CN108504299A - A kind of general-purpose High-strength adhesive tape and preparation method thereof - Google Patents
A kind of general-purpose High-strength adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN108504299A CN108504299A CN201810444698.4A CN201810444698A CN108504299A CN 108504299 A CN108504299 A CN 108504299A CN 201810444698 A CN201810444698 A CN 201810444698A CN 108504299 A CN108504299 A CN 108504299A
- Authority
- CN
- China
- Prior art keywords
- adhesive tapes
- adhesive
- adhesive tape
- pressure sensitive
- tapes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of general-purpose High-strength adhesive tapes, including the core A adhesive tapes that cohesive force is strong, the upper and lower surface of A adhesive tapes are respectively equipped with B adhesive tapes and C adhesive tapes；The High-strength adhesive tape High-strength adhesive tape prepares A adhesive tapes using elastomer pressure sensitive glue or resin pressure sensitive adhesive band as raw material, is then connected and fixed B adhesive tapes and C adhesive tapes in the upper and lower surface of A adhesive tapes.The adhesive tape of the present invention can be used for being bonded a variety of materials, such as plastics, rubber, metal, foam, metope lacquer painting, wood, various cloth materials, various paper wood materials, use scope is wide, and 90 degree of peel strengths reach as high as 42N/cm, the High-strength adhesive tape is by distinguishing compound B adhesive tapes and C adhesive tapes composition in the upper and lower surface of A adhesive tapes simultaneously, there are chemical bonds between A adhesive tapes and B adhesive tapes, A adhesive tapes and C adhesive tapes, and during having ensured use, with B, C adhesive tape delamination does not occur for A adhesive tapes.
Description
Technical field
The invention belongs to adhesive and adhesive product field, it is related to a kind of general-purpose High-strength adhesive tape and preparation method thereof.
Background technology
Current industrial circle and domestic environments is often used the bonding that glue realizes multiple material, but there is some for glue
Disadvantage, such as：Bond area is uncontrollable and leads to bonding plane unsightly, hardening time is long, and solvent volatile zone pollutes.It is pressure-sensitive
Adhesive tape is another common adhesives, and use is extremely convenient, as long as applying small pressure realizes bonding, is not required to
It will long-time or hot setting；It is directly bonded after die-cuttable molding, and can realize continuous production, be bonded ultrahigh in efficiency.But often
It is often limited to advise the bonded base material type of pressure sensitive adhesive tape, for example, can the adhesive tapes of bonding plastics can not be bonded cloth material, bonding
The adhesive tape of glass can not bonded metal etc..
Invention content
The purpose of the present invention is to provide a kind of general-purpose High-strength adhesive tapes, can be used for being bonded a variety of materials, such as plastics, rubber
The materials such as glue, metal, foam, metope lacquer painting, wood, various cloth materials, various paper woods, use scope is wide, and 90 degree of strippings are strong
Degree reaches as high as 42N/cm, while the High-strength adhesive tape is to distinguish compound B adhesive tapes and C adhesive tapes by the upper and lower surface in A adhesive tapes
Composition, there are chemical bonds between A adhesive tapes and B adhesive tapes, A adhesive tapes and C adhesive tapes, during having ensured use, A adhesive tapes and B, C
Delamination does not occur for adhesive tape.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of general-purpose High-strength adhesive tape, including core A adhesive tapes that cohesive force is strong, the upper and lower surface difference of A adhesive tapes
Equipped with B adhesive tapes and C adhesive tapes；
The High-strength adhesive tape prepares A adhesive tapes using elastomer pressure sensitive glue or resin pressure sensitive adhesive band as raw material, then in A adhesive tapes
Upper and lower surface be connected and fixed B adhesive tapes and C adhesive tapes.
Further, which can be used for being bonded a variety of materials, and 90 degree of peel strengths reach as high as 42N/
cm。
Further, the thickness of A adhesive tapes is 500-800 microns；The thickness of B adhesive tapes and C adhesive tapes is 25-100 microns.
Further, A adhesive tapes, B adhesive tapes and C adhesive tapes are elastomer pressure sensitive adhesive tape or resin pressure sensitive adhesive band.
Further, the elastomer pressure sensitive adhesive tape is that natural rubber pressure sensitive adhesive tape, synthetic rubber and reclaimed rubber are pressure-sensitive
One kind in adhesive tape.
Further, the resin pressure sensitive adhesive band be polyacrylate adhesive tape, urethane rubber belt, polyvinyl chloride rubber belt,
One kind in polyvingl ether adhesive tape.
A kind of preparation method of general-purpose High-strength adhesive tape, specific preparation process are：With elastomer pressure sensitive glue or resin type pressure
Sensitive tape is that raw material prepares A adhesive tapes, is then connected and fixed B adhesive tapes and C adhesive tapes in the upper and lower surface of A adhesive tapes.
Further, specific preparation process is：Using elastomer pressure sensitive glue or resin pressure sensitive adhesive band A glue is prepared as raw material
B adhesive tapes and C adhesive tapes, are then fitted in the upper and lower surface of A adhesive tapes by band, B adhesive tapes and C adhesive tapes respectively.
Further, specific preparation process is：A adhesive tapes are prepared as raw material using elastomer pressure sensitive glue or resin pressure sensitive adhesive,
Then elastomer pressure sensitive glue or resin pressure sensitive adhesive are respectively coated in the upper and lower surface of A adhesive tapes so that the upper and lower surface shape of A adhesive tapes
At B adhesive tape layers and C adhesive tape layers.
Beneficial effects of the present invention：
1, the adhesive tape for preparing of the present invention can be used for being bonded a variety of materials, as plastics, rubber, metal, foam, metope lacquer painting,
The materials such as wood, various cloth materials, various paper woods, use scope is wide, and 90 degree of peel strengths reach as high as 42N/cm.
2, High-strength adhesive tape of the invention is by distinguishing compound B adhesive tapes and C adhesive tapes composition, A in the upper and lower surface of A adhesive tapes
There are chemical bonds between adhesive tape and B adhesive tapes, A adhesive tapes and C adhesive tapes, and during having ensured use, A adhesive tapes and B, C adhesive tape are not
Delamination occurs.
Description of the drawings
In order to facilitate the understanding of those skilled in the art, the present invention will be further described below with reference to the drawings.
Fig. 1 is general-purpose High-strength adhesive tape structural schematic diagram of the present invention.
Specific implementation mode
Embodiment 1：
A kind of general-purpose High-strength adhesive tape, including the strong core A adhesive tapes 1 of cohesive force, the upper and lower surface difference of A adhesive tapes 1
The fixed B adhesive tapes 2 of fitting and C adhesive tapes 3；According to material to be bonded difference, different B adhesive tapes 2, C adhesive tapes 3, A adhesive tapes 1 can be selected
There are chemical bonds between B adhesive tapes 2, A adhesive tapes 1 and C adhesive tapes 3, during having ensured use, A adhesive tapes 1 and B adhesive tapes 2, C glue
Delamination does not occur for band 3；It can be used for being bonded a variety of materials, such as plastics, rubber, metal, foam, metope lacquer painting, glass, ceramic tile, wood
Head, various cloth materials, various paper woods etc.；Wherein B adhesive tapes 2 and C adhesive tapes 3 and material cohesive force to be bonded are strong, initial bonding strength is strong；
The specific preparation process of the High-strength adhesive tape is：Following table on the polyurethane adhesive A adhesive tapes for being 800 microns by a kind of thickness
The face polyacrylic acid ester gum B adhesive tapes that coating thickness is 25 microns respectively, the polyacrylic acid ester gum C adhesive tapes that thickness is 50 microns, are pressed
National standard is tested, which was 28.8N/cm to 90 degree of peel strengths of PVC board after 72 hours；72 hours to the 90 of ABS plates
Degree peel strength is 31.5N/cm, dynamic shear strength 20N/mm2.
Embodiment 2
The structure of High-strength adhesive tape is same as Example 1, and preparation method is as follows：
It is 50 microns that the polyacrylic acid ester gum A adhesive tape upper and lower surfaces that a kind of thickness is 600 microns, which are respectively coated thickness,
Modified polyacrylate glue B adhesive tapes, the modified polyacrylate glue C adhesive tapes that thickness is 50 microns, are tested, the glue by national standard
With after 72 hours to 90 degree of peel strengths of stainless steel plate be 35.6N/cm；72 hours 90 degree of peel strengths to aluminium sheet are 42N/
cm。
Embodiment 3
The structure of High-strength adhesive tape is same as Example 1, and preparation method is as follows：
The modified rubber A adhesive tape upper and lower surfaces that a kind of thickness is 500 microns are respectively coated the poly- ammonia that thickness is 100 microns
Ester B adhesive tapes, the polyacrylate C adhesive tapes that thickness is 100 microns, are tested, the adhesive tape is after 72 hours to glass by national standard
90 degree of peel strengths are 37.2N/cm；72 hours 90 degree of peel strengths to acrylic plate are 29.1N/cm.
Embodiment 4
The structure of High-strength adhesive tape is same as Example 1, and preparation method is as follows：
The polyurethane A adhesive tapes upper and lower surface modification that coating thickness is 80 microns respectively that a kind of thickness is 800 microns is gathered
Acrylate B adhesive tapes and modified polyacrylate C adhesive tapes are tested by national standard, and the adhesive tape is after 72 hours to 90 degree of strippings of PE
It is 28.6N/cm from intensity, T peel strengths are 25N/cm.
Present invention disclosed above preferred embodiment is only intended to help to illustrate the present invention.There is no detailed for preferred embodiment
All details are described, are not limited the invention to the specific embodiments described.Obviously, according to the content of this specification,
It can make many modifications and variations.These embodiments are chosen and specifically described to this specification, is in order to preferably explain the present invention
Principle and practical application, to enable skilled artisan to be best understood by and utilize the present invention.The present invention is only
It is limited by claims and its full scope and equivalent.
Claims (9)
1. a kind of general-purpose High-strength adhesive tape, which is characterized in that including the strong core A adhesive tapes of cohesive force, the upper surface of A adhesive tapes is under
Surface is respectively equipped with B adhesive tapes and C adhesive tapes；
The High-strength adhesive tape prepares A adhesive tapes using elastomer pressure sensitive glue or resin pressure sensitive adhesive band as raw material, then in the upper of A adhesive tapes
Lower surface is connected and fixed B adhesive tapes and C adhesive tapes.
2. a kind of general-purpose High-strength adhesive tape according to claim 1, which is characterized in that the general-purpose High-strength adhesive tape can be used for
A variety of materials are bonded, 90 degree of peel strengths reach as high as 42N/cm.
3. a kind of general-purpose High-strength adhesive tape according to claim 1, which is characterized in that the thickness of A adhesive tapes is that 500-800 is micro-
Rice；The thickness of B adhesive tapes and C adhesive tapes is 25-100 microns.
4. a kind of general-purpose High-strength adhesive tape according to claim 1, which is characterized in that A adhesive tapes, B adhesive tapes and C adhesive tapes are bullet
Property body pressure sensitive adhesive tape or resin pressure sensitive adhesive band.
5. a kind of general-purpose High-strength adhesive tape according to claim 4, which is characterized in that the elastomer pressure sensitive adhesive tape is day
One kind in T PNR pressure sensitive adhesive tape, synthetic rubber and reclaimed rubber pressure sensitive adhesive tape.
6. a kind of general-purpose High-strength adhesive tape according to claim 4, which is characterized in that the resin pressure sensitive adhesive band is poly-
One kind in acrylate adhesive tape, urethane rubber belt, polyvinyl chloride rubber belt, polyvingl ether adhesive tape.
7. a kind of preparation method of general-purpose High-strength adhesive tape according to claim 1, which is characterized in that specific preparation process
For：A adhesive tapes are prepared as raw material using elastomer pressure sensitive glue or resin pressure sensitive adhesive band, it is then solid in the connection of the upper and lower surface of A adhesive tapes
Determine B adhesive tapes and C adhesive tapes.
8. a kind of preparation method of general-purpose High-strength adhesive tape according to claim 7, which is characterized in that specific preparation process
For：A adhesive tapes, B adhesive tapes and C adhesive tapes are prepared as raw material using elastomer pressure sensitive glue or resin pressure sensitive adhesive band, then by B adhesive tapes and C
Adhesive tape is fitted in the upper and lower surface of A adhesive tapes respectively.
9. a kind of preparation method of general-purpose High-strength adhesive tape according to claim 7, which is characterized in that specific preparation process
For：A adhesive tapes are prepared as raw material using elastomer pressure sensitive glue or resin pressure sensitive adhesive, are then respectively coated in the upper and lower surface of A adhesive tapes
Elastomer pressure sensitive glue or resin pressure sensitive adhesive so that the upper and lower surface of A adhesive tapes forms B adhesive tape layers and C adhesive tape layers.