CN108118535A - A kind of garment material wash and wear finisher and finishing technique - Google Patents
A kind of garment material wash and wear finisher and finishing technique Download PDFInfo
- Publication number
- CN108118535A CN108118535A CN201711433453.3A CN201711433453A CN108118535A CN 108118535 A CN108118535 A CN 108118535A CN 201711433453 A CN201711433453 A CN 201711433453A CN 108118535 A CN108118535 A CN 108118535A
- Authority
- CN
- China
- Prior art keywords
- agent
- pressing
- finishing
- cloth specimen
- garment material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of garment material wash and wear finisher and finishing technique, the finishing agent is made of the following raw material configuration：Reducing agent 20g/L, bleeding agent 1-2g/L and PH conditioning agent 10g/L, the finishing technique, which includes anti-shrinking, spray finishing agent, Xun Huan pressing, low temperature drying and cooling collection step, the present invention, has the advantages that simple for process, stability is good, color change is small.
Description
Technical field
The invention belongs to garment material technical fields, and in particular to a kind of garment material wash and wear finisher and finishing technique.
Background technology
Wool fabric is much disappeared since its excellent characteristic is for example soft, good warmth retention property, gloss are soft etc.
The welcome of the person of expense, in the world to Machine Washable, can the product of tumble drying, few flatiron and anti-fold be known as easy care product, as
Easily nursing Woolens, first have to solve is felting phenomenon of the fabric in machine washing process；Secondly, it is desirable that fabric table after drying
Face is smooth, and to have certain washable conformal performance for the intrinsic pleat paulownia of some clothes (such as seams of a trouser leg, cuff), these
New requirement proposes new requirement to the modernization processing of wool fabric, and pure wool and wool blended at high proportion or intertexture take
The pleat paulownia stability of dress is always insoluble problem.
The content of the invention
There is provided it is an object of the invention to overcome the deficiencies in the prior art it is a kind of it is simple for process, stability is good, color becomes
Change small garment material wash and wear finisher and finishing technique.
The technical scheme is that：A kind of garment material wash and wear finisher, the finishing agent are matched somebody with somebody by the following raw material
Put composition：Reducing agent 20g/L, bleeding agent 1-2g/L and PH conditioning agent 10g/L.
A kind of non-ironing finishing technique of garment material, the finishing technique include the following steps：
Step 1：Cloth specimen is placed in the solution of solvent-borne type silicone resin and carries out immersion treatment by anti-shrinking；
Step 2：Finishing agent is sprayed, sprays finishing agent on the cloth specimen surface that immersion treatment is crossed, wherein the concentration of reducing agent is in finishing agent
2%, band liquid measure is 60%；
Step 3：Pressing is cycled, the cloth specimen that step 2 is obtained carries out cycling pressing using hot plate pressing machine, and wherein pressing temperature is
100 DEG C, the pressing time is 3min, and pressing number is at least 2 times；
Step 4：Low temperature drying, the cloth specimen that step 3 is obtained, which is placed in low temperature environment, dries, and wherein drying temperature is
60-70 DEG C, the time is baked and banked up with earth as 2min；
Step 5：Cooling is collected, and the cloth specimen placement that step 4 obtains is carried out natural cooling at normal temperatures and pressures, treats the temperature of cloth specimen
It is collected when being cooled to room temperature spare.
Beneficial effects of the present invention：Using the fracture strength and breaking ductility of fabric of this technique after anti-shrinking
All increase, in finishing agent treatment process, ultimate strength increase may be because high temperature and reducing agent common work
Under, the supramolecular structure of wool fiber is changed, and is reset between macromolecular, internal stress is eliminated, by nothing
Setting state is changed into crystalline state so that ultimate strength and breaking ductility improve, while after this method processing fabric color change
Small, the present invention has the advantages that simple for process, stability is good, color change is small.
Specific embodiment
With reference to embodiment, the present invention is further illustrated.
Embodiment 1
A kind of garment material wash and wear finisher, the finishing agent are made of the following raw material configuration：Reducing agent 20g/L, infiltration
Agent 1-2g/L and PH conditioning agent 10g/L.
A kind of non-ironing finishing technique of garment material, the finishing technique include the following steps：
Step 1：Cloth specimen is placed in the solution of solvent-borne type silicone resin and carries out immersion treatment by anti-shrinking；
Step 2：Finishing agent is sprayed, sprays finishing agent on the cloth specimen surface that immersion treatment is crossed, wherein the concentration of reducing agent is in finishing agent
2%, band liquid measure is 60%；
Step 3：Pressing is cycled, the cloth specimen that step 2 is obtained carries out cycling pressing using hot plate pressing machine, and wherein pressing temperature is
100 DEG C, the pressing time is 3min, and pressing number is 2 times；
Step 4：Low temperature drying, the cloth specimen that step 3 is obtained, which is placed in low temperature environment, dries, and wherein drying temperature is 60
DEG C, the time is baked and banked up with earth as 2min；
Step 5：Cooling is collected, and the cloth specimen placement that step 4 obtains is carried out natural cooling at normal temperatures and pressures, treats the temperature of cloth specimen
It is collected when being cooled to room temperature spare.
It is all increased, arranged using the fracture strength and breaking ductility of fabric of this technique after anti-shrinking
In agent treatment process, increasing for ultimate strength may be because under the collective effect of high temperature and reducing agent, and wool fiber surpasses
Molecular structure is changed, and is reset between macromolecular, is eliminated internal stress, is changed into crystalline state by amorphous state,
So that ultimate strength and breaking ductility improve, at the same after this method processing fabric color change it is small, the present invention has technique
Simply, the advantages of stability is good, color change is small.
Claims (2)
1. a kind of garment material wash and wear finisher, it is characterised in that：The finishing agent is made of the following raw material configuration：Reduction
Agent 20g/L, bleeding agent 1-2g/L and PH conditioning agent 10g/L.
2. a kind of non-ironing finishing technique of garment material, it is characterised in that：The finishing technique includes the following steps：
Step 1：Cloth specimen is placed in the solution of solvent-borne type silicone resin and carries out immersion treatment by anti-shrinking；
Step 2：Finishing agent is sprayed, sprays finishing agent on the cloth specimen surface that immersion treatment is crossed, wherein the concentration of reducing agent is in finishing agent
2%, band liquid measure is 60%；
Step 3：Pressing is cycled, the cloth specimen that step 2 is obtained carries out cycling pressing using hot plate pressing machine, and wherein pressing temperature is
100 DEG C, the pressing time is 3min, and pressing number is at least 2 times；
Step 4：Low temperature drying, the cloth specimen that step 3 is obtained, which is placed in low temperature environment, dries, and wherein drying temperature is
60-70 DEG C, the time is baked and banked up with earth as 2min；
Step 5：Cooling is collected, and the cloth specimen placement that step 4 obtains is carried out natural cooling at normal temperatures and pressures, treats the temperature of cloth specimen
It is collected when being cooled to room temperature spare.