성 폴리우레탄 박막층(12)의 표면에 표면 코팅층 형성용액 표면 코팅층 형성용액을 도포하여, 70℃의 온도로 1.5 시간 건조하여 표면 코팅층(11)을 형성하는 것을 특징으로 하는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제작방법.
A method of producing an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience,
A surface coating layer forming solution mixing process 310 for preparing a surface coating layer forming solution,
A thermoplastic polyurethane thin film constituting the thermoplastic polyurethane thin film layer 12 was prepared and a coating layer forming solution was applied on the surface of the prepared thermoplastic polyurethane thin film by a spraying method to form a thermoplastic polyurethane thin film layer 12 A surface coating layer forming step 320 for forming a surface coating layer,
A step of forming a coloring layer, a pattern, a decoration or a character on the surface of the base film 21 and applying an adhesive to the back surface to form an adhesive layer 22 and attaching a release paper 23 temporarily adhered to the adhesive layer 22 A base film layer processing step 330 for processing the base film layer 20,
A surface coating film layer joining the thermoplastic polyurethane thin film layer 12 formed with the surface coating layer 11 formed in the surface coating layer forming step 320 and the base film layer 20 processed in the base film layer processing step 330 Including step 340,
The surface coating layer forming solution is prepared by uniformly mixing a silicone dioxide mixed composition in which silicon dioxide, sodium fluoride, and toluene diisocyanate are mixed in a predetermined ratio in a mixed solvent in which acrylic acid, isopropyl alcohol, and distilled water are mixed in a predetermined ratio And,
A solution for forming a surface coating layer-forming solution surface coating layer is applied to the surface of the processed thermoplastic polyurethane thin film layer 12 in the surface coating layer forming step 320 and dried at a temperature of 70 ° C for 1.5 hours to form a surface coating layer 11 And a surface coating film layer having antifouling property and scratch resilience.
청구항 6 또는 청구항 7에 있어서,
상기 표면 코팅층(11)은 10㎛ ~ 15㎛ 의 두께를 가지도록 형성된 것을 특징으로 하는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제작방법.
The method according to claim 6 or 7,
Wherein the surface coating layer (11) is formed to have a thickness of 10 탆 to 15 탆, wherein the surface coating layer has antifouling property and scratch resilience.
삭제delete 청구항 6 또는 청구항 7에 있어서,
상기 표면 코팅층 형성용액은 아크릴산 15중량%, 이소 프로필 알코올 45중량%, 증류수 15중량%, 이산화규소 7중량%, 플루오린화나트륨 8중량%, 톨루엔 디 이소시아네이트 10중량%의 조성비를 갖는 것을 특징으로 하는 방오성 및 스크래치 복원성을 가지는 표면 코팅 필름층을 포함하는 접착 시트지의 제작방법.The method according to claim 6 or 7,
Wherein the surface coating layer forming solution has a composition ratio of 15 wt% of acrylic acid, 45 wt% of isopropyl alcohol, 15 wt% of distilled water, 7 wt% of silicon dioxide, 8 wt% of sodium fluoride and 10 wt% of toluene diisocyanate A method for producing an adhesive sheet comprising a surface coating film layer having antifouling property and scratch resilience.
KR1020170057832A 2017-05-10 2017-05-10 Adhesive sheet comprising a surface-coating film layer having antifouling property and scratch-resisting property and Method for producing the same KR101882756B1 (en)