CN108382013A - 一种用于清洁卫生用品的银纤维无纺布 - Google Patents

一种用于清洁卫生用品的银纤维无纺布 Download PDF

Info

Publication number
CN108382013A
CN108382013A CN201711497018.7A CN201711497018A CN108382013A CN 108382013 A CN108382013 A CN 108382013A CN 201711497018 A CN201711497018 A CN 201711497018A CN 108382013 A CN108382013 A CN 108382013A
Authority
CN
China
Prior art keywords
content
silver
woven fabrics
fiber
sanitary product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711497018.7A
Other languages
English (en)
Inventor
朱红军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Haixin Nonwoven Industry Co Ltd
Original Assignee
Guangzhou Haixin Nonwoven Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Haixin Nonwoven Industry Co Ltd filed Critical Guangzhou Haixin Nonwoven Industry Co Ltd
Priority to CN201711497018.7A priority Critical patent/CN108382013A/zh
Publication of CN108382013A publication Critical patent/CN108382013A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于清洁卫生用品的银纤维无纺布，该银纤维无纺布包括基层和底层，所述基层是由含量为40‑50wt％的麻纤维，含量为25‑35wt％的银纤维，含量为5‑10wt％的矿石纤维以及含量为2‑10wt％的竹纤维组成，所述底层是由棉纤维和玻璃纤维组成，在玻璃纤维中添加高分子吸水树脂。本发明得到的一种用于清洁卫生用品的银纤维无纺布，通过设置银纤维使其具有很好的抗菌能力，同时底层包含玻璃纤维，使得其绝缘性好、耐热性强、抗腐蚀性好，最终更适合对卫生用品的长时间清洁，提高使用寿命。

Description

一种用于清洁卫生用品的银纤维无纺布
技术领域
本发明涉及一种无纺布的技术领域，特别是涉及到一种用于清洁卫生用品的银纤维无纺布。
背景技术
无纺布(英文名:Non Woven Fabric或者Nonwoven cloth)又称不织布，是由定向的或随机的纤维而构成，是新一代环保材料，因具有布的外观和某些性能而称其为布，无纺布具有防潮、透气、柔韧、质轻、不助燃、容易分解、无毒无刺激性、色彩丰富、价格低廉、可循环再用等特点。无纺布是一种非织造布，它是直接利用高聚物切片、短纤维或长丝将纤维通过气流或机械成网，然后经过水刺，针刺，或热轧加固，最后经过后整理形成的无编织的布料。具有柔软、透气和平面结构的新型纤维制品，优点是不产生纤维屑，强韧、耐用、丝般柔软，也是增强材料的一种，而且还有棉质的感觉，和棉织品相比，无纺布的袋子容易成形，而且造价便宜，被广泛的应用到很多地方，例如帽子、手套以及最常见的用于清洗卫生用品的无纺布，但是目前用于清洗卫生用品的无纺布长时间使用后容易滋生细菌，导致抗菌效果差，同时透气性差，最终导致使用寿命低，因此需要改进。
发明内容
本发明的目的是为了解决上述现有技术的不足而提供一种能够抗菌、透气，抗腐蚀、使用寿命长的一种用于清洁卫生用品的银纤维无纺布。
为了实现上述目的，本发明所设计的一种用于清洁卫生用品的银纤维无纺布，该银纤维无纺布包括基层和底层，所述基层是由含量为40-50wt％的麻纤维，含量为25-35wt％的银纤维，含量为5-10wt％的矿石纤维以及含量为2-10wt％的竹纤维组成，所述底层是由棉纤维和玻璃纤维组成，在玻璃纤维中添加高分子吸水树脂。
作为优选，所述棉纤维在底层中所占重量百分比为70％～80％，剩余为玻璃纤维。
作为优选，在底层的表面涂覆有一层微生物隔离层，所述微生物隔离层是内部包含有活性陶瓷粉末、抗静电剂、银粉的抗菌涂料。
作为优选，所述抗菌涂料中的成分通过明胶液混合。
作为优选，所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：20-30％的活性陶瓷粉末；10-20％抗静电剂；15-20％银粉，剩余含量为明胶液。
作为优选，所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：25％的活性陶瓷粉末；15％抗静电剂；18％银粉，剩余42％含量的明胶液。
作为优选，所述棉纤维在底层中所占重量百分比为75％，剩余25％的玻璃纤维。
本发明得到的一种用于清洁卫生用品的银纤维无纺布，通过设置银纤维使其具有很好的抗菌能力，同时底层包含玻璃纤维，使得其绝缘性好、耐热性强、抗腐蚀性好，最终更适合对卫生用品的长时间清洁，提高使用寿命。
附图说明
图1是本实施例1中所提供一种用于清洁卫生用品的银纤维无纺布的结构示意图。
附图标记中：1.基层；2.底层。
具体实施方式
下面结合附图和实施例对本发明进一步说明。
实施例1：
如图1所示，本实施例中所提供的一种用于清洁卫生用品的银纤维无纺布，该银纤维无纺布包括基层1和底层2，所述基层1是由含量为40-50wt％的麻纤维，含量为25-35wt％的银纤维，含量为5-10wt％的矿石纤维以及含量为2-10wt％的竹纤维组成，所述底层2是由棉纤维和玻璃纤维组成，在玻璃纤维中添加高分子吸水树脂。在本实施中所述基层1是由含量为40wt％的麻纤维，含量为25wt％的银纤维，含量为5wt％的矿石纤维以及含量为2wt％的竹纤维组成。
作为优选，所述棉纤维在底层2中所占重量百分比为70％～80％，剩余为玻璃纤维，在本实施例中所述棉纤维在底层2中所占重量百分比为70％，剩余30％为玻璃纤维。
本实施例得到的一种用于清洁卫生用品的银纤维无纺布，通过设置银纤维使其具有很好的抗菌能力，同时底层2包含玻璃纤维，使得其绝缘性好、耐热性强、抗腐蚀性好，最终更适合对卫生用品的长时间清洁，提高使用寿命。
实施例2：
本实施例中所提供的一种用于清洁卫生用品的银纤维无纺布，该银纤维无纺布包括基层1和底层2，所述基层1是由含量为40-50wt％的麻纤维，含量为25-35wt％的银纤维，含量为5-10wt％的矿石纤维以及含量为2-10wt％的竹纤维组成，所述底层2是由棉纤维和玻璃纤维组成，在玻璃纤维中添加高分子吸水树脂，在本实施中所述基层1是由含量为50wt％的麻纤维，含量为35wt％的银纤维，含量为10wt％的矿石纤维以及含量为10wt％的竹纤维组成。
作为优选，所述棉纤维在底层2中所占重量百分比为70％～80％，剩余为玻璃纤维。在本实施例中所述棉纤维在底层2中所占重量百分比为80％，剩余20％为玻璃纤维。
实施例3：
本实施例中所提供的一种用于清洁卫生用品的银纤维无纺布，该银纤维无纺布包括基层1和底层2，所述基层1是由含量为40-50wt％的麻纤维，含量为25-35wt％的银纤维，含量为5-10wt％的矿石纤维以及含量为2-10wt％的竹纤维组成，所述底层2是由棉纤维和玻璃纤维组成，在玻璃纤维中添加高分子吸水树脂。在本实施中所述基层1是由含量为45wt％的麻纤维，含量为30wt％的银纤维，含量为8wt％的矿石纤维以及含量为7wt％的竹纤维组成
作为优选，所述棉纤维在底层2中所占重量百分比为70％～80％，剩余为玻璃纤维。在本实施例中所述棉纤维在底层2中所占重量百分比为75％，剩余25％为玻璃纤维。
作为优选，在底层2的表面涂覆有一层微生物隔离层，所述微生物隔离层是内部包含有活性陶瓷粉末、抗静电剂、银粉的抗菌涂料。
作为优选，所述抗菌涂料中的成分通过明胶液混合。
作为优选，所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：20-30％的活性陶瓷粉末；10-20％抗静电剂；15-20％银粉，剩余含量为明胶液。
作为优选，所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：25％的活性陶瓷粉末；15％抗静电剂；18％银粉，剩余42％含量的明胶液。
作为优选，所述棉纤维在底层2中所占重量百分比为75％，剩余25％的玻璃纤维。
实施例4：
本实施例中所提供的一种用于清洁卫生用品的银纤维无纺布，该银纤维无纺布包括基层1和底层2，所述基层1是由含量为42wt％的麻纤维，含量为30wt％的银纤维，含量为7wt％的矿石纤维以及含量为9wt％的竹纤维组成，所述底层2是由棉纤维和玻璃纤维组成，在玻璃纤维中添加高分子吸水树脂。
作为优选，所述棉纤维在底层2中所占重量百分比为78％，剩余为22％的玻璃纤维。
作为优选，在底层2的表面涂覆有一层微生物隔离层，所述微生物隔离层是内部包含有活性陶瓷粉末、抗静电剂、银粉的抗菌涂料。
作为优选，所述抗菌涂料中的成分通过明胶液混合。
作为优选，所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：20-30％的活性陶瓷粉末；10-20％抗静电剂；15-20％银粉，剩余含量为明胶液，在本实施例中所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：20％的活性陶瓷粉末；10％抗静电剂；15％银粉，剩余含量为明胶液。
实施例5：
本实施例中所提供的一种用于清洁卫生用品的银纤维无纺布，该银纤维无纺布包括基层1和底层2，所述基层1是由含量为48wt％的麻纤维，含量为32wt％的银纤维，含量为8wt％的矿石纤维以及含量为6wt％的竹纤维组成，所述底层2是由棉纤维和玻璃纤维组成，在玻璃纤维中添加高分子吸水树脂。
作为优选，所述棉纤维在底层2中所占重量百分比为79％，剩余为21％的玻璃纤维。
作为优选，在底层2的表面涂覆有一层微生物隔离层，所述微生物隔离层是内部包含有活性陶瓷粉末、抗静电剂、银粉的抗菌涂料。
作为优选，所述抗菌涂料中的成分通过明胶液混合。
作为优选，所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：30％的活性陶瓷粉末；20％抗静电剂；20％银粉，剩余含量为明胶液。

Claims (7)

1.一种用于清洁卫生用品的银纤维无纺布，其特征在于：该银纤维无纺布包括基层(1)和底层(2)，所述基层(1)是由含量为40-50wt％的麻纤维，含量为25-35wt％的银纤维，含量为5-10wt％的矿石纤维以及含量为2-10wt％的竹纤维组成，所述底层(2)是由棉纤维和玻璃纤维组成，在玻璃纤维中添加高分子吸水树脂。
2.根据权利要求1所述的一种用于清洁卫生用品的银纤维无纺布，其特征在于：所述棉纤维在底层(2)中所占重量百分比为70％～80％，剩余为玻璃纤维。
3.根据权利要求1或2所述的一种用于清洁卫生用品的银纤维无纺布，其特征在于：在底层(2)的表面涂覆有一层微生物隔离层，所述微生物隔离层是内部包含有活性陶瓷粉末、抗静电剂、银粉的抗菌涂料。
4.根据权利要求3所述的一种用于清洁卫生用品的银纤维无纺布，其特征在于：所述抗菌涂料中的成分通过明胶液混合。
5.根据权利要求3所述的一种用于清洁卫生用品的银纤维无纺布，其特征在于：所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：20-30％的活性陶瓷粉末；10-20％抗静电剂；15-20％银粉，剩余含量为明胶液。
6.根据权利要求4所述的一种用于清洁卫生用品的银纤维无纺布，其特征在于：所述抗菌涂料中活性陶瓷粉末、抗静电剂、银粉的重量百分比分别是：25％的活性陶瓷粉末；15％抗静电剂；18％银粉，剩余42％含量的明胶液。
7.根据权利要求2所述的一种用于清洁卫生用品的银纤维无纺布，其特征在于：所述棉纤维在底层(2)中所占重量百分比为75％，剩余25％的玻璃纤维。
CN201711497018.7A 2017-12-31 2017-12-31 一种用于清洁卫生用品的银纤维无纺布 Pending CN108382013A (zh)