CN108193516A - A kind of preparation process of the wool blended fabric of terylene - Google Patents
A kind of preparation process of the wool blended fabric of terylene Download PDFInfo
- Publication number
- CN108193516A CN108193516A CN201611123826.2A CN201611123826A CN108193516A CN 108193516 A CN108193516 A CN 108193516A CN 201611123826 A CN201611123826 A CN 201611123826A CN 108193516 A CN108193516 A CN 108193516A
- Authority
- CN
- China
- Prior art keywords
- terylene
- blended fabric
- wool blended
- wool
- preparation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of preparation process of the wool blended fabric of terylene, includes the following steps：(1) polyester fiber and fleece fibre blended spinning are obtained into the wool blended fabric of terylene；(2) the wool blended fabric of terylene after washing is subjected to refining processing, dehydration and drying successively；(3) it dyes；(4) by the wool blended fabric of terylene drying and shaping on forming machine after the dyeing after dyeing, temperature is 120 150 DEG C, and speed is 10 20m/min.The preparation process of the wool blended fabric of terylene described in the invention solves the problems, such as that chromatography is difficult, technological process is long, stablize the more reasonable upper dye flow of fabric, production clean environment firendly, product quality by this method, realize the popular of wool terylene fabric, and it is widely used in home textile articles for use, and be very suitable for autumn and winter use.
Description
Technical field
The invention belongs to textile technology field, more particularly, to a kind of preparation process of the wool blended fabric of terylene.
Background technology
One of blended development trend for having become fabric.With people's environmental protection and the enhancing of health care consciousness, clothes are pursued
It is comfortable, beautiful, even health care etc. is functional becomes fashion.Two or more natural fibre blended not only be ensure that into fabric
The advantages of natural sex, the feature of environmental protection also make to have complementary advantages between several fibers, performance each component fiber simultaneously overcomes its shortcoming, realizes
The complementation of its performance, fabric have more fully performance.
Wool fiber both has good moisture permeability with polyester fiber, and it is resistance to also contain wool favorable elasticity, height
Mill property, the advantages that terylene polymer fiber degree is big, intensity is high, high temperature resistance, are widely used in all kinds of clothing fabrics, deep by vast
Consumer likes.But since terylene, wool fiber have different structures, different dyeabilities, enterprise is given in dyeing often
Bring the problem of chromatography is difficult, technological process is long.
Invention content
In view of this, the invention is directed to a kind of preparation process of the wool blended fabric of terylene, existing to solve
The technical issues of wool and polyester fiber chromatography are difficult in technology.
In order to achieve the above objectives, the technical solution of the invention is realized in：
A kind of preparation process of the wool blended fabric of terylene, includes the following steps：
(1) polyester fiber and fleece fibre blended spinning are obtained into the wool blended fabric of terylene, the polyester fiber and wool are fine
The mass ratio of dimension is 1：(1-2)；By the wool blended fabric washing 20-40min of terylene, bath raio 1：(25-40), and add in cleaning
Agent, the dosage of cleaning agent is every liter of water 5g, and water temperature is 60 DEG C；
(2) the wool blended fabric of terylene after washing is subjected to refining processing, dehydration and drying successively, wherein, at refining
The weight ratio of the wool blended fabric of terylene and water is 1 in reason：(8-10)；
(3) the wool blended fabric weight 1 of terylene after being dried by step (3)：3 bath raio adds water, step (3) into dye vat
Successively plus after dyeing assistant and disperse dyes, 90 are warming up to according to 1.2 DEG C per minute for the wool blended fabric of terylene after drying
DEG C, and washed after temperature-constant operation 1h；Then the wool blended fabric weight 1 of terylene of required dyeing is pressed：3 bath raio adds water,
Dyeing assistant is added in, 100 DEG C is warming up to by 1 DEG C/min, is washed the terylene wool after being dyed after constant temperature holding 1h and mixed
Textile fabric；
(4) by the wool blended fabric of terylene drying and shaping on forming machine after the dyeing after dyeing, temperature 120-150
DEG C, speed 10-20m/min.
Further, a concentration of 1-5g/L of scouring agent used in the step (2), refining processing time are small for 0.5-1
When, concise temperature is 65 DEG C；
Further, preparation process further includes whole after the wool blended fabric of terylene after the step (4) is dried carries out
Science and engineering sequence.
Further, the finishing process is put into for the wool blended fabric of terylene after will the step (4) be dried
It is dried after being disseminated in submissive liquid.
Further, the submissive liquid includes softening agent and leavening agent.
Further, the mass ratio of softening agent and leavening agent is (3-5) in the submissive liquid：2.
Further, the mass ratio of polyester fiber and wool fiber is 1 in the step (1)：1.5.
Further, the fibre fineness 16.5Mic of the wool fiber, fibre length 80mm.
Relative to the prior art, the preparation process of the wool blended fabric of terylene described in the invention is with following excellent
Gesture：
It is difficult, technological process length that the preparation process of the wool blended fabric of terylene described in the invention solves chromatography
Problem stablizes the more reasonable upper dye flow of fabric, production clean environment firendly, product quality by this method, realizes wool
Terylene fabric it is popular, and be widely used in home textile articles for use, and be very suitable for autumn and winter use.
Specific embodiment
Unless otherwise stated, term used herein is respectively provided with the meaning that those skilled in the art routinely understand, in order to
The present invention is easy to understand, some terms used herein have been subjected to following definitions.
It using in the specification and in the claims, singular type "one" and " this " include plural reference, unless on
Hereafter separately there is clear statement.For example, term " (one) cell " includes the cell of plural number, including its mixture.
All Digital IDs, such as pH, temperature, time, concentration are all approximations including range.It is to be understood that although
Term " about " is all added before always not describing all Digital IDs explicitly.While it will also be understood that, although not always clearly
Narration, reagent described herein is only example, and equivalent is known in the art.
With reference to embodiment come the present invention will be described in detail create.
Embodiment 1
A kind of preparation process of the wool blended fabric of terylene, includes the following steps：
(1) polyester fiber and fleece fibre blended spinning are obtained into the wool blended fabric of terylene, the polyester fiber and wool are fine
The mass ratio of dimension is 1：1.5, the fibre fineness 16.5Mic of wool fiber, fibre length 80mm；By the wool blended fabric water of terylene
Wash 25min, bath raio 1：30, and detergent is added in, the dosage of cleaning agent is every liter of water 5g, and water temperature is 60 DEG C；
(2) the wool blended fabric of terylene after washing is subjected to refining processing, dehydration and drying successively, wherein, at refining
The weight ratio of the wool blended fabric of terylene and water is 1 in reason：8, a concentration of 2g/L of scouring agent, refining processing time are 0.5 hour,
Concise temperature is 65 DEG C；
(3) the wool blended fabric weight 1 of terylene after being dried by step (3)：3 bath raio adds water, step (3) into dye vat
Successively plus after dyeing assistant and disperse dyes, 90 are warming up to according to 1.2 DEG C per minute for the wool blended fabric of terylene after drying
DEG C, and washed after temperature-constant operation 1h；Then the wool blended fabric weight 1 of terylene of required dyeing is pressed：3 bath raio adds water,
Dyeing assistant is added in, 100 DEG C is warming up to by 1 DEG C/min, is washed the terylene wool after being dyed after constant temperature holding 1h and mixed
Textile fabric；
(4) by the wool blended fabric of terylene drying and shaping on forming machine after the dyeing after dyeing, temperature is 120 DEG C,
Speed is 10m/min.
Embodiment 2
A kind of preparation process of the wool blended fabric of terylene, includes the following steps：
(1) polyester fiber and fleece fibre blended spinning are obtained into the wool blended fabric of terylene, the polyester fiber and wool are fine
The mass ratio of dimension is 1：2, the fibre fineness 16.5Mic of wool fiber, fibre length 80mm；By the wool blended fabric washing of terylene
40min, bath raio 1：40, and detergent is added in, the dosage of cleaning agent is every liter of water 5g, and water temperature is 60 DEG C；
(2) the wool blended fabric of terylene after washing is subjected to refining processing, dehydration and drying successively, wherein, at refining
The weight ratio of the wool blended fabric of terylene and water is 1 in reason：10, a concentration of 5g/L of scouring agent, refining processing time are 40min,
Concise temperature is 65 DEG C；
(3) the wool blended fabric weight 1 of terylene after being dried by step (3)：3 bath raio adds water, step (3) into dye vat
Successively plus after dyeing assistant and disperse dyes, 90 are warming up to according to 1.2 DEG C per minute for the wool blended fabric of terylene after drying
DEG C, and washed after temperature-constant operation 1h；Then the wool blended fabric weight 1 of terylene of required dyeing is pressed：3 bath raio adds water,
Dyeing assistant is added in, 100 DEG C is warming up to by 1 DEG C/min, is washed the terylene wool after being dyed after constant temperature holding 1h and mixed
Textile fabric；
(4) by the wool blended fabric of terylene drying and shaping on forming machine after the dyeing after dyeing, temperature is 140 DEG C,
Speed is 20m/min.
(5) the wool blended fabric of terylene after the step (4) is dried is put into submissive liquid and is dried after dip dyeing, described soft
Include softening agent and leavening agent along liquid, the mass ratio of softening agent and leavening agent is 3 in the submissive liquid：2.
Embodiment 3
A kind of preparation process of the wool blended fabric of terylene, includes the following steps：
(1) polyester fiber and fleece fibre blended spinning are obtained into the wool blended fabric of terylene, the polyester fiber and wool are fine
The mass ratio of dimension is 1：1, the fibre fineness 16.5Mic of wool fiber, fibre length 80mm；By the wool blended fabric washing of terylene
35min, bath raio 1：30, and detergent is added in, the dosage of cleaning agent is every liter of water 5g, and water temperature is 60 DEG C；
(2) the wool blended fabric of terylene after washing is subjected to refining processing, dehydration and drying successively, wherein, at refining
The weight ratio of the wool blended fabric of terylene and water is 1 in reason：9, a concentration of 4g/L of scouring agent, refining processing time are 0.5 hour,
Concise temperature is 65 DEG C；
(3) the wool blended fabric weight 1 of terylene after being dried by step (3)：3 bath raio adds water, step (3) into dye vat
Successively plus after dyeing assistant and disperse dyes, 90 are warming up to according to 1.2 DEG C per minute for the wool blended fabric of terylene after drying
DEG C, and washed after temperature-constant operation 1h；Then the wool blended fabric weight 1 of terylene of required dyeing is pressed：3 bath raio adds water,
Dyeing assistant is added in, 100 DEG C is warming up to by 1 DEG C/min, is washed the terylene wool after being dyed after constant temperature holding 1h and mixed
Textile fabric；
(4) by the wool blended fabric of terylene drying and shaping on forming machine after the dyeing after dyeing, temperature is 150 DEG C,
Speed is 17m/min.
(5) the wool blended fabric of terylene after the step (4) is dried is put into submissive liquid and is dried after dip dyeing, described soft
Include softening agent and leavening agent along liquid, the mass ratio of softening agent and leavening agent is 5 in the submissive liquid：2.
The foregoing is merely the preferred embodiments of the invention, are not intended to limit the invention creation, all at this
Within the spirit and principle of innovation and creation, any modification, equivalent replacement, improvement and so on should be included in the invention
Protection domain within.
Claims (8)
1. a kind of preparation process of the wool blended fabric of terylene, it is characterised in that：The preparation process includes the following steps：
(1) polyester fiber and fleece fibre blended spinning are obtained into the wool blended fabric of terylene, the polyester fiber and wool fiber
Mass ratio is 1：(1-2)；By the wool blended fabric washing 20-40min of terylene, bath raio 1：(25-40), and detergent is added in,
The dosage of cleaning agent is every liter of water 5g, and water temperature is 60 DEG C；
(2) the wool blended fabric of terylene after washing is subjected to refining processing, dehydration and drying successively, wherein, in refining treatment
The weight ratio of the wool blended fabric of terylene and water is 1：(8-10)；
(3) the wool blended fabric weight 1 of terylene after being dried by step (3)：3 bath raio is into dye vat plus water, step (3) are dried
Successively plus after dyeing assistant and disperse dyes, 90 DEG C are warming up to according to 1.2 DEG C per minute for the wool blended fabric of terylene afterwards, and
It is washed after temperature-constant operation 1h；Then the wool blended fabric weight 1 of terylene of required dyeing is pressed：3 bath raio adds water, adds in dye
Color auxiliary agent is warming up to 100 DEG C by 1 DEG C/min, and constant temperature is washed the wool blended face of the terylene after being dyed after keeping 1h
Material；
(4) by the wool blended fabric of terylene drying and shaping on forming machine after the dyeing after dyeing, temperature is 120-150 DEG C,
Speed is 10-20m/min.
2. the preparation process of the wool blended fabric of terylene according to claim 1, it is characterised in that：In the step (2)
A concentration of 1-5g/L of scouring agent used, refining processing time are 0.5-1 hours, and concise temperature is 65 DEG C.
3. the preparation process of the wool blended fabric of terylene according to claim 1 or 2, it is characterised in that：Preparation process is also
Finishing process is carried out including the wool blended fabric of terylene after the step (4) is dried.
4. the preparation process of the wool blended fabric of terylene according to claim 3, it is characterised in that：The finishing process
It is put into after being disseminated in submissive liquid and dries for the wool blended fabric of terylene after will the step (4) be dried.
5. the preparation process of the wool blended fabric of terylene described in claim 4, it is characterised in that：The submissive liquid includes softness
Agent and leavening agent.
6. the preparation process of the wool blended fabric of terylene according to claim 5, it is characterised in that：It is soft in the submissive liquid
The mass ratio of soft dose and leavening agent is (3-5)：2.
7. the preparation process of the wool blended fabric of terylene according to claim 1, it is characterised in that：In the step (1)
The mass ratio of polyester fiber and wool fiber is 1：1.5.
8. the preparation process of the wool blended fabric of terylene described in claim 1, it is characterised in that：The fibre of the wool fiber
Tie up fineness 16.5Mic, fibre length 80mm.