CN108439801A - 一次烧成发泡通体装饰板材及其制备方法 - Google Patents
一次烧成发泡通体装饰板材及其制备方法 Download PDFInfo
- Publication number
- CN108439801A CN108439801A CN201810338014.2A CN201810338014A CN108439801A CN 108439801 A CN108439801 A CN 108439801A CN 201810338014 A CN201810338014 A CN 201810338014A CN 108439801 A CN108439801 A CN 108439801A
- Authority
- CN
- China
- Prior art keywords
- slurry
- foaming
- sand
- layer
- firing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
原料 | 台山中温砂 | 新丰砂 | 莫村中温砂 | 四会泥 | 广西藤县砂 |
用量 | 11% | 9% | 5% | 18% | 10% |
原料 | 新会泥 | 广四砂 | 莲塘中温砂 | 中山砂 | 滑石泥 |
用量 | 3% | 6% | 10% | 5% | 3% |
原料 | 北海石粉 | 减水剂 | 改性羧甲基纤维素钠 | 碳化硅 | 二氧化锰 |
用量 | 18.7% | 0.75% | 0.1% | 0.3% | 0.15% |
原料 | 锆白不透水熔块 | 球土 | 硅酸锆 | 氧化铝 | 羧甲基纤维素钠 | 三聚磷酸钠 |
用量 | 79.4% | 5% | 10% | 5% | 0.25% | 0.35% |
原料 | 台山中温砂 | 新丰砂 | 莫村中温砂 | 四会泥 | 广西藤县砂 |
用量 | 10% | 10% | 4% | 19% | 9% |
原料 | 新会泥 | 广四砂 | 莲塘中温砂 | 中山砂 | 滑石泥 |
用量 | 4% | 5% | 11% | 4% | 4% |
原料 | 北海石粉 | 减水剂 | 改性羧甲基纤维素钠 | 碳化硅 | 二氧化锰 |
用量 | 18.7% | 0.8% | 0.05% | 0.35% | 0.1% |
原料 | 锆白不透水熔块 | 球土 | 硅酸锆 | 氧化铝 | 羧甲基纤维素钠 | 三聚磷酸钠 |
用量 | 78% | 6% | 9% | 6.4% | 0.2% | 0.4% |
原料 | 四会原矿泥 | 新会泥 | 江西滑石 | 中山石粉 |
用量 | 19% | 6% | 3% | 9% |
原料 | 莲塘中温砂 | 新丰砂 | 台山中温砂 | 抛光渣 |
用量 | 5% | 9% | 9% | 40% |
原料 | 台山中温砂 | 新丰砂 | 莫村中温砂 | 四会泥 | 广西藤县砂 |
用量 | 12% | 8% | 6% | 17% | 11% |
原料 | 新会泥 | 广四砂 | 莲塘中温砂 | 中山砂 | 滑石泥 |
用量 | 2% | 7% | 9% | 6% | 1% |
原料 | 北海石粉 | 减水剂 | 改性羧甲基纤维素钠 | 碳化硅 | 二氧化锰 |
用量 | 20% | 0.5% | 0.15% | 0.2% | 0.15% |
原料 | 锆白不透水熔块 | 球土 | 硅酸锆 | 氧化铝 | 羧甲基纤维素钠 | 三聚磷酸钠 |
用量 | 80% | 4% | 11.4% | 4% | 0.3% | 0.3% |
原料 | 锆白不透水熔块 | 球土 | 硅酸锆 | 氧化铝 | 羧甲基纤维素钠 | 三聚磷酸钠 |
用量 | 79.4% | 5% | 10% | 5% | 0.25% | 0.35% |
原料 | 锆白不透水熔块 | 球土 | 硅酸锆 | 氧化铝 | 羧甲基纤维素钠 | 三聚磷酸钠 |
用量 | 78% | 6% | 9% | 6.4% | 0.2% | 0.4% |
原料 | 四会原矿泥 | 新会泥 | 江西滑石 | 中山石粉 |
用量 | 19% | 6% | 3% | 9% |
原料 | 莲塘中温砂 | 新丰砂 | 台山中温砂 | 抛光渣 |
用量 | 4% | 7% | 7% | 45% |
原料 | 四会原矿泥 | 新会泥 | 江西滑石 | 中山石粉 |
用量 | 19% | 6% | 3% | 9% |
原料 | 莲塘中温砂 | 新丰砂 | 台山中温砂 | 抛光渣 |
用量 | 3% | 5% | 5% | 50% |
Claims (10)