CN108208917A - A kind of preparation method of novel tobacco product dedicated foil - Google Patents
A kind of preparation method of novel tobacco product dedicated foil Download PDFInfo
- Publication number
- CN108208917A CN108208917A CN201810023211.5A CN201810023211A CN108208917A CN 108208917 A CN108208917 A CN 108208917A CN 201810023211 A CN201810023211 A CN 201810023211A CN 108208917 A CN108208917 A CN 108208917A
- Authority
- CN
- China
- Prior art keywords
- tobacco
- reaction kettle
- homogeneous reaction
- uniformly mixed
- tobacco powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of preparation method of novel tobacco product dedicated foil, includes the following steps：1) tobacco leaf is crushed into tobacco powder；2) tobacco powder is sufficiently mixed with water in homogeneous reaction kettle；3) plus fiber is weighed, is beaten using mill, adds in homogeneous reaction kettle after disperseing using Homogenizing pump and is uniformly mixed with material in step 2)；4) Alevaire is weighed, homogeneous reaction kettle is added in and is uniformly mixed with material in step 3)；5) adhesive is weighed, and prepares the solution as 2% concentration：6) solution prepared in step 5) is added in homogeneous reaction kettle to be uniformly mixed with material in step 4)；7) material mixed in step 6) is dehydrated using vacuum dryer；8) material dewatered in step 7) using roll squeezer is molded, by drying, chopping, is prepared into and heats the tobacco product that do not burn.The present invention organically combines thick slurry method and roll-in method, solves the uniformly mixed sex chromosome mosaicism of raw material.
Description
Technical field
The present invention relates to reconstituted tobacoo technical field, the preparation method of specifically a kind of novel tobacco product dedicated foil.
Background technology
In recent years, electronic cigarette, heating do not burn the novel tobaccos such as tobacco product product just in rapid rising, tobacco business height
The degree concern technology trends of novel tobacco product and industry development situation.Heating does not burn tobacco product as novel tobacco
Staple product in product is to heat tobacco using external heat source rather than light tobacco to generate tobacco flavor gas, there is charcoal
The modes such as heating, electrical heating.For the characteristics of not burning tobacco product is heated, develop and heat tobacco product special thin of not burning
Piece realizes the Core Features such as the carrying of its fragrance, atomization, has energetically facilitation to the development of novel tobacco product.
Invention content
In view of the deficiencies of the prior art, the present invention provides a kind of preparation method of novel tobacco product dedicated foil, will be thick
Slurry processes and roll-in method are organically combined, and solve the uniformly mixed sex chromosome mosaicism of raw material, and the reconstituted tobacoo product prepared can be real
The Core Features such as existing fragrance carrying, atomization have energetically facilitation to the development of novel tobacco product.
Technical solution is used by the present invention solves above-mentioned technical problem：A kind of novel tobacco product dedicated foil is provided
Preparation method, include the following steps：
1) tobacco leaf is crushed into tobacco powder；
2) tobacco powder of constant weight is weighed, according to weight ratio tobacco powder：Water=1:5-1:10 are filled in homogeneous reaction kettle
Divide mixing；
3) plus fiber is weighed according to the 2-8% of tobacco powder weight, is beaten using mill to 15-25 ° of SR, using Homogenizing pump
It adds in homogeneous reaction kettle after dispersion and is uniformly mixed with material in step 2)；
4) Alevaire is weighed according to the 20-40% of tobacco powder weight, adds in homogeneous reaction kettle and mixed with material in step 3)
It is even；
5) adhesive is weighed according to the 3-8% of tobacco powder weight, and prepares the solution as 2% concentration：
6) solution prepared in step 5) is added in homogeneous reaction kettle to be uniformly mixed with material in step 4)；
7) material mixed in step 6) is dehydrated using vacuum dryer, temperature is 60-80 DEG C, after dry
The moisture content of material is 20-40%；
8) material dewatered in step 7) using roll squeezer is molded, by drying, chopping, is prepared into heating and does not burn
Tobacco product.
Further, mixing of the plus fiber for one or both of broad-leaved wood fiber and needle-leaved wood fibre.
Further, the Alevaire is one kind in glycerine, propylene glycol.
Further, the adhesive is the mixing of one or both of sodium alginate, chitosan, guar gum, CMC.
This method organically combines thick slurry method and roll-in method, solves the uniformly mixed sex chromosome mosaicism of raw material, prepares
Reconstituted tobacoo product can realize the Core Features such as fragrance carrying, atomization, have to the development of novel tobacco product and energetically promote
Into effect.
Specific embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.The specific embodiments described herein are merely illustrative of the present invention, is not used to limit this hair
It is bright.
Embodiment 1
1) tobacco leaf is crushed into tobacco powder；
2) tobacco powder of constant weight is weighed, according to weight ratio tobacco powder：Water=1:5 are fully mixed in homogeneous reaction kettle
It closes；
3) needle-leaved wood fibre is weighed according to the 3% of tobacco powder weight, is beaten using mill to 15 ° of SR, using Homogenizing pump point
Dissipate after add in homogeneous reaction kettle in 2) in material be uniformly mixed；
4) 30% according to tobacco powder weight weighs glycerine, add in homogeneous reaction kettle with 3) in material be uniformly mixed；
5) 3% according to tobacco powder weight weighs sodium alginate, and prepares the solution as 2% concentration：
6) by solution prepared in 5) add in homogeneous reaction kettle with 4) in material be uniformly mixed；
7) 6) material mixed in is dehydrated using vacuum dryer, temperature is 70 DEG C, it is dry after material
Moisture content is 20%；
8) 7) dewatered material in using roll squeezer is molded, by drying, chopping, is prepared into heating not burning tobacco
Sensory quality assessment is carried out after product.
Embodiment 2
1) tobacco leaf is crushed into tobacco powder；
2) tobacco powder of constant weight is weighed, according to weight ratio tobacco powder：Water=1:8 are fully mixed in homogeneous reaction kettle
It closes；
3) broad-leaved wood fiber and needle-leaved wood fibre are weighed according to the 5% of tobacco powder weight, is beaten using mill to 20 ° of SR, then
After Homogenizing pump disperses add in homogeneous reaction kettle in 2) in material be uniformly mixed；
4) 20% according to tobacco powder weight weighs propylene glycol, add in homogeneous reaction kettle with 3) in material be uniformly mixed；
5) 4% according to tobacco powder weight weighs chitosan, and prepares the solution as 2% concentration：
6) by solution prepared in 5) add in homogeneous reaction kettle with 4) in material be uniformly mixed；
7) 6) material mixed in is dehydrated using vacuum dryer, temperature is 80 DEG C, it is dry after material
Moisture content is 30%；
8) 7) dewatered material in using roll squeezer is molded, by drying, chopping, is prepared into heating not burning tobacco
Sensory quality assessment is carried out after product.
Embodiment 3
1) tobacco leaf is crushed into tobacco powder；
2) tobacco powder of constant weight is weighed, according to weight ratio tobacco powder：Water=1:10 are fully mixed in homogeneous reaction kettle
It closes；
3) broad-leaved wood fiber is weighed according to the 6% of tobacco powder weight, is beaten using mill to 18 ° of SR, using Homogenizing pump point
Dissipate after add in homogeneous reaction kettle in 2) in material be uniformly mixed；
4) 30% according to tobacco powder weight weighs glycerine, add in homogeneous reaction kettle with 3) in material be uniformly mixed；
5) 4% according to tobacco powder weight weighs CMC, and prepares the solution as 2% concentration：
6) by solution prepared in 5) add in homogeneous reaction kettle with 4) in material be uniformly mixed；
7) 6) material mixed in is dehydrated using vacuum dryer, temperature is 80 DEG C, it is dry after material
Moisture content is 35%；
8) 7) dewatered material in using roll squeezer is molded, by drying, chopping, is prepared into heating not burning tobacco
Sensory quality assessment is carried out after product.
Embodiment 4
1) tobacco leaf is crushed into tobacco powder；
2) tobacco powder of constant weight is weighed, according to weight ratio tobacco powder：Water=1:6 are fully mixed in homogeneous reaction kettle
It closes；
3) broad-leaved wood fiber and needle-leaved wood fibre are weighed according to the 8% of tobacco powder weight, is beaten using mill to 22 ° of SR, then
After Homogenizing pump disperses add in homogeneous reaction kettle in 2) in material be uniformly mixed；
4) 40% according to tobacco powder weight weighs propylene glycol, add in homogeneous reaction kettle with 3) in material be uniformly mixed；
5) 3% according to tobacco powder weight weighs sodium alginate, and prepares the solution as 2% concentration：
6) by solution prepared in 5) add in homogeneous reaction kettle with 4) in material be uniformly mixed；
7) 6) material mixed in is dehydrated using vacuum dryer, temperature is 75 DEG C, it is dry after material
Moisture content is 25%；
8) 7) dewatered material in using roll squeezer is molded, by drying, chopping, is prepared into heating not burning tobacco
Sensory quality assessment is carried out after product.
Embodiment 5
1) tobacco leaf is crushed into tobacco powder；
2) tobacco powder of constant weight is weighed, according to weight ratio tobacco powder：Water=1：9 are fully mixed in homogeneous reaction kettle
It closes；
3) needle-leaved wood fibre is weighed according to the 3% of tobacco powder weight, is beaten using mill to 25 ° of SR, using Homogenizing pump point
Dissipate after add in homogeneous reaction kettle in 2) in material be uniformly mixed；
4) 30% according to tobacco powder weight weighs glycerine, add in homogeneous reaction kettle with 3) in material be uniformly mixed；
5) 4% according to tobacco powder weight weighs guar gum, and prepares the solution as 2% concentration：
6) by solution prepared in 5) add in homogeneous reaction kettle with 4) in material be uniformly mixed；
7) 6) material mixed in is dehydrated using vacuum dryer, temperature is 65 DEG C, it is dry after material
Moisture content is 30%；
8) 7) dewatered material in using roll squeezer is molded, by drying, chopping, is prepared into heating not burning tobacco
Sensory quality assessment is carried out after product.
Dedicated foil prepared by Examples 1 to 5, which prepares to become, heats the tobacco product that do not burn, and is commented by aesthetic quality
Valency, the heating being prepared into using dedicated foil are not burnt tobacco product product sensory stable quality, and fragrance is sufficient, atomizing effect
It is good.
The above description is merely a specific embodiment, but protection scope of the present invention is not limited thereto, any
Belong to those skilled in the art in the technical scope disclosed by the present invention, the change or replacement that can be readily occurred in all should
It is included within the scope of the present invention.Therefore, protection scope of the present invention should be subject to the protection scope in claims.
Claims (4)
1. a kind of preparation method of novel tobacco product dedicated foil, it is characterised in that include the following steps：
1) tobacco leaf is crushed into tobacco powder；
2) tobacco powder of constant weight is weighed, according to weight ratio tobacco powder：Water=1:5-1:10 are fully mixed in homogeneous reaction kettle
It closes；
3) plus fiber is weighed according to the 2-8% of tobacco powder weight, is beaten to 15-25 ° of SR using mill, disperseed using Homogenizing pump
It adds in homogeneous reaction kettle and is uniformly mixed with material in step 2) afterwards；
4) Alevaire is weighed according to the 20-40% of tobacco powder weight, adds in homogeneous reaction kettle and be uniformly mixed with material in step 3)；
5) adhesive is weighed according to the 3-8% of tobacco powder weight, and prepares the solution as 2% concentration：
6) solution prepared in step 5) is added in homogeneous reaction kettle to be uniformly mixed with material in step 4)；
7) material mixed in step 6) is dehydrated using vacuum dryer, temperature is 60-80 DEG C, material after drying
Moisture content be 20-40%；
8) material dewatered in step 7) using roll squeezer is molded, by drying, chopping, is prepared into heating not burning tobacco
Product.
2. the preparation method of novel tobacco product dedicated foil as described in claim 1, it is characterised in that：The plus fiber
Mixing for one or both of broad-leaved wood fiber and needle-leaved wood fibre.
3. the preparation method of novel tobacco product dedicated foil as described in claim 1, it is characterised in that：The Alevaire is
One kind in glycerine, propylene glycol.
4. the preparation method of novel tobacco product dedicated foil as described in claim 1, it is characterised in that：The adhesive is
The mixing of one or both of sodium alginate, chitosan, guar gum, CMC.