CN108103779A - A kind of environment-friendly type spinning sizing agent and preparation method thereof - Google Patents
A kind of environment-friendly type spinning sizing agent and preparation method thereof Download PDFInfo
- Publication number
- CN108103779A CN108103779A CN201711366024.9A CN201711366024A CN108103779A CN 108103779 A CN108103779 A CN 108103779A CN 201711366024 A CN201711366024 A CN 201711366024A CN 108103779 A CN108103779 A CN 108103779A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- sizing agent
- type spinning
- spinning sizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly type spinning sizing agent and preparation method thereof, the environment-friendly type spinning sizing agent is made of the raw material of following parts by weight：20 30 parts of plant amylum, 35 parts of coconut oil, 5 10 parts of animal origin, 57 parts of polyethylene glycol, 35 parts of polyethylene wax, 13 parts of urea, 57 parts of mannitol, 13 parts of antifoaming agent, 13 parts of sodium lignin sulfonate, 35 parts of bentonite, 30 50 parts of deionized water.The environment-friendly type spinning sizing agent preparation method of the present invention is relatively reasonable, adds the adhesion strength between fiber, improves the tension strength of yarn, to adapt to beat up in the hightension in weaving process, reduces broken end, improve efficiency.The environment-friendly type spinning sizing agent manufacturing process of the present invention is simple to operation, and low in raw material price easily obtains, and viscosity stabilization, can be gelatinized completely.
Description
Technical field
The invention belongs to textile Sizing Technology fields, specifically relate to a kind of environment-friendly type spinning sizing agent and its preparation side
Method.
Background technology
Warp sizing is one of critical process in textile manufacturing.With the development of science and technology, various tencel phases
After appearance, novel high speed loom is also such as emerged rapidly in large numbersBamboo shoots after a spring rain.The update of textile product, the continuous development of kind and new technology it is wide
General application promotes warp sizing technology also increasingly updating, and constantly advances.Three big elements of warp sizing are that slurry, sizing are set
Standby and slashing technique, three complement each other.Good sizing not only will will also lean on advanced slashing technique by good slurry and formula
And equipment, and the selection of slurry plays conclusive effect with cooperation.With the development of textile industry, existing slurry is reasonably selected
Material, active development new slurry, the slurry formula to study science should meet the requirement of slashing technique, energy saving again, reduce
Environmental pollution reduces sizing costs, this is a highly important technical work.
Warp sizing is the key link of Textile Engineering, and the main purpose of sizing is to improve the wearability of yarn, is spun at present
It knits slurry and is broadly divided into starch, polyethylene glycols, polyacrylic acid three categories slurry, at home and abroad play an important role.But
At present there is also some problems, such as：Polyethylene glycol slurry cannot degrade, and cause serious environmental problem, by by
Gradually substitute, viscosity is serious again for traditional polypropylene slurry, causes leasing difficult, and Starch Size viscosity fluctuation is big, gelatinizing
It can be poor.So it is badly in need of developing a kind of environmental protection, cheap, biodegradable slurry, to meet the needs of slurry market.
The content of the invention
It is an object of the invention to provide a kind of environment-friendly type spinning sizing agent and preparation method thereof, to solve above-mentioned background technology
The problem of middle proposition.
To achieve the above object, the present invention provides following technical solution：
A kind of environment-friendly type spinning sizing agent, according to parts by weight, including following components：20-30 parts of plant amylum, coconut oil 3-
5 parts, 5-10 parts of animal origin, 5-7 parts of polyethylene glycol, 3-5 parts of polyethylene wax, 1-3 parts of urea, 5-7 parts of mannitol, antifoaming agent 1-
3 parts, 1-3 parts of sodium lignin sulfonate, 3-5 parts of bentonite, 30-50 parts of deionized water.
Preferably, the plant amylum for cornstarch, sweet potato starch, tapioca, wheaten starch, peanut starch,
Pea starch, potato starch it is one or more than one kinds of.
Preferably, the antifoaming agent is aqueous silicone oil.
Preferably, the environment-friendly type spinning sizing agent, according to parts by weight, including following components：20 parts of plant amylum, coconut palm
It is 3 parts of seed oil, 5 parts of animal origin, 5 parts of polyethylene glycol, 3 parts of polyethylene wax, 1 part of urea, 5 parts of mannitol, 1 part of antifoaming agent, wooden
Plain 1 part of sodium sulfonate, 3 parts of bentonite, 30 parts of deionized water.
Preferably, the environment-friendly type spinning sizing agent, according to parts by weight, including following components：30 parts of plant amylum, coconut palm
It is 5 parts of seed oil, 10 parts of animal origin, 7 parts of polyethylene glycol, 5 parts of polyethylene wax, 3 parts of urea, 7 parts of mannitol, 3 parts of antifoaming agent, wooden
Plain 3 parts of sodium sulfonate, 5 parts of bentonite, 50 parts of deionized water.
Preferably, the environment-friendly type spinning sizing agent, according to parts by weight, including following components：25 parts of plant amylum, coconut palm
It is 4 parts of seed oil, 8 parts of animal origin, 6 parts of polyethylene glycol, 4 parts of polyethylene wax, 2 parts of urea, 6 parts of mannitol, 2 parts of antifoaming agent, wooden
Plain 2 parts of sodium sulfonate, 4 parts of bentonite, 40 parts of deionized water.
Preferably, the antifoaming agent is aqueous silicone oil.
Preferably, the preparation method of the environment-friendly type spinning sizing agent, specific steps include：
Step 1,30-50 parts of deionized water is added in a kettle, and rise temperature is to 40-50 DEG C；
Step 2,20-30 parts of plant amylum, 3-5 parts of coconut oil, 5-10 parts of animal origin, 5-7 parts of polyethylene glycol are added in,
It 500-1000 revs/min, stirs 20-30 minutes；
Step 3, temperature is reduced to 30-40 DEG C, adds in 3-5 parts of polyethylene wax, 1-3 parts of urea, 5-7 parts of mannitol, 500-
It 1000 revs/min, stirs 20-30 minutes；
Step 4,1-3 parts of antifoaming agent of addition, 1-3 parts of sodium lignin sulfonate, 3-5 parts of bentonite, 500-1000 revs/min,
Stirring 20-30 minutes；
Step 5, stirring is closed down, obtains prepared environment-friendly liquid type spinning sizing agent；
Step 6, stand and be cooled in stirred tank environment-friendly liquid type spinning sizing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Compared with prior art, the beneficial effects of the invention are as follows：
1st, environment-friendly type spinning sizing agent manufacturing process of the invention is simple to operation, and low in raw material price easily obtains, and viscosity
Stablize, can be gelatinized completely.
2nd, mutual compatibility, synergistic effect, collectively constituting property between various raw materials used in environment-friendly type spinning sizing agent of the invention
The excellent product of energy.
3rd, environment-friendly type spinning sizing agent of the invention in application process, does not generate poisonous gas or solid matter.
4th, environment-friendly type spinning sizing agent preparation method of the invention is relatively reasonable, adds the adhesion strength between fiber, improves
The tension strength of yarn, to adapt to beat up in the hightension in weaving process, reduces broken end, improves efficiency.
5th, environment-friendly type spinning sizing agent of the invention has good film forming, is easy to desizing.
6th, environment-friendly type spinning sizing agent anti-aging property of the invention is good, has good affinity.
7th, environment-friendly type spinning sizing agent of the invention improves stability, film forming, degree of adhesion, the transparency of paste liquid.
8th, technique is simplified, safe operation is simple, is easy to industrialized production.
9th, use of the invention can receive good economic benefit.
Example is embodied
The invention discloses a kind of environment-friendly type spinning sizing agent, according to parts by weight, including following components：Plant amylum 20-
30 parts, 3-5 parts of coconut oil, 5-10 parts of animal origin, 5-7 parts of polyethylene glycol, 3-5 parts of polyethylene wax, 1-3 parts of urea, mannitol
5-7 parts, 1-3 parts of antifoaming agent, 1-3 parts of sodium lignin sulfonate, 3-5 parts of bentonite, 30-50 parts of deionized water.
The present invention also provides a kind of preparation method of environment-friendly type spinning sizing agent, specific steps include：
Step 1,30-50 parts of deionized water is added in a kettle, and rise temperature is to 40-50 DEG C；
Step 2,20-30 parts of plant amylum, 3-5 parts of coconut oil, 5-10 parts of animal origin, 5-7 parts of polyethylene glycol are added in,
It 500-1000 revs/min, stirs 20-30 minutes；
Step 3, temperature is reduced to 30-40 DEG C, adds in 3-5 parts of polyethylene wax, 1-3 parts of urea, 5-7 parts of mannitol, 500-
It 1000 revs/min, stirs 20-30 minutes；
Step 4,1-3 parts of antifoaming agent of addition, 1-3 parts of sodium lignin sulfonate, 3-5 parts of bentonite, 500-1000 revs/min,
Stirring 20-30 minutes；
Step 5, stirring is closed down, obtains prepared environment-friendly liquid type spinning sizing agent；
Step 6, stand and be cooled in stirred tank environment-friendly liquid type spinning sizing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 1
The invention discloses a kind of environment-friendly type spinning sizing agent, according to parts by weight, including following components：Plant amylum 20
Part, 3 parts of coconut oil, 5 parts of animal origin, 5 parts of polyethylene glycol, 3 parts of polyethylene wax, 1 part of urea, 5 parts of mannitol, 1 part of antifoaming agent,
1 part of sodium lignin sulfonate, 3 parts of bentonite, 30 parts of deionized water.
The present invention also provides a kind of preparation method of environment-friendly type spinning sizing agent, specific steps include：
Step 1,30 parts of deionized water is added in a kettle, and rise temperature is to 40 DEG C；
Step 2,20 parts of plant amylum of addition, 3 parts of coconut oil, 5 parts of animal origin, 5 parts of polyethylene glycol, 500 revs/min,
Stirring 20 minutes；
Step 3, temperature is reduced to 30 DEG C, is added in 3 parts of polyethylene wax, 1 part of urea, 5 parts of mannitol, 500 revs/min, is stirred
It mixes 20 minutes；
Step 4,1 part of antifoaming agent, 1 part of sodium lignin sulfonate, 3 parts of bentonite are added in, 500 revs/min, is stirred 20 minutes；
Step 5, stirring is closed down, obtains prepared environment-friendly liquid type spinning sizing agent；
Step 6, stand and be cooled in stirred tank environment-friendly liquid type spinning sizing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 2
The invention discloses a kind of environment-friendly type spinning sizing agent, according to parts by weight, including following components：Plant amylum 25
Part, 4 parts of coconut oil, 8 parts of animal origin, 6 parts of polyethylene glycol, 4 parts of polyethylene wax, 2 parts of urea, 6 parts of mannitol, 2 parts of antifoaming agent,
2 parts of sodium lignin sulfonate, 4 parts of bentonite, 40 parts of deionized water.
The present invention also provides a kind of preparation method of environment-friendly type spinning sizing agent, specific steps include：
Step 1,40 parts of deionized water is added in a kettle, and rise temperature is to 45 DEG C；
Step 2,25 parts of plant amylum of addition, 4 parts of coconut oil, 8 parts of animal origin, 6 parts of polyethylene glycol, 800 revs/min,
Stirring 25 minutes；
Step 3, temperature is reduced to 35 DEG C, is added in 4 parts of polyethylene wax, 2 parts of urea, 6 parts of mannitol, 800 revs/min, is stirred
It mixes 25 minutes；
Step 4,2 parts of antifoaming agent, 2 parts of sodium lignin sulfonate, 4 parts of bentonite are added in, 800 revs/min, is stirred 25 minutes；
Step 5, stirring is closed down, obtains prepared environment-friendly liquid type spinning sizing agent；
Step 6, stand and be cooled in stirred tank environment-friendly liquid type spinning sizing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 3
The invention discloses a kind of environment-friendly type spinning sizing agent, according to parts by weight, including following components：Plant amylum 30
Part, 5 parts of coconut oil, 10 parts of animal origin, 7 parts of polyethylene glycol, 5 parts of polyethylene wax, 3 parts of urea, 7 parts of mannitol, antifoaming agent 3
Part, 3 parts of sodium lignin sulfonate, 5 parts of bentonite, 50 parts of deionized water.
The present invention also provides a kind of preparation method of environment-friendly type spinning sizing agent, specific steps include：
Step 1,50 parts of deionized water is added in a kettle, and rise temperature is to 50 DEG C；
Step 2,30 parts of plant amylum of addition, 5 parts of coconut oil, 10 parts of animal origin, 7 parts of polyethylene glycol, 1000 revs/min
Clock stirs 30 minutes；
Step 3, temperature is reduced to 40 DEG C, is added in 5 parts of polyethylene wax, 3 parts of urea, 7 parts of mannitol, 800 revs/min, is stirred
It mixes 30 minutes；
Step 4,3 parts of antifoaming agent, 3 parts of sodium lignin sulfonate, 5 parts of bentonite are added in, 1000 revs/min, is stirred 20 minutes；
Step 5, stirring is closed down, obtains prepared environment-friendly liquid type spinning sizing agent；
Step 6, stand and be cooled in stirred tank environment-friendly liquid type spinning sizing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 4
The invention discloses a kind of environment-friendly type spinning sizing agent, according to parts by weight, including following components：Plant amylum 25
Part, 4 parts of coconut oil, 10 parts of animal origin, 7 parts of polyethylene glycol, 5 parts of polyethylene wax, 1 part of urea, 5 parts of mannitol, antifoaming agent 3
Part, 3 parts of sodium lignin sulfonate, 3 parts of bentonite, 40 parts of deionized water.
The present invention also provides a kind of preparation method of environment-friendly type spinning sizing agent, specific steps include：
Step 1,40 parts of deionized water is added in a kettle, and rise temperature is to 45 DEG C；
Step 2,25 parts of plant amylum of addition, 4 parts of coconut oil, 10 parts of animal origin, 7 parts of polyethylene glycol, 800 revs/min,
Stirring 20 minutes；
Step 3, temperature is reduced to 30 DEG C, is added in 5 parts of polyethylene wax, 1 part of urea, 5 parts of mannitol, 500 revs/min, is stirred
It mixes 30 minutes；
Step 4,3 parts of antifoaming agent, 3 parts of sodium lignin sulfonate, 3 parts of bentonite are added in, 1000 revs/min, is stirred 20 minutes；
Step 5, stirring is closed down, obtains prepared environment-friendly liquid type spinning sizing agent；
Step 6, stand and be cooled in stirred tank environment-friendly liquid type spinning sizing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Test case
The environment-friendly type spinning sizing agent of embodiment 1,2,3,4 is tested for the property, test result is as follows：
The above-mentioned various embodiments enumerated, under the premise of reconcilable, can be mutually combined implementation, those skilled in the art
The explanation to embodiment above can be combined, as the foundation being combined to the technical characteristic in different embodiments.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of environment-friendly type spinning sizing agent, it is characterised in that：The environment-friendly type spinning sizing agent includes the raw material of following parts by weight：
20-30 parts of plant amylum, 3-5 parts of coconut oil, 5-10 parts of animal origin, 5-7 parts of polyethylene glycol, 3-5 parts of polyethylene wax, urea 1-
3 parts, 5-7 parts of mannitol, 1-3 parts of antifoaming agent, 1-3 parts of sodium lignin sulfonate, 3-5 parts of bentonite, 30-50 parts of deionized water.
2. environment-friendly type spinning sizing agent according to claim 1, it is characterised in that：The plant amylum for cornstarch,
Sweet potato starch, tapioca, wheaten starch, peanut starch, pea starch, potato starch it is one or more than one kinds of.
3. environment-friendly type spinning sizing agent according to claim 1, it is characterised in that：The antifoaming agent is aqueous silicone oil.
4. environment-friendly type spinning sizing agent according to claim 1, it is characterised in that：According to parts by weight, including following components：
20 parts of plant amylum, 3 parts of coconut oil, 5 parts of animal origin, 5 parts of polyethylene glycol, 3 parts of polyethylene wax, 1 part of urea, 5 parts of mannitol,
1 part of antifoaming agent, 1 part of sodium lignin sulfonate, 3 parts of bentonite, 30 parts of deionized water.
5. environment-friendly type spinning sizing agent according to claim 1, it is characterised in that：According to parts by weight, including following components：
25 parts of plant amylum, 4 parts of coconut oil, 8 parts of animal origin, 6 parts of polyethylene glycol, 4 parts of polyethylene wax, 2 parts of urea, 6 parts of mannitol,
2 parts of antifoaming agent, 2 parts of sodium lignin sulfonate, 4 parts of bentonite, 40 parts of deionized water.
6. environment-friendly type spinning sizing agent according to claim 1, it is characterised in that：According to parts by weight, including following components：
30 parts of plant amylum, 5 parts of coconut oil, 10 parts of animal origin, 7 parts of polyethylene glycol, 5 parts of polyethylene wax, 3 parts of urea, mannitol 7
Part, 3 parts of antifoaming agent, 3 parts of sodium lignin sulfonate, 5 parts of bentonite, 50 parts of deionized water.
7. a kind of preparation method using environment-friendly type spinning sizing agent any one of the claims 1-6, it is characterised in that：
Specific steps include：
Step 1,30-50 parts of deionized water is added in a kettle, and rise temperature is to 40-50 DEG C；
Step 2,20-30 parts of plant amylum, 3-5 parts of coconut oil, 5-10 parts of animal origin, 5-7 parts of polyethylene glycol, 500- are added in
It 1000 revs/min, stirs 20-30 minutes；
Step 3, temperature is reduced to 30-40 DEG C, adds in 3-5 parts of polyethylene wax, 1-3 parts of urea, 5-7 parts of mannitol, 500-1000
Rev/min, it stirs 20-30 minutes；
Step 4,1-3 parts of antifoaming agent, 1-3 parts of sodium lignin sulfonate, 3-5 parts of bentonite are added in, 500-1000 revs/min, is stirred
20-30 minutes；
Step 5, stirring is closed down, obtains prepared environment-friendly liquid type spinning sizing agent；
Step 6, stand and be cooled in stirred tank environment-friendly liquid type spinning sizing agent and be less than 20 DEG C, blowing encapsulation, finished product.