CN108285696A - Zeolite interior wall wall material and its processing method - Google Patents
Zeolite interior wall wall material and its processing method Download PDFInfo
- Publication number
- CN108285696A CN108285696A CN201810102799.3A CN201810102799A CN108285696A CN 108285696 A CN108285696 A CN 108285696A CN 201810102799 A CN201810102799 A CN 201810102799A CN 108285696 A CN108285696 A CN 108285696A
- Authority
- CN
- China
- Prior art keywords
- parts
- zeolite
- agent
- interior wall
- wall material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of zeolite interior wall wall material and preparation method thereof, the zeolite interior wall wall material includes the following raw material：Water, dispersant, wetting agent, function additive, antifoaming agent, antifreezing agent, fungicide, titanium dioxide, kaolin, coarse whiting, talcum powder, zeolite, styrene-acrylic emulsion, coalescents, levelling agent, mould inhibitor, removes the aldehyde factor and thickener at hydroxypropyl cellulose.The zeolite interior wall wall material of the present invention, since zeolite has unique cavernous structure, makes it have ion exchangeable, adsorbing separation, high catalytic activity, reversible dehydration property, thermal stability and acid resistance using zeolite as main material.The zeolite interior wall wall material of the present invention, have it is pure natural, can breathe, eliminate the unusual smell, purification, fire protection flame retarding and other effects by force.The smooth exquisiteness of film, it is rich in color, it is suitable for the inner wall decoration in a variety of places such as household, school, market, has remarkable result to the purification of room air.
Description
Technical field
The present invention relates to a kind of zeolite interior wall wall material and its processing methods.
Background technology
Currently, the fast development of China's real estate brought to building decorating industry it is booming, caused by finishing material
Room air pollution especially brings health hazard directly to occupant group to children, the elderly, pregnant woman and Exposed person.
China is every year due to about hundreds of hundred million dollars of loss caused by room air pollution, the health caused by indoor pollution
Problem has become public health problem outstanding, while with the development of economy and social materialss are enriched constantly, people couple
The requirement of quality of life is being continuously improved so that pursuing more graceful comfortable domestic environment becomes the mainstream of the modern life.
Thus causing house ornamentation, decorative engineering especially interior decoration constantly heats up in the market, also allows the environment occurred in fitment process dirty
Dye and the dispute caused therefrom grow in intensity.In face of the health problem constantly to heat up, the no longer single attention finishing of people
Aesthetics, but increasingly pay attention to living environment comfort, safety and environmental protection.
Zeolite interior wall wall material is a kind of using zeolite as the environmental friendly indoor decoration wall material of main raw material(s), has zero formaldehyde, meeting
Breathing, strong to purify, the functions such as releasing negative oxygen ion.Due to zeolite interior wall wall material raw material health environment-friendly and with dress well
Decorations property is for the house decorative material of new generation of diatom ooze, wallpaper and emulsion paint, and the interior decoration material of commercial type is waited for
It is added to a large amount of artificial synthesized preparation in material product, easy tos produce harmful substance.
Invention content
An object of the present invention is to provide a kind of zeolite interior wall wall materials.
A kind of zeolite interior wall wall material of the present invention, includes the raw material of following parts by weight：25 parts~30 parts of water, hydroxypropyl are fine
0.1 part~0.2 part of dimension element, 0.3 part~0.5 part of dispersant, 0.1 part~0.2 part of wetting agent, 0.1 part~0.2 part of function additive,
0.2 part~0.4 part of antifoaming agent, 1 part~1.5 parts of antifreezing agent, 0.1 part~0.2 part of fungicide, 8 parts~15 parts of titanium dioxide, kaolin
5 parts~8 parts, 5 parts~8 parts of coarse whiting, 2 parts~5 parts of talcum powder, 30 parts~40 parts of zeolite, 15 parts~20 parts of styrene-acrylic emulsion, film forming helps
0.5 part~1 part of agent, 0.2 part~0.3 part of levelling agent, 0.3 part~0.5 part of mould inhibitor remove 1 part~1.5 parts of the aldehyde factor and thickener
0.5 part~1 part.
The zeolite interior wall wall material of the present invention, since zeolite has unique cavernous structure, makes it using zeolite as main material
With ion exchangeable, adsorbing separation, high catalytic activity, reversible dehydration property, thermal stability and acid resistance.The zeolite of the present invention
Interior wall wall material, have it is pure natural, can breathe, eliminate the unusual smell, purification, fire protection flame retarding and other effects by force.The smooth exquisiteness of film, color are rich
Richness is suitable for the inner wall decoration in a variety of places such as household, school, market, has remarkable result to the purification of room air.
In addition, the zeolite interior wall wall material that the present invention is above-mentioned, can also have following additional technical characteristic：
As the preferred embodiment of the present invention, the zeolite interior wall wall material includes the raw material of following parts by weight：Water
25 parts, 0.2 part of hydroxypropyl cellulose, 0.3 part of dispersant, 0.2 part of wetting agent, 0.1 part of function additive, 0.4 part of antifoaming agent is antifreeze
1 part of agent, 0.2 part of fungicide, 8 parts of titanium dioxide, 8 parts of kaolin, 5 parts of coarse whiting, 5 parts of talcum powder, 30 parts of zeolite, styrene-acrylic emulsion 20
Part, 0.5 part of coalescents, 0.3 part of levelling agent, 0.3 part of mould inhibitor, except 0.5 part of 1.5 parts of the aldehyde factor and thickener.
As the preferred embodiment of the present invention, the zeolite interior wall wall material includes the raw material of following parts by weight：Water
30 parts, 0.1 part of hydroxypropyl cellulose, 0.5 part of dispersant, 0.1 part of wetting agent, 0.2 part of function additive, 0.2 part of antifoaming agent is antifreeze
1.5 parts of agent, 0.1 part of fungicide, 15 parts of titanium dioxide, 5 parts of kaolin, 8 parts of coarse whiting, 2 parts of talcum powder, 40 parts of zeolite, styrene-acrylic emulsion
15 parts, 1 part of coalescents, 0.2 part of levelling agent, 0.5 part of mould inhibitor, except 1 part of 1 part of the aldehyde factor and thickener.
As the preferred embodiment of the present invention, the zeolite interior wall wall material includes the raw material of following parts by weight：Water
27 parts, 0.15 part of hydroxypropyl cellulose, 0.4 part of dispersant, 0.15 part of wetting agent, 0.15 part of function additive, 0.3 part of antifoaming agent,
1.3 parts of antifreezing agent, 0.15 part of fungicide, 12 parts of titanium dioxide, 7 parts of kaolin, 6 parts of coarse whiting, 4 parts of talcum powder, 35 parts of zeolite, phenylpropyl alcohol
22 parts of lotion, 0.75 part of coalescents, 0.25 part of levelling agent, 0.4 part of mould inhibitor, except 0.7 part of 1.3 parts of the aldehyde factor and thickener.
It is another object of the present invention to the preparation methods for proposing the zeolite interior wall wall material.
The preparation method of the zeolite interior wall wall material, includes the following steps：S101：Stainless steel dispersion is added in the water
In tank, then the dispersion tank is placed under dispersion machine, adjusts rotating speed to 350r/min~450r/min, then by the hydroxypropyl
Base cellulose, the dispersant, the wetting agent, the function additive, the antifoaming agent of half, the antifreezing agent and
The fungicide, which is added in the dispersion tank, stirs 10min~15min；S102：By the titanium dioxide, kaolin, described
Coarse whiting, the talcum powder and the zeolite are put into the dispersion tank, then adjust dispersion machine rotating speed to 600r/min~
800r/min simultaneously stirs 25min~35min；S103：The obtained products of the step S102 are ground with grinding machine；S104：It will
The product that the step S103 is obtained is again placed in dispersion machine, and it is 350r/min~450r/min to adjust rotating speed, is then added
Enter the styrene-acrylic emulsion, the coalescents, levelling agent, mould inhibitor, except the aldehyde factor and the remaining antifoaming agent and stir
8min~12min；S105：The thickener is added and adjusts the viscosity for the product that the step S104 is obtained to 90ku/25 DEG C
~95ku/25 DEG C, it then filters and dispenses, obtain zeolite interior wall wall material.
Further, in the step S103, the grain size after grinding is not more than 25 μm.
Further, in the step S105, the thickener is added and adjusts the product that the step S104 is obtained
Viscosity to 92.5ku/25 DEG C, then filter and dispense.
Further, in the step S105, when filtering, the aperture of the filter screen used is 30 μm~40 μm.
The additional aspect and advantage of the present invention will be set forth in part in the description, and will partly become from the following description
Obviously, or practice through the invention is recognized.
Specific implementation mode
The embodiment of the present invention is described below in detail, the embodiment is exemplary, it is intended to for explaining the present invention, and
It is not considered as limiting the invention.
In the present invention, the dispersant is polyphosphoric acids sodium salt；
The wetting agent is polyoxyethylated alkyl phenol；
The function additive is AMP-95；
The antifoaming agent is silicone oil；
The antifreezing agent is propylene glycol；
The fungicide is 1,2- benzisothiazole-3-ketones；
The coalescents are Taxanol；
The levelling agent is 1,2- propylene glycol；
The mould inhibitor is Kathon；
The aldehyde factor of removing is amino-compound；
The thickener is polyacrylate alkali swollen thickener,
It will be appreciated by those skilled in the art that its range is not limited to that.
Embodiment 1
Embodiment 1 proposes a kind of zeolite interior wall wall material, includes the raw material of following parts by weight：25 parts of water, hydroxypropyl are fine
0.2 part of dimension element, 0.3 part of polyphosphoric acids sodium salt, 0.2 part of polyoxyethylated alkyl phenol, AMP-950.1 parts, 0.4 part of silicone oil, the third two
1 part of alcohol, 0.2 part of 1,2-benzisothiazolin-3-one, 8 parts of titanium dioxide, 8 parts of kaolin, 5 parts of coarse whiting, 5 parts of talcum powder, zeolite 30
Part, 20 parts of styrene-acrylic emulsion, 0.5 part of Taxanol, 0.3 part of 1,2-PD, 0.3 part of Kathon,
0.5 part of 1.5 parts of amino-compound and polyacrylate alkali swollen thickener.
The preparation method of the zeolite interior wall wall material of embodiment 1, includes the following steps：
(1) by the water be added stainless steel dispersion tank in, then the dispersion tank is placed under dispersion machine, adjust rotating speed to
350r/min, then by the hydroxypropyl cellulose, the polyphosphoric acids sodium salt, the polyoxyethylated alkyl phenol, described
The dispersion tank is added in AMP-95, the silicone oil of half, the propylene glycol and the 1,2- benzisothiazole-3-ketones
Middle stirring 15min.
(2) titanium dioxide, the kaolin, the coarse whiting, the talcum powder and the zeolite are put into described point
It dissipates in tank, the rotating speed for then adjusting dispersion machine to 600r/min and stirs 35min.
(3) product that the step (2) obtains is ground to grain size with grinding machine and is not more than 25 μm.
(4) product that the step (3) obtains is again placed in dispersion machine, and it is 350r/min to adjust rotating speed, then
Be added the styrene-acrylic emulsion, Taxanol, 1,2- propylene glycol, Kathon, amino-compound and
The remaining silicone oil simultaneously stirs 12min.
(5) the polyacrylate alkali swollen thickener is added and adjust the viscosity of the product that the step (4) obtains to
90ku/25 DEG C, filter screen filtration and packing of the aperture for 40 μm are then used, zeolite interior wall wall material is obtained.
Embodiment 2
Embodiment 2 proposes a kind of zeolite interior wall wall material, includes the raw material of following parts by weight：30 parts of water, hydroxypropyl are fine
0.1 part of dimension element, 0.5 part of polyphosphoric acids sodium salt, 0.1 part of polyoxyethylated alkyl phenol, AMP-950.2 parts, 0.2 part of silicone oil, the third two
1.5 parts of alcohol, 0.1 part of 1,2-benzisothiazolin-3-one, 15 parts of titanium dioxide, 5 parts of kaolin, 8 parts of coarse whiting, 2 parts of talcum powder, boiling
40 parts of stone, 15 parts of styrene-acrylic emulsion, Taxanol1 parts, 0.2 part of 1,2-PD, 0.5 part of Kathon,
1 part of 1 part of amino-compound and polyacrylate alkali swollen thickener.
The preparation method of the zeolite interior wall wall material of embodiment 2, includes the following steps：
(1) by the water be added stainless steel dispersion tank in, then the dispersion tank is placed under dispersion machine, adjust rotating speed to
450r/min, then by the hydroxypropyl cellulose, the polyphosphoric acids sodium salt, the polyoxyethylated alkyl phenol, described
The dispersion tank is added in AMP-95, the silicone oil of half, the propylene glycol and the 1,2- benzisothiazole-3-ketones
Middle stirring 10min.
(2) titanium dioxide, the kaolin, the coarse whiting, the talcum powder and the zeolite are put into described point
It dissipates in tank, the rotating speed for then adjusting dispersion machine to 800r/min and stirs 25min.
(3) product that the step (2) obtains is ground to grain size with grinding machine and is not more than 25 μm.
(4) product that the step (3) obtains is again placed in dispersion machine, and it is 450r/min to adjust rotating speed, then
Be added the styrene-acrylic emulsion, Taxanol, 1,2- propylene glycol, Kathon, amino-compound and
The remaining silicone oil simultaneously stirs 8min.
(5) the polyacrylate alkali swollen thickener is added and adjust the viscosity of the product that the step (4) obtains to
95ku/25 DEG C, filter screen filtration and packing of the aperture for 30 μm are then used, zeolite interior wall wall material is obtained.
Embodiment 3
Embodiment 3 proposes a kind of zeolite interior wall wall material, includes the raw material of following parts by weight：27 parts of water, hydroxypropyl are fine
0.15 part of dimension element, 0.4 part of polyphosphoric acids sodium salt, 0.15 part of polyoxyethylated alkyl phenol, AMP-950.15 parts, 0.3 part of silicone oil, third
1.3 parts of glycol, 0.15 part of 1,2-benzisothiazolin-3-one, 12 parts of titanium dioxide, 7 parts of kaolin, 6 parts of coarse whiting, 4 parts of talcum powder,
35 parts of zeolite, 22 parts of styrene-acrylic emulsion, Taxanol0.75 parts, 0.25 part of 1,2-PD, Kathon
0.4 part, 0.7 part of 1.3 parts of amino-compound and polyacrylate alkali swollen thickener.
The preparation method of the zeolite interior wall wall material of embodiment 3, includes the following steps：
(1) by the water be added stainless steel dispersion tank in, then the dispersion tank is placed under dispersion machine, adjust rotating speed to
400r/min, then by the hydroxypropyl cellulose, the polyphosphoric acids sodium salt, the polyoxyethylated alkyl phenol, described
The dispersion tank is added in AMP-95, the silicone oil of half, the propylene glycol and the 1,2- benzisothiazole-3-ketones
Middle stirring 13min.
(2) titanium dioxide, the kaolin, the coarse whiting, the talcum powder and the zeolite are put into described point
It dissipates in tank, the rotating speed for then adjusting dispersion machine to 700r/min and stirs 30min.
(3) product that the step (2) obtains is ground to grain size with grinding machine and is not more than 25 μm.
(4) product that the step (3) obtains is again placed in dispersion machine, and it is 400r/min to adjust rotating speed, then
Be added the styrene-acrylic emulsion, Taxanol, 1,2- propylene glycol, Kathon, amino-compound and
The remaining silicone oil simultaneously stirs 10min.
(5) the polyacrylate alkali swollen thickener is added and adjust the viscosity of the product that the step (4) obtains to
92.5ku/25 DEG C, filter screen filtration and packing of the aperture for 35 μm are then used, zeolite interior wall wall material is obtained.
To sum up, zeolite interior wall wall material of the invention, using zeolite as main material, since zeolite has unique poroid knot
Structure makes it have ion exchangeable, adsorbing separation, high catalytic activity, reversible dehydration property, thermal stability and acid resistance.This hair
Bright zeolite interior wall wall material, have it is pure natural, can breathe, eliminate the unusual smell, purification, fire protection flame retarding and other effects by force.The smooth exquisiteness of film,
It is rich in color, it is suitable for the inner wall decoration in a variety of places such as household, school, market, has remarkable result to the purification of room air.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means specific features, structure, material or spy described in conjunction with this embodiment or example
Point is included at least one embodiment or example of the invention.In the present specification, schematic expression of the above terms are not
It must be directed to identical embodiment or example.Moreover, particular features, structures, materials, or characteristics described can be in office
It can be combined in any suitable manner in one or more embodiments or example.In addition, without conflicting with each other, the skill of this field
Art personnel can tie the feature of different embodiments or examples described in this specification and different embodiments or examples
It closes and combines.
Although the embodiments of the present invention has been shown and described above, it is to be understood that above-described embodiment is example
Property, it is not considered as limiting the invention, those skilled in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, changes, replacing and modification.
Claims (8)
1. a kind of zeolite interior wall wall material, which is characterized in that include the raw material of following parts by weight：25 parts~30 parts of water, hydroxypropyl
0.1 part~0.2 part of cellulose, 0.3 part~0.5 part of dispersant, 0.1 part~0.2 part of wetting agent, function additive 0.1 part~0.2
Part, 0.2 part~0.4 part of antifoaming agent, 1 part~1.5 parts of antifreezing agent, 0.1 part~0.2 part of fungicide, 8 parts~15 parts of titanium dioxide, height
5 parts~8 parts of ridge soil, 5 parts~8 parts of coarse whiting, 2 parts~5 parts of talcum powder, 30 parts~40 parts of zeolite, 15 parts~20 parts of styrene-acrylic emulsion, at
0.5 part~1 part of film auxiliary agent, 0.2 part~0.3 part of levelling agent, 0.3 part~0.5 part of mould inhibitor except 1 part~1.5 parts of the aldehyde factor and increase
Thick dose 0.5 part~1 part.
2. zeolite interior wall wall material according to claim 1, which is characterized in that include the raw material of following parts by weight：Water 25
Part, 0.2 part of hydroxypropyl cellulose, 0.3 part of dispersant, 0.2 part of wetting agent, 0.1 part of function additive, 0.4 part of antifoaming agent, antifreezing agent
1 part, 0.2 part of fungicide, 8 parts of titanium dioxide, 8 parts of kaolin, 5 parts of coarse whiting, 5 parts of talcum powder, 30 parts of zeolite, 20 parts of styrene-acrylic emulsion,
0.5 part of coalescents, 0.3 part of levelling agent, 0.3 part of mould inhibitor, except 0.5 part of 1.5 parts of the aldehyde factor and thickener.
3. zeolite interior wall wall material according to claim 1, which is characterized in that include the raw material of following parts by weight：Water 30
Part, 0.1 part of hydroxypropyl cellulose, 0.5 part of dispersant, 0.1 part of wetting agent, 0.2 part of function additive, 0.2 part of antifoaming agent, antifreezing agent
1.5 parts, 0.1 part of fungicide, 15 parts of titanium dioxide, 5 parts of kaolin, 8 parts of coarse whiting, 2 parts of talcum powder, 40 parts of zeolite, styrene-acrylic emulsion 15
Part, 1 part of coalescents, 0.2 part of levelling agent, 0.5 part of mould inhibitor, except 1 part of 1 part of the aldehyde factor and thickener.
4. zeolite interior wall wall material according to claim 1, which is characterized in that include the raw material of following parts by weight：Water 27
Part, 0.15 part of hydroxypropyl cellulose, 0.4 part of dispersant, 0.15 part of wetting agent, 0.15 part of function additive, 0.3 part of antifoaming agent are prevented
Freeze 1.3 parts of agent, 0.15 part of fungicide, 12 parts of titanium dioxide, 7 parts of kaolin, 6 parts of coarse whiting, 4 parts of talcum powder, 35 parts of zeolite, phenylpropyl alcohol breast
22 parts of liquid, 0.75 part of coalescents, 0.25 part of levelling agent, 0.4 part of mould inhibitor, except 0.7 part of 1.3 parts of the aldehyde factor and thickener.
5. the preparation method of claim 1-4 any one of them zeolite interior wall wall materials, which is characterized in that include the following steps：
S101：By the water be added stainless steel dispersion tank in, then the dispersion tank is placed under dispersion machine, adjust rotating speed to
350r/min~450r/min, then by the hydroxypropyl cellulose, the dispersant, the wetting agent, the function additive,
The antifoaming agent, the antifreezing agent and the fungicide of half, which are added in the dispersion tank, stirs 10min~15min；
S102：The titanium dioxide, the kaolin, the coarse whiting, the talcum powder and the zeolite are put into the dispersion
In tank, the rotating speed for then adjusting dispersion machine to 600r/min~800r/min and stirs 25min~35min；
S103：The obtained products of the step S102 are ground with grinding machine；
S104：The obtained products of the step S103 are again placed in dispersion machine, and it is 350r/min~450r/ to adjust rotating speed
Then min is added the styrene-acrylic emulsion, the coalescents, levelling agent, mould inhibitor, removes the aldehyde factor and the remaining defoaming
Agent simultaneously stirs 8min~12min；
S105：The thickener is added and adjusts the viscosity of the product that the step S104 is obtained to 90ku/25 DEG C~95ku/25
DEG C, it then filters and dispenses, obtain zeolite interior wall wall material.
6. the preparation method of zeolite interior wall wall material according to claim 5, which is characterized in that in the step S103,
Grain size after grinding is not more than 25 μm.
7. the preparation method of zeolite interior wall wall material according to claim 5, which is characterized in that in the step S105,
The thickener is added and adjust the product that the step S104 is obtained viscosity to 92.5ku/25 DEG C, then filter and dispense.
8. the preparation method of zeolite interior wall wall material according to claim 5, which is characterized in that in the step S105,
When filtering, the aperture of the filter screen used is 30 μm~40 μm.