CN108264789B - 一种水包水多彩涂料及其制备方法 - Google Patents
一种水包水多彩涂料及其制备方法 Download PDFInfo
- Publication number
- CN108264789B CN108264789B CN201711490189.7A CN201711490189A CN108264789B CN 108264789 B CN108264789 B CN 108264789B CN 201711490189 A CN201711490189 A CN 201711490189A CN 108264789 B CN108264789 B CN 108264789B
- Authority
- CN
- China
- Prior art keywords
- water
- paint
- colloid
- emulsion
- multicolor paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种水包水多彩涂料以及制备水包水多彩涂料的方法，基础漆、胶体与无机基料之间重量比例为(20‑45):(20‑40):(30‑60)，基础漆混合制作成彩色粒子后与胶体混合进行胶化，形成保护胶体；将无机基料加入到保护胶体中，陈化得到所述水包水多彩涂料。本发明水包水多彩涂料在储存过程中具有良好的稳定性，保存期长，并具有更好的环保性、耐水白性、耐候性，防火性，同时具备逼真的仿花岗岩、大理石的饰面效果。
Description
技术领域
本发明涉及一种无机涂料，尤其涉及一种无机水包水多彩涂料、以及所述无机水包水多彩涂料的制备方法。
背景技术
涂料是涂覆在被保护或被装饰的物体表面、并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。以有机溶剂为分散介质的油性涂料由于不符合环保的要求，已经逐渐被水性涂料所取代。
水包水多彩涂料又被称为液态石、水包水多彩理石漆，是一种新型水性涂料，实际上水包水多彩涂料是一种水性乳胶涂料的分散水相(一种悬浮体系)，采用改性有机硅树脂乳液为基料，运用特殊包覆技术，将各色色漆包覆成胶状水性彩色颗粒，悬浮在特定的水性分散体中。
水包水多彩理石漆色彩丰富多彩，并可按要求提供特殊颜色且仿真性极高，其在设计商不受任何限制，可以根据设计师的意图任意改变形状。施工完毕干燥后，具有耐磨损、耐冲刷、耐紫外线照射、抗静电、耐高温、耐酸雨、防水、防龟裂、高强度、耐长期多种气候条件变化的特性，具有易于保养和清洗、自洁性优异、多色彩一次喷涂、施工容易等优点。
但是，悬浮体系在储存过程中，尤其是高温、低温条件下，稳定性比较差。
发明内容
针对目前水包水多彩涂料所存在的储存问题，本发明提供了一种水包水多彩涂料以及制备水包水多彩涂料的方法。
本发明第一个方面是提供一种水包水多彩涂料，包括：基础漆、胶体和无机基料，基础漆、胶体与无机基料之间重量比例为(20-45):(20-40):(30-60)，更优选为(25-40):(25-40):(35-50)，更优选为(30-35):(30-35):(40-45)；所述基础漆包裹于胶体中形成保护胶体，所述保护胶体分散于无机基料中。
在一种优选实施例中，所述胶体，按照重量比例，包括：
水性胶粉 10-20份；
缓凝剂 3-5份；
水 70-80份。
在本发明一种优选实施例中，所述无机基料，按照重量比例，包括：
碱金属硅酸盐 20-30份；
硅溶胶 20-30份；
水 40-60份。
在本发明一种优选实施例中，所述无机基料，按照重量比例，还包括：
防冻剂 0.1～0.5份；和/或
防腐杀菌剂 0.1～0.5份。
在本发明一种优选实施例中，所述基础漆，按照重量比例，包括：
在一种优选实施例中，所述基础漆，按照重量比例，还包括：
消泡剂 0.1～0.5份；和/或
成膜助剂 1-2份。
在一种优选实施例中，所述碱金属硅酸盐选用硅酸钠、硅酸钾或硅酸锂的一种或几种混合物。
在一种优选实施例中，所述耐碱阴离子乳液选用阴离子型的苯丙乳液、硅丙乳液或纯丙乳液、聚氨酯乳液、聚丙烯酰胺乳液、石蜡乳液、硅氧烷乳液的一种或几种混合物。
在一种优选实施例中，所述亲水性保护胶选自聚乙烯醇、甲基纤维素或乙基纤维素的一种或其混合物。
在一种优选实施例中，所述稳定剂选自季铵盐、硅烷偶联剂的一种或其混合物。
在一种优选实施例中，所述润湿分散剂选自磷酸酯、硫酸酯或磺酸钠盐类阴离子表面活性剂的一种或其混合物。
在一种优选实施例中，所述增稠剂为选自羧甲基纤维素(CMC)、羟乙基纤维素(HEC)、黄原胶、淀粉多糖类或无机膨润土等的一种或其混合物。
本发明第二个方面是提供一种制备所述水包水多彩涂料的方法，包括：
基础漆混合制作成彩色粒子；
将彩色粒子与胶体混合进行胶化，形成保护胶体；
将无机基料加入到保护胶体中，陈化得到所述水包水多彩涂料。
在本发明一种优选实施例中，将胶体各组分混合，未形成胶化之前，加入彩色粒子。
在一种优选实施例中，所述胶化进行1-2小时。
在一种优选实施例中，所述陈化进行至少1小时，更优选为1-5小时，更优选为2-4小时，更优选为2-3小时。
本发明上下文内容中，所述耐碱是指在本发明水包水多彩涂料呈碱性时不会发生不期望的化学反应。
本发明采用无机碱金属硅酸盐溶液(水玻璃)和硅溶胶为无机胶凝体系，相比单纯以乳液为体系的多彩涂料，具有更好的环保性、耐水白性、耐候性，防火性；同时具备逼真的仿花岗岩、大理石的饰面效果。
本发明水包水多彩涂料在储存过程中具有良好的稳定性，保存期长。
具体实施例
实施例1
1、胶体包括：
水性胶粉13kg
缓凝剂4kg
水73kg
2、无机基料
硅酸钠30kg
硅溶胶30kg
防冻剂0.5kg
水55kg
3、基础漆
硅酸钠40kg
阴离子型苯丙乳液6kg
色浆10kg
甲基纤维素2kg
季铵盐稳定剂0.5kg
润湿分散剂0.6kg
无机膨润土0.4kg
消泡剂0.4kg
成膜助剂1kg
水25kg
本实施例中水包水多彩涂料制备方法如下：
先调色基础漆的各成分混合均匀，放入造粒机制成彩粒；
将胶体的各成分混合均匀；
最后将调色基础漆加入到保护胶中，搅拌均匀，胶化反应1-2小时；
再加入无机基料，继续陈化2小时。
实施例2
1、胶体包括：
水性胶粉15kg
缓凝剂5kg
水75kg
2、无机基料
硅酸钠25kg
硅溶胶27kg
防冻剂0.3kg
水60kg
3、基础漆
硅酸钠45kg
阴离子型纯丙乳液8kg
色浆12kg
乙基纤维素1kg
硅烷偶联剂0.3kg
润湿分散剂0.5kg
黄原胶0.4kg
消泡剂0.4kg
成膜助剂1kg
水20kg
本实施例中水包水多彩涂料制备方法如下：
先调色基础漆的各成分混合均匀，放入造粒机制成彩粒；
将胶体的各成分混合均匀；
最后将调色基础漆加入到保护胶中，搅拌均匀，胶化反应1-2小时；
再加入无机基料，继续陈化2小时。
实施例3
1、胶体包括：
水性胶粉19kg
缓凝剂3kg
水70kg
2、无机基料
硅酸钾25kg
硅溶胶28kg
防冻剂0.2kg
防腐杀菌剂0.2kg
水50kg
3、基础漆
硅酸钠50kg
阴离子型乙丙乳液7kg
色浆14kg
聚乙烯醇2kg
硅烷偶联剂0.5kg
润湿分散剂0.6kg
羧甲基纤维素0.4kg
消泡剂0.4kg
成膜助剂1kg
水20kg
本实施例中水包水多彩涂料制备方法如下：
先调色基础漆的各成分混合均匀，放入造粒机制成彩粒；
将胶体的各成分混合均匀；
最后将调色基础漆加入到保护胶中，搅拌均匀，胶化反应1-2小时；再加入无机基料，继续陈化2小时。
对比例1
1、组分1
硅酸钾25kg
硅酸钠50kg
硅溶胶28kg
防冻剂0.2kg
色浆14kg
聚乙烯醇2kg
硅烷偶联剂0.5kg
润湿分散剂0.6kg
消泡剂0.4kg
成膜助剂1kg
水70kg
2、组分2
阴离子型乙丙乳液8kg
羧甲基纤维素0.4kg
本对比例中涂料制备方法如下：
组分1的各组分混合均匀，搅拌35分钟；
加入组分2，搅拌10分钟。
对比例2
1、无机基料
硅酸钾25kg
硅溶胶28kg
防冻剂0.2kg
防腐杀菌剂0.2kg
水50kg
2、基础漆
硅酸钠50kg
阴离子型乙丙乳液7kg
色浆14kg
聚乙烯醇2kg
硅烷偶联剂0.5kg
润湿分散剂0.6kg
羧甲基纤维素0.4kg
消泡剂0.4kg
成膜助剂1kg
水20kg
本对比例中涂料制备方法如下：
先调色基础漆的各成分混合均匀，放入造粒机制成彩粒；将调色基础漆加入无机基料，搅拌混合，然后静止2小时。
对比例3
1、胶体包括：
水性胶粉19kg
缓凝剂3kg
硅溶胶28kg
防冻剂0.2kg
防腐杀菌剂0.2kg
水120kg
2、基础漆
有机硅40kg
阴离子型乙丙乳液7kg
色浆14kg
聚乙烯醇2kg
硅烷偶联剂0.5kg
润湿分散剂0.6kg
羧甲基纤维素0.4kg
消泡剂0.4kg
成膜助剂1kg
水20kg
本实施例中水包水多彩涂料制备方法如下：
先调色基础漆的各成分混合均匀，放入造粒机制成彩粒；
将胶体的各成分混合均匀；
最后将调色基础漆加入到保护胶中，搅拌均匀，胶化反应1-2小时。
本发明上述水包水多彩涂料性能检测如下：
本发明水包水多彩涂料，耐候性、自洁性、耐酸耐碱性能良好，符合HG/T4343-2012标准。
本发明上述水包水多彩涂料环保性能检测如下：
本发明水包水多彩涂料，环保性能良好，未检出挥发性有机物(VOC)、以及重金属等污染物。
本发明上述水包水多彩涂料储存性能检测如下：
本发明采用有机乳液、无机凝胶体系制备得到的水包水多彩涂料，相比于非水包水涂料、有机或无机凝胶为主的体系，具有明显更好的储存稳定性。
以上对本发明的具体实施例进行了详细描述，但其只是作为范例，本发明并不限制于以上描述的具体实施例。对于本领域技术人员而言，任何对本发明进行的等同修改和替代也都在本发明的范畴之中。因此，在不脱离本发明的精神和范围下所作的均等变换和修改，都应涵盖在本发明的范围内。
Claims (10)
1.一种水包水多彩涂料，其特征在于，包括：基础漆、胶体和无机基料，基础漆、胶体与无机基料之间重量比例为(20-45):(20-40):(30-60)；所述无机基料包括碱金属硅酸盐和硅溶胶；所述基础漆包括碱金属硅酸盐溶液和耐碱阴离子乳液；所述基础漆包裹于胶体中形成保护胶体，所述保护胶体分散于无机基料中。
2.根据权利要求1所述的水包水多彩涂料，其特征在于，所述胶体，按照重量比例，包括：
水性胶粉 10-20份；
缓凝剂 3-5份；
水 70-80份。
3.根据权利要求1所述的水包水多彩涂料，其特征在于，所述无机基料，按照重量比例，包括：
碱金属硅酸盐 20-30份；
硅溶胶 20-30份；
水 40-60份。
4.根据权利要求3所述的水包水多彩涂料，其特征在于，所述无机基料，按照重量比例，还包括：
防冻剂 0.1～0.5份；和/或
防腐杀菌剂 0.1～0.5份。
5.根据权利要求1所述的水包水多彩涂料，其特征在于，所述基础漆，按照重量比例，包括：
6.根据权利要求5所述的水包水多彩涂料，其特征在于，所述基础漆，按照重量比例，还包括：
消泡剂 0.1～0.5份；和/或
成膜助剂 1-2份。
7.根据权利要求3-6中任意一项所述的水包水多彩涂料，其特征在于，所述碱金属硅酸盐选用硅酸钠、硅酸钾或硅酸锂的一种或几种混合物。
8.根据权利要求5所述的水包水多彩涂料，其特征在于，所述耐碱阴离子乳液选用阴离子型的苯丙乳液、硅丙乳液或纯丙乳液、聚氨酯乳液、聚丙烯酰胺乳液、石蜡乳液、硅氧烷乳液的一种或几种混合物。
9.根据权利要求5所述的水包水多彩涂料，其特征在于，所述亲水性保护胶选自聚乙烯醇、甲基纤维素或乙基纤维素的一种或其混合物。
10.一种制备权利要求1所述水包水多彩涂料的方法，其特征在于，包括：
基础漆混合制作成彩色粒子；
将彩色粒子与胶体混合进行胶化，形成保护胶体；
将无机基料加入到保护胶体中，陈化得到所述水包水多彩涂料。