CN107829321A - A kind of alkali-resistant penetrant and preparation method thereof - Google Patents
A kind of alkali-resistant penetrant and preparation method thereof Download PDFInfo
- Publication number
- CN107829321A CN107829321A CN201710983553.7A CN201710983553A CN107829321A CN 107829321 A CN107829321 A CN 107829321A CN 201710983553 A CN201710983553 A CN 201710983553A CN 107829321 A CN107829321 A CN 107829321A
- Authority
- CN
- China
- Prior art keywords
- parts
- alkali
- resistant penetrant
- dimethicone
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of alkali-resistant penetrant and preparation method thereof, the alkali-resistant penetrant is made up of the raw material of following parts by weight:10 20 parts of SAS, 35 parts of sulfonated oil, 10 15 parts of secondary phosphate, 57 parts of neopelex, 57 parts of isooctanol polyethoxylate, 35 parts of sorb glucosides, 37 parts of lauroylamidopropyl betaine, 35 parts of dimethicone, 30 40 parts of deionized water.The alkali-resistant penetrant of the present invention has good emulsification, infiltration, scourability, degradable, suitable for each process of dyeing and printing process.The alkali-resistant penetrant manufacturing process of the present invention is simple to operation, and low in raw material price is easily obtained, and nontoxic, and volatility is low, and human body is not stimulated, and penetration is strong, conflicts with other auxiliary agents while using not producing.
Description
Technical field
The invention belongs to technical field of textile auxiliary agent, specifically relates to a kind of alkali-resistant penetrant and preparation method thereof.
Background technology
Bleeding agent has been as its name suggests osmosis, and with fixed hydrophilic lipophilic group, in the surface energy of solution
Align, and the material that can be remarkably decreased surface tension.
In dyeing and finishing process, in order that the material such as dyestuff is quickly penetrated into fabric and gone, it is necessary to add bleeding agent.
It is poor with other auxiliary agent interworking effects but existing bleeding agent fastness to alkali is not high, capillary effect is poor, the production of white powder point is had during high-temperature boiling
It is raw, so as to influence using effect.Some bleeding agents also contain APEO, not easily biological-degradable, are unfavorable for environmental protection.
The content of the invention
It is an object of the invention to provide a kind of alkali-resistant penetrant and preparation method thereof, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical scheme:
A kind of alkali-resistant penetrant, according to important number, including following components:SAS 10-20 parts, sulfonated oil 3-
5 parts, secondary phosphate 10-15 parts, neopelex 5-7 parts, isooctanol polyethoxylate 5-7 parts, sorb glucosides 3-5
Part, lauroylamidopropyl betaine 3-7 parts, dimethicone 3-5 parts, deionized water 30-40 parts.
Preferably, described alkali-resistant penetrant, according to parts by weight, including following components:10 parts of SAS, sulphur
3 parts of carburetion, 10 parts of secondary phosphate, 5 parts of neopelex, 5 parts of isooctanol polyethoxylate, 3 parts of sorb glucosides, bay
3 parts of amido propyl betaine, 3 parts of dimethicone, 30 parts of deionized water.
Preferably, described alkali-resistant penetrant, according to parts by weight, including following components:15 parts of SAS, sulphur
4 parts of carburetion, 13 parts of secondary phosphate, 6 parts of neopelex, 6 parts of isooctanol polyethoxylate, 4 parts of sorb glucosides, bay
5 parts of amido propyl betaine, 4 parts of dimethicone, 35 parts of deionized water.
Preferably, described alkali-resistant penetrant, according to parts by weight, including following components:20 parts of SAS, sulphur
5 parts of carburetion, 15 parts of secondary phosphate, 7 parts of neopelex, 7 parts of isooctanol polyethoxylate, 5 parts of sorb glucosides, bay
7 parts of amido propyl betaine, 5 parts of dimethicone, 40 parts of deionized water.
A kind of preparation method of alkali-resistant penetrant, is comprised the following steps that:
Step 1, deionized water 30-40 parts are added in a kettle, and rise temperature is to 50-60 DEG C;
Step 2, SAS 10-20 parts, sulfonated oil 3-5 parts, secondary phosphate 10-15 parts, detergent alkylate are added
Sodium sulfonate 5-7 parts, 500-1000 revs/min, stir 10-20 minutes;
Step 3,30-40 DEG C is cooled to, adds isooctanol polyethoxylate 5-7 parts, lauroylamidopropyl betaine 3-7
Part, 500-1000 revs/min, stir 20-30 minutes;
Step 4, it is cooled to 20-30 DEG C, adds sorb glucosides 3-5 parts, dimethicone 3-5 parts, 500-1000 revs/min
Clock, stir 20-30 minutes;
Step 5, stirring is closed down, the liquid alkali-resistant penetrant prepared;
Step 6, stand and be cooled in stirred tank liquid alkali-resistant penetrant and be less than 20 DEG C, blowing encapsulation, finished product.
Compared with prior art, the beneficial effects of the invention are as follows:
1st, alkali-resistant penetrant manufacturing process of the invention is simple to operation, and low in raw material price easily obtains, and nontoxic,
Volatility is low, and human body is not stimulated.
2nd, alkali-resistant penetrant of the invention has good emulsification, infiltration, scourability, degradable, suitable for dyeing and printing process
Each process.
3rd, mutual compatibility, synergy between various raw materials used in alkali-resistant penetrant of the invention, it is excellent to collectively constitute performance
Different product.
4th, alkali-resistant penetrant of the invention does not produce poisonous gas or solid matter in application process.
5th, alkali-resistant penetrant penetration of the invention is strong, conflicts with other auxiliary agents while using not producing.
6th, technique is simplified, safe operation is simple, is easy to industrialized production.
7th, use of the invention can receive good economic benefit.
Example is embodied
The invention discloses a kind of alkali-resistant penetrant, according to important number, including following components:SAS 10-
20 parts, sulfonated oil 3-5 parts, secondary phosphate 10-15 parts, neopelex 5-7 parts, isooctanol polyethoxylate 5-7 parts,
Sorb glucosides 3-5 parts, lauroylamidopropyl betaine 3-7 parts, dimethicone 3-5 parts, deionized water 30-40 parts.
Present invention also offers a kind of preparation method of alkali-resistant penetrant, comprise the following steps that:
Step 1, deionized water 30-40 parts are added in a kettle, and rise temperature is to 50-60 DEG C;
Step 2, SAS 10-20 parts, sulfonated oil 3-5 parts, secondary phosphate 10-15 parts, detergent alkylate are added
Sodium sulfonate 5-7 parts, 500-1000 revs/min, stir 10-20 minutes;
Step 3,30-40 DEG C is cooled to, adds isooctanol polyethoxylate 5-7 parts, lauroylamidopropyl betaine 3-7
Part, 500-1000 revs/min, stir 20-30 minutes;
Step 4, it is cooled to 20-30 DEG C, adds sorb glucosides 3-5 parts, dimethicone 3-5 parts, 500-1000 revs/min
Clock, stir 20-30 minutes;
Step 5, stirring is closed down, the liquid alkali-resistant penetrant prepared;
Step 6, stand and be cooled in stirred tank liquid alkali-resistant penetrant and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 1
The invention discloses a kind of alkali-resistant penetrant, according to important number, including following components:SAS 10
Part, 3 parts of sulfonated oil, 10 parts of secondary phosphate, 5 parts of neopelex, 5 parts of isooctanol polyethoxylate, sorb glucosides 3
Part, 3 parts of lauroylamidopropyl betaine, 3 parts of dimethicone, 30 parts of deionized water.
Present invention also offers a kind of preparation method of alkali-resistant penetrant, comprise the following steps that:
Step 1,30 parts of deionized water is added in a kettle, and rise temperature is to 50 DEG C;
Step 2,10 parts of SAS, 3 parts of sulfonated oil, 10 parts of secondary phosphate, neopelex 5 are added
Part, 500 revs/min, stir 20 minutes;
Step 3, it is cooled to 30 DEG C, adds 5 parts of isooctanol polyethoxylate, 3 parts of lauroylamidopropyl betaine, 500 turns/
Minute, stir 20 minutes;
Step 4,20 DEG C are cooled to, 3 parts of sorb glucosides, 3 parts of dimethicone is added, 500 revs/min, stirs 20 minutes;
Step 5, stirring is closed down, the liquid alkali-resistant penetrant prepared;
Step 6, stand and be cooled in stirred tank liquid alkali-resistant penetrant and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 2
The invention discloses a kind of alkali-resistant penetrant, according to important number, including following components:SAS 15
Part, 4 parts of sulfonated oil, 13 parts of secondary phosphate, 6 parts of neopelex, 6 parts of isooctanol polyethoxylate, sorb glucosides 4
Part, 5 parts of lauroylamidopropyl betaine, 4 parts of dimethicone, 35 parts of deionized water.
Present invention also offers a kind of preparation method of alkali-resistant penetrant, comprise the following steps that:
Step 1,35 parts of deionized water is added in a kettle, and rise temperature is to 55 DEG C;
Step 2,15 parts of SAS, 4 parts of sulfonated oil, 13 parts of secondary phosphate, neopelex 6 are added
Part, 900 revs/min, stir 15 minutes;
Step 3, it is cooled to 35 DEG C, adds 6 parts of isooctanol polyethoxylate, 5 parts of lauroylamidopropyl betaine, 900 turns/
Minute, stir 25 minutes;
Step 4,25 DEG C are cooled to, 4 parts of sorb glucosides, 4 parts of dimethicone is added, 900 revs/min, stirs 25 minutes;
Step 5, stirring is closed down, the liquid alkali-resistant penetrant prepared;
Step 6, stand and be cooled in stirred tank liquid alkali-resistant penetrant and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 3
The invention discloses a kind of alkali-resistant penetrant, according to important number, including following components:SAS 20
Part, 5 parts of sulfonated oil, 15 parts of secondary phosphate, 7 parts of neopelex, 7 parts of isooctanol polyethoxylate, sorb glucosides 5
Part, 7 parts of lauroylamidopropyl betaine, 5 parts of dimethicone, 40 parts of deionized water.
Present invention also offers a kind of preparation method of alkali-resistant penetrant, comprise the following steps that:
Step 1,40 parts of deionized water is added in a kettle, and rise temperature is to 60 DEG C;
Step 2,20 parts of SAS, 5 parts of sulfonated oil, 15 parts of secondary phosphate, neopelex 7 are added
Part, 1000 revs/min, stir 10 minutes;
Step 3, it is cooled to 40 DEG C, adds 7 parts of isooctanol polyethoxylate, 7 parts of lauroylamidopropyl betaine, 1000
Rev/min, stir 30 minutes;
Step 4,30 DEG C are cooled to, 5 parts of sorb glucosides, 5 parts of dimethicone is added, 1000 revs/min, stirs 30 points
Clock;
Step 5, stirring is closed down, the liquid alkali-resistant penetrant prepared;
Step 6, stand and be cooled in stirred tank liquid alkali-resistant penetrant and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 4
The invention discloses a kind of alkali-resistant penetrant, according to important number, including following components:SAS 20
Part, 4 parts of sulfonated oil, 15 parts of secondary phosphate, 7 parts of neopelex, 7 parts of isooctanol polyethoxylate, sorb glucosides 3
Part, 5 parts of lauroylamidopropyl betaine, 4 parts of dimethicone, 30 parts of deionized water.
Present invention also offers a kind of preparation method of alkali-resistant penetrant, comprise the following steps that:
Step 1,30 parts of deionized water is added in a kettle, and rise temperature is to 60 DEG C;
Step 2,20 parts of SAS, 4 parts of sulfonated oil, 15 parts of secondary phosphate, neopelex 7 are added
Part, 1000 revs/min, stir 10 minutes;
Step 3, it is cooled to 30 DEG C, adds 7 parts of isooctanol polyethoxylate, 5 parts of lauroylamidopropyl betaine, 900 turns/
Minute, stir 20 minutes;
Step 4,20 DEG C are cooled to, 3 parts of sorb glucosides, 4 parts of dimethicone is added, 1000 revs/min, stirs 20 points
Clock;
Step 5, stirring is closed down, the liquid alkali-resistant penetrant prepared;
Step 6, stand and be cooled in stirred tank liquid alkali-resistant penetrant and be less than 20 DEG C, blowing encapsulation, finished product.
Test case:
The bleeding agent of embodiment 1,2,3,4 is carried out to alkali resistance (naoh concentration 50g/L), sedimentation time survey
Examination, test result are as follows:
Embodiment | Alkali resistance | Sedimentation time (s) |
1 | Clarification | 15 |
2 | Clarification | 13.6 |
3 | Clarification | 10.6 |
4 | Clarification | 12.3 |
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
- A kind of 1. alkali-resistant penetrant, it is characterised in that:The alkali-resistant penetrant includes the raw material of following parts by weight:Secondary alkyl sulphur Sour sodium 10-20 parts, sulfonated oil 3-5 parts, secondary phosphate 10-15 parts, neopelex 5-7 parts, isooctanol polyoxyethylene Ether 5-7 parts, sorb glucosides 3-5 parts, lauroylamidopropyl betaine 3-7 parts, dimethicone 3-5 parts, deionized water 30-40 Part.
- A kind of 2. alkali-resistant penetrant according to claim 1, it is characterised in that:According to parts by weight, including following components: 10 parts of SAS, 3 parts of sulfonated oil, 10 parts of secondary phosphate, 5 parts of neopelex, isooctanol polyethoxylate 5 Part, 3 parts of sorb glucosides, 3 parts of lauroylamidopropyl betaine, 3 parts of dimethicone, 30 parts of deionized water.
- A kind of 3. alkali-resistant penetrant according to claim 1, it is characterised in that:According to parts by weight, including following components: 15 parts of SAS, 4 parts of sulfonated oil, 13 parts of secondary phosphate, 6 parts of neopelex, isooctanol polyethoxylate 6 Part, 4 parts of sorb glucosides, 5 parts of lauroylamidopropyl betaine, 4 parts of dimethicone, 35 parts of deionized water.
- A kind of 4. alkali-resistant penetrant according to claim 1, it is characterised in that:According to parts by weight, including following components: 20 parts of SAS, 5 parts of sulfonated oil, 15 parts of secondary phosphate, 7 parts of neopelex, isooctanol polyethoxylate 7 Part, 5 parts of sorb glucosides, 7 parts of lauroylamidopropyl betaine, 5 parts of dimethicone, 40 parts of deionized water.
- A kind of a kind of 5. preparation method of any described alkali-resistant penetrant in 1-4 using the claims, it is characterised in that: Comprise the following steps that:Step 1, deionized water 30-40 parts are added in a kettle, and rise temperature is to 50-60 DEG C;Step 2, SAS 10-20 parts, sulfonated oil 3-5 parts, secondary phosphate 10-15 parts, DBSA are added Sodium 5-7 parts, 500-1000 revs/min, stir 10-20 minutes;Step 3,30-40 DEG C is cooled to, adds isooctanol polyethoxylate 5-7 parts, lauroylamidopropyl betaine 3-7 parts, 500-1000 revs/min, stir 20-30 minutes;Step 4,20-30 DEG C is cooled to, sorb glucosides 3-5 parts, dimethicone 3-5 parts is added, 500-1000 revs/min, stirs Mix 20-30 minutes;Step 5, stirring is closed down, the liquid alkali-resistant penetrant prepared;Step 6, stand and be cooled in stirred tank liquid alkali-resistant penetrant and be less than 20 DEG C, blowing encapsulation, finished product.