CN107973532A - A kind of glass roasting plate cannot not having the function of viscously and preparation method thereof - Google Patents
A kind of glass roasting plate cannot not having the function of viscously and preparation method thereof Download PDFInfo
- Publication number
- CN107973532A CN107973532A CN201610922676.5A CN201610922676A CN107973532A CN 107973532 A CN107973532 A CN 107973532A CN 201610922676 A CN201610922676 A CN 201610922676A CN 107973532 A CN107973532 A CN 107973532A
- Authority
- CN
- China
- Prior art keywords
- roasting plate
- glass roasting
- ceramic coating
- glass
- viscously
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of glass roasting plate cannot not having the function of viscously and preparation method thereof, including：Glass roasting plate；Ceramic coating layer coated in the glass roasting plate inner surface；The ceramic coating layer includes priming paint and finishing coat, wherein the thickness of the priming paint and the finishing coat is 35~45 μm；The production method of the glass roasting plate cannot not having the function of viscously includes following procedure of processing：Temperature → test package is moved back in ceramic coating pretreatment → glass roasting plate pretreatment → basecoat paint → finishing coat spraying → curing preheating → curing heating → curing.Glass roasting plate provided by the invention has anti-sticking, heat-resistant quality, not only the food in glass roasting plate container can directly be toasted, and food is not bound on glass roasting plate, easy to clean, it is easy to use, at the same processing technology by sandblasting, japanning, preheating, heat and move back warm processing, make the ceramic coating layer on glass roasting plate durable, not only high temperature resistant but also rub resistance, and it is not likely to produce buckling deformation.
Description
Technical field
The present invention relates to kitchen utensils technical field, a kind of more particularly to glass cannot not having the function of viscously is baked
Disk.
Background technology
Glassware plays very important effect in people's daily life, and the glass container in kitchen is even more everywhere may be used
See.Due to glass roasting plate Nantural non-toxic, and the easily appetite of enhancing people in the state of tableware is transparent so that dish is more
Add tempting, therefore dinner glass is widely used.But due to the easy adhesion food of glass roasting plate, especially it is contained in glass and bakes
Food is toasted in disk, sticky food not easy cleaning, has seriously affected the degree easy to use of glass container.
Therefore, how to provide a kind of glass roasting plate cannot not having the function of viscously is asking for those skilled in the art's urgent need to resolve
Topic.
The content of the invention
In view of this, the present invention provides a kind of glass roasting plate cannot not having the function of viscously, have anti-sticking, heat-resisting, solid resistance to
With, indeformable characteristic, prevent, using glass roasting plate baking adhesion food, solving the problems, such as that glass roasting plate is difficult cleaning of.
In order to achieve the above object, the present invention adopts the following technical scheme that：
A kind of glass roasting plate cannot not having the function of viscously, including：Glass roasting plate；Further include：Coated in the glass roasting plate
The ceramic coating layer on surface；The ceramic coating layer includes priming paint and finishing coat, wherein the thickness of the priming paint and the finishing coat is equal
For 35~45 μm.
A kind of production method for the glass roasting plate cannot not having the function of viscously, includes the following steps：
A. ceramic coating pre-processes：By ceramic coating be put into rotary mixer stirring 4 it is small when；Ceramic coating is by following heavy
Measure the component composition of part：85~100 parts of isopropanol, 45~80 parts of Ludox, 10~20 parts of water, 10~30 parts of titanium dioxide, methyl
85~100 parts of trimethoxy silane；The purpose of 4 hours of stirring is because mixture cannot be stored for a long time, in order to deposit for a long time
Put several raw materials separately to pack when dispatching from the factory, only raw material is mixed before manufacture；
B. glass roasting plate pre-processes：Glass roasting plate is positioned, and the inner surface of glass roasting plate is directed at sand-blasting machine
Nozzle, carries out 120 mesh blasting treatments to the inner surface of glass roasting plate, forms processing inner surface；
C. basecoat paint：The ceramic coating being stirred in step a is loaded into spray gun, to table in the processed processing of step b
Face carries out basecoat paint；
D. finishing coat sprays：After the priming paint drying prepared by step c, the spray paint on priming paint, produces and carries
The glass roasting plate of ceramic coating layer；
Wherein it should be noted that the ceramic coating used in spraying of the finishing coat with priming paint is identical.
E. preheating is cured：The glass roasting plate with ceramic coating layer prepared in step d is put into annealing kiln preheating, preheating
Temperature rises to 280 DEG C from room temperature, and constant temperature keeps 30min at a temperature of 280 DEG C；
F. heating is cured：Annealing kiln is heated to 280 DEG C~300 DEG C, to after the pre-heat treatment glass roasting plate heating 25~
35min；
G. cure and move back temperature：Annealing kiln is reduced to 40 DEG C by 200 DEG C, the glass roasting plate after heating is carried out to move back warm processing,
And constant temperature keeps 25~35min at a temperature of 40 DEG C, the curing molding of product is completed；
H. test package：Examine product ceramic coating layer it is whether uniform and whether quick-fried paint, qualified products are wrapped
Dress, storage.
Preferably, in a kind of above-mentioned glass roasting plate cannot not having the function of viscously, the glass roasting plate mainly uses borosilicic acid
Salt is made.
Preferably, in a kind of above-mentioned production method for the glass roasting plate cannot not having the function of viscously, the sandblasting in step b is dry
Sandblasting, includes but not limited to brown steel sand.
Preferably, in a kind of above-mentioned production method for the glass roasting plate cannot not having the function of viscously, step e, step f, step g
The length of used annealing kiln is 30~40m.
Preferably, in a kind of above-mentioned production method for the glass roasting plate cannot not having the function of viscously, step a, step b can be at the same time
Carry out.
Preferably, in a kind of above-mentioned glass roasting plate cannot not having the function of viscously, the ceramic coating layer includes at least one kind
The ceramic coating of color.
Preferably, in a kind of above-mentioned glass roasting plate cannot not having the function of viscously, at least one layer of the ceramic coating layer.
Preferably, in a kind of above-mentioned production method for the glass roasting plate cannot not having the function of viscously, step e preheating temperatures rise to
It is 45~60min the time required to 280 DEG C.
Preferably, in a kind of above-mentioned production method for the glass roasting plate cannot not having the function of viscously, step g cure move back temperature from
It is 25~35min that 200 DEG C, which are reduced to 40 DEG C of required times,.
It can be seen via above technical scheme that compared with prior art, have the present disclosure provides one kind and do not glue work(
Glass roasting plate of energy and preparation method thereof, carries out blasting treatment to the inner surface of glass roasting plate first, prepares processing inner surface,
Glass roasting plate inner surface is cleared up by the sand blasting process of 120 mesh, makes it have certain roughness, so that glass
Glass baking tray inner surface mechanical performance is improved, and obtains good paint adhesion, is conducive to the levelling and decoration of ceramic coating,
Extend the durability of ceramic coating layer at the same time, prevent ceramic coating layer buckling deformation；Secondly ceramic coating passes through rotary mixer
Load spray gun after stirring evenly, successively in processing inner surface spray-applied primer and finishing coat, and the thickness of priming paint and finishing coat is 35
~45 μm, wherein in order to ensure adhesive force and compactness, the spraying of finishing coat needs time interval, is carried out after priming paint is fully dry
Spraying, not only prevents priming paint and finishing coat from mixing as one layer, but also firmer, beautiful；Then it is fixed ceramic coating layer cure
Type processing, the glass roasting plate that will coat ceramic coating layer pass through preheating, heat and move back warm processing successively in annealing kiln, and often
A treatment process is kept for the regular hour under set temperature parameter respectively, and abundant elimination glass roasting plate and ceramic coating layer are answered
Power, reduces crackle and the probability of rupture, improves the service life of glass roasting plate and ceramic coating layer；In last ceramic coating layer
Toner can add according to demand, and the colorant of priming paint, finishing coat can be different, and can spray multi-layer ceramics dope layer,
Make glass roasting plate riotous with colour.
The present invention solves the problems, such as to need to brush oil using glass roasting plate baking food, avoids glass roasting plate adhesion food not
Easy cleaning；Present invention collection is easy to use, glittering and translucent, healthy natural, durable, cannot not having the function of viscously, indeformable etc. excellent
Point is the optimal selection of kitchenware in one.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
There is attached drawing needed in technology description to be briefly described, it should be apparent that, drawings in the following description are only this
The embodiment of invention, for those of ordinary skill in the art, without creative efforts, can also basis
The attached drawing of offer obtains other attached drawings.
Fig. 1 attached drawings are production method step schematic diagram of the invention.
Embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment, belongs to the scope of protection of the invention.
The embodiment of the invention discloses a kind of glass roasting plate cannot not having the function of viscously and preparation method thereof, not only bake glass
Disk has the advantages that anti-sticking, heat-resisting, durable, indeformable；And processing technology is filled by pretreatment and stage curing shaping
Divide the stress for eliminating interiors of products, avoid cracking and burst.Embodiment one：
A kind of glass roasting plate cannot not having the function of viscously, including：Glass roasting plate；Further include：Coated in glass roasting plate inner surface
Ceramic coating layer；Ceramic coating layer includes priming paint and finishing coat, and the thickness of wherein priming paint and finishing coat is 35 μm.
A kind of production method for the glass roasting plate cannot not having the function of viscously, includes the following steps：
A. ceramic coating pre-processes：By ceramic coating be put into rotary mixer stirring 4 it is small when；Ceramic coating is by following heavy
Measure the component composition of part：85 parts of isopropanol, 45 parts of Ludox, 10 parts of water, 10 parts of titanium dioxide, 85 parts of methyltrimethoxysilane；
, wherein it is desired to explanation, form the raw material of ceramic coating have it is a variety of, in order to store for a long time plurality of raw materials more use
Separately packaging, before manufacture mixes various raw materials.The plurality of raw materials of ceramic coating is stirred to together so that various raw materials fill
Divide mixing.
B. glass roasting plate pre-processes：Glass roasting plate is positioned, and the inner surface of glass roasting plate is directed at sand-blasting machine
Nozzle, carries out 120 mesh blasting treatments to the inner surface of glass roasting plate, forms processing inner surface；
C. basecoat paint：The ceramic coating being stirred in step a is loaded into spray gun, to table in the processed processing of step b
Face carries out basecoat paint；
D. finishing coat sprays：After the priming paint drying prepared by step c, the spray paint on priming paint, produces and carries
The glass roasting plate of ceramic coating layer；
E. preheating is cured：The glass roasting plate with ceramic coating layer prepared in step d is put into annealing kiln preheating, preheating
Temperature rises to 280 DEG C from room temperature, and constant temperature keeps 30min at a temperature of 280 DEG C；
F. heating is cured：Annealing kiln is heated to 280 DEG C, 25min is heated to the glass roasting plate after the pre-heat treatment；
G. cure and move back temperature：Annealing kiln is reduced to 40 DEG C by 200 DEG C, the glass roasting plate after heating is carried out to move back warm processing,
And constant temperature keeps 25min at a temperature of 40 DEG C, the curing molding of product is completed；
H. test package：Examine product ceramic coating layer it is whether uniform and whether quick-fried paint, qualified products are wrapped
Dress, storage.
In order to further optimize above-mentioned technical proposal, glass roasting plate is mainly made using borosilicate.
In order to further optimize above-mentioned technical proposal, the sandblasting in step b is dry blasting, includes but not limited to brown steel sand.
In order to further optimize above-mentioned technical proposal, step e, the length of annealing kiln used in step f, step g is 30
~40m.
In order to further optimize above-mentioned technical proposal, step a, step b can be carried out at the same time.
In order to further optimize above-mentioned technical proposal, ceramic coating layer, which includes at least, adds a kind of ceramic coating of colorant.
In order to further optimize above-mentioned technical proposal, it is 45min that step e preheating temperatures, which rise to 280 DEG C of required times,.
In order to further optimize above-mentioned technical proposal, step g, which cures to move back the time required to temperature is reduced to 40 DEG C from 200 DEG C, is
25min。
Embodiment two：
A kind of glass roasting plate cannot not having the function of viscously, including：Body glass roasting plate；Further include：Coated in glass roasting plate
The ceramic coating layer on surface；Ceramic coating layer includes priming paint and finishing coat, and the thickness of wherein priming paint and finishing coat is 40 μm.
A kind of production method for the glass roasting plate cannot not having the function of viscously, includes the following steps：
A. ceramic coating pre-processes：By ceramic coating be put into rotary mixer stirring 4 it is small when；Ceramic coating is by following heavy
Measure the component composition of part：92 parts of isopropanol, 60 parts of Ludox, 15 parts of water, 20 parts of titanium dioxide, 92 parts of methyltrimethoxysilane；
, wherein it is desired to explanation, form the raw material of ceramic coating have it is a variety of, in order to store for a long time plurality of raw materials more use
Separately packaging, before manufacture mixes various raw materials.The plurality of raw materials of ceramic coating is stirred to together so that various raw materials fill
Divide mixing.
B. glass roasting plate pre-processes：Glass roasting plate is positioned, and the inner surface of glass roasting plate is directed at sand-blasting machine
Nozzle, carries out 120 mesh blasting treatments to the inner surface of glass roasting plate, forms processing inner surface；
C. basecoat paint：The ceramic coating being stirred in step a is loaded into spray gun, to table in the processed processing of step b
Face carries out basecoat paint；
D. finishing coat sprays：After the priming paint drying prepared by step c, the spray paint on priming paint, produces and carries
The glass roasting plate of ceramic coating layer；
E. preheating is cured：The glass roasting plate with ceramic coating layer prepared in step d is put into annealing kiln preheating, preheating
Temperature rises to 280 DEG C from room temperature, and constant temperature keeps 30min at a temperature of 280 DEG C；
F. heating is cured：Annealing kiln is heated to 290 DEG C, 30min is heated to the glass roasting plate after the pre-heat treatment；
G. cure and move back temperature：Annealing kiln is reduced to 40 DEG C by 200 DEG C, the glass roasting plate after heating is carried out to move back warm processing,
And constant temperature keeps 30min at a temperature of 40 DEG C, the curing molding of product is completed；
H. test package：Examine product ceramic coating layer it is whether uniform and whether quick-fried paint, qualified products are wrapped
Dress, storage.
In order to further optimize above-mentioned technical proposal, glass roasting plate is mainly made using borosilicate.
In order to further optimize above-mentioned technical proposal, the sandblasting in step b is dry blasting, includes but not limited to brown steel sand.
In order to further optimize above-mentioned technical proposal, step e, the length of annealing kiln used in step f, step g is 30
~40m.
In order to further optimize above-mentioned technical proposal, step a, step b can be carried out at the same time.
In order to further optimize above-mentioned technical proposal, ceramic coating layer, which includes at least, adds a kind of ceramic coating of colorant.
In order to further optimize above-mentioned technical proposal, it is 52min that step e preheating temperatures, which rise to 280 DEG C of required times,.
In order to further optimize above-mentioned technical proposal, step g, which cures to move back the time required to temperature is reduced to 40 DEG C from 200 DEG C, is
30min。
Embodiment three：
A kind of glass roasting plate cannot not having the function of viscously, including：Glass roasting plate；Further include：Coated in glass roasting plate inner surface
Ceramic coating layer；Ceramic coating layer includes priming paint and finishing coat, and the thickness of wherein priming paint and finishing coat is 45 μm.
A kind of production method for the glass roasting plate cannot not having the function of viscously, it is characterised in that include the following steps：
A. ceramic coating pre-processes：By ceramic coating be put into rotary mixer stirring 4 it is small when；Ceramic coating is by following heavy
Measure the component composition of part：100 parts of isopropanol, 80 parts of Ludox, 20 parts of water, 30 parts of titanium dioxide, methyltrimethoxysilane 100
Part；
, wherein it is desired to explanation, form the raw material of ceramic coating have it is a variety of, in order to store for a long time plurality of raw materials more use
Separately packaging, before manufacture mixes various raw materials.The plurality of raw materials of ceramic coating is stirred to together so that various raw materials fill
Divide mixing.
B. glass roasting plate pre-processes：Glass roasting plate is positioned, and the inner surface of glass roasting plate is directed at sand-blasting machine
Nozzle, carries out 120 mesh blasting treatments to the inner surface of glass roasting plate, forms processing inner surface；
C. basecoat paint：The ceramic coating being stirred in step a is loaded into spray gun, to table in the processed processing of step b
Face carries out basecoat paint；
D. finishing coat sprays：After the priming paint drying prepared by step c, the spray paint on priming paint, produces and carries
The glass roasting plate of ceramic coating layer；
E. preheating is cured：The glass roasting plate with ceramic coating layer prepared in step d is put into annealing kiln, preheating temperature
280 DEG C are risen to from room temperature, and constant temperature keeps 30min at a temperature of 280 DEG C；
F. heating is cured：Annealing kiln is heated to 300 DEG C, 30min is heated to the glass roasting plate after the pre-heat treatment；
G. cure and move back temperature：Annealing kiln is reduced to 40 DEG C by 200 DEG C, the glass roasting plate after heating is carried out to move back warm processing,
And constant temperature keeps 35min at a temperature of 40 DEG C, the curing molding of product is completed；
H. test package：Examine product ceramic coating layer it is whether uniform and whether quick-fried paint, qualified products are wrapped
Dress, storage.
In order to further optimize above-mentioned technical proposal, glass roasting plate is mainly made using borosilicate.
In order to further optimize above-mentioned technical proposal, the sandblasting in step b is dry blasting, includes but not limited to brown steel sand.
In order to further optimize above-mentioned technical proposal, step e, the length of annealing kiln used in step f, step g is 30
~40m.
In order to further optimize above-mentioned technical proposal, step a, step b can be carried out at the same time；Ceramic coating pre-processes and glass
Baking tray pre-processes point of no tandem, improves production efficiency in order to save time, step a and step b can be carried out at the same time.
In order to further optimize above-mentioned technical proposal, ceramic coating layer, which includes at least, adds a kind of ceramic coating of colorant；
The ceramic coating that different colorants forms a variety of colors is added in ceramic coating, be sprayed on glass roasting plate produce it is rich and varied
Product.
In order to further optimize above-mentioned technical proposal, it is 60min that step e preheating temperatures, which rise to 280 DEG C of required times,.
In order to further optimize above-mentioned technical proposal, step g, which cures to move back the time required to temperature is reduced to 40 DEG C from 200 DEG C, is
35min。
Each embodiment is described by the way of progressive in this specification, what each embodiment stressed be and other
The difference of embodiment, between each embodiment identical similar portion mutually referring to.For device disclosed in embodiment
For, since it is corresponded to the methods disclosed in the examples, so description is fairly simple, related part is said referring to method part
It is bright.
The foregoing description of the disclosed embodiments, enables professional and technical personnel in the field to realize or use the present invention.
A variety of modifications to these embodiments will be apparent for those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, it is of the invention
The embodiments shown herein is not intended to be limited to, and is to fit to and the principles and novel features disclosed herein phase one
The most wide scope caused.
Claims (9)
1. a kind of glass roasting plate cannot not having the function of viscously, including：Glass roasting plate；It is characterized in that, further include：Coated in coated in
The ceramic coating layer of the glass roasting plate inner surface；The ceramic coating layer includes priming paint and finishing coat, wherein the priming paint and institute
The thickness for stating finishing coat is 35~45 μm.
2. a kind of production method for the glass roasting plate cannot not having the function of viscously, it is characterised in that include the following steps：
A. ceramic coating pre-processes：By ceramic coating be put into rotary mixer stirring 4 it is small when；Ceramic coating is by following parts by weight
Component composition：85~100 parts of isopropanol, 45~80 parts of Ludox, 10~20 parts of water, 10~30 parts of titanium dioxide, methyl trimethoxy
85~100 parts of oxysilane；
B. glass roasting plate pre-processes：Glass roasting plate is positioned, and the inner surface of glass roasting plate is aligned to the nozzle of sand-blasting machine,
120 mesh blasting treatments are carried out to the inner surface of glass roasting plate, form processing inner surface；
C. basecoat paint：By the ceramic coating being stirred in step a load spray gun, it is processed to step b processing inner surface into
Row basecoat paint；
D. finishing coat sprays：After the priming paint drying prepared by step c, the spray paint on priming paint, is produced with ceramics
The glass roasting plate of dope layer；
E. preheating is cured：The glass roasting plate with ceramic coating layer prepared in step d is put into annealing kiln, preheating temperature is from room
Temperature rise is to 280 DEG C, and constant temperature keeps 30min at a temperature of 280 DEG C；
F. heating is cured：Annealing kiln is heated to 280 DEG C~300 DEG C, to after the pre-heat treatment glass roasting plate heating 25~
35min；
G. cure and move back temperature：Annealing kiln is reduced to 40 DEG C by 200 DEG C, to the glass roasting plate after heating move back warm processing, and
Constant temperature keeps 25~35min at a temperature of 40 DEG C, completes the curing molding of product；
H. test package：Examine product ceramic coating layer it is whether uniform and whether quick-fried paint, qualified products are packed, are entered
Storehouse.
A kind of 3. glass roasting plate cannot not having the function of viscously according to claim 1, it is characterised in that the glass roasting plate master
To be made using borosilicate.
A kind of 4. production method of glass roasting plate cannot not having the function of viscously according to claim 2, it is characterised in that step
Sandblasting in b is dry blasting, includes but not limited to brown steel sand.
A kind of 5. production method of glass roasting plate cannot not having the function of viscously according to claim 2, it is characterised in that step
E, the length of annealing kiln used in step f, step g is 30~40m.
A kind of 6. production method of glass roasting plate cannot not having the function of viscously according to claim 2, it is characterised in that step
A, step b can be carried out at the same time.
A kind of 7. glass roasting plate cannot not having the function of viscously according to claim 1, it is characterised in that the ceramic coating layer
Including at least a kind of ceramic coating of colorant of addition.
A kind of 8. production method of glass roasting plate cannot not having the function of viscously according to claim 2, it is characterised in that step
E preheating temperatures are 45~60min the time required to rising to 280 DEG C.
A kind of 9. production method of glass roasting plate cannot not having the function of viscously according to claim 2, it is characterised in that step
It is 25~35min that g curings, which are moved back the time required to temperature is reduced to 40 DEG C from 200 DEG C,.