CN108300323A - A kind of Sunscreen paint used for building exterior wall and preparation method thereof - Google Patents

A kind of Sunscreen paint used for building exterior wall and preparation method thereof Download PDF

Info

Publication number
CN108300323A
CN108300323A CN201711023217.4A CN201711023217A CN108300323A CN 108300323 A CN108300323 A CN 108300323A CN 201711023217 A CN201711023217 A CN 201711023217A CN 108300323 A CN108300323 A CN 108300323A
Authority
CN
China
Prior art keywords
parts
exterior wall
building exterior
paint used
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711023217.4A
Other languages
Chinese (zh)
Inventor
陈强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Sanshui Manya Environmental Technology Co Ltd
Original Assignee
Foshan Sanshui Manya Environmental Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Sanshui Manya Environmental Technology Co Ltd filed Critical Foshan Sanshui Manya Environmental Technology Co Ltd
Priority to CN201711023217.4A priority Critical patent/CN108300323A/en
Publication of CN108300323A publication Critical patent/CN108300323A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a kind of Sunscreen paint used for building exterior wall and preparation method thereof, is grouped as by the group of following parts by weight：45 60 parts of plant fiber, 13 parts of styrene-acrylic emulsion, 35 parts of polythene wax emulsion, 12 parts of attapulgite, 7 12 parts of film forming agent, 30 90 parts of water, 35 parts of thickener, 12 parts of Sodium Hyaluronate, 25 parts of sun-screening agent.The present invention is good by coating performance of keeping humidity prepared by above-mentioned formula, it is easy to form the coating that surface is uniform and smooth, is not easily cracked on construction wall surface, ultraviolet resistance is strong, and it is not sun-proof to solve existing coating, easily dry and cracked problem also reduces the cost of coating, simplifies the preparation method of coating.

Description

A kind of Sunscreen paint used for building exterior wall and preparation method thereof
Technical field
The present invention relates to paint fields more particularly to a kind of Sunscreen paint used for building exterior wall and preparation method thereof.
Background technology
Currently, exterior wall for building is generally used paint spraying, paint finishing can be fine with basis material in body surface Complete and tough and tensile protective film is bonded and is formed, building coating has the function of that decoration functions, defencive function and livability are improved.Respectively Proportion shared by kind function is not quite similar because using purpose different.Decoration functions are to improve its by the beautification of building The function of appearance value.Currently, coating used for building exterior wall generally uses composite fibre, Polymer Solution, mountain flour, thickener, chlorine The phenomenon that materials such as change magnesium are made, and the coating of external wall is directly exposed under sunlight, dry and cracked with will appear long, discoloration, peeling, The beauty for influencing external wall is exposed to the sun in the sun, forms cracking, cause the continuous extension in crack for a long time, wall body structure built on the sand, Wall is caused to cave in when serious.
Therefore, the existing technology needs to be improved and developed.
Invention content
In view of above-mentioned deficiencies of the prior art, the purpose of the present invention is to provide a kind of Sunscreen paint used for building exterior wall and its Preparation method, it is intended to which it is easily dry and cracked after long-term be exposed to the sun to solve existing coating, the problem of discoloration, peeling.
Technical scheme is as follows：
A kind of Sunscreen paint used for building exterior wall, is counted composed of the following components in parts by weight：
45-60 parts of animal and plant fiber；
1-3 parts of styrene-acrylic emulsion；
3-5 parts of polythene wax emulsion；
1-2 parts of attapulgite；
7-12 parts of film forming agent；
30-90 parts of water；
3-5 parts of thickener；
1-2 parts of Sodium Hyaluronate；
2-5 parts of sun-screening agent.
The film forming agent is by modified starch, propylene glycol phenylate, lyase, rubber latex, dihydric phosphate, saikoside, Creat lactone, one or more of galactomannan sugar composition.
The thickener is by hexamethylene, Lauryl Alcohol ester, polyvinyl alcohol, oxidized starch-acrylamide copolymer, Qula It is logical, one or more compositions in acrylyl oxy-ethyl-trimethyl salmiac.
The animal and plant fiber is by wool fiber, and rabbit fur fibre, elm bast, as bark fiber, silk fiber, bamboo is fine It ties up, aloe fibre, one or more compositions in flax fiber.
The preparation method of the elm bast is：Elm bark is steeped in acid solution and is impregnated 10-20 hours, is taken out, clear water It is washed till pH to be in neutrality, dry, rub 1-2 hours, be made in shredder.
The preparation method of the Oak Tree hide fiber is：Oak bark is steeped in acid solution and is impregnated 8-12 hours, is taken out, clear water is washed It is in neutrality, dries to pH, rub 0.5-1 hours and be made in shredder.
The preparation method of the bamboo fibre is：Dry culm stalk is crushed, rubbed using shredder it is broken, in 1% saline solution It impregnates 3-8 days, takes out, clear water impregnates, and cleaning is dried, is made.
The sun-screening agent is by glycerophosphate, glycerin diacetate, potassium stearate, False flax seed oil, polyoxyethylene nonyl phenyl second Alkene ether, Herba Lysimachiae foenumgraeci extract, nano-titanium oxide, one or more compositions in mulberrin.
A kind of preparation method of Sunscreen paint used for building exterior wall as described above is：When preparation, 45-60 parts of plant fiber, 1-3 parts of styrene-acrylic emulsion, 3-5 parts of polythene wax emulsion, 1-2 parts of attapulgite, 7-12 parts of film forming agent, which is added in 30-90 parts of water, to be stirred 2-10min is heated to 40-50 DEG C, and 3-5 parts of thickener, 1-2 parts of Sodium Hyaluronate, 2-5 parts of stirrings of sun-screening agent are then added 1min is cooled to room temperature and is made.
Advantageous effect：The present invention is good by coating performance of keeping humidity prepared by above-mentioned formula, and shape is easy on construction wall surface Coating that is uniform and smooth at surface, not being easily cracked, ultraviolet resistance is strong, solves that existing coating is not sun-proof, and easily dry and cracked asks Topic, also reduces the cost of coating, simplifies the preparation method of coating.
Specific implementation mode
A kind of Sunscreen paint used for building exterior wall of present invention offer and preparation method thereof, to make the purpose of the present invention, technical side Case and effect are clearer, clear, and the present invention is described in more detail below.It should be appreciated that specific reality described herein It applies example to be only used to explain the present invention, be not intended to limit the present invention.
The present invention provides a kind of Sunscreen paints used for building exterior wall, count in parts by weight composed of the following components：
45-60 parts of animal and plant fiber；
1-3 parts of styrene-acrylic emulsion；
3-5 parts of polythene wax emulsion；
1-2 parts of attapulgite；
7-12 parts of film forming agent；
30-90 parts of water；
3-5 parts of thickener；
1-2 parts of Sodium Hyaluronate；
2-5 parts of sun-screening agent.
The film forming agent is by modified starch, propylene glycol phenylate, lyase, rubber latex, dihydric phosphate, saikoside, Creat lactone, one or more of galactomannan sugar composition.
The thickener is by hexamethylene, Lauryl Alcohol ester, polyvinyl alcohol, oxidized starch-acrylamide copolymer, Qula It is logical, one or more compositions in acrylyl oxy-ethyl-trimethyl salmiac.For the animal and plant fiber by wool fiber, the rabbit hair is fine Dimension, elm bast, as bark fiber, silk fiber, bamboo fibre, aloe fibre, one or more compositions in flax fiber.
The preparation method of the elm bast is：Elm bark is steeped in acid solution and is impregnated 10-20 hours, is taken out, clear water It is washed till pH to be in neutrality, dry, rub 1-2 hours, be made in shredder.
The preparation method of the Oak Tree hide fiber is：Oak bark is steeped in acid solution and is impregnated 8-12 hours, is taken out, clear water is washed It is in neutrality, dries to pH, rub 0.5-1 hours and be made in shredder.
The preparation method of the bamboo fibre is：Dry culm stalk is crushed, rubbed using shredder it is broken, in 1% saline solution It impregnates 3-8 days, takes out, clear water impregnates, and cleaning is dried, is made.
The sun-screening agent is by glycerophosphate, glycerin diacetate, potassium stearate, False flax seed oil, polyoxyethylene nonyl phenyl second Alkene ether, Herba Lysimachiae foenumgraeci extract, nano-titanium oxide, one or more compositions in mulberrin.
Preparation method the present invention also provides Sunscreen paint used for building exterior wall as described above is：When preparation, plant fiber 45-60 parts, 1-3 parts of styrene-acrylic emulsion, 3-5 parts of polythene wax emulsion, 1-2 parts of attapulgite, 7-12 parts of 30-90 parts of additions of film forming agent 2-10min is stirred in water, is heated to 40-50 DEG C, and 3-5 parts of thickener, 1-2 parts of Sodium Hyaluronate, 2-5 parts of sun-screening agent is then added 1min is stirred, is cooled to room temperature and is made.
Below by the embodiment technical solution that the present invention is further explained.
Embodiment 1
Present invention Sunscreen paint used for building exterior wall, is counted composed of the following components in parts by weight：
45 parts of animal and plant fiber；
1 part of styrene-acrylic emulsion；
3 parts of polythene wax emulsion；
1 part of attapulgite；
7 parts of film forming agent；
30 parts of water；
3 parts of thickener；
1 part of Sodium Hyaluronate；
2 parts of sun-screening agent.
The film forming agent by ...
The thickener by ...
The animal and plant fiber by ...
Described sun-proof dose by ...
The preparation method of present invention Sunscreen paint used for building exterior wall is：When preparation, by the animal and plant fiber of above-mentioned parts by weight, benzene Acrylic emulsion, polythene wax emulsion, attapulgite, film forming agent are added to the water stirring 2min, heat to 40 DEG C, and thickening is then added Agent, Sodium Hyaluronate, sun-screening agent stir 1min, are cooled to room temperature and are made.
Embodiment 2
Present invention Sunscreen paint used for building exterior wall, is counted composed of the following components in parts by weight：
60 parts of animal and plant fiber；
3 parts of styrene-acrylic emulsion；
5 parts of polythene wax emulsion；
2 parts of attapulgite；
12 parts of film forming agent；
90 parts of water；
5 parts of thickener；
2 parts of Sodium Hyaluronate；
5 parts of sun-screening agent.
The film forming agent by ...
The thickener by ...
The animal and plant fiber by ...
Described sun-proof dose by ...
The preparation method of present invention Sunscreen paint used for building exterior wall is：When preparation, by the animal and plant fiber of above-mentioned parts by weight, benzene Acrylic emulsion, polythene wax emulsion, attapulgite, film forming agent are added to the water stirring 5min, heat to 45 DEG C, and thickening is then added Agent, Sodium Hyaluronate, sun-screening agent stir 1min, are cooled to room temperature and are made.
Embodiment 3
Present invention Sunscreen paint used for building exterior wall, is counted composed of the following components in parts by weight：
50 parts of animal and plant fiber；
2 parts of styrene-acrylic emulsion；
4 parts of polythene wax emulsion；
1.5 parts of attapulgite；
9 parts of film forming agent；
45 parts of water；
4 parts of thickener；
1 part of Sodium Hyaluronate；
3 parts of sun-screening agent.
The film forming agent by ...
The thickener by ...
The animal and plant fiber by ...
Described sun-proof dose by ...
The preparation method of present invention Sunscreen paint used for building exterior wall is：When preparation, by the animal and plant fiber of above-mentioned parts by weight, benzene Acrylic emulsion, polythene wax emulsion, attapulgite, film forming agent are added to the water stirring 10min, heat to 50 DEG C, and thickening is then added Agent, Sodium Hyaluronate, sun-screening agent stir 1min, are cooled to room temperature and are made.
Through performance test, coating used for building exterior wall prepared by the present invention meets relevant national standard, through long term ultraviolet and The performance that strong illumination is not easily cracked, surface is smooth, and sun-proof performance is good.
The present invention is good by coating performance of keeping humidity prepared by above-mentioned formula, is easy to form surface on construction wall surface uniform Coating that is smooth, not being easily cracked, ultraviolet resistance is strong, solves that existing coating is not sun-proof, and easily dry and cracked problem also reduces The cost of coating, the preparation method for simplifying coating.
It should be understood that the application of the present invention is not limited to the above for those of ordinary skills can With improvement or transformation based on the above description, all these modifications and variations should all belong to the guarantor of appended claims of the present invention Protect range.

Claims (9)

1. a kind of Sunscreen paint used for building exterior wall, which is characterized in that count in parts by weight composed of the following components：
45-60 parts of animal and plant fiber；
1-3 parts of styrene-acrylic emulsion；
3-5 parts of polythene wax emulsion；
1-2 parts of attapulgite；
7-12 parts of film forming agent；
30-90 parts of water；
3-5 parts of thickener；
1-2 parts of Sodium Hyaluronate；
2-5 parts of sun-screening agent.
2. Sunscreen paint used for building exterior wall according to claim 1, which is characterized in that the film forming agent by modified starch, Propylene glycol phenylate, lyase, rubber latex, dihydric phosphate, saikoside, creat lactone, one kind in galactomannan sugar Or several compositions.
3. Sunscreen paint used for building exterior wall according to claim 1, which is characterized in that the thickener is by hexamethylene, and ten Two carbon alcohol esters, polyvinyl alcohol, oxidized starch-acrylamide copolymer, Qula is logical, in acrylyl oxy-ethyl-trimethyl salmiac One or more compositions.
4. Sunscreen paint used for building exterior wall according to claim 1, which is characterized in that the animal and plant fiber is by wool fibre Dimension, rabbit fur fibre, elm bast, as bark fiber, silk fiber, bamboo fibre, aloe fibre, one kind in flax fiber or A variety of compositions.
5. Sunscreen paint used for building exterior wall according to claim 4, which is characterized in that the preparation side of the elm bast Method is：Elm bark is steeped in acid solution and is impregnated 10-20 hours, is taken out, clear water is washed till pH and is in neutrality, dry, rubbed in shredder It 1-2 hours, is made.
6. Sunscreen paint used for building exterior wall according to claim 4, which is characterized in that the preparation side of the Oak Tree hide fiber Method is：Oak bark is steeped in acid solution and is impregnated 8-12 hours, is taken out, clear water is washed till pH and is in neutrality, dry, rubbed in shredder It is made within 0.5-1 hours.
7. Sunscreen paint used for building exterior wall according to claim 4, which is characterized in that the preparation method of the bamboo fibre For：Dry culm stalk is crushed, is rubbed using shredder broken, is impregnated 3-8 days in 1% saline solution, taking-up, clear water immersion, clearly It washes, dries, be made.
8. Sunscreen paint used for building exterior wall according to claim 1, which is characterized in that the sun-screening agent is by phosphoglycerol Salt, glycerin diacetate, potassium stearate, False flax seed oil, nonylphenol polyoxyethylene ether, Herba Lysimachiae foenumgraeci extract, nano-titanium oxide, One or more compositions in mulberrin.
9. a kind of preparation method of Sunscreen paint used for building exterior wall as described in claim 1-8 is any, which is characterized in that described Method is：When preparation, 45-60 parts of plant fiber, 1-3 parts of styrene-acrylic emulsion, 3-5 parts of polythene wax emulsion, 1-2 parts of attapulgite, 7-12 parts of film forming agent, which is added in 30-90 parts of water, stirs 2-10min, heats to 40-50 DEG C, and 3-5 parts of thickener is then added, transparent 1-2 parts of matter acid sodium, 2-5 parts of stirring 1min of sun-screening agent, is cooled to room temperature and is made.
CN201711023217.4A 2017-10-27 2017-10-27 A kind of Sunscreen paint used for building exterior wall and preparation method thereof Pending CN108300323A (en)