CN108251200A - A kind of clean type copper-aluminum composite board cold rolling oil and preparation method thereof - Google Patents
A kind of clean type copper-aluminum composite board cold rolling oil and preparation method thereof Download PDFInfo
- Publication number
- CN108251200A CN108251200A CN201810167831.6A CN201810167831A CN108251200A CN 108251200 A CN108251200 A CN 108251200A CN 201810167831 A CN201810167831 A CN 201810167831A CN 108251200 A CN108251200 A CN 108251200A
- Authority
- CN
- China
- Prior art keywords
- rolling oil
- composite board
- aluminum composite
- oil
- cold rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of clean type copper-aluminum composite board cold rolling oil and preparation method thereof, belongs to Lubrication Technology field.The weight percent of lubricant is:It is oily based on mineral oil D85, D100, D115:89.5%~90.65%;Extreme pressure agent includes dialkyl dithiophosphate, poly alkyl alcohol glycol ester and acid dibutyl phosphite:0.3%~0.8%;Oiliness improver includes lauric acid and laruyl alcohol and butyl stearate:9.0%~9.6%;Corrosion inhibiter dimercaptothiodiazole:0.05%~0.1%.The present invention uses common aluminum cold-rolling oil, add in phosphorus system and alkoxide extreme pressure anti-wear additives, ROLLING OIL film strength can be effectively improved, using laruyl alcohol, lauric acid and butyl stearate as compound oiliness improver, it is effectively guaranteed the stability of ROLLING OIL antifriction ability, a small amount of dimercaptothiodiazole is also added into as corrosion inhibiter simultaneously, for preventing copper base surface oxidation.Prepared ROLLING OIL has both extreme-pressure anti-wear, corrosion-resistant and surface cleaning.
Description
Technical field
The present invention relates to technical field of lubricant, for the lubrication in the Copper-Aluminum compound strip operation of rolling, particularly
A kind of clean type copper-aluminum composite board cold rolling oil and preparation method thereof.
Background technology
Copper-Aluminum compound strip has the light inexpensive double grading of the highly conductive of copper, heat conduction and aluminium concurrently, is aerospace, electricity
The emerging strategics industry key function material such as son, generation of electricity by new energy, automobile power cell, LED illumination, communication.At present individually
The lubricating oil produced by Copper-Aluminum compound plate sheet and strip is relatively fewer, and imported oil is expensive.Copper-Aluminum compound strip rolled
Technological lubrication problem in journey becomes increasingly conspicuous.Copper-aluminum composite board layers of copper, aluminium layer, boundary layer deformability be not in the operation of rolling
Together, and higher there are contact in the operation of rolling, contact area is larger, and sliding speed is larger, and frictional surface temperature is high and after rolling
The features such as surface quality, it is desirable that ROLLING OIL has good greasy property, and the resistance of deformation for efficiently reducing copper Aluminum sheets is poor,
It can guarantee the spatter property of composite surface simultaneously, improve strip surface quality.A kind of stability is invented, extreme pressure property, wear resistence is good,
The ROLLING OIL of annealing spatter property and fine corrosion resistance becomes the task of top priority of production copper-aluminum composite board.
Invention content
The object of the present invention is to provide a kind of stability, lubricity, extreme pressure anti-wear, annealing spatter property is excellent and at low cost
Copper-aluminum composite board ROLLING OIL.
The present invention is achieved by the following technical programs:A kind of clean type copper-aluminum composite board cold rolling oil, it is main
Component and shared weight percent are as follows.
The weight of extreme pressure agent antiwear additive dialkyl dithiophosphate, poly alkyl alcohol glycol ester and acid dibutyl phosphite
Amount is than being 1:1:1~3:3:2;Oiliness improver selects lauric acid and laruyl alcohol to be compounded with butyl stearate, and compounding weight ratio is 1:1:4
~3:3:2;Dimercaptothiodiazole is introduced as corrosion inhibiter simultaneously, to prevent copper aluminum substrate surface oxidation discoloration problem.
The production method of ROLLING OIL as described above:Making step is:By base oil D85, D100 and D115, oiliness improver bay
Acid, laruyl alcohol, butyl stearate, extreme pressure agent dialkyl dithiophosphate, poly alkyl alcohol ethylene glycol phosphate, acid phosphorous acid
Dibutyl ester and corrosion inhibiter dimercaptothiodiazole sequentially add reaction kettle, are heated under the conditions of being 80-120 revs/min in rotating speed
Stirring when temperature reaches 70~80 DEG C, keeps the temperature and continues stirring 45-55 minute, then stop heating and continues to stir to room temperature, obtain
To clear homogeneous oil body, that is, it is made into ROLLING OIL.
Through above-mentioned technical proposal, the beneficial effects of the present invention are:
1st, using oil based on low viscosity mineral oil D85, D100 and D115, aluminum substrate can be effectively ensured and roll rear surface
Spatter property;Using lauric acid, laruyl alcohol and butyl stearate as oiliness improver so that ROLLING OIL not only has relatively low friction system
It counts and stabilization can be kept during long mill;By adding in dialkyl dithiophosphate, poly alkyl alcohol glycol ester and acidity
Dibutyl phosphite is simultaneously compounded so that prepared ROLLING OIL film strength reaches more than 600N, meets the rolling of copper plate/strip foil
It needs, and improves ROLLING OIL abrasion resistance;In addition the surface oxidation problem of copper base can be improved by adding in a small amount of corrosion inhibiter.
2nd, ROLLING OIL of the invention can be used for copper-aluminum composite board cold rolling process, the copper obtained using the rolling lubrication
Aluminum composite plate minimum rolled thickness is 45 μm, and composite plate rolls that rear template is smooth, and surface quality is controlled.
Specific embodiment
Below by way of specific embodiment to the present invention carry out more in detail description, but the present invention be not limited only to it is following
Embodiment.
Embodiment 1
1 specific each component of embodiment formula is as shown in the table.
According to above-mentioned each component formula, by base oil D100, lauric acid, laruyl alcohol, butyl stearate, dialkyl dithio
Phosphate, poly alkyl alcohol ethylene glycol phosphate, acid dibutyl phosphite and dimercaptothiodiazole sequentially add, oiliness improver bay
The weight ratio of acid, laruyl alcohol and butyl stearate is 1:1:4;Extreme pressure agent dialkyl dithiophosphate, poly alkyl alcohol ethylene glycol
The weight ratio of phosphate and acid dibutyl phosphite is 3:1:1;Corrosion inhibiter dimercaptothiodiazole accounts for the 0.1% of complete oily proportion.
Rotating speed is placed in carry out heating stirring in 80-120 revs/min of reaction kettle, when temperature reaches 70~80 DEG C, heat preservation is simultaneously persistently stirred
It mixes 45-55 minutes, then stops heating and continue stirring to room temperature, obtain the uniform oil body of pale yellow transparent.
Embodiment 2
1 specific each component of embodiment formula is as shown in the table.
Serial number | Ingredient names | Weight (g) |
1 | D85 | 90.05 |
2 | Dialkyl dithiophosphate | 0.1 |
3 | Poly alkyl alcohol ethylene glycol phosphate | 0.1 |
4 | Acid dibutyl phosphite | 0.1 |
5 | Lauric acid | 3.6 |
6 | Laruyl alcohol | 3.6 |
7 | Butyl stearate | 2.4 |
8 | Dimercaptothiodiazole | 0.05 |
According to 2 each component formula of embodiment, by base oil D85, lauric acid, laruyl alcohol, butyl stearate, dialkyl disulfides
Substituted phosphate, poly alkyl alcohol ethylene glycol phosphate, acid dibutyl phosphite and dimercaptothiodiazole sequentially add, the oiliness improver moon
The weight ratio of cinnamic acid, laruyl alcohol and butyl stearate is 3:3:2;Extreme pressure agent dialkyl dithiophosphate, poly alkyl alcohol second two
The weight ratio of alcohol phosphate and acid dibutyl phosphite is 1:1:1;Corrosion inhibiter dimercaptothiodiazole accounts for complete oily proportion
0.05%.Rotating speed is placed in carry out heating stirring in 80-120 revs/min of reaction kettle, when temperature reaches 70~80 DEG C, heat preservation
And continue stirring 45-55 minutes, then stop heating and continue stirring to room temperature, obtain the uniform oil body of water white transparency.
Embodiment 3
1 specific each component of embodiment formula is as shown in the table.
Serial number | Ingredient names | Weight (g) |
1 | D115 | 89.8 |
2 | Dialkyl dithiophosphate | 0.1 |
3 | Poly alkyl alcohol ethylene glycol phosphate | 0.3 |
4 | Acid dibutyl phosphite | 0.1 |
5 | Lauric acid | 1.6 |
6 | Laruyl alcohol | 1.6 |
7 | Butyl stearate | 6.4 |
8 | Dimercaptothiodiazole | 0.1 |
According to above-mentioned each component formula, by D115, butyl stearate, laruyl alcohol, lauric acid, dialkyl dithiophosphoric acid
Ester, poly alkyl alcohol ethylene glycol phosphate, acid dibutyl phosphite and dimercaptothiodiazole sequentially add, oiliness improver lauric acid,
The weight ratio of laruyl alcohol and butyl stearate is 1:1:4;Extreme pressure agent dialkyl dithiophosphate, poly alkyl alcohol ethylene glycol phosphoric acid
The weight ratio of ester and acid dibutyl phosphite is 1:3:1;Corrosion inhibiter dimercaptothiodiazole accounts for the 0.1% of complete oily proportion.Turning
Speed is carries out heating stirring in 80-120 revs/min of reaction kettle, when temperature reaches 70-80 DEG C, keeps the temperature and continues to stir 45-55 points
Clock then stops heating and continues stirring to room temperature, obtains the uniform oil body of water white transparency.
2nd, product performance index obtained is as follows:
Claims (3)
1. a kind of clean type copper-aluminum composite board cold rolling oil, it is characterised in that key component and shared weight percent are as follows:
2. clean type copper-aluminum composite board cold rolling oil as described in claim 1, it is characterised in that extreme pressure agent antiwear additive dialkyl group
The weight ratio of phosphorodithioate, poly alkyl alcohol glycol ester and acid dibutyl phosphite is 1:1:1~3:3:2;Oiliness improver
Lauric acid and laruyl alcohol is selected to be compounded with butyl stearate, compounding weight ratio is 1:1:4~3:3:2.
3. the preparation method of clean type copper-aluminum composite board cold rolling oil as described in claim 1, it is characterised in that making step
For:By base oil D85, D100 and D115, oiliness improver lauric acid, laruyl alcohol, butyl stearate, extreme pressure agent dialkyl dithio phosphorus
Acid esters, poly alkyl alcohol ethylene glycol phosphate, acid dibutyl phosphite and corrosion inhibiter dimercaptothiodiazole sequentially add reaction kettle,
In rotating speed to carry out heating stirring under the conditions of 80-120 revs/min, when temperature reaches 70~80 DEG C, keep the temperature and continue to stir 45-
55 minutes, then stop heating and continue stirring to room temperature, obtain clear homogeneous oil body, that is, be made into ROLLING OIL.