CN108277551A - 一种聚氨酯复合纤维 - Google Patents

一种聚氨酯复合纤维 Download PDF

Info

Publication number
CN108277551A
CN108277551A CN201711391623.6A CN201711391623A CN108277551A CN 108277551 A CN108277551 A CN 108277551A CN 201711391623 A CN201711391623 A CN 201711391623A CN 108277551 A CN108277551 A CN 108277551A
Authority
CN
China
Prior art keywords
polyurethane
diisocyanate
composite fibre
polyalkylene ether
polyurethane composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711391623.6A
Other languages
English (en)
Inventor
周建
颜玉荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Hao Yang Pu Technology Co Ltd
Original Assignee
Suzhou Hao Yang Pu Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Hao Yang Pu Technology Co Ltd filed Critical Suzhou Hao Yang Pu Technology Co Ltd
Priority to CN201711391623.6A priority Critical patent/CN108277551A/zh
Publication of CN108277551A publication Critical patent/CN108277551A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种聚氨酯复合纤维，由聚氨酯脲与聚氨酯混合形成，所述聚氨酯脲包括共聚聚亚烷基醚二醇、至少一种二异氰酸酯和二胺，所述聚氨酯由聚酯多醇、聚醚多醇、有机二异氰酸酯和链增长剂得到，所述共聚聚亚烷基醚二醇由亚烷基醚形成，所述聚酯多醇由线性二羟酸、支化非环形一级二醇及三官能及更高官能度的醇反应得到；所述链增长剂为1,4‑丁二醇，所述二异氰酸酯为4,4’‑亚甲基双(苯基异氰酸酯)和/或1‑异氰酸基‑2‑[(4‑氰氧苯基)甲基]苯。

Description

一种聚氨酯复合纤维
技术领域
本发明涉及一种聚氨酯复合纤维，属于聚氨酯合成纤维技术领域。
背景技术
目前针对特殊场合的衣料，虽具有弹性，但使用时间长，容易存在弹性功能降低，出现严重断丝的情况，现有的聚氨酯纤维衣料已无法满足现市场需求。
故，需要一种新的技术方案以解决上述技术问题。
发明内容
本发明为解决现有技术中存在的不足，提出一种聚氨酯复合纤维。
为了解决上述技术问题，本发明提供了一种聚氨酯复合纤维，由聚氨酯脲与聚氨酯混合形成，所述聚氨酯脲包括共聚聚亚烷基醚二醇、至少一种二异氰酸酯和二胺，所述聚氨酯由聚酯多醇、聚醚多醇、有机二异氰酸酯和链增长剂得到，所述共聚聚亚烷基醚二醇由亚烷基醚形成，所述聚酯多醇由线性二羟酸、支化非环形一级二醇及三官能及更高官能度的醇反应得到；所述链增长剂为1,4-丁二醇，所述二异氰酸酯为4,4’-亚甲基双(苯基异氰酸酯)和/或1-异氰酸基-2-[(4-氰氧苯基)甲基]苯。
作为本发明的进一步优化，本发明所述的共聚聚亚烷基醚二醇由碳数为2-10的不同的亚烷基醚形成。
作为本发明的进一步优化，本发明所述的二胺为两个胺基之间的烷基部分的碳数为3以下的直链。
作为本发明的进一步优化，本发明所述的共聚聚亚烷基醚二醇的数均分子量为1000-3000。
作为本发明的进一步优化，本发明所述的有机二异氰酸酯为亚二甲苯基二异氰酸酯或4,4’-二环己基甲烷二异氰酸酯。
有益效果：本发明与现有技术相比，具有以下优点：本发明的聚氨酯复合纤维弹性优良，具有良好的耐氧性和热残余变形特性。
具体实施方式
下面结合具体实施例，进一步阐明本发明，应理解这些实例仅用于说明本发明而不用于限制本发明的范围，在阅读了本发明之后，本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
本实施例的一种聚氨酯复合纤维，由聚氨酯脲与聚氨酯混合形成，该聚氨酯脲包括共聚聚亚烷基醚二醇、至少一种二异氰酸酯和二胺，本实施例的聚氨酯由聚酯多醇、聚醚多醇、有机二异氰酸酯和链增长剂得到，共聚聚亚烷基醚二醇由亚烷基醚形成，聚酯多醇由线性二羟酸、支化非环形一级二醇及三官能及更高官能度的醇反应得到；本实施例的链增长剂为1,4-丁二醇，二异氰酸酯为4,4’-亚甲基双(苯基异氰酸酯)和/或1-异氰酸基-2-[(4-氰氧苯基)甲基]苯。
具体的，本实施例的共聚聚亚烷基醚二醇由碳数为2-10的不同的亚烷基醚形成，且共聚聚亚烷基醚二醇的数均分子量为1000-3000，二胺为两个胺基之间的烷基部分的碳数为3以下的直链，其中，本实施例的有机二异氰酸酯为亚二甲苯基二异氰酸酯或4,4’-二环己基甲烷二异氰酸酯。

Claims (5)

1.一种聚氨酯复合纤维，其特征在于：由聚氨酯脲与聚氨酯混合形成，所述聚氨酯脲包括共聚聚亚烷基醚二醇、至少一种二异氰酸酯和二胺，所述聚氨酯由聚酯多醇、聚醚多醇、有机二异氰酸酯和链增长剂得到，所述共聚聚亚烷基醚二醇由亚烷基醚形成，所述聚酯多醇由线性二羟酸、支化非环形一级二醇及三官能及更高官能度的醇反应得到；所述链增长剂为1,4-丁二醇，所述二异氰酸酯为4,4’-亚甲基双(苯基异氰酸酯)和/或1-异氰酸基-2-[(4-氰氧苯基)甲基]苯。
2.根据权利要求1所述的一种聚氨酯复合纤维，其特征在于：所述共聚聚亚烷基醚二醇由碳数为2-10的不同的亚烷基醚形成。
3.根据权利要求1所述的一种聚氨酯复合纤维，其特征在于：所述二胺为两个胺基之间的烷基部分的碳数为3以下的直链。
4.根据权利要求1所述的一种聚氨酯复合纤维，其特征在于：所述共聚聚亚烷基醚二醇的数均分子量为1000-3000。
5.根据权利要求1所述的一种聚氨酯复合纤维，其特征在于：所述有机二异氰酸酯为亚二甲苯基二异氰酸酯或4,4’-二环己基甲烷二异氰酸酯。
CN201711391623.6A 2017-12-21 2017-12-21 一种聚氨酯复合纤维 Withdrawn CN108277551A (zh)