CN108246969A - 一种低加入量消失模涂料多功能添加剂 - Google Patents
一种低加入量消失模涂料多功能添加剂 Download PDFInfo
- Publication number
- CN108246969A CN108246969A CN201810084315.7A CN201810084315A CN108246969A CN 108246969 A CN108246969 A CN 108246969A CN 201810084315 A CN201810084315 A CN 201810084315A CN 108246969 A CN108246969 A CN 108246969A
- Authority
- CN
- China
- Prior art keywords
- lost foam
- agent
- foam paint
- additive
- low addition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低加入量消失模涂料多功能添加剂。该添加剂为粉末状,是由以下重量比的原料制备而成:粘结剂38‑49%、抗裂剂16‑27%,透气剂5‑8.5%,悬浮剂28‑39%,消泡剂1‑5%,高温粘结剂5‑10%,余量为防腐剂。每种原材料均由市场外购,不用再单独深加工。制备添加剂时将各种粉状原料按所需比例称取,依次加入干粉混合机搅拌混合30—40分钟,然后出料包装,即可对外销售。使用本添加剂配制干粉消失模涂料时,按耐火粉料与添加剂之比为100:5的比例配制,用干粉混合机搅拌混均匀即为成品消失模涂料。本添加剂入量低、质量稳定,完全颠覆了市场普遍销售加入量100:10的添加剂,使消失模铸造厂家节省50%的加入量大大降低了生产成本,提高了市场竞争力。
Description
技术领域
本发明涉及消失模涂料技术领域,尤其涉及一种低加入量消失模涂料多功能添加剂。
背景技术
消失模涂料在消失模铸造工艺中起着至关重要的作用,消失模铸造厂家过去有的外购成品涂料、有的购买消失模涂料添加剂自配涂料,来满足生产需求。最近几年市场竞争急剧激烈,铸造厂家外购成品涂料成本太高,长途运输不便,大大影响企业正常生产。购买市场销售的传统消失模涂料添加剂加入量一般是占耐火粉料的10%,造成涂料成本居高不下。根据这种市场环境下,本技术应运而生,在个方面技术指标达到使用要求的情况下,加入量比传统添加剂减少50%,大大降低铸造企业生产成本,减少了浪费,提高了企业竞争力。
发明内容
本发明的目的在于提供一种低加入量消失模涂料多功能添加剂,以解决上述技术问题。
为实现上述目的本发明采用以下技术方案:一种低加入量消失模涂料多功能添加剂,该添加剂为粉末状,是由以下重量比的原料制备而成:粘结剂38-49%、抗裂剂16-27%,透气剂5-8.5%,悬浮剂28-39%,消泡剂1-5%,高温粘结剂5-10%,余量为防腐剂。
作为本发明进一步的方案,所述粘结剂为玉米淀粉、聚乙烯醇粉末、可再分散乳胶粉、水溶性酚醉醛树脂、羟丙基甲基纤维素中的任意两种或两种以上。
作为本发明进一步的方案,抗裂剂为黄麻纤维、聚丙稀短纤维,
作为本发明进一步的方案,透气剂为木质纤维,木屑、碳化稻科中的任一种。
作为本发明进一步的方案,悬浮剂为凹凸棒土、海泡石粉、钙基澎润土、硅酸镁铝中的任意两种或两种以上。
作为本发明进一步的方案,消泡剂为有机硅消泡剂。
作为本发明进一步的方案,高温粉结剂为磷酸二氢铝、三聚磷酸钠、六偏磷酸钠中的任一种。
作为本发明进一步的方案,防腐剂为苯甲酸钠、丙酸钙、脱氢醋酸钠中的任一种。
一种低加入量消失模涂料多功能添加剂的使用方法包括如下步骤:使用时将100份重量的耐火粉料加入5份的该添加剂混合加入8份的水搅拌30分钟,根据使用粘度再加水调节搅匀即可使用。
本发明的有益效果是:本发明的方法配制简单,用量少,成本低,可以上从根本上解决上述问题,从而不再为消失模涂料而影响铸件质量;配制的涂料适用于所有材质——铸铁、铸钢、合金钢、高锰钢等消失模铸造;本添加剂使用范围广泛,能与各种耐火材料一次性配制,而不需要再添加任何原料。1吨添加剂能配23吨粉状消失模涂料,可配制40吨以上的液体消失模涂料,而市面上销售的添加剂只能配制11吨粉状消失模涂料,19吨液体消失模涂料,为消失模铸造厂家大大的节约了生产成本。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
生产1000KG消失模涂料粉状添加剂,称取玉米淀粉270KG,水溶性酚酫树脂20KG,凹凸棒土280KG,硅酸镁铝90KG,黄麻纤维60KG、木质纤维60KG、磷酸二氢铝50KG、木屑40KG、有机硅消包剂101KG、苯甲酸钠30KG、羟丙基甲级纤维90KG,加入混合机混合搅拌30分钟可出料包装。
实施例2
生产1000KG消失模涂料粉状添加剂,称取玉米淀粉230KG、水溶性酚酫树脂30KG、凹凸棒土250KG,硅酸镁铝120KG,黄麻纤维40KG、木质纤维80KG、磷酸二氢铝40KG、木屑50KG、有机硅消包剂31KG、苯甲酸钠3KG、羟丙基甲级纤维100KG,以上原料加入混合机混合搅拌30分钟即可出料包装。
该消失模涂料粉状添加剂使用时将100份重量的耐火粉料加入5份的本添加剂混合加入8份的水搅拌30分钟,根据使用粘度再加水调节搅匀即可使用。使用本添加剂配制干粉消失模涂料时,按耐火粉料与添加剂之比为100:5的比例配制,用干粉混合机搅拌混合均匀即为成品消失模涂料。本添加剂入量低、质量稳定,完全颠覆了市场普遍销售加入量100:10的添加剂,使消失模铸造厂家节省一半的加入量大大降低了生产成本,提高了市场竞争力。
本产品配制的涂料能达到铸件光洁易脱砂的良好效果,在铸铁、碳钢、高锰钢等应中采用廉价的石英粉、铝矾土、镁橄榄石粉、棕钢玉、生产优质的铸钢、铸铁件。
尽管已经示出和描述了本发明的实施例,对于本领域的普通技术人员而言,可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种低加入量消失模涂料多功能添加剂,其特征在于,该添加剂为粉末状,是由以下重量比的原料制备而成:粘结剂38-49%、抗裂剂16-27%,透气剂5-8.5%,悬浮剂28-39%,消泡剂1-5%,高温粘结剂5-10%,余量为防腐剂。
2.根据权利要求1所述的一种低加入量消失模涂料多功能添加剂,其特征在于,所述粘结剂为玉米淀粉、聚乙烯醇粉末、可再分散乳胶粉、水溶性酚醛树脂、羟丙基甲基纤维素中的任意两种或两种以上。
3.根据权利要求1所述的一种低加入量消失模涂料多功能添加剂,其特征在于,抗裂剂为黄麻纤维、聚丙稀短纤维,
根据权利要求1所述的一种低加入量消失模涂料多功能添加剂,其特征在于,透气剂为木质纤维,木屑、碳化稻壳中的其中一种。
4.根据权利要求1所述的一种低加入量消失模涂料多功能添加剂,其特征在于,悬浮剂为凹凸棒土、海泡石粉、钙基澎润土、硅酸镁铝中的任意两种或两种以上。
5.根据权利要求1所述的一种低加入量消失模涂料多功能添加剂,其特征在于,消泡剂为有机硅消泡剂。
6.根据权利要求1所述的一种低加入量消失模涂料多功能添加剂,其特征在于,高温粘结剂为磷酸二氢铝、三聚磷酸钠、六偏磷酸钠中的任一种。
7.根据权利要求1所述的一种低加入量消失模涂料多功能添加剂,其特征在于,防腐剂为苯甲酸钠、丙酸钙、脱氢醋酸钠中的任一种。
8.一种如权利要求1-8任一所述的低加入量消失模涂料多功能添加剂的使用方法,其特征在于,包括如下步骤:使用时将100份重量的耐火粉料加入5份的该添加剂混合加入8份的水搅拌30分钟,根据使用粘度再加水调节搅匀即可使用。