CN108251231A - A kind of electrode clean agent and preparation method thereof - Google Patents
A kind of electrode clean agent and preparation method thereof Download PDFInfo
- Publication number
- CN108251231A CN108251231A CN201810165920.7A CN201810165920A CN108251231A CN 108251231 A CN108251231 A CN 108251231A CN 201810165920 A CN201810165920 A CN 201810165920A CN 108251231 A CN108251231 A CN 108251231A
- Authority
- CN
- China
- Prior art keywords
- parts
- clean agent
- electrode clean
- electrode
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of electrode clean agent and preparation method thereof, the electrode clean agent includes:15 parts of sodium citrate, 35 parts of sodium carbonate, 0.8 3 parts of sodium alginate, 48 parts of carboxymethyl cellulose, 0.5 3 parts of neopelex, 0.5 3 parts of amber acid diester sulfonate, 16 parts of Fatty acid methyl ester ethoxylate, 80 100 parts of water;The cleaning agent property is mild, without irritation, does not generate corrosion to electrode, and cleaning effect is good, can effectively remove the dirt of electrode surface attachment, while has the effect of sterilization, and will not generate volatile organic matter, meets the requirement of environmental protection;The method is easy to operate, easy to implement, is suitble to large-scale production.
Description
Technical field
The present invention relates to cleaning agent and its preparing technical field, more particularly to a kind of electrode clean agent and preparation method thereof.
Background technology
Electrode can be adhered to dirty with being difficult to avoid that in use by metal ion attachment, grease type, protein etc.
Dye.The aqueous and oiliness of traditional electrode clean agent point;Aqueous electrode clean agent is mainly that relatively low sour or weakly alkaline of concentration is washed
Agent is washed, to electrode to generating certain corrosiveness, shortens the service life of electrode, and acid after use or alkali are needed at neutralization
Reason, wastes medicament to a certain extent;Oiliness electrode clean agent is mainly organic solvent, after being cleaned using the agent of oiliness electrode clean
Electrode need to dry, remaining organic solvent can volatilize in phase environment on electrode, not only endanger the health of staff, but also
Also pollute environment.
As it can be seen that the prior art could be improved and improve.
Invention content
Part in view of above-mentioned deficiencies of the prior art, the purpose of the present invention is to provide a kind of electrode clean agent and its preparations
Method, it is intended to it is above-mentioned insufficient to solve the problems, such as that electrode clean agent in the prior art has.
In order to achieve the above object, this invention takes following technical schemes:
A kind of electrode clean agent includes the ingredient of following parts by weight:
1-5 parts of sodium citrate,
3-5 parts of sodium carbonate,
0.8-3 parts of sodium alginate,
4-8 parts of carboxymethyl cellulose,
0.5-3 parts of neopelex,
0.5-3 parts of amber acid diester sulfonate,
1-6 parts of Fatty acid methyl ester ethoxylate,
80-100 parts of water.
In the electrode clean agent, the parts by weight of sodium alginate are 2.8 parts in the electrode clean agent.
In the electrode clean agent, neopelex in the electrode clean agent, amber acid diester sulfonate and
The weight ratio of Fatty acid methyl ester ethoxylate is 1: 1: 2.
In the electrode clean agent, the electrode clean agent includes the carboxymethyl cellulose of 6 parts by weight.
In the electrode clean agent, the biennial wormwood extract of 0.3-1 parts by weight is further included in the electrode clean agent.
A kind of preparation method of electrode clean agent, including:Sodium citrate, sodium carbonate and sodium alginate are mixed according to proportioning
It stirs evenly, cools down at 35~50 DEG C afterwards, stand 40min;Then other raw materials are added in, at the uniform velocity stir 2.5h at room temperature,
And PH to 6~8 is adjusted, obtain the electrode clean agent.
Advantageous effect:
The present invention provides a kind of electrode clean agent and preparation method thereof, the cleaning agent property is mild, right without irritation
Electrode does not generate corrosion, and cleaning effect is good, can effectively remove the dirt of electrode surface attachment, while has the effect of sterilization,
And volatile organic matter will not be generated, meet the requirement of environmental protection;The method is easy to operate, easy to implement, is suitble to big rule
Mould produces.
Specific embodiment
The present invention provides a kind of electrode clean agent and preparation method thereof, to make the purpose of the present invention, technical solution and effect
Clearer, clear and definite, the present invention is described in more detail by the following examples.It should be appreciated that specific reality described herein
Example is applied only to explain the present invention, is not intended to limit the present invention.
The present invention provides a kind of electrode clean agent, includes the ingredient of following parts by weight:
1-5 parts of sodium citrate,
3-5 parts of sodium carbonate,
0.8-3 parts of sodium alginate,
4-8 parts of carboxymethyl cellulose,
0.5-3 parts of neopelex,
0.5-3 parts of amber acid diester sulfonate,
1-6 parts of Fatty acid methyl ester ethoxylate,
80-100 parts of water.
The dirt-removing power of neopelex is strong, and foaming power and foam stability and chemical stability are good, and
Sufficient raw, production cost are low;Amber acid diester sulfonate have excellent moistening permeability, performance is mild, to skin,
Eye irritation is low, and raw material is abundant;Fatty acid methyl ester ethoxylate has efficient cleaning performance, and having in water is preferable
Dissolubility has good resistance to hard water ability, can prevent the accumulation of dirt in cleaning solution and anti-stained electrode;Detergent alkylate
Sodium sulfonate and amber acid diester sulfonate are used cooperatively with Fatty acid methyl ester ethoxylate, and synergistic effect makes the detergent
Decontamination performance it is more excellent, can quickly and completely remove the dirt of electrode surface.
Using the electrode clean agent of mentioned component, operating personnel, which are in direct contact, to generate stimulation to human hand, and property is mild,
And dirt-removing power is eager to excel than general commercially available aqueous electrode clean agent or oiliness electrode clean agent, and the time of consuming is short, and
Residual will not be generated.
Preferably, the parts by weight of sodium alginate are 2.8 parts in the electrode clean agent;Sodium alginate can improve the electricity
The stability of pole cleaning agent makes its system keep uniform, ensures its cleaning capacity;Applicant proves through a large number of experiments, institute
When the parts by weight for stating sodium alginate in electrode clean agent are 2.8 parts, the electrode clean agent is stablized the most, and viscosity is most suitable for.
Preferably, neopelex, amber acid diester sulfonate and Fatty acid methyl ester in the electrode clean agent
The weight ratio of ethoxylate is 1: 1: 2;Applicant obtains by many experiments, when above-mentioned three kinds of substances use the proportioning, institute
The cleaning effect for stating electrode clean agent is ideal, and the moderate foam generated, easily rinses, will not generate residual.
Preferably, the electrode clean agent includes the carboxymethyl cellulose of 6 parts by weight;Carboxymethyl cellulose property is steady
It is fixed, the stability of the motor cleaning agent can be improved, extends its pot-life, and with certain sterilization, anti-corrosion function;Shen
It asks someone by a large amount of it is demonstrated experimentally that when the content of carboxymethyl cellulose is 6 parts by weight, generated effect is most preferable.
Further, the biennial wormwood extract of 0.3-1 parts by weight is further included in the electrode clean agent;Argy wormwood has special perfume (or spice)
Taste has effects that sterilizing, can kill the electrode clean agent and clean the bacterium on motor surface, extend electrode clean
The holding time of agent.
A kind of preparation method of electrode clean agent, including:Sodium citrate, sodium carbonate and sodium alginate are mixed according to proportioning
It stirs evenly, cools down at 35~50 DEG C afterwards, stand 40min;Then other raw materials are added in, at the uniform velocity stir 2.5h at room temperature,
And PH to 6~8 is adjusted, obtain the electrode clean agent.
The application method of the electrode clean agent is:Electrode is immersed in the cleaning at normal temperatures or at 30~50 DEG C
Then 5~10min in agent is rinsed 1~2 time with deionized water, naturally dry or is dried with filter paper;Operating personnel are using this
Mask and gloves need not be worn during cleaning solution, direct skin contact will not generate stimulation, easy to use.
Embodiment 1
The electrode clean agent includes the ingredient of following parts by weight:
5 parts of sodium citrate,
3 parts of sodium carbonate,
2.8 parts of sodium alginate,
6 parts of carboxymethyl cellulose,
2.5 parts of neopelex,
2.5 parts of amber acid diester sulfonate,
5 parts of Fatty acid methyl ester ethoxylate,
0.8 part of biennial wormwood extract,
80 parts of water;
The preparation method of the motor cleaning agent, including:By sodium citrate, sodium carbonate and sodium alginate according to proportioning mix after
It stirs evenly, cools down at 40 DEG C, stand 40min;Then other raw materials are added in, at the uniform velocity stir 2.5h at room temperature, and adjust PH
To 7, the electrode clean agent is obtained.
Embodiment 2
The electrode clean agent includes the ingredient of following parts by weight:
1 part of sodium citrate,
5 parts of sodium carbonate,
0.8 part of sodium alginate,
4 parts of carboxymethyl cellulose,
3 parts of neopelex,
1.0 parts of amber acid diester sulfonate,
2 parts of Fatty acid methyl ester ethoxylate,
0.5 part of biennial wormwood extract,
90 parts of water;
The preparation method of the motor cleaning agent, including:By sodium citrate, sodium carbonate and sodium alginate according to proportioning mix after
It stirs evenly, cools down at 35 DEG C, stand 40min;Then other raw materials are added in, at the uniform velocity stir 2.5h at room temperature, and adjust PH
To 6.5, the electrode clean agent is obtained.
Embodiment 3
The electrode clean agent includes the ingredient of following parts by weight:
3 parts of sodium citrate,
4 parts of sodium carbonate,
1.4 parts of sodium alginate,
8 parts of carboxymethyl cellulose,
0.3 part of neopelex,
0.5 part of amber acid diester sulfonate,
1 part of Fatty acid methyl ester ethoxylate,
1 part of biennial wormwood extract,
95 parts of water;
The preparation method of the motor cleaning agent, including:By sodium citrate, sodium carbonate and sodium alginate according to proportioning mix after
It stirs evenly, cools down at 45 DEG C, stand 40min;Then other raw materials are added in, at the uniform velocity stir 2.5h at room temperature, and adjust PH
To 6, the electrode clean agent is obtained.
Embodiment 4
The electrode clean agent includes the ingredient of following parts by weight:
2 parts of sodium citrate,
3.5 parts of sodium carbonate,
3 parts of sodium alginate,
5 parts of carboxymethyl cellulose,
1.5 parts of neopelex,
3 parts of amber acid diester sulfonate,
6 parts of Fatty acid methyl ester ethoxylate,
0.3 part of biennial wormwood extract,
100 parts of water;
The preparation method of the motor cleaning agent, including:By sodium citrate, sodium carbonate and sodium alginate according to proportioning mix after
It stirs evenly, cools down at 50 DEG C, stand 40min;Then other raw materials are added in, at the uniform velocity stir 2.5h at room temperature, and adjust PH
To 7.5, the electrode clean agent is obtained.
Embodiment 5
The electrode clean agent includes the ingredient of following parts by weight:
4 parts of sodium citrate,
4.5 parts of sodium carbonate,
2.2 parts of sodium alginate,
7 parts of carboxymethyl cellulose,
2 parts of neopelex,
2 parts of amber acid diester sulfonate,
4 parts of Fatty acid methyl ester ethoxylate,
0.6 part of biennial wormwood extract,
85 parts of water;
The preparation method of the motor cleaning agent, including:By sodium citrate, sodium carbonate and sodium alginate according to proportioning mix after
It stirs evenly, cools down at 42 DEG C, stand 40min;Then other raw materials are added in, at the uniform velocity stir 2.5h at room temperature, and adjust PH
To 8, the electrode clean agent is obtained.
Please refer to table 1, the electrode clean agent prepared by above-described embodiment 1-5 and general commercially available aqueous electrode clean agent and
The cleaning performance comparing result of oiliness electrode clean agent is:
Cleaning agent | Scavenging period/min | Cleaning temperature | Volatility | Corrosivity | Cleaning performance |
Embodiment 1 | 8 | Room temperature | Nothing | Nothing | It is rinsed 1~2 time with deionized water after cleaning, surface-brightening, no dirt residual |
Embodiment 2 | 8 | Room temperature | Nothing | Nothing | It is rinsed 1~2 time with deionized water after cleaning, surface-brightening, no dirt residual |
Embodiment 3 | 8 | Room temperature | Nothing | Nothing | It is rinsed 1~2 time with deionized water after cleaning, surface-brightening, no dirt residual |
Embodiment 4 | 8 | Room temperature | Nothing | Nothing | It is rinsed 1~2 time with deionized water after cleaning, surface-brightening, no dirt residual |
Embodiment 5 | 8 | Room temperature | Nothing | Nothing | It is rinsed 1~2 time with deionized water after cleaning, surface-brightening, no dirt residual |
Comparison 1(It is aqueous) | 15 | Room temperature | There is Determining Micro Acid volatilization | Not directly contact | It is rinsed 4~5 times with deionized water after cleaning, there is oily matter residual |
Comparison 2(Oiliness) | 15 | Room temperature | There are a large amount of volatilizations | Not directly contact | It is rinsed 2~3 times with deionized water after cleaning, the dirt of metal ion attachment or caking capacity is difficult to fully erased |
As can be seen from the above table, the present invention in the electrode clean agent compared with commercially available aqueous or oiliness electrode clean agent,
Not only scavenging period is short, but also the effect cleaned also has apparent advantage.
It, can according to the technique and scheme of the present invention and its hair it is understood that for those of ordinary skills
Bright design is subject to equivalent substitution or change, and all these changes or replacement should all belong to the guarantor of appended claims of the invention
Protect range.
Claims (6)
1. a kind of electrode clean agent, which is characterized in that include the ingredient of following parts by weight:
1-5 parts of sodium citrate,
3-5 parts of sodium carbonate,
0.8-3 parts of sodium alginate,
4-8 parts of carboxymethyl cellulose,
0.5-3 parts of neopelex,
0.5-3 parts of amber acid diester sulfonate,
1-6 parts of Fatty acid methyl ester ethoxylate,
80-100 parts of water.
2. electrode clean agent according to claim 1, which is characterized in that the weight of sodium alginate in the electrode clean agent
Part is 2.8 parts.
3. electrode clean agent according to claim 1, which is characterized in that dodecyl benzene sulfonic acid in the electrode clean agent
The weight ratio of sodium, amber acid diester sulfonate and Fatty acid methyl ester ethoxylate is 1: 1: 2.
4. electrode clean agent according to claim 1, which is characterized in that the electrode clean agent includes 6 parts by weight
Carboxymethyl cellulose.
5. electrode clean agent according to claim 1, which is characterized in that 0.3-1 weights are further included in the electrode clean agent
Measure the biennial wormwood extract of part.
6. a kind of preparation method of electrode clean agent as described in claim 1-4, which is characterized in that including:By sodium citrate,
Sodium carbonate and sodium alginate stir evenly after being mixed according to proportioning at 35~50 DEG C, cool down, and stand 40min;Then it is added in
Its raw material at the uniform velocity stirs 2.5h at room temperature, and adjusts PH to 6~8, obtains the electrode clean agent.