CN108221475A - A kind of modified pulp toughener - Google Patents
A kind of modified pulp toughener Download PDFInfo
- Publication number
- CN108221475A CN108221475A CN201711340603.6A CN201711340603A CN108221475A CN 108221475 A CN108221475 A CN 108221475A CN 201711340603 A CN201711340603 A CN 201711340603A CN 108221475 A CN108221475 A CN 108221475A
- Authority
- CN
- China
- Prior art keywords
- parts
- account
- raw material
- weight
- following raw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of modified pulp toughener, are made of following raw material according to parts by weight：Polyamidoimide account for 14 parts, 25 parts of maleic anhydride, 0.5 2 parts of polyhydroxy chemical coupling agent, phosphite account for 24 parts, ethylene copolymer account for 0.8 3 parts, 26 parts of ethylene-propylene diene copolymer, 38 parts of pentaerythrite, 37 parts of 48 parts of antifoaming agent and stabilizer.There is the present invention raw material to be easy to get, is of low cost, and be conducive to enhance the intensity and toughness of paper products using this product, it is often more important that paper products surface gloss be improved, so that paper products have the characteristics that preferably condition.
Description
Technical field
The present invention relates to pulp production technology research and development field more particularly to a kind of modified pulp toughener.
Background technology
In people's lives, more and more fields need to use paper products, during painting this in manufacture embroidery,
It needs to use many paper, and the intensity of required paper and toughness reguirements are all higher, especially flexible requirement
It is very high, therefore manufacture producer's meeting that embroidery is painted originally and oneself prepare paper as needed, and common pulp formulation is complicated, and
Manufacturing cost is high, therefore the favor that suitable toughener already receives production of paper products person is added in when producing paper pulp.
Invention content
The purpose of the present invention is to solve shortcoming in the prior art, and a kind of modified pulp toughening proposed
Agent.
To achieve these goals, present invention employs following technical solutions：
A kind of modified pulp toughener, is made of following raw material according to parts by weight：Polyamidoimide accounts for 1-4 parts, maleic acid
2-5 parts of acid anhydride, 0.5-2 parts of polyhydroxy chemical coupling agent, phosphite account for 2-4 parts, ethylene copolymer account for 0.8-3 parts, EPDM
3-7 parts of 2-6 parts of glue, 3-8 parts of pentaerythrite, 4-8 parts of antifoaming agent and stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：1-4 parts of mineral oil, 0.5-2 parts of tetrabutyl phosphonium bromide phosphorus, paraffin account for
3-8 parts account for 1-4 parts with peregal；
The stabilizer is made of following raw material according to parts by weight：2-4 parts of isopropanol, 1-5 parts of lignosulfonate, xanthans 2-7
The water of part, 3-5 parts of dibutyl tin laurate and surplus.
A kind of above-mentioned modified pulp toughener, is made of following raw material according to parts by weight：Polyamidoimide accounts for 1-3
Part, 2-4 parts of maleic anhydride, 0.5-1.9 parts of polyhydroxy chemical coupling agent, phosphite account for 2-3.8 parts, ethylene copolymer account for 0.8-
3-6 parts of 2.9 parts, 2-5 parts of ethylene-propylene diene copolymer, 3-7 parts of pentaerythrite, 4-7 parts of antifoaming agent and stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：1-3 parts of mineral oil, 0.5-1.9 parts of tetrabutyl phosphonium bromide phosphorus, paraffin
It accounts for 3-7 parts and peregal accounts for 1-3 parts；
The stabilizer is made of following raw material according to parts by weight：2-3.9 parts of isopropanol, 1-4 parts of lignosulfonate, xanthans 2-
6 parts, the water of 3-4.9 parts of dibutyl tin laurate and surplus.
A kind of above-mentioned modified pulp toughener, is made of following raw material according to parts by weight：Polyamidoimide accounts for 2-3
Part, 3-4 parts of maleic anhydride, 0.6-1.9 parts of polyhydroxy chemical coupling agent, phosphite account for 2.1-3.8 parts, ethylene copolymer accounts for
4-6 parts of 0.9-2.9 parts, 3-5 parts of ethylene-propylene diene copolymer, 4-7 parts of pentaerythrite, 5-7 parts of antifoaming agent and stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：2-3 parts of mineral oil, 0.6-1.9 parts of tetrabutyl phosphonium bromide phosphorus, paraffin
It accounts for 4-7 parts and peregal accounts for 2-3 parts；
The stabilizer is made of following raw material according to parts by weight：2.1-3.9 parts of isopropanol, 2-4 parts of lignosulfonate, xanthans
3-6 parts, the water of 3.1-4.9 parts of dibutyl tin laurate and surplus.
A kind of above-mentioned modified pulp toughener, is made of following raw material according to parts by weight：Polyamidoimide accounts for 2.5
Part, 3.5 parts of maleic anhydride, 1.25 parts of polyhydroxy chemical coupling agent, phosphite account for 3 parts, ethylene copolymer account for 1.9 parts, ternary
5 parts of the third glue of second 4,5.5 parts of pentaerythrite, 6 parts of antifoaming agent and stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：2.5 parts of mineral oil, 1.25 parts of tetrabutyl phosphonium bromide phosphorus, paraffin account for
5.5 parts account for 2.5 parts with peregal；
The stabilizer is made of following raw material according to parts by weight：3 parts of isopropanol, 3 parts of lignosulfonate, 4.5 parts of xanthans, two
The water of 4 parts of dibutyl tin laurate and surplus.
Compared with prior art, the beneficial effects of the invention are as follows：
A kind of modified pulp of the present invention with toughener there is raw material to be easy to get, be of low cost, and be conducive to enhance using this product
The intensity and toughness of paper products, it is often more important that paper products surface gloss is improved, so that paper products have preferably
The advantageous effects such as condition.
Specific embodiment
Embodiment 1
A kind of modified pulp toughener, is made of following raw material according to parts by weight：Polyamidoimide accounts for 1 part, maleic anhydride 2
Part, 0.5 part of polyhydroxy chemical coupling agent, phosphite account for 2 parts, ethylene copolymer account for 0.8 part, 2 parts of ethylene-propylene diene copolymer, Ji Wusi
3 parts of 3 parts of alcohol, 4 parts of antifoaming agent and stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：1 part of mineral oil, 0.5 part of tetrabutyl phosphonium bromide phosphorus, paraffin account for 3 parts
1 part is accounted for peregal；
The stabilizer is made of following raw material according to parts by weight：2 parts of isopropanol, 1 part of lignosulfonate, 2 parts of xanthans, February
The water of 3 parts of dilaurylate and surplus.
Embodiment 2
A kind of above-mentioned modified pulp toughener, is made of following raw material according to parts by weight：Polyamidoimide accounts for 4 parts, horse
Come 5 parts of acid anhydrides, 2 parts of polyhydroxy chemical coupling agent, phosphite account for 4 parts, ethylene copolymer account for 3 parts, 6 parts of ethylene-propylene diene copolymer, season
7 parts of penta 8 parts of tetrol, 8 parts of antifoaming agent and stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：4 parts of mineral oil, 2 parts of tetrabutyl phosphonium bromide phosphorus, paraffin account for 8 parts and
Peregal accounts for 4 parts；
The stabilizer is made of following raw material according to parts by weight：4 parts of isopropanol, 5 parts of lignosulfonate, 7 parts of xanthans, February
The water of 5 parts of dilaurylate and surplus.
Embodiment 3
A kind of above-mentioned modified pulp toughener, is made of following raw material according to parts by weight：Polyamidoimide account for 2.5 parts,
3.5 parts of maleic anhydride, 1.25 parts of polyhydroxy chemical coupling agent, phosphite account for 3 parts, ethylene copolymer account for 1.9 parts, EPDM
5 parts of glue 4,5.5 parts of pentaerythrite, 6 parts of antifoaming agent and stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：2.5 parts of mineral oil, 1.25 parts of tetrabutyl phosphonium bromide phosphorus, paraffin account for
5.5 parts account for 2.5 parts with peregal；
The stabilizer is made of following raw material according to parts by weight：3 parts of isopropanol, 3 parts of lignosulfonate, 4.5 parts of xanthans, two
The water of 4 parts of dibutyl tin laurate and surplus.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be under the premise of this patent objective not be departed from the knowledge that one skilled in the relevant art has
It makes a variety of changes.
Claims (4)
1. a kind of modified pulp toughener, which is characterized in that be made of following raw material according to parts by weight：Polyamidoimide accounts for
1-4 parts, 2-5 parts of maleic anhydride, 0.5-2 parts of polyhydroxy chemical coupling agent, phosphite account for 2-4 parts, ethylene copolymer account for 0.8-3
Part, 2-6 parts of ethylene-propylene diene copolymer, 3-8 parts of pentaerythrite, 4-8 parts of antifoaming agent and 3-7 parts of stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：1-4 parts of mineral oil, 0.5-2 parts of tetrabutyl phosphonium bromide phosphorus, paraffin account for
3-8 parts account for 1-4 parts with peregal；
The stabilizer is made of following raw material according to parts by weight：2-4 parts of isopropanol, 1-5 parts of lignosulfonate, xanthans 2-7
The water of part, 3-5 parts of dibutyl tin laurate and surplus.
2. a kind of modified pulp toughener according to claim 1, which is characterized in that according to parts by weight by following raw material
Composition：Polyamidoimide account for 1-3 parts, 2-4 parts of maleic anhydride, 0.5-1.9 parts of polyhydroxy chemical coupling agent, phosphite account for 2-
3.8 parts, ethylene copolymer account for 0.8-2.9 parts, 2-5 parts of ethylene-propylene diene copolymer, 3-7 parts of pentaerythrite, 4-7 parts of antifoaming agent and stabilizer
3-6 parts；
The antifoaming agent is made of following raw material according to parts by weight：1-3 parts of mineral oil, 0.5-1.9 parts of tetrabutyl phosphonium bromide phosphorus, paraffin
It accounts for 3-7 parts and peregal accounts for 1-3 parts；
The stabilizer is made of following raw material according to parts by weight：2-3.9 parts of isopropanol, 1-4 parts of lignosulfonate, xanthans 2-
6 parts, the water of 3-4.9 parts of dibutyl tin laurate and surplus.
3. a kind of modified pulp toughener according to claim 1, which is characterized in that according to parts by weight by following raw material
Composition：Polyamidoimide accounts for 2-3 parts, 3-4 parts of maleic anhydride, 0.6-1.9 parts of polyhydroxy chemical coupling agent, phosphite account for
2.1-3.8 parts, ethylene copolymer account for 0.9-2.9 parts, 3-5 parts of ethylene-propylene diene copolymer, 4-7 parts of pentaerythrite, 5-7 parts of antifoaming agent and steady
Determine 4-6 parts of agent；
The antifoaming agent is made of following raw material according to parts by weight：2-3 parts of mineral oil, 0.6-1.9 parts of tetrabutyl phosphonium bromide phosphorus, paraffin
It accounts for 4-7 parts and peregal accounts for 2-3 parts；
The stabilizer is made of following raw material according to parts by weight：2.1-3.9 parts of isopropanol, 2-4 parts of lignosulfonate, xanthans
3-6 parts, the water of 3.1-4.9 parts of dibutyl tin laurate and surplus.
4. a kind of modified pulp toughener according to claim 1, which is characterized in that according to parts by weight by following raw material
Composition：Polyamidoimide account for 2.5 parts, 3.5 parts of maleic anhydride, 1.25 parts of polyhydroxy chemical coupling agent, phosphite account for 3 parts,
Ethylene copolymer account for 1.9 parts, ethylene-propylene diene copolymer 4,5.5 parts of pentaerythrite, 5 parts of 6 parts of antifoaming agent and stabilizer；
The antifoaming agent is made of following raw material according to parts by weight：2.5 parts of mineral oil, 1.25 parts of tetrabutyl phosphonium bromide phosphorus, paraffin account for
5.5 parts account for 2.5 parts with peregal；
The stabilizer is made of following raw material according to parts by weight：3 parts of isopropanol, 3 parts of lignosulfonate, 4.5 parts of xanthans, two
The water of 4 parts of dibutyl tin laurate and surplus.