CN108342818A - A kind of cotton feeling knitted fabric - Google Patents
A kind of cotton feeling knitted fabric Download PDFInfo
- Publication number
- CN108342818A CN108342818A CN201710055956.5A CN201710055956A CN108342818A CN 108342818 A CN108342818 A CN 108342818A CN 201710055956 A CN201710055956 A CN 201710055956A CN 108342818 A CN108342818 A CN 108342818A
- Authority
- CN
- China
- Prior art keywords
- cotton
- false twist
- knitted fabric
- fabric
- twist yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of cotton feeling knitted fabrics.The knitting fabric is to be formed by weft-knitted fabric, and at least dyeing portion A and dyeing portion B with different in size, different tones or different brightness on fabric by mixed fine false twist yarn；Wherein mixed fine false twist yarn is combined by the cation-dyeable polyester long filament and disperse dye dyeable polyester filament, to melt rate be 1~40% for it.The knitting fabric of the present invention has very strong cotton feel, and has good water imbibition, and brindled sense is presented in cloth cover, is suitable for making T-shirt and gym suit etc..
Description
Technical field
The present invention relates to a kind of cotton feeling knitted fabrics, and in particular to a kind of surface has marbled effect and water-absorbing fast-drying is excellent
Cotton feeling knitted fabric more.
Background technology
Pure cotton Product softness pro-skin is widely used in underwear, movement T-shirt etc., but actually there is also easily rise
The problems such as wrinkle, deformation, especially movement are easy viscous glutinous skin after perspiring, snugness of fit is poor；Cotton price in recent years simultaneously
Unprecedentedly soaring, most textile enterprise are considered as such as terylene synthetic fibers to replace cotton yarn to reduce production cost.Synthesis
The anti-cotton face fabric of fiber-like, mainly based on terylene short fiber yarn and terylene air-texturing processing yarn.
As disclosed a kind of imitative cotton knitted fabric in patent document CN201210569158.1, spun yarn, polyester-cotton blend are washed by pure
Spun yarn and spandex weave, then are obtained by the low alkali processing of high temperature and imitate cotton effect, but the filoplume of spun yarn is more, moisture
Fiber ends can not be reached, capillary effect is restricted, and water-absorbing fast-drying still needs to further improve, and table yarn is terylene
Abundant brindled sense is not present in spun yarn, cloth cover.
A kind of low-denier cotton-feeling filament yarn is for another example disclosed in patent document CN201310343075.5, warp thread, weft yarn are equal
For low denier polyamide fibre ATY, and solves the problems, such as fine-denier through weaving yarns difficulty, compared to spun yarn by specific weaving technology
Class product water-absorbing fast-drying is improved；But woven fabric cloth cover is fine and close, and movement extensibility is not as good as knitted fabric, and the surfaces ATY
Cortex there is silk arc and wire ring, will appear that hook silk bad when applied in terms of knitted fabric, in addition, ATY processing energy consumptions are also larger.
Invention content
In view of the above problems, the purpose of the present invention is to provide one kind having good water-absorbing fast-drying, good hook silk performance
And the cotton feeling knitted fabric of marbled effect.
Technical solution of the invention：
The cotton feeling knitted fabric of the present invention to be formed by weft-knitted fabric by mixed fine false twist yarn, and at least has on fabric
There are different in size, different tones or the dyeing portion A and dyeing portion B of different brightness；Wherein mixed fine false twist yarn by sun from
Sub- dye capable of dyeing polyester filament and disperse dye dyeable polyester filament are combined, its melt rate be 1~40%.
The disordered arrangements of long filament after the present invention is processed using the different dyeabilities and mixed fine false twisting of fibrous raw material, in fabric
Broadwise on obtain the dyeing portion of different tones or different brightness, and the length in these dyeing portions is random.This
The cotton feeling knitted fabric of invention not only has the appearance and feel of similar cotton product, and has good water-absorbing fast-drying, fits
It shares in making T-shirt and gym suit etc..
Description of the drawings
Fig. 1 is the section SEM descriptions of the mixed fine false twist yarn of the present invention（150 times）.
Specific implementation mode
The knitting fabric of the present invention to be formed by weft-knitted fabric by mixed fine false twist yarn, and at least has length on fabric
It is short differ, the dyeing portion A and dyeing portion B of different tone or different brightness；Wherein mixed fine false twist yarn is contaminated by cation
Material can contaminate polyester filament（Hereinafter referred to as CDP）With disperse dye dyeable polyester filament（Hereinafter referred to as common PET）It is combined, it
It is 1~40% to melt rate.
The cotton feeling knitted fabric of the present invention, at least with different in size, different tones or different brightness on cloth cover
Dyeing portion A and dyeing portion B assigns marbled effect of the fabric similar to cotton product by the presence of dyeing portion A and dyeing portion B.
The mixed fine false twist yarn of the present invention, destroys the row being mutually parallel between original long filament by false twist texturing processing first
Column-shaped state, in conjunction with the polyester filament using different colourabilitys as fibrous raw material, the more conventional stretch textured yarn of structure is more not
Uniformly, there is from microcosmic thickness section in the longitudinal direction, increase the diffusing reflection of web surface, thus obtain similar
The appearance of cotton product.
The rate of melting refers in the present invention, on mixed fibre false twist yarn section there is the radical for the single fiber for melting state to account for
The ratio of total radical.Melting rate, fibre false twist yarn is excessively smooth less than if 1%, mixing, the diffusing reflection of web surface seldom, light
Pool sense is too strong, there is apparent chemical fibre style；Melt rate higher than if 40%, mix fibre false twist yarn it is microcosmic on thickness section phenomenon
Excessively apparent, feel is not fine and smooth, and melts portion（Details）Height is spent due to melting, yarn rigidity is bigger, the pelvic bone of fabric
Sense is partially strong, therefore the rate of melting that fibre false twist yarn is mixed in the present invention is 1~40%.
If, may by its cloth cover brindled sense obtained if CDP contents are less than 30 weight % in mixed fibre false twist yarn
It can reduce, cotton sense weakens；And if its content is higher than 70 weight %, cloth cover will appear the tone of more CDP after dyeing, speckle
Length is long, the effect of similar crosspiece occurs, and natural brindled sense has a declining tendency.It is preferable therefore that mixed fibre false twist yarn
The content of middle CDP is 30~70 weight %, the content of common PET is 70~30 weight %.
In the present invention, in order to ensure fabric similar cotton product natural brindled sense and feel, preferably mixed fine false twisting adds
The rate of melting of work silk is 3~35%.
In the present invention, the common PET-POY for being preferably 100%~300% by elongation at break enters after hot plate heats
Navel carries out false twisting, and the CDP-DTY for being then 30%~50% with elongation at break merges, and interlacing, institute are carried out into winding apparatus
It states hot plate and is heated to be contact heating, preferably 210~250 DEG C of heating temperature.If heating temperature is too low, it is possible to lead to mixed fibre
False twist yarn to melt rate too low, there is stronger reflecting feel and apparent chemical fibre style；And if heating temperature is too high, again
Be likely to result in mixed fine false twist yarn melts that rate is too high, the phenomenon that rigidity is bigger than normal, feel is not fine and smooth occurs.Gained is mixed fine false
It is to melt state, or it is to melt that the only described dispersion, which can contaminate polyester filament, to twist the only described the CDP fabrics long filament in processed filament
State.Obtain mixed fine false twist yarn, this mode is rear inserted mode, and only CDP fibers are to melt in the mixed fine false twist yarn of gained
State, or only common PET fiber is to melt state, structure is parallel type, melts rate between 3~35%, reflecting feel is more
Close to cotton product；And the speckle on fabric has with short, dyeing portion A, dyeing portion B length between 0.5~80.0mm,
It randomly mixes, brindled sense is more natural.
In the present invention, preferably by CDP-POY and elongation at break that elongation at break is 100%~300% be 100%~
After 300% common PET-POY merges, navel progress false twisting is entered after hot plate heats, the hot plate is heated to be non-contact
Formula heats, preferably 370~460 DEG C of heating temperature.If heating temperature is too low, it is possible to lead to melting for mixed fine false twist yarn
Rate is too low, stronger reflecting feel and apparent chemical fibre style occurs；And if heating temperature is too high, and be likely to result in mixed fine false
That twists processed filament melts that rate is too high, the phenomenon that rigidity is bigger than normal, feel is not fine and smooth occurs.Cation in the mixed fine false twist yarn of gained
Polyester filament and dispersion, which can be contaminated, can contaminate polyester filament while to melt state.The mixed fine false twist yarn of gained be parallel type structure or
Core-sheath structure, CDP therein and common PET have simultaneously melts state, and two kinds of POY long filaments are uniformly mixed, yarn section hair
First portion melts, and melts rate between 15~25%, and reflecting feel is relatively low, and feel is closer to cotton.Come compared to inserted mode after preceding note
It says, dyeing portion A, the speckle length of dyeing portion B are shorter, while a large amount of dyeing portion C occur, and the length in each dyeing portion is 0.5
Between~50.0 mm, fabric goniochromatic effect can be assigned, brindled sense is more natural.
In the present invention, preferred fabric（Surface）Broadwise on there are length be 0.5~80.0mm striped.Strip length is super
If crossing 80.0mm, the brindled sense that cloth cover is presented may be more dull, manual, may also have similar cloth cover crosspiece sometimes
Appearance, lack natural sense.
In the present invention, the total fiber number of fibre false twist yarn is mixed less than if 100dtex, is made on the volume machine of same needle number
Fabric densification sense and thickness have a declining tendency, it is difficult to obtain the bony and solid sense of similar cotton product；And total fiber number is more than
If 300dtex, densification sense and thickness are excessive, and imitative cotton effect has a declining tendency.It is therefore preferable that mixed fibre false twist yarn is total
Fiber number is 100~300dtex.
In the present invention, if the filament number of mixed fine false twist yarn is more than 1.1dtex, it is possible to fabric can be influenced
Fine and smooth feel；And in order to obtain the soft feeling of similar cotton product, filament number is the smaller the better, but if filament number is less than
If 0.5dtex, feel is soft glutinous, and the pelvic bone sense of fabric has a declining tendency, therefore filament number is preferably 0.5~1.1dtex.
In the present invention, there are dyeing portion C between preferably dyeing portion A and dyeing portion B, and the long filament of mutual interlacing can be because of color
The overlapping of tune is mixed to form new tone, and cloth cover will present more natural brindled sense appearance.
The cotton feeling knitted fabric of the present invention is fluffing product, and the feel after fluffing is closer to cotton product, fluffing processing institute
Equipment is not particularly limited, and can be used Italian Sperotto rubbers roughing-up machine, and 5~30m/min of speed, tension 0.4~
0.6MPa, 160~240# of rubber mesh number.
The cotton feeling knitted fabric of the present invention, braiding tissue are not particularly limited, organize plain stitch or pearl may be used
Deng, it is preferred to use plain stitch.
The test method of involved each parameter is as follows in the present invention：
（1）Melt rate
1. along the broadwise of fabric, 5 pieces of the sample cloth of 1cm × 0.5cm sizes is arbitrarily intercepted；
2. sample cloth is placed on electronic scanner microscope（SEM）Lower progress section photographic analysis；
3. the radical for melting the single fiber under state observed under 150 multiplying powers and total fiber radical are recorded, further according under
Formula, which calculates, mixes fibre false twist yarn on monolithic sample cloth and melts rate,
Melt the total fiber radical of single fiber radical/single processed filament of rate (%)=melt state；
4. continuing to observe remaining 4 pieces, and calculate the average value of 5 pieces of sample cloth.
（2）Barre length
1. observing under the microscope, dyeing portion A, the dyeing portion of 30 different tones or different gradations are randomly selected from fabric
B, dyeing portion C；
2. being measured to the length of the dyeing portion A of selection, the length of the length and most short part of longest part is measured；
3. then measuring the length of its longest part and most short part respectively using same method to other dyeing portion B, C
Length；
The broadwise item of fabric is judged with extreme length, the shortest length of above-mentioned dyeing portion A, the dyeing portion B measured and dyeing portion C
Line length.
（3）Brindled sense
10 people of this field experience person judges fabric appearance, thinks that brindled sense is abundant and day then sentences more than or equal to 8 people
It is set to zero, brindled sense is thought more than or equal to 8 people, and some dullnesses are then determined as △, think that brindled sense is very single more than or equal to 8 people
It adjusts and manual, be determined as ×.
（4）Imitative cotton feel
20 people of non-experience person carries out sensory evaluation to fabric, it is believed that imitative cotton good hand touch number be greater than or equal to 15 people then and be it is excellent, 10
It is then poor that~14 people, which are then during good, 5~9 people are then, less than 5 people,.
With reference to Examples and Comparative Examples, the invention will be further described.
Embodiment 1
On 28 needle one-side circular knitting machines, the 210dtex-288f parallel types that 100% selection back insertion type obtains mix fine false twist yarn
（It is 30%, CDP to melt rate：The content ratio of common PET is 52：48）, woven to obtain fabric using plain stitch, then into
Row refining（90 DEG C × 20 minutes）, CDP dyeing（120 DEG C × 30 minutes）, common PET dyeing（130 DEG C × 40 minutes）, finished product is fixed
Type（160 DEG C × 90 seconds）, fluffing processing obtain the present invention cotton feeling knitted fabric.
There is dyeing portion A different in size and dyeing portion B, brindled sense is abundant and natural, imitates cotton on the fabric cloth cover of gained
Feel is excellent.Each performance parameter is shown in Table 1.
Embodiment 2
Select the mixed fine false twist yarn of the parallel type for the 230dtex-288f that feed-type obtains simultaneously（It is 21%, CDP to melt rate：It is general
The content ratio of logical PET is 57：43）, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
There is dyeing portion A different in size, dyeing portion B and dyeing portion C, brindled sense enriches and day on the fabric cloth cover of gained
So, it is excellent to imitate cotton feel.Each performance parameter is shown in Table 1.
Embodiment 3
The mixed fine false twist yarn of parallel type for the 154dtex-144f that selection back insertion type obtains（It is 3%, CDP to melt rate：Commonly
The content ratio of PET is 55：45）, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
There is dyeing portion A different in size and dyeing portion B, brindled sense is abundant and natural, imitates cotton on the fabric cloth cover of gained
Feel is excellent.Each performance parameter is shown in Table 1.
Embodiment 4
Select the mixed fine false twist yarn of the core-sheath-type for the 170dtex-216f that feed-type obtains simultaneously（It is 15%, CDP to melt rate：It is general
The content ratio of logical PET is 41：59）, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
There is dyeing portion A different in size, dyeing portion B and dyeing portion C, brindled sense enriches and day on the fabric cloth cover of gained
So, it is excellent to imitate cotton feel.Each performance parameter is shown in Table 1.
Embodiment 5
The mixed fine false twist yarn of parallel type for the 153dtex-168f that selection back insertion type obtains（It is 5%, CDP to melt rate：Commonly
The content ratio of PET is 22：78）, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
The fabric of gained has length longer dyeing portion A and dyeing portion B, some are dull for brindled sense, and it is excellent to imitate cotton feel.Respectively
Performance parameter is shown in Table 1.
Embodiment 6
Select the mixed fine false twist yarn of the parallel type for the 165dtex-168f that feed-type obtains simultaneously（It is 25%, CDP to melt rate：It is general
The content ratio of logical PET is 80：20）, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
There are dyeing portion A different in size, dyeing portion B and dyeing portion C, some lists of brindled sense on the fabric cloth cover of gained
It adjusts, it is excellent to imitate cotton feel.Each performance parameter of gained fabric is shown in Table 1.
Embodiment 7
The mixed fine false twist yarn of parallel type for the 103dtex-180f that selection back insertion type obtains（It is 8%, CDP to melt rate：Commonly
The content ratio of PET is 32：68）, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
There is length longer dyeing portion A and dyeing portion B, brindled sense is abundant and natural, imitates cotton on the fabric cloth cover of gained
Feel is excellent.Each performance parameter of gained fabric is shown in Table 1.
Embodiment 8
Select the mixed fine false twist yarn of the core-sheath-type for the 299dtex-288f that feed-type obtains simultaneously（It is 20%, CDP to melt rate：It is general
The content ratio of logical PET is 44：56）, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
There is the longer dyeing portion A of length, dyeing portion B and dyeing portion C, brindled sense enriches and day on the fabric cloth cover of gained
So, it is excellent to imitate cotton feel.Each performance parameter is shown in Table 1.
Embodiment 9
The rate of melting of the mixed fine false twist yarn of parallel type used is 40%, remaining obtains the cotton sense knitting of the present invention with embodiment 3
Fabric.
There is dyeing portion A different in size and dyeing portion B, brindled sense is abundant and natural, imitates cotton on the fabric cloth cover of gained
Feel is good.Specifically it is shown in Table 1.
Embodiment 10
Select the mixed fine false twist yarn of the parallel type for the 93dtex-96f that feed-type obtains simultaneously（It is 19%, CDP to melt rate：Commonly
The content ratio of PET is 35：65）, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
There is the longer dyeing portion A of length, dyeing portion B and dyeing portion C, brindled sense enriches and day on the fabric cloth cover of gained
So, it is good to imitate cotton feel.Each performance parameter is shown in Table 1.
Embodiment 11
Fluffing processing is not carried out, remaining obtains the cotton feeling knitted fabric of the present invention with embodiment 1.
There is dyeing portion A different in size and dyeing portion B, brindled sense is abundant and natural, imitates cotton on the fabric cloth cover of gained
In feel.Each performance parameter is shown in Table 1.
Comparative example 1
The rate of melting of the mixed fine false twist yarn of parallel type used is 0%, remaining obtains knitting fabric with embodiment 1.
There are dyeing portion A different in size and dyeing portion B on the fabric cloth cover of gained, some are dull for brindled sense, imitate cotton feel
Difference.Each performance parameter is shown in Table 1.
Comparative example 2
The rate of melting of the mixed fine false twist yarn of parallel type used is 0%, remaining obtains cotton feeling knitted fabric with embodiment 2.
There are dyeing portion A, dyeing portion B and dyeing portion C different in size, some lists of brindled sense on the fabric cloth cover of gained
It adjusts, it is poor to imitate cotton feel.Each performance parameter of gained fabric is shown in Table 1.
Comparative example 3
Select the CDP-DTY of 112dtex-144f（It is 0% to melt rate）And common PET-the DTY of 100dtex-144f（Melt rate
It is 0%）Feeding is woven simultaneously, remaining obtains cotton feeling knitted fabric with embodiment 1.
Dyeing portion A and dyeing portion B are long on the fabric of gained, there is an appearance of similar crosspiece, and brindled sense is very dull and people
It is poor to imitate cotton feel for work.
Table 1
According to table 1,
（1）By embodiment 3 and embodiment 5 it is found that under equal conditions, the face for the mixed fibre false twist processing yarn that CDP contents are 55% is used
Expect with use CDP contents for 22% it is mixed fibre false twist processing yarn fabric compared with, the imitation cotton feeling of the two is suitable, but the former speckle
Sense is better than the latter.
（2）By embodiment 3 and embodiment 9 it is found that under equal conditions, the mixed fibre false twist processing yarn that the rate of melting is 3% is used
Fabric with use the rate of melting for the fabric of 40% mixed fine false twist processing yarn compared with, the brindled sense of the two is suitable, but the former imitative cotton
Feel is better than the latter.
（3）By embodiment 10 and embodiment 7 it is found that under equal conditions, using the mixed fine false twisting processing of total fiber number 93dtex
For the fabric of yarn compared with using the fabric of the mixed fine false twist processing yarn of total fiber number 103dtex, the brindled sense of the two is suitable, but the former
Imitative cotton feel not as good as the latter.
（4）By embodiment 11 and embodiment 1 it is found that under equal conditions, fluffing processing gained fabric is not carried out and is risen
Hair processing gained fabric is compared, and the brindled sense of the two is suitable, but the former imitative cotton feel is not as good as the latter.
（5）By comparative example 1 and embodiment 1 it is found that under equal conditions, the mixed fibre false twist processing yarn that the rate of melting is 0% is used
The former brindled sense, imitative cotton feel are far away from rear compared with the fabric of 30% mixed fine false twist processing yarn with using the rate of melting for fabric
Person.
（6）By comparative example 2 and embodiment 2 it is found that under equal conditions, the mixed fibre false twist processing yarn that the rate of melting is 0% is used
The former brindled sense, imitative cotton feel are far away from rear compared with the fabric of 21% mixed fine false twist processing yarn with using the rate of melting for fabric
Person.
（7）By comparative example 3 and embodiment 1 it is found that under equal conditions, braiding gained is fed using CDP and common PET simultaneously
Fabric is compared with the fabric of mixed fine false twist processing yarn using CDP/ common PETs, the former brindled sense, imitative cotton feel are far away from rear
Person.
Claims (9)
1. a kind of cotton feeling knitted fabric, it is characterized in that：The knitting fabric is to be formed by weft-knitting by mixed fine false twist yarn
Object, and the knitting fabric is up to the dyeing portion A and dyeing portion B less with different in size, different tones or different brightness；Institute
Stating mixed fibre, false twist yarn is combined by the cation-dyeable polyester long filament and disperse dye dyeable polyester filament, it melts
Rate is 1~40%.
2. according to the cotton feeling knitted fabric described in claim 1, it is characterized in that：In the mixed fine false twist yarn, the sun from
Sub- dye capable of dyeing polyester filament content is 30~70 weight %, the disperse dye dyeable polyester filament content is 70~30 weights
Measure %.
3. cotton feeling knitted fabric according to claim 1, it is characterized in that：The rate of melting of the mixed fine false twist yarn is 3
~35%.
4. cotton feeling knitted fabric according to claim 1, it is characterized in that：The total fiber number of the mixed fine false twisting processing long filament is
100~300dtex, filament number are 0.5~1.1dtex.
5. cotton feeling knitted fabric according to any one of claims 1 to 4, it is characterized in that：The mixed fine false twist yarn
In, the only described the CDP fabrics long filament is to melt state, or it is to melt state that the only described dispersion, which can contaminate polyester filament,.
6. cotton feeling knitted fabric according to any one of claims 1 to 4, it is characterized in that：The mixed fine false twist yarn
In, the CDP fabrics long filament and the dispersion can contaminate polyester filament while to melt state.
7. cotton feeling knitted fabric according to claim 1, it is characterized in that：There are length in the broadwise of the knitting fabric is
The striped of 0.5~80.0mm.
8. cotton feeling knitted fabric according to claim 6, it is characterized in that：In the knitting fabric, the dyeing portion A and dyeing
There are dyeing portion C between portion B.
9. cotton feeling knitted fabric according to claim 1, it is characterized in that：The knitting fabric is fluffing product.