CN108373876A - A kind of elastic outer wall paint and preparation method thereof - Google Patents

A kind of elastic outer wall paint and preparation method thereof Download PDF

Info

Publication number
CN108373876A
CN108373876A CN201610963599.8A CN201610963599A CN108373876A CN 108373876 A CN108373876 A CN 108373876A CN 201610963599 A CN201610963599 A CN 201610963599A CN 108373876 A CN108373876 A CN 108373876A
Authority
CN
China
Prior art keywords
wall paint
elastic outer
agent
antifoaming agent
elastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610963599.8A
Other languages
Chinese (zh)
Inventor
罗攀登
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guizhou Paint Jinzhou Paint Co Ltd
Original Assignee
Guizhou Paint Jinzhou Paint Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guizhou Paint Jinzhou Paint Co Ltd filed Critical Guizhou Paint Jinzhou Paint Co Ltd
Priority to CN201610963599.8A priority Critical patent/CN108373876A/en
Publication of CN108373876A publication Critical patent/CN108373876A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of elastic outer wall paint and preparation method thereof, Parts by Ingredients ratio is：Water 175 185, multifunctional assistant 1.4 1.6, antifoaming agent 1.4 1.6, ethylene glycol 13 17, dispersant 3.5 4.5, wetting agent 1.8 2.2, titanium white 195 205, calcined kaolin 48 52, coarse whiting 146 154, coalescents 7.5 8.5, preservative 1.4 1.6, thickener 4.5 5.5, elastic emulsion 380 420, adhesive 96 104, levelling agent 2.8 3.2 and antifoaming agent 1.4 1.6, are prepared by the above ingredient.The control of titanium white and lotion and its proportioning is added in the present invention so that there is elastic outer wall paint obtained more preferable flexibility and Resisting fractre intensity, viscosity can reach KU 95 105, viscosity is good and pollution-free, makes simple, ageing resistance is good, holding color is lasting, high covering power, and anti-solarization function is strong, water repelling property is good, speed of agitator and time, material can be allowed preferably to merge and being mutually twisted property of weighing area is more preferable, and lacquer painting is more preferable good smooth, enhances resistance to soiling.

Description

A kind of elastic outer wall paint and preparation method thereof
Technical field
The present invention relates to a kind of elastic outer wall paints and preparation method thereof, belong to decorative materials technology.
Background technology
Exterior wall paint is mainly used in building, has two kinds of functions：First, protecting building from external environment influence Or influenced to minimize, exterior wall paint can be formed on its surface continuous film, this film after being applied on building Have the effects that corrosion-resistant, anti-pollution, UV resistant irradiation, protects reinforcing bar not perishable, protect concrete not easy-weathering, chlorine Change, to extend the service life of building；Second is that decoration building, exterior wall paint, which is painted on after building surface to be formed, to be had The film of different colours, various luster and different texture, to play the role of beautifying the environment.
As one of China's chemical building material industry high performance outer wall paint, F-C paint is with the weatherability of its overlength, excellent The many merits such as the decorative effect of corrosion resistance, good self-cleaning and top grade, just increasingly by more and more exterior wall application works Journey is used.
External Thermal Insulation Technology for External promotes and applies in China also only has the 4-5 years, solvent of constructing in External Wall heat insulation base layer For type fluorocarbon exterior wall paint system, such system is by insulating layer, anti-cracking plastering putty layer (rear abbreviation putty layer), dope layer etc. Three system levels collectively form.The function of wherein insulating layer is heat preservation energy-saving；The function of putty layer be the protection of levelling, cracking resistance and Assistance modeling；The function of dope layer is decoration protection.Three system levels are realized jointly imitates the heat preservation of building, protection and decoration Fruit.
Exterior wall paint filler material complexity now on the market is various, and material is unstable, emulsion paint film-formation result and coloring force difference, It fades after time 1-2, floating, decortication, and also existing exterior wall paint flexibility difference and Resisting fractre intensity are small.
Invention content
The technical problem to be solved by the present invention is to：A kind of elastic outer wall paint and preparation method thereof is provided, is had more preferable flexible Property and Resisting fractre intensity, pollution-free, film-formation result and tinting strength, tinting power number, retention time are lasting, and not floating and decortication are existing to solve The problem of technology.
The technical solution that the present invention takes is：A kind of elastic outer wall paint, Parts by Ingredients ratio are：Water 175-185 is more Function additive 1.4-1.6, antifoaming agent 1.4-1.6, ethylene glycol 13-17, dispersant 3.5-4.5, wetting agent 1.8-2.2, titanium white 195-205, calcined kaolin 48-52, coarse whiting 146-154, coalescents 7.5-8.5, preservative 1.4-1.6, thickener 4.5- 5.5, elastic emulsion 380-420, adhesive 96-104, levelling agent 2.8-3.2 and antifoaming agent 1.4-1.6, are prepared by the above ingredient It forms.
A kind of elastic outer wall paint and preparation method thereof, this approach includes the following steps：
（1）Paint making apparatus is cleaned out；
（2）The water of proportioning is added in blender, multifunctional assistant, antifoaming agent, ethylene glycol, dispersant, wetting agent, titanium white, forges Kaolin, coarse whiting and coalescents are burnt, are stirred 45 minutes, rotating speed 250r/min；
（3）Step（2）Middle mixture is dispersed to fineness<When 50UM, the preservative that proportioning is added stirs 15 minutes, and rotating speed is 200r/min, then the thickener, elastic emulsion, adhesive, levelling agent and the antifoaming agent that match stir 10-15 minutes, and rotating speed is Elastic outer wall paint is made in 280r/min；
（4）Detect elastic outer wall paint performance.
The heat-resisting property of elastic outer wall paint produced by the present invention can reach 30 DEG C, and fineness can reach 1250 mesh, pH value 7-8, viscosity KU 95-105, proportion（kg/1）1:1.2.
Beneficial effects of the present invention：Compared with prior art, the control of titanium white and lotion and its proportioning is added in the present invention, makes Obtaining elastic outer wall paint obtained, there is more preferable flexibility and Resisting fractre intensity, viscosity can reach KU 95-105, and viscosity is good, system Make simple, ageing resistance is good, keeps color lasting, and high covering power, anti-solarization function is strong, and water repelling property is good, speed of agitator and when Between material can be allowed preferably to merge and being mutually twisted property of weighing area is more preferable, lacquer painting is more preferable good smooth, enhances resistance to soiling, titanium white and breast The control of liquid and thickener also can allow storage time longer, not precipitate, and color dot is clear, not colour mixture, spraying effect.
Specific implementation mode
The present invention is described further with reference to specific embodiment.
Embodiment 1：A kind of elastic outer wall paint, Parts by Ingredients ratio are：Water 180kg, multifunctional assistant 1.5kg, disappears Infusion 1.5kg, ethylene glycol 15kg, dispersant 4kg, wetting agent 2kg, titanium white 200kg, 50 kg of calcined kaolin, coarse whiting 150 Kg, coalescents 8kg, preservative 1.5kg, thickener 5kg, elastic emulsion 400kg, adhesive 100kg, levelling agent 3kg and disappear Infusion 1.5kg, preparation method includes the following steps：
（1）Paint making apparatus is cleaned out；
（2）The water of proportioning is added in blender, multifunctional assistant, antifoaming agent, ethylene glycol, dispersant, wetting agent, titanium white, forges Kaolin, coarse whiting and coalescents are burnt, are stirred 45 minutes, rotating speed 250r/min；
（3）Step（2）Middle mixture is dispersed to fineness<When 50UM, the preservative that proportioning is added stirs 15 minutes, and rotating speed is 200r/min, then the thickener, elastic emulsion, adhesive, levelling agent and the antifoaming agent that match stir 10-15 minutes, and rotating speed is Elastic outer wall paint is made in 280r/min；
（4）Detect elastic outer wall paint performance.
Embodiment 2：A kind of elastic outer wall paint, Parts by Ingredients ratio are：Water 175kg, multifunctional assistant 1.4kg, disappears Infusion 1.4kg, ethylene glycol 13kg, dispersant 3.5kg, wetting agent 1.8kg, titanium white 195kg, calcined kaolin 48kg, coarse whiting 146kg, coalescents 7.5kg, preservative 1.4kg, thickener 4.5kg, elastic emulsion 380kg, adhesive 96kg, levelling agent 2.8kg and antifoaming agent 1.4kg, preparation method includes the following steps：
（1）Paint making apparatus is cleaned out；
（2）The water of proportioning is added in blender, multifunctional assistant, antifoaming agent, ethylene glycol, dispersant, wetting agent, titanium white, forges Kaolin, coarse whiting and coalescents are burnt, are stirred 45 minutes, rotating speed 250r/min；
（3）Step（2）Middle mixture is dispersed to fineness<When 50UM, the preservative that proportioning is added stirs 15 minutes, and rotating speed is 200r/min, then the thickener, elastic emulsion, adhesive, levelling agent and the antifoaming agent that match stir 10-15 minutes, and rotating speed is Elastic outer wall paint is made in 280r/min；
（4）Detect elastic outer wall paint performance.
Embodiment 3：A kind of elastic outer wall paint, Parts by Ingredients ratio are：Water 185kg, 1.6 kg of multifunctional assistant, disappears Infusion 1.6kg, ethylene glycol 17kg, dispersant 4.5kg, 2.2 kg of wetting agent, 205 kg of titanium white, 52 kg of calcined kaolin, weight 154 kg of calcium, 8.5 kg of coalescents, 1.6 kg of preservative, 5.5 kg of thickener, 420 kg of elastic emulsion, adhesive 104 Kg, levelling agent 3.2kg and antifoaming agent 1.6kg, preparation method includes the following steps：
（1）Paint making apparatus is cleaned out；
（2）The water of proportioning is added in blender, multifunctional assistant, antifoaming agent, ethylene glycol, dispersant, wetting agent, titanium white, forges Kaolin, coarse whiting and coalescents are burnt, are stirred 45 minutes, rotating speed 250r/min；
（3）Step（2）Middle mixture is dispersed to fineness<When 50UM, the preservative that proportioning is added stirs 15 minutes, and rotating speed is 200r/min, then the thickener, elastic emulsion, adhesive, levelling agent and the antifoaming agent that match stir 10-15 minutes, and rotating speed is Elastic outer wall paint is made in 280r/min；
（4）Detect elastic outer wall paint performance.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any Those familiar with the art in the technical scope disclosed by the present invention, can easily think of the change or the replacement, and should all contain Within protection scope of the present invention, therefore, protection scope of the present invention should be based on the protection scope of the described claims lid.

Claims (2)

1. a kind of elastic outer wall paint, it is characterised in that：Its Parts by Ingredients ratio is：Water 175-185, multifunctional assistant 1.4- 1.6, antifoaming agent 1.4-1.6, ethylene glycol 13-17, dispersant 3.5-4.5, wetting agent 1.8-2.2, titanium white 195-205, calcining are high Ridge soil 48-52, coarse whiting 146-154, coalescents 7.5-8.5, preservative 1.4-1.6, thickener 4.5-5.5, elastic emulsion 380-420, adhesive 96-104, levelling agent 2.8-3.2 and antifoaming agent 1.4-1.6, are prepared by the above ingredient.
2. a kind of elastic outer wall paint according to claim 1 and preparation method thereof, it is characterised in that：This method includes following Step：
（1）Paint making apparatus is cleaned out；
（2）The water of proportioning is added in blender, multifunctional assistant, antifoaming agent, ethylene glycol, dispersant, wetting agent, titanium white, forges Kaolin, coarse whiting and coalescents are burnt, are stirred 45 minutes, rotating speed 250r/min；
（3）Step（2）Middle mixture is dispersed to fineness<When 50UM, the preservative that proportioning is added stirs 15 minutes, and rotating speed is 200r/min, then the thickener, elastic emulsion, adhesive, levelling agent and the antifoaming agent that match stir 10-15 minutes, and rotating speed is Elastic outer wall paint is made in 280r/min；
（4）Detect elastic outer wall paint performance.
CN201610963599.8A 2016-10-28 2016-10-28 A kind of elastic outer wall paint and preparation method thereof Pending CN108373876A (en)