CN108065749A - A kind of method that ink indicia is formed on aqueous ceramic non-sticking lining and non-stick pan tool and its manufacturing method - Google Patents
A kind of method that ink indicia is formed on aqueous ceramic non-sticking lining and non-stick pan tool and its manufacturing method Download PDFInfo
- Publication number
- CN108065749A CN108065749A CN201610999248.2A CN201610999248A CN108065749A CN 108065749 A CN108065749 A CN 108065749A CN 201610999248 A CN201610999248 A CN 201610999248A CN 108065749 A CN108065749 A CN 108065749A
- Authority
- CN
- China
- Prior art keywords
- sticking lining
- aqueous
- matrix
- ink indicia
- stick pan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to electric heating appliance technical fields, disclose a kind of method that ink indicia is formed on aqueous ceramic non-sticking lining and non-stick pan tool and its manufacturing method.This method includes：(1) aqueous base oil is sprayed in the inner surface of matrix, and is toasted at 35 55 DEG C to form non-sticking lining bottom；(2) bat printing processing is carried out on the surface of the non-sticking lining bottom to form ink indicia；(3) aqueous face oil is sprayed in the base inner surface for being formed with ink indicia, is then sintered curing process, forms non-sticking lining surface layer.This method can ensure on the premise of bat printing is intact, and the aqueous ceramic non-sticking lining for possessing high-bond, high rigidity, high-wear resistance and high-corrosion resistance is formed on matrix.
Description
Technical field
The present invention relates to electric heating appliance technical fields, and in particular, to one kind forms oil on aqueous ceramic non-sticking lining
The method and non-stick pan tool and its manufacturing method of ink mark.
Background technology
At present, there are mainly three types of wear-resistant unsticky coatings on the market：The first, it is a small amount of by being added in fluorine carbon type resin
Subtle SiO2、Al2O3、TiO2Etc. the higher abrasion resistant particles of hardness, improve entire non-sticking lining by these hard salient points
Wear-resisting property；Second, organic siliconresin wear-resistant coating；The third, is prepared by sol-gal process with SiO2Based on it is inorganic
Coating directly prepares purely inorganic wear-resistant coating.Since the health problem of organic coating is there are hidden danger, Teflon thing is particularly
After part, consumer is greatly lowered the acceptance level using fluororesin as the organic coating of representative.Inorganic ceramic coating is because of its health
Property, wearability, service life length etc. number of advantages, just liked be subject to more and more consumers.
Since ceramic non-stick coating possesses a series of excellent performances, by the welcome of consumer.In its face coat
Portion's pad-transfer printing ink prepares the logo such as water level line, can improve the aesthetic utility of coating.However, due to aqueous ceramic coating bat printing
Technics comparing is complicated, and at present there is no suitable tampon-printing process can ensure on the premise of bat printing is intact, ensures that aqueous ceramic does not glue
Possess good combination power between coating and matrix, and with the good performances such as corrosion-resistant, wear-resistant.
The content of the invention
The purpose of the invention is to ink indicia in aqueous ceramic non-sticking lining in the prior art is overcome to form difficulty
Drawbacks described above provides a kind of method that ink indicia is formed on aqueous ceramic non-sticking lining and non-stick pan tool and its manufacturer
Method, the forming method of the ink indicia can ensure on the premise of bat printing is intact, formed on matrix and possess high-bond, height
The aqueous ceramic non-sticking lining of hardness, high-wear resistance and high-corrosion resistance.
In a first aspect, to achieve these goals, oil is formed on aqueous ceramic non-sticking lining the present invention provides one kind
The method of ink mark, this method include：
(1) aqueous base oil is sprayed in the inner surface of matrix, and is toasted at 35-55 DEG C to form non-sticking lining bottom
Layer；
(2) bat printing processing is carried out on the surface of the non-sticking lining bottom to form ink indicia；
(3) aqueous face oil is sprayed in the base inner surface for being formed with ink indicia, is then sintered curing process, is formed
Non-sticking lining surface layer.
Second aspect, the present invention provides a kind of non-stick pan tool, the non-stick pan tool includes cookware matrix and is formed in institute
State the aqueous ceramic non-sticking lining on cookware base inner surface, the aqueous ceramic non-sticking lining includes non-sticking lining bottom, no
Adhesive coating layer surface layer and the ink indicia being printed between the non-sticking lining bottom and the non-sticking lining surface layer.
The third aspect, the present invention provides a kind of manufacturing method of tack-free pot, this method includes：The shape on cookware matrix
Into aqueous ceramic non-sticking lining, the forming method of the aqueous ceramic non-sticking lining according to it is of the present invention in aqueous ceramic not
The method that ink indicia is formed on adhesive coating layer carries out.
The ink indicia forming method of the present invention, can ensure on the premise of retroussage is intact, be formed on matrix
Possess high-bond (test of hundred lattice is 0 grade), high rigidity (Mitsubishi's pencil test may be up to 9H), high abrasion (2.5kg load, 3M
Scouring pad is worn up to 1.2 ten thousand times or more) and high-corrosion resistance aqueous ceramic non-sticking lining, consumer can be catered to cooker
Product coating is healthy, the serial demand such as durable, and can ensure that the coating of entire cookware matrix surface has and longer use the longevity
Life.
Other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Specific embodiment
The specific embodiment of the present invention is described in detail below.It is it should be appreciated that described herein specific
Embodiment is merely to illustrate and explain the present invention, and is not intended to limit the invention.
The endpoint of disclosed scope and any value are not limited to the accurate scope or value herein, these scopes or
Value should be understood to comprising the value close to these scopes or value.For numberical range, between the endpoint value of each scope, respectively
It between the endpoint value of a scope and individual point value and can be individually combined with each other between point value and obtain one or more
New numberical range, these numberical ranges should be considered as specific open herein.
In a first aspect, the present invention provides a kind of method that ink indicia is formed on aqueous ceramic non-sticking lining, the party
Method includes：
(1) aqueous base oil is sprayed in the inner surface of matrix, and is toasted at 35-55 DEG C to form non-sticking lining bottom
Layer；
(2) bat printing processing is carried out on the surface of the non-sticking lining bottom to form ink indicia；
(3) aqueous face oil is sprayed in the base inner surface for being formed with ink indicia, is then sintered curing process, is formed
Non-sticking lining surface layer.
In the case of process of the present invention it is preferred, this method further includes：Before step (1), first by the inner surface of matrix
Blasting treatment is carried out, the remaining particle of base inner surface is then removed, and carries out the pre-heat treatment and cooling treatment successively.
For the method for blasting treatment, there is no particular limitation, can be various methods commonly used in the art, as long as can
By carrying out blasting treatment to base inner surface its inner surface is made to obtain certain surface roughness, such as 60- can be used
The brown steel sand of 80 mesh, it is 6-8kgf/cm to control Jet Stream pressure2.It, need to be remaining by base inner surface after blasting treatment
The removings such as fine powder particles, for the method for removing, there is no particular limitation, and can be blown clean with high pressure draught can also lead to
It crosses washing to remove, this is well known to the skilled person, and details are not described herein.
For the condition of the pre-heat treatment, there is no particular limitation, can be various methods commonly used in the art, as long as can
Remove intrinsic silicon and the moisture of surface layer absorption, in order to further improve aqueous ceramic non-sticking lining obtained and matrix it
Between combination power, under preferable case, the condition of the pre-heat treatment includes：Temperature is 50-80 DEG C, time 5-15min.
Under preferable case, the temperature of base inner surface is down to 30-45 DEG C by cooling treatment, aqueous bottom is sprayed to provide
The suitable temperature of oil.
In the method for the present invention, the present inventor is it has furthermore been found that pass through base during the aqueous base oil of control spraying
The temperature on internal surface, enables to possess good combination power between aqueous ceramic non-sticking lining bottom and matrix, therefore, is
Improve the combination power between aqueous ceramic non-sticking lining bottom and matrix, under preferable case, in step (1), when spraying controls
The temperature of base inner surface is 30-45 DEG C.It is further preferred that the thickness for controlling the non-sticking lining bottom formed is 10-25 μm.
In the method for the present invention, the present inventor has further been found that the base during control sprays aqueous base oil
On the basis of internal surface temperature, stringent control sprays the temperature and time toasted after aqueous base oil, can significantly improve aqueous
The hardness and wear-resisting property of combination power, aqueous ceramic non-sticking lining between ceramic non-stick coating bottom strata and matrix, and be conducive to
The successful spraying of follow-up aqueous face oil, it is therefore preferable that in the case of, in step (1), the condition of baking includes：Temperature is 35-55
DEG C, time 5-20min, it is further preferred that temperature is 40-50 DEG C, time 8-15min.
The present invention method in, for aqueous base oil, there is no particular limitation, can be sintering commonly used in the art after into
It is divided into inorganic SiO2It can contain Ludox, filler, fluorine silicon with the various aqueous base oils of a small amount of resin, such as aqueous base oil
Alkane, resin and water, specifically, in terms of the weight of aqueous base oil, aqueous base oil can the Ludox containing 50-70wt%, 4-
The filler of 8wt%, the silicon fluoride of 4-8wt%, the water of the resin of 4-8wt% and 6-38wt%.Foregoing aqueous base oil can pass through
It is commercially available or voluntarily prepare.
In the case of process of the present invention it is preferred, in step (2), the condition of the bat printing processing includes：Loaded load is
3-5kg/f, time 0.3-1s.The bat printing raw material can be the conventional selection of this field, be, for example, ink.
In the case of process of the present invention it is preferred, in step (3), the condition of spraying includes：Temperature is 30-45 DEG C, is formed
Non-sticking lining surface layer thickness be 10-25 μm.
The present invention method in, for aqueous face oil there is no particular limitation, can be sintering commonly used in the art after into
Divide predominantly inorganic SiO2Various aqueous faces oil, such as aqueous face oil can contain Ludox, filler, pearl powder and water,
Specifically, in terms of the weight of aqueous base oil, aqueous face oil can the Ludox containing 40-60wt%, 4-8wt% filler,
The pearl powder of 4-8wt% and the water of 10-44wt%.Foregoing aqueous face oil can be commercially available or voluntarily prepare.
In the method for the present invention, by base oil, ink knead dough oil, sintering curing is molded together under the high temperature conditions, preferable case
Under, in step (3), the condition of the sintering curing processing includes：5-10min first is handled at 50-80 DEG C, then in 260-300
DEG C processing 10-20min.Wherein, the volatilization of coat inside solvent, and high temperature are mainly completed in 50-80 DEG C of low-temperature zone (5-10min)
260-300 DEG C of section (10-20min) mainly completes the curing molding of coating.
In the case of process of the present invention it is preferred, described matrix is aluminum pot matrix.It is method according to the invention it is possible to complete
The preparation of aqueous ceramic non-sticking lining containing ink indicia (logo) on into pot matrix.
Second aspect, the present invention provides a kind of non-stick pan tool, the non-stick pan tool includes cookware matrix and is formed in institute
State the aqueous ceramic non-sticking lining on cookware base inner surface, the aqueous ceramic non-sticking lining includes non-sticking lining bottom, no
Adhesive coating layer surface layer and the ink indicia being printed between the non-sticking lining bottom and the non-sticking lining surface layer.
In the non-stick pan tool of the present invention, under preferable case, the non-stick pan tool is not viscous aluminum pot.
Non-stick pan tool according to the present invention, the aqueous ceramic non-sticking lining can be foregoing in aqueous pottery according to the present invention
The method that ink indicia is formed on porcelain non-sticking lining is formed, and is not repeated to describe herein.
The third aspect, the present invention provides a kind of manufacturing method of tack-free pot, this method includes：The shape on cookware matrix
Into aqueous ceramic non-sticking lining, the forming method of the aqueous ceramic non-sticking lining according to it is of the present invention in aqueous ceramic not
The method that ink indicia is formed on adhesive coating layer carries out.
Embodiment
The present invention will be described in detail by way of examples below.It is unless otherwise instructed, used in following embodiment
Each material is commercially available, and each method used is the common method of this field.
Aqueous base oil is purchased from Shunde District of Foshan City Jin Cheng non-sticking linings factory, and the trade mark is JC8000 (base oil).
For aqueous face oil purchased from Shunde District of Foshan City Jin Cheng non-sticking linings factory, the trade mark is JC8000 (face oil).
Embodiment 1
1) the brown steel sand of 60-80 mesh is used, in 7kgf/cm2Jet Stream pressure under to aluminum pot inner surface carry out sandblasting
Processing, is then blown clean the remaining powder particle of inner surface of pot body with air-flow；
2) pot is preheated into 10min at 60 DEG C；
3) treat that inner surface of pot body temperature is down to 40 DEG C, aqueous base oil is sprayed in its inner surface；
4) pot for being coated with aqueous base oil is put into hot blast heater, 10min is toasted at 45 DEG C, forming thickness is
20 μm of non-sticking lining bottom；
6) retroussage processing is carried out on the surface of pot non-sticking lining bottom, the loaded load of bat printing is 4.5kg/f, when
Between for 0.5s, the water level line pattern of pot in preparation；
7) after pot being heated 4min at 40 DEG C, the temperature of inner surface of pot body is controlled as 40 DEG C, sprays aqueous face oil；
8) pot is sintered curing process in forced air drying passage stove, wherein, 8min first is handled at 60 DEG C, then
15min is handled at 280 DEG C, forms the non-sticking lining surface layer that thickness is 15 μm, obtains non-stick pan tool A1, wherein, water level line pattern
Bat printing is intact.
Embodiment 2
1) the brown steel sand of 60-80 mesh is used, in 6kgf/cm2Jet Stream pressure under to aluminum pot inner surface carry out sandblasting
Processing, is then blown clean the remaining powder particle of inner surface of pot body with air-flow；
2) pot is preheated into 15min at 50 DEG C；
3) treat that inner surface of pot body temperature is down to 45 DEG C, aqueous base oil is sprayed in its inner surface；
4) pot for being coated with aqueous base oil is put into hot blast heater, 8min is toasted at 50 DEG C, forming thickness is
15 μm of non-sticking lining bottom；
6) retroussage processing is carried out on the surface of pot non-sticking lining bottom, the loaded load of bat printing is 5kg/f, the time
For 0.3s, the water level line pattern of pot in preparation；
7) after pot being heated 3min at 45 DEG C, the temperature of inner surface of pot body is controlled as 45 DEG C, sprays aqueous face oil；
8) pot is sintered curing process in forced air drying passage stove, wherein, 10min first is handled at 50 DEG C, so
10min is handled at 300 DEG C afterwards, forms the non-sticking lining surface layer that thickness is 20 μm, obtains non-stick pan tool A2, wherein, water level line chart
Case bat printing is intact.
Embodiment 3
1) the brown steel sand of 60-80 mesh is used, in 8kgf/cm2Jet Stream pressure under to aluminum pot inner surface carry out sandblasting
Processing, is then blown clean the remaining powder particle of inner surface of pot body with air-flow；
2) pot is preheated into 7min at 80 DEG C；
3) treat that inner surface of pot body temperature is down to 35 DEG C, aqueous base oil is sprayed in its inner surface；
4) pot for being coated with aqueous base oil is put into hot blast heater, 15min is toasted at 40 DEG C, forming thickness is
22 μm of non-sticking lining bottom；
6) retroussage processing is carried out on the surface of pot non-sticking lining bottom, the loaded load of bat printing is 3kg/f, the time
For 0.8s, the water level line pattern of pot in preparation；
7) after pot being heated 5min at 35 DEG C, the temperature of inner surface of pot body is controlled as 35 DEG C, sprays aqueous face oil；
8) pot is sintered curing process in forced air drying passage stove, wherein, 5min first is handled at 80 DEG C, then
20min is handled at 260 DEG C, forms the non-sticking lining surface layer that thickness is 18 μm, obtains non-stick pan tool A3, wherein, water level line pattern
Bat printing is intact.
Embodiment 4
According to the method for embodiment 1, the difference is that, in step (4), the temperature of baking is 35 DEG C, and time 20min is obtained
Have A4 to non-stick pan, wherein, water level line pattern bat printing is intact.
Embodiment 5
According to the method for embodiment 1, the difference is that, in step (4), the temperature of baking is 55 DEG C, and time 5min is obtained
Non-stick pan has A5, wherein, water level line pattern bat printing is intact.
Comparative example 1
According to the method for embodiment 1, the difference is that, in step (4), the temperature of baking is 30 DEG C, and time 25min is obtained
Have D1 to non-stick pan, wherein, ink viscosity is larger during because of bat printing, and ink is easily pulled up after bat printing is complete, and pattern is caused to occur
Breakage, and after sintering curing processing, it is susceptible to the phenomenon that uneven.
Comparative example 2
According to the method for embodiment 1, the difference is that, in step (4), the temperature of baking is 60 DEG C, and time 5min is obtained
Non-stick pan has D2, wherein, since aqueous base oil baking temperature is higher so that its internal moisture evaporation is more, and base oil humidity becomes
Must be too low, although the bat printing effect of ink is preferable, aqueous face oil is difficult to merge with aqueous base oil, ultimately results in aqueous base oil and goes out
Phenomena such as now reuniting with local bulge.
Experimental example
The non-stick pan tool D1-D2 (pot in i.e.) that the non-stick pan tool A1-A5 and comparative example 1-2 that embodiment 1-5 is obtained is obtained,
It is tested as follows.
1st, acid and alkali resistance, salt：
(1) it is acidproof：The acetum that concentration is 5 weight % is added in into interior pot until interior pot inner wall maximum scale water level
Interior pot is put into energization closing lid laser heating in corresponding stew and boils (holding fluidized state) 10 minutes by place, then 100 DEG C of heat preservation leachings
Steep 24 it is small when, interior pot is cleaned up after the test, visually inspect coating surface changing condition, the results are shown in Table 1.
(2) it is alkaline-resisting：The sodium hydroxide solution that concentration is 0.5 weight % is added in into interior pot until interior pot inner wall maximum quarter
It spends at water level, interior pot, which is put into energization closing lid laser heating in corresponding stew, boils (holding fluidized state) 10 minutes, then 100 DEG C
When heat-insulation soaking 24 is small, interior pot is cleaned up after the test, coating surface changing condition is visually inspected, the results are shown in Table 1.
(3) salt tolerant：The sodium chloride solution that concentration is 5 weight % is added in into interior pot until interior pot inner wall maximum scale water
Position place, interior pot be put into energization closing lid laser heating in corresponding pot boil 8 it is small when (it is every 2 it is small when amount of makeup water 1 time, liquid level is protected
Hold the position in on-test), it is a cycle when 100 DEG C of heat preservations 16 are small, coating surface is visually inspected after each cycle experiment
Changing condition the results are shown in Table 1.
2nd, scratch-resistant：According to GB/T 6739-1996 gently, hardness-testing device is put down to the coating table in A1-A5, D1-D2 respectively
Face holds pulley both sides, and with the speed of 10cm/s to 10mm is pushed forward, whether observation coating surface is scraped off, according to Mitsubishi's lead
The order of hardness, by soft to progressively testing firmly, record pencil completely will not scratch-resistant coatings surface maximum hardness, as coating
Scratch resistance scratch hardness, the results are shown in Table 1.
3rd, with reference to power：According to GB/T 9286-1998,1mm is drawn in the base coat of A1-A5, D1-D2 respectively with blade2
Small 100 lattice of lattice of square, cling coating with " 3M610 test tapes " in same 45 ° of diagonal positions, it is then quick with 90 ° of angles
Pull-up adhesive plaster, is repeated 3 times, and according to the grade scale of table in GB/T9286-1998 1, records grade, the results are shown in Table 1.
4th, it is wear-resisting：With liquid detergent compound concentration be 5 weight % washings, 3M (7447C) scouring pad, heavy burden 2.5kgf,
The one way that swings is 1 time, and whether every 250 replacements scouring pad, every 250 inspections coating has exposing base material (to expose >=10
Lines are termination test), it the results are shown in Table 1.
Table 1
As it can be seen from table 1 the method for the present invention can ensure on the premise of retroussage is intact, formed on matrix
Possesses the aqueous ceramic non-sticking lining of high-bond, high rigidity, high-wear resistance and high-corrosion resistance.
The results contrast of embodiment 1 in table 1 and embodiment 4-5 are understood, in method of the invention, spraying aqueous bottom
It is toasted after oil, the temperature of baking is 40-50 DEG C, when the time is 8-15min, can significantly improve matrix and aqueous ceramic not
Combination power between adhesive coating layer, hence it is evident that improve the hardness and wear-resisting property of aqueous ceramic non-sticking lining.
The preferred embodiment of the present invention has been described above in detail, still, during present invention is not limited to the embodiments described above
Detail, within the scope of the technical concept of the present invention, a variety of simple variants can be carried out to technical scheme, this
A little simple variants all belong to the scope of protection of the present invention.
It is further to note that the specific technical features described in the above specific embodiments, in not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to it is various can
The combination of energy no longer separately illustrates.
In addition, various embodiments of the present invention can be combined randomly, as long as it is without prejudice to originally
The thought of invention, it should also be regarded as the disclosure of the present invention.
Claims (11)
- A kind of 1. method that ink indicia is formed on aqueous ceramic non-sticking lining, which is characterized in that this method includes：(1) aqueous base oil is sprayed in the inner surface of matrix, and is toasted at 35-55 DEG C to form non-sticking lining bottom；(2) bat printing processing is carried out on the surface of the non-sticking lining bottom to form ink indicia；(3) aqueous face oil is sprayed in the base inner surface for being formed with ink indicia, is then sintered curing process, formation is not glued Coating surface layer.
- 2. according to the method described in claim 1, wherein, in step (1), the condition of baking includes：Temperature is 35-55 DEG C, excellent Elect 40-50 DEG C as；Time is 5-20min, is preferably 8-15min.
- 3. method according to claim 1 or 2, wherein, in step (1), the condition of spraying includes：Temperature is 30-45 DEG C, The thickness of the non-sticking lining bottom of formation is 10-25 μm.
- 4. method according to claim 1 or 2, wherein, in step (2), the condition of the bat printing processing includes：Loading carries Lotus is 3-5kg/f, time 0.3-1s.
- 5. method according to claim 1 or 2, wherein, in step (3), the condition of spraying includes：Temperature is 30-45 DEG C, The thickness of the non-sticking lining surface layer of formation is 10-25 μm.
- 6. method according to claim 1 or 2, wherein, in step (3), the condition of the sintering curing processing includes：First 5-10min is handled at 50-80 DEG C, then handles 10-20min at 260-300 DEG C.
- 7. according to the method described in any one in claim 1-6, wherein, this method further includes：Before step (1), first The inner surface of matrix is subjected to blasting treatment, then removes the remaining particle of base inner surface, and carry out successively the pre-heat treatment and Cooling treatment；Preferably, the condition of the pre-heat treatment includes：Temperature is 50-80 DEG C, time 5-15min；Preferably, the temperature of base inner surface is down to 30-45 DEG C by the cooling treatment.
- 8. according to the method described in any one in claim 1-7, wherein, described matrix is aluminum pot matrix.
- 9. a kind of non-stick pan tool, which is characterized in that the non-stick pan tool includes cookware matrix and is formed in the cookware matrix Aqueous ceramic non-sticking lining on surface, the aqueous ceramic non-sticking lining include non-sticking lining bottom, non-sticking lining surface layer, with And the ink indicia being printed between the non-sticking lining bottom and the non-sticking lining surface layer.
- 10. non-stick pan tool according to claim 9, wherein, the non-stick pan tool is not viscous aluminum pot.
- 11. a kind of manufacturing method of tack-free pot, which is characterized in that this method includes：Aqueous ceramic is formed on cookware matrix Non-sticking lining, the forming method of the aqueous ceramic non-sticking lining according to the method described in any one in claim 1-8 into Row.