CN108555540A - A kind of processing technology of floor decorative metal strip - Google Patents
A kind of processing technology of floor decorative metal strip Download PDFInfo
- Publication number
- CN108555540A CN108555540A CN201810373221.1A CN201810373221A CN108555540A CN 108555540 A CN108555540 A CN 108555540A CN 201810373221 A CN201810373221 A CN 201810373221A CN 108555540 A CN108555540 A CN 108555540A
- Authority
- CN
- China
- Prior art keywords
- metal strip
- shape
- cutting
- scribing line
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Dried the invention discloses casting, Plastic Forming, shape scribing line, sawing, filing, the spray painting of a kind of processing technology of floor decorative metal strip, including waste material and etc..It is cast to irregular aluminum alloy materials, refine into unified strip, it is forged according to the Selection utilization metal forming machinery of thickness, metal strip can be processed according to the demand of thickness by changing group technology, by carrying out shape scribing line to the metal strip after forging and stamping, and it is cut by abrasive wheel cutting machine, it is processed simultaneously by filing, the group technology can cut metal strip according to the demand of size, workpiece surface can also be made to reach required size and shape, the degree of roughness of work piece cut knife-edge part is reduced simultaneously, by in paint spray booth, according to the selection of color and the resistance of increase metal, it paints to bar surface, and it is dried under conditions of 40 60 DEG C, the selection of color can be increased, the beauty and antiseptic property of metal strip.
Description
Technical field
The present invention relates to decoration metal strip technical field more particularly to a kind of processing technologys of floor decorative metal strip.
Background technology
With the development of technique, machine replaces manual operations, metal product could largely enter society among family, with
It various cosmetic decorations and our life, such as can also use metal strip in bottom plate decoration and be decorated.
Decoration metal strip needs to be processed to reach the shape and decorative effect of anticipation, existing bottom plate dress before use
The selection of selection and color of size can not be carried out according to the specific requirements of people by adoring metal strip processing, and it is impossible to meet people
Decoration demand.For this purpose, it is proposed that a kind of processing technology of floor decorative metal strip, to solve to mention in above-mentioned background technology
The problem of.
Invention content
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of floor decorative metal strip proposed
Processing technology.
To achieve the goals above, present invention employs following technical solutions:
A kind of processing technology of floor decorative metal strip, specifically includes following steps:
The casting of S1, waste material:Irregular aluminum alloy materials are refined at 700-800 DEG C, then pass through mould again
Mold casting is cooled and shaped at unified strip;
S2, Plastic Forming:By metal strip after cooling in S1 according to required decoration thickness, under the conditions of 100-150 DEG C,
It is forged and pressed under the pressure of 480-520bar using metal forming machinery, to reach required thickness;
S3, shape scribing line:It is crossed on the aluminium sheet after being forged and pressed in S2 according to required shape using there is coloured pencil,
The cutting ruler in follow-up cutting process is avoided to spend greatly;
S4, sawing:First the scribed aluminium sheet in S3 is fixed, then utilizes abrasive wheel cutting machine along scribing line position
It is cut, removes extra position, to reach required shape;
S5, filing:Machining is carried out to the knife-edge part of surface of aluminum plate and cutting after cutting using file, makes workpiece
Surface reaches required size and shape, while reducing the degree of roughness of work piece cut knife-edge part;
S6, spray painting drying:In paint spray booth, according to the selection of color and the resistance of increase metal, to bar surface
It paints, and is dried under conditions of 40-60 DEG C, increase the beauty and antiseptic property of metal strip;
S7, classification:Metal strip after being dried to spray painting carries out classification storage according to the difference of the characteristics such as color, size, just
It is selected according to the style of decoration in user.
Preferably, in S1, the refining of aluminium plate is carried out using industrial furnace in casting process, and for other metals
Refining, refined when alternative refining temperature with meeting different types of metal.
Preferably, it when shape is crossed in S3, when selection can be easy the color distinguished with aluminium plate intrinsic colour, and adopts
With dark color.
Preferably, in S4 sawings, cutter need to be cut along the outside of scribing line or scribing line as far as possible, avoid cutting
Cut the inside of scribing line.
A kind of production method of pathological section provided by the invention, compared with prior art, the present invention have as follows a little:
1, it by being cast to irregular aluminum alloy materials, refines at unified strip, and according to the selection of thickness
It is forged using metal forming machinery, metal strip can be processed according to the demand of thickness by changing group technology;
2, it by carrying out shape scribing line to the metal strip after forging and stamping, and is cut by abrasive wheel cutting machine, is passed through simultaneously
Filing is processed, which can cut metal strip according to the demand of size, workpiece surface can also be made to reach
Required size and shape, while reducing the degree of roughness of work piece cut knife-edge part;
3, by paint spray booth, according to the selection of color and the resistance of increase metal, being sprayed to bar surface
Paint, and dried under conditions of 40-60 DEG C, the selection of color, the beauty of metal strip and antiseptic property can be increased;
4, present invention process is simple, and selection processing can be carried out according to thickness, size, degree of roughness and color, increases
Decorate the applicability and aesthetics of metal strip.
Specific implementation mode
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment 1
A kind of processing technology of floor decorative metal strip, specifically includes following steps:
The casting of S1, waste material:Irregular aluminum alloy materials are refined at 700 DEG C, are then cast again by model
Unified strip is caused, and is cooled and shaped;
S2, Plastic Forming:By metal strip after cooling in S1 according to required decoration thickness, under the conditions of 100 DEG C, utilize
Metal forming machinery is forged and pressed under the pressure of 480bar, to reach required thickness;
S3, shape scribing line:It is crossed on the aluminium sheet after being forged and pressed in S2 according to required shape using there is coloured pencil,
The cutting ruler in follow-up cutting process is avoided to spend greatly;
S4, sawing:First the scribed aluminium sheet in S3 is fixed, then utilizes abrasive wheel cutting machine along scribing line position
It is cut, removes extra position, to reach required shape;
S5, filing:Machining is carried out to the knife-edge part of surface of aluminum plate and cutting after cutting using file, makes workpiece
Surface reaches required size and shape, while reducing the degree of roughness of work piece cut knife-edge part;
S6, spray painting drying:In paint spray booth, according to the selection of color and the resistance of increase metal, to bar surface
It paints, and is dried under conditions of 40 DEG C, increase the beauty and antiseptic property of metal strip;
S7, classification:Metal strip after being dried to spray painting carries out classification storage according to the difference of the characteristics such as color, size, just
It is selected according to the style of decoration in user.
Embodiment 2
A kind of processing technology of floor decorative metal strip, specifically includes following steps:
The casting of S1, waste material:Irregular aluminum alloy materials are refined at 750 DEG C, are then cast again by model
Unified strip is caused, and is cooled and shaped;
S2, Plastic Forming:By metal strip after cooling in S1 according to required decoration thickness, under the conditions of 130 DEG C, utilize
Metal forming machinery is forged and pressed under the pressure of 500bar, to reach required thickness;
S3, shape scribing line:It is crossed on the aluminium sheet after being forged and pressed in S2 according to required shape using there is coloured pencil,
The cutting ruler in follow-up cutting process is avoided to spend greatly;
S4, sawing:First the scribed aluminium sheet in S3 is fixed, then utilizes abrasive wheel cutting machine along scribing line position
It is cut, removes extra position, to reach required shape;
S5, filing:Machining is carried out to the knife-edge part of surface of aluminum plate and cutting after cutting using file, makes workpiece
Surface reaches required size and shape, while reducing the degree of roughness of work piece cut knife-edge part;
S6, spray painting drying:In paint spray booth, according to the selection of color and the resistance of increase metal, to bar surface
It paints, and is dried under conditions of 50 DEG C, increase the beauty and antiseptic property of metal strip;
S7, classification:Metal strip after being dried to spray painting carries out classification storage according to the difference of the characteristics such as color, size, just
It is selected according to the style of decoration in user.
Embodiment 3
A kind of processing technology of floor decorative metal strip, specifically includes following steps:
The casting of S1, waste material:Irregular aluminum alloy materials are refined at 800 DEG C, are then cast again by model
Unified strip is caused, and is cooled and shaped;
S2, Plastic Forming:By metal strip after cooling in S1 according to required decoration thickness, under the conditions of 150 DEG C, utilize
Metal forming machinery is forged and pressed under the pressure of 520bar, to reach required thickness;
S3, shape scribing line:It is crossed on the aluminium sheet after being forged and pressed in S2 according to required shape using there is coloured pencil,
The cutting ruler in follow-up cutting process is avoided to spend greatly;
S4, sawing:First the scribed aluminium sheet in S3 is fixed, then utilizes abrasive wheel cutting machine along scribing line position
It is cut, removes extra position, to reach required shape;
S5, filing:Machining is carried out to the knife-edge part of surface of aluminum plate and cutting after cutting using file, makes workpiece
Surface reaches required size and shape, while reducing the degree of roughness of work piece cut knife-edge part;
S6, spray painting drying:In paint spray booth, according to the selection of color and the resistance of increase metal, to bar surface
It paints, and is dried under conditions of 60 DEG C, increase the beauty and antiseptic property of metal strip;
S7, classification:Metal strip after being dried to spray painting carries out classification storage according to the difference of the characteristics such as color, size, just
It is selected according to the style of decoration in user.
In summary:The processing technology of the floor decorative metal strip of the present invention, by not compared with traditional technology
The aluminum alloy materials of rule are cast, and refining is forged at unified strip, and according to the Selection utilization metal forming machinery of thickness
It makes, metal strip can be processed according to the demand of thickness by changing group technology, by carrying out shape to the metal strip after forging and stamping
Shape is crossed, and is cut by abrasive wheel cutting machine, while being processed by filing, which can be according to the demand of size
Metal strip is cut, workpiece surface can also be made to reach required size and shape, while reducing work piece cut knife
The degree of roughness at mouthful place, by paint spray booth, according to the selection of color and the resistance of increase metal, to bar surface into
Row spray painting, and dried under conditions of 40-60 DEG C, the selection of color, the beauty of metal strip and antiseptic property can be increased,
Present invention process is simple, and selection processing can be carried out according to thickness, size, degree of roughness and color, increases decoration metal strip
Applicability and aesthetics.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of processing technology of floor decorative metal strip, which is characterized in that specifically include following steps:
The casting of S1, waste material:Irregular aluminum alloy materials are refined at 700-800 DEG C, are then cast again by model
Unified strip is caused, and is cooled and shaped;
S2, Plastic Forming:By metal strip after cooling in S1 according to required decoration thickness, under the conditions of 100-150 DEG C, utilize
Metal forming machinery is forged and pressed under the pressure of 480-520bar, to reach required thickness;
S3, shape scribing line:It crosses, avoids on the aluminium sheet after being forged and pressed in S2 using there is coloured pencil according to required shape
Cutting ruler is spent greatly in follow-up cutting process;
S4, sawing:First the scribed aluminium sheet in S3 is fixed, is then carried out along scribing line position using abrasive wheel cutting machine
Cutting, removes extra position, to reach required shape;
S5, filing:Machining is carried out to the knife-edge part of surface of aluminum plate and cutting after cutting using file, makes workpiece surface
Reach required size and shape, while reducing the degree of roughness of work piece cut knife-edge part;
S6, spray painting drying:In paint spray booth, according to the selection of color and the resistance of increase metal, bar surface is carried out
Spray painting, and dried under conditions of 40-60 DEG C, increase the beauty and antiseptic property of metal strip;
S7, classification:Metal strip after being dried to spray painting carries out classification storage according to the difference of the characteristics such as color, size, convenient for making
User selects according to the style of decoration.
2. a kind of processing technology of floor decorative metal strip according to claim 1, it is characterised in that:In S1, casting
The refining of aluminium plate is carried out when making process using industrial furnace, and for the refining of other metals, when alternative refining temperature is with full
The different types of metal refining of foot.
3. a kind of processing technology of floor decorative metal strip according to claim 1, it is characterised in that:Shape is drawn in S3
When line, when the color for selecting that differentiation can be easy with aluminium plate intrinsic colour, and using dark.
4. a kind of processing technology of floor decorative metal strip according to claim 1, it is characterised in that:In S4 sawings,
Cutter need to be cut along the outside of scribing line or scribing line as far as possible, avoid the inside for cutting to scribing line.