A kind of production technology of the warming home textile yarn of novel antibacterial Download PDFInfo
- Publication number
- CN108193336A CN108193336A CN201810123464.XA CN201810123464A CN108193336A CN 108193336 A CN108193336 A CN 108193336A CN 201810123464 A CN201810123464 A CN 201810123464A CN 108193336 A CN108193336 A CN 108193336A
- Authority
- CN
- China
- Prior art keywords
- yarn
- warming
- fiber
- novel antibacterial
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Weaving methods of the warming home textile yarn of novel antibacterial, the antibacterial thermal insulating yarn is made of the coffee carbon fiber of weight ratio 35 65% and 15% 25% Modal fibre and 15% 25%PTT fiber blends, and processing method includes the processes such as blowing, cotton carding, drafting, rove, spun yarn.Present invention process is simple, mass automatic production can be achieved, the new type yarn is with pro-skin is comfortable, yarn strength is high, filoplume is few, antibacterial, it is warming, pilling is not easy with good sucting wet air permeability, meets the consumer demands such as family, hotel, family's textile fabric fluffy insulation after being weaved by the present invention, has a good application prospect.
Description
Technical field
The present invention relates to textile fields, and in particular to a kind of production technology of the warming home textile yarn of novel antibacterial.
Background technology
Family textile fabric usually require that ventilative, warming, moisture absorption, it is currently used be cotton person's textile fabric etc., warmth retention property is preferable,
But all there are some shortcomings, such as Boardy Feeling, and fluffy degree is poor, and sucting wet air permeability is slightly poor, and easily raw acarid causes respiratory tract, skin
Etc. diseases.
Invention content
Goal of the invention：In order to solve the deficiencies in the prior art, the present invention provides a kind of warming home textile yarns of novel antibacterial
Line, family's textile fabric fluffy insulation after weaving, pro-skin is comfortable, yarn strength is high, filoplume is few, and antibacterial is warming, is not easy pilling, tool
There is good sucting wet air permeability.Present invention process is simple, can mass produce, improve the use value of product, meet consumption
Demand, so as to improve added value of product, the market competitiveness is extremely strong, is the ideal substitute products of existing product.
Technical solution：A kind of Weaving method of the warming household yarn of novel antibacterial, the warming household yarn of the novel antibacterial
Line is by coffee carbon fiber, Modal fibre and ptt fiber is blended forms, and Weaving method includes cotton cleaning process, carding step, simultaneously
Process, Roving Frames, spinning process；Concrete operation step is as follows：
(1) cotton cleaning process：Coffee carbon fiber, Modal fibre and three kinds of raw fibres progress of ptt fiber are blended, it is blended
It is preceding add in mass ratio be 1% antistatic agent, 1% moisturizer, it is blended after fiber be sent into Cotton blending in hopper machine, utilize coiled mechanism
Into cotton roll；Cotton rolling quantity is 370-420g/m；
(2) carding step：In opening and cleaning step, weight of card sliver 3.8-4g/m, cylinder speed 300-340r/min, thorn
Roller speed is 700-800r/min；
(3) mixing in doubling step：Drafting multiple head simultaneously, it is pre- simultaneously, end and respectively 1.7 times, 1.7 times, 1.2 times, obtain preferably fine
Degree of stretching and bar evenness are tieed up, drafting roller gauge uses 12mm × 19mm；
(4) Roving Frames：The small quantification of 4.2-5.2g/10m of rove, twist factor 50-60, drafting multiple is 1.2-2 times,
Roller gauge is 25mm × 35mm, and rove strip dry CV value is 5-5.5%；
(5) spinning process：Reduce using antistatic carbon black rubber roller and suitably the front roller speed of spun yarn, back area draft times
1.2-1.5 times of number, twist factor 340-380 sth. made by twisting/m obtains warming spun yarn and antibacterial spun yarn.
As an optimization：The warming household yarn of the novel antibacterial is made of following parts by weight：35-65 parts of coffee carbon
Fiber, 15-25 parts of Modal fibre and 15-25 parts of ptt fiber.
As an optimization：The coffee carbon fiber is 1.5D-10D, 38mm-42mm, hollow round hole, abnormity, the coffee
Coffee carbon fiber is sprayed by 1-3% nanometer titanium dioxide antibiotic liquid, is sprayed as 20-50g/m2, dried at 90-110 DEG C.
As an optimization：The Modal fibre specification is 1.4D-1.6D, 37-39mm.
As an optimization：The ptt fiber specification is 0.8D-1.2D, 36-39mm, ultra-fine, imitates suede short fibre.
Advantageous effect：Specific advantage is as follows：
1st, present invention process is simple, it can be achieved that mass automatic production, which has that pro-skin is comfortable, yarn is strong
Power is high, filoplume is few, and antibacterial is warming, is not easy pilling with good sucting wet air permeability, meets the consumers' such as family, hotel
Demand, family's textile fabric fluffy insulation after being weaved by the present invention, has a good application prospect
2nd, in the present invention, Modal fibre offer pro-skin is comfortable, filoplume is few, height is warming, excellent sucting wet air permeability.
The hollow nature of ptt fiber provides comfortable, warming, the excellent sucting wet air permeability of pro-skin.Coffee carbon fiber provides high-tenacity, Gao Bao
Warm, low pilling rate, abnormity, the spraying of nanometer titanium dioxide antibiotic liquid improve its excellent sucting wet air permeability and antibiotic property.
3rd, in the present invention, the electrostatic agent, moisturizer addition fiber antistatic property, be conducive to the spinning of rear road, drop
Low filoplume.
4th, simultaneously drafting multiple suitably increase is conducive to improve Fiber Straightness head simultaneously, in advance in the drawing process in the present invention,
End draft multiple is small, is conducive to strip bar evenness.
Specific embodiment
The technical solution in the embodiment of the present invention will be clearly and completely described below, so that the technology of this field
Personnel can be better understood from advantages and features of the invention, so as to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only part of the embodiment of the present invention, instead of all the embodiments, based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, shall fall within the protection scope of the present invention.
Specific embodiment 1
A kind of warming household yarn of novel antibacterial, by coffee carbon fiber, Modal fibre and ptt fiber is blended forms.Institute
The warming household yarn of novel antibacterial stated is made of following parts by weight：35 parts of coffee carbon fiber, 15 parts of Modal fibre
With 15 parts of ptt fiber.The coffee carbon fiber is 1.5D, and 38mm, hollow round hole is special-shaped, the coffee carbon fiber warp
It crosses 1% nanometer titanium dioxide antibiotic liquid to be sprayed, spray as 20g/m2, dried at 90 DEG C.The Modal fibre rule
Lattice are 1.4D, 37mm.The ptt fiber specification is 0.8D, 36mm, ultra-fine, imitates suede short fibre.
The Weaving method of the warming household yarn of the novel antibacterial includes cotton cleaning process, carding step, mixing in doubling step, thick
Yarn process, spinning process；Concrete operation step is as follows：
(1) cotton cleaning process：Coffee carbon fiber, Modal fibre and three kinds of raw fibres progress of ptt fiber are blended, it is blended
It is preceding add in mass ratio be 1% antistatic agent, 1% moisturizer, it is blended after fiber be sent into Cotton blending in hopper machine, utilize coiled mechanism
Into cotton roll；Cotton rolling quantity is 370g/m；
(2) carding step：In opening and cleaning step, weight of card sliver 3.8g/m, cylinder speed 300r/min, licker-in speed
For 700r/min；
(3) mixing in doubling step：Drafting multiple head simultaneously, it is pre- simultaneously, end and respectively 1.7 times, 1.7 times, 1.2 times, obtain preferably fine
Degree of stretching and bar evenness are tieed up, drafting roller gauge uses 12mm × 19mm；
(4) Roving Frames：The small quantification of 4.2g/10m of rove, twist factor 50, drafting multiple are 1.2 times, roller gauge
For 25mm × 35mm, rove strip dry CV value is 5%；
(5) spinning process：Reduce using antistatic carbon black rubber roller and suitably the front roller speed of spun yarn, back area draft times
1.2 times of number, twist factor 340 twists with the fingers/m, obtains warming spun yarn and antibacterial spun yarn.
Specific embodiment 2
A kind of warming household yarn of novel antibacterial, by coffee carbon fiber, Modal fibre and ptt fiber is blended forms.Institute
The warming household yarn of novel antibacterial stated is made of following parts by weight：65 parts of coffee carbon fiber, 25 parts of Modal fibre
With 25 parts of ptt fiber.The coffee carbon fiber is 10D, and 42mm, hollow round hole is special-shaped, and the coffee carbon fiber passes through
3% nanometer titanium dioxide antibiotic liquid is sprayed, and is sprayed as 50g/m2, dried at 110 DEG C.The Modal fibre specification
For 1.6D, 39mm.The ptt fiber specification is 1.2D, 39mm, ultra-fine, imitates suede short fibre.
The Weaving method of the warming household yarn of the novel antibacterial includes cotton cleaning process, carding step, mixing in doubling step, thick
Yarn process, spinning process；Concrete operation step is as follows：
(1) cotton cleaning process：Coffee carbon fiber, Modal fibre and three kinds of raw fibres progress of ptt fiber are blended, it is blended
It is preceding add in mass ratio be 1% antistatic agent, 1% moisturizer, it is blended after fiber be sent into Cotton blending in hopper machine, utilize coiled mechanism
Into cotton roll；Cotton rolling quantity is 420g/m；
(2) carding step：In opening and cleaning step, weight of card sliver 4g/m, cylinder speed 340r/min, licker-in speed is
800r/min；
(3) mixing in doubling step：Drafting multiple head simultaneously, it is pre- simultaneously, end and respectively 1.7 times, 1.7 times, 1.2 times, obtain preferably fine
Degree of stretching and bar evenness are tieed up, drafting roller gauge uses 12mm × 19mm；
(4) Roving Frames：The small quantification of 5.2g/10m of rove, twist factor 60, drafting multiple are 2 times, and roller gauge is
25mm × 35mm, rove strip dry CV value are 5.5%；
(5) spinning process：Reduce using antistatic carbon black rubber roller and suitably the front roller speed of spun yarn, back area draft times
1.5 times of number, twist factor 380 twists with the fingers/m, obtains warming spun yarn and antibacterial spun yarn.
Specific embodiment 3
A kind of warming household yarn of novel antibacterial, by coffee carbon fiber, Modal fibre and ptt fiber is blended forms.Institute
The warming household yarn of novel antibacterial stated is made of following parts by weight：55 parts of coffee carbon fiber, 19 parts of Modal fibre
With 22 parts of ptt fiber.The coffee carbon fiber is 7D, and 40mm, hollow round hole is special-shaped, and the coffee carbon fiber passes through
2% nanometer titanium dioxide antibiotic liquid is sprayed, and is sprayed as 35g/m2, dried at 100 DEG C.The Modal fibre specification
For 1.5D, 38mm.The ptt fiber specification is 1.1D, 38mm, ultra-fine, imitates suede short fibre.
The Weaving method of the warming household yarn of the novel antibacterial includes cotton cleaning process, carding step, mixing in doubling step, thick
Yarn process, spinning process；Concrete operation step is as follows：
(1) cotton cleaning process：Coffee carbon fiber, Modal fibre and three kinds of raw fibres progress of ptt fiber are blended, it is blended
It is preceding add in mass ratio be 1% antistatic agent, 1% moisturizer, it is blended after fiber be sent into Cotton blending in hopper machine, utilize coiled mechanism
Into cotton roll；Cotton rolling quantity is 390g/m；
(2) carding step：In opening and cleaning step, weight of card sliver 3.9g/m, cylinder speed 320r/min, licker-in speed
For 750r/min；
(3) mixing in doubling step：Drafting multiple head simultaneously, it is pre- simultaneously, end and respectively 1.7 times, 1.7 times, 1.2 times, obtain preferably fine
Degree of stretching and bar evenness are tieed up, drafting roller gauge uses 12mm × 19mm；
(4) Roving Frames：The small quantification of 4.8g/10m of rove, twist factor 56, drafting multiple are 1.7 times, roller gauge
For 25mm × 35mm, rove strip dry CV value is 5.3%；
(5) spinning process：Reduce using antistatic carbon black rubber roller and suitably the front roller speed of spun yarn, back area draft times
1.4 times of number, twist factor 360 twists with the fingers/m, obtains warming spun yarn and antibacterial spun yarn.
Present invention process is simple, it can be achieved that mass automatic production, which has that pro-skin is comfortable, yarn strength
Height, filoplume are few, and antibacterial is warming, are not easy pilling with good sucting wet air permeability, meet the need of the consumers such as family, hotel
It asks, family's textile fabric fluffy insulation after being weaved by the present invention has a good application prospect
In the present invention, Modal fibre offer pro-skin is comfortable, filoplume is few, height is warming, excellent sucting wet air permeability.
The hollow nature of ptt fiber provides comfortable, warming, the excellent sucting wet air permeability of pro-skin.Coffee carbon fiber provides high-tenacity, Gao Bao
Warm, low pilling rate, abnormity, the spraying of nanometer titanium dioxide antibiotic liquid improve its excellent sucting wet air permeability and antibiotic property.
In the present invention, the electrostatic agent, moisturizer addition fiber antistatic property, be conducive to the spinning of rear road, reduce
Filoplume.
Simultaneously drafting multiple suitably increase is conducive to improve Fiber Straightness head simultaneously, in advance in drawing process in the present invention, last
And drafting multiple is small, is conducive to strip bar evenness.
Claims (5)
1. a kind of Weaving method of the warming household yarn of novel antibacterial, it is characterised in that：The warming household yarn of the novel antibacterial
Line is by coffee carbon fiber, Modal fibre and ptt fiber is blended forms, and Weaving method includes cotton cleaning process, carding step, simultaneously
Process, Roving Frames, spinning process；Concrete operation step is as follows：
(1) cotton cleaning process：Coffee carbon fiber, Modal fibre and three kinds of raw fibres progress of ptt fiber are blended, add before blended
Enter mass ratio be 1% antistatic agent, 1% moisturizer, it is blended after fiber be sent into Cotton blending in hopper machine, cotton is made using lapper
Volume；Cotton rolling quantity is 370-420g/m；
(2) carding step：In opening and cleaning step, weight of card sliver 3.8-4g/m, cylinder speed 300-340r/min, licker-in speed
It spends for 700-800r/min；
(3) mixing in doubling step：Drafting multiple head simultaneously, it is pre- simultaneously, end and respectively 1.7 times, 1.7 times, 1.2 times, obtain preferable fiber and stretch
Straight degree and bar evenness, drafting roller gauge use 12mm × 19mm；
(4) Roving Frames：The small quantification of 4.2-5.2g/10m of rove, twist factor 50-60, drafting multiple is 1.2-2 times, roller
Gauge is 25mm × 35mm, and rove strip dry CV value is 5-5.5%；
(5) spinning process：Reduce using antistatic carbon black rubber roller and suitably the front roller speed of spun yarn, back zone drafting multiple
1.2-1.5 times, twist factor 340-380 sth. made by twisting/m obtains warming spun yarn and antibacterial spun yarn.
2. the Weaving method of the warming home textile yarn of novel antibacterial according to claim 1, it is characterised in that：Described is new
Type antibacterial thermal insulating household yarn is made of following parts by weight：35-65 parts of coffee carbon fiber, 15-25 parts of Modal fibre
With 15-25 parts of ptt fiber.
3. the Weaving method of the warming home textile yarn of novel antibacterial according to claim 2, it is characterised in that：The coffee
Coffee carbon fiber is 1.5D-10D, and 38mm-42mm, hollow round hole, abnormity, the coffee carbon fiber is by 1-3% nano-silicas
Change titanium antimicrobial fluid to be sprayed, spray as 20-50g/m2, dried at 90-110 DEG C.
4. the Weaving method of the warming home textile yarn of novel antibacterial according to claim 2, it is characterised in that：It is described not
Dai Er fiber dimensious is 1.4D-1.6D, 37-39mm.
5. the Weaving method of the warming home textile yarn of novel antibacterial according to claim 2, it is characterised in that：Described
Ptt fiber specification is 0.8D-1.2D, 36-39mm, ultra-fine, imitates suede short fibre.