CN112570645A - 一种消失模铸造涂料添加剂 - Google Patents

一种消失模铸造涂料添加剂 Download PDF

Info

Publication number
CN112570645A
CN112570645A CN202011613105.6A CN202011613105A CN112570645A CN 112570645 A CN112570645 A CN 112570645A CN 202011613105 A CN202011613105 A CN 202011613105A CN 112570645 A CN112570645 A CN 112570645A
Authority
CN
China
Prior art keywords
coating
parts
lost foam
foam casting
additive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202011613105.6A
Other languages
English (en)
Inventor
张国华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Huaen Industrial Co ltd
Original Assignee
Shanxi Huaen Industrial Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Huaen Industrial Co ltd filed Critical Shanxi Huaen Industrial Co ltd
Priority to CN202011613105.6A priority Critical patent/CN112570645A/zh
Publication of CN112570645A publication Critical patent/CN112570645A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种消失模铸造涂料添加剂,涉及消失模涂料,以达到提高涂料透气性的目的。一种消失模铸造涂料添加剂,由下列重量份的各组分组成:木屑微粉7‑8、六偏磷酸钠1‑1.5、异丁叉二脲1‑2。本发明可广泛适用于市售的各种消失模铸造涂料,其中异丁叉二脲释氮,六偏磷酸钠使木屑微粉稳定分散,木屑在高温下燃烧,使得涂层中产生大量的微小气泡,达到显著提高涂料透气性的目的。

Description

一种消失模铸造涂料添加剂
技术领域
本发明涉及消失模涂料,具体涉及一种消失模铸造涂料添加剂。
背景技术
消失模铸造技术是将与铸件尺寸形状相似的发泡塑料模型粘结组合成模型簇,刷涂耐火涂层并烘干后,埋在干石英砂中振动造型,在一定条件下浇注液体金属,使模型气化并占据模型位置,凝固冷却后形成所需铸件的方法。与传统的铸造技术相比,由于采用极易气化的泡沫塑料制作模型,无需取模与制作模芯、无分型面,因而无飞边毛刺,该工艺过程完全摒弃了传统工艺工序复杂、工作过程污染物排放量大、工人劳动强度高的不利因素,实现的是一种工序简单,效率高,近无公害的清洁生产。
传统的铸造涂料只是在铸件和铸型中间起到阻挡隔离作用,达到防粘砂目的,从防止铸件粘砂的角度来说,白模外表涂挂涂料,而且涂层要尽可能的致密,但是致密的涂层不利于聚苯乙烯白模气化后生成的气体往外逸散。
本发明研发目的在于提高涂料透气性。
发明内容
本发明的目的是提供一种消失模铸造涂料添加剂,以达到提高涂料透气性的目的。
本发明是通过以下技术方案实现的:
一种消失模铸造涂料添加剂,由下列重量份的各组分组成:
木屑微粉7-8、六偏磷酸钠1-1.5、异丁叉二脲1-2。
进一步地,所述的木屑微粉的目数为325-400。
优选地,由木屑微粉7份、六偏磷酸钠1.5份、异丁叉二脲2份组成。
使用时,将本发明添加剂添加到传统的消失模铸造涂料中,混合均匀即可,其中添加量为涂料总质量的4-6%,本发明添加剂中六偏磷酸钠露置于空气中逐渐而呈粘胶状物、可以促使木屑微粉均匀稳定的分散在涂料中,当高温的铁水浇铸到砂箱中的模族后,涂料中的木屑微粉熔化,形成细小的空隙,而异丁叉二脲具有缓慢释放氮素的性能,可以提高木屑微粉的燃烧,从而进一步提高和保证涂料的透气性。
本发明可广泛适用于市售的各种消失模铸造涂料,其中异丁叉二脲释氮,六偏磷酸钠使木屑微粉稳定分散,木屑在高温下燃烧,使得涂层中产生大量的微小气泡,达到显著提高涂料透气性的目的。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例1
准确称取目数为325-400的木屑微粉3.5Kg、六偏磷酸钠0.5Kg、异丁叉二脲1Kg,混合均匀,添加到125Kg的普通市售消失模铸造涂料中即可。
实施例2
准确称取目数为325-400的木屑微粉4Kg、六偏磷酸钠0.75Kg、异丁叉二脲0.5Kg,混合均匀,添加到105Kg的普通市售消失模铸造涂料中即可。
实施例3
准确称取目数为325-400的木屑微粉3.75Kg、六偏磷酸钠0.6Kg、异丁叉二脲0.75Kg,混合均匀,添加到85Kg的普通市售消失模铸造涂料中即可。
实施例4
准确称取目数为325-400的木屑微粉3. 5Kg、六偏磷酸钠0.75Kg、异丁叉二脲1Kg,混合均匀,添加到105Kg的普通市售消失模铸造涂料中即可。
经对比实验发现,相比普通涂料,本发明添加剂可以显著提高涂层透气性,模样能充分燃烧,铸型内腔无附着的黑釉,铸件无夹渣、局部增碳等缺陷。
最后说明的是,以上实施例仅用以说明本发明的技术方案而非限制,尽管参照较佳实施例对本发明进行了详细说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的宗旨和范围,其均应涵盖在本发明的权利要求范围当中。

Claims (3)

1.一种消失模铸造涂料添加剂,其特征在于,由下列重量份的各组分组成:
木屑微粉7-8、六偏磷酸钠1-1.5、异丁叉二脲1-2。
2.根据权利要求1所述的一种消失模铸造涂料添加剂,其特征在于,所述的木屑微粉的目数为325-400。
3.根据权利要求1或2所述的一种消失模铸造涂料添加剂,其特征在于,由木屑微粉7份、六偏磷酸钠1.5份、异丁叉二脲2份组成。
CN202011613105.6A 2020-12-30 2020-12-30 一种消失模铸造涂料添加剂 Pending CN112570645A (zh)