CN108060496A - Anti- plumage fabric plus material producing method and anti-plumage face material - Google Patents

Anti- plumage fabric plus material producing method and anti-plumage face material Download PDF

Info

Publication number
CN108060496A
CN108060496A CN201810011419.5A CN201810011419A CN108060496A CN 108060496 A CN108060496 A CN 108060496A CN 201810011419 A CN201810011419 A CN 201810011419A CN 108060496 A CN108060496 A CN 108060496A
Authority
CN
China
Prior art keywords
production
plumage
weaving
opening
sizing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810011419.5A
Other languages
Chinese (zh)
Inventor
凌良仲
孙仁斌
周卫东
王娟娟
于灿
刘莹莹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU YUEDA HOMETEXTILE Co Ltd
Original Assignee
JIANGSU YUEDA HOMETEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU YUEDA HOMETEXTILE Co Ltd filed Critical JIANGSU YUEDA HOMETEXTILE Co Ltd
Priority to CN201810011419.5A priority Critical patent/CN108060496A/en
Publication of CN108060496A publication Critical patent/CN108060496A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of anti-plumage fabric plus material producing method, for the production method using the high grade cotton yarn more than or equal to 60S of super fine denier Modal fibre spinning as raw materials for production, the production method includes warping process, sizing operation and weaving process;The control condition of the weaving process is half clear opening, and 80~84mm of amount of opening, warp tension≤1400N, the back rest is less than brest beams, 310~320 ° of opening time, 90~100 ° of Filling Insertion Time.Above-mentioned anti-plumage face material, using the high grade cotton yarn more than or equal to 60S of super fine denier Modal fibre spinning as raw materials for production, the advantageous characteristic of Modal fibre can fully be preserved, and there is anti-plumage effect after weaving, it can be used in the fabric of natural feather bedding and clothing, improve the application range of Modal fibre.

Description

Anti- plumage fabric plus material producing method and anti-plumage face material
Technical field
The present invention relates to a kind of anti-plumage face material, and in particular to a kind of anti-plumage fabric plus material producing method and anti-plumage face material.
Background technology
The filler of quilt has:Doughnut, cashmere and wool, silk, natural feather etc. coat the common face of these fillers Material is pure cotton, polyester cotton dimity or poplin cloth etc..These fabrics generally require special final finishing for example immersion coating, resin finishing, Anti- plumage pads, and gap between fabric count yarn is reduced, to achieve the effect that DOWN PROOF, so as to avoid drilling out for filler.And Fabric through final finishing processing is often not environmentally, it is impossible to meet people and pursue nature, environmental protection, green, the theory of low-carbon.
Modal fibre is a kind of regenerated celulose fibre of Austrian Lenzin company exploitation, with natural flexibility Repeatedly soft and bright color and luster is still kept after washing.Modal fibre is soft, smooth, pure color, and with pure Soft affine, the luxurious gloss as silk of cotton, numb matter it is penetrating clean refreshing, drapability is good, along with its good gas permeability and The features such as easily arranging.Modal fibre has care skin, skin is made to enjoy unprecedented comfort, so it is known as " Second Skin of people ".But its fabric has the characteristics that stiffness is poor, is mostly used the production in underwear.In order to improve pure Modal production The shortcomings that stiffness of product is poor, Modal fibre is generally carried out blended or interweaved with other fibers, to meet consumers in general's need It asks.However traditional Modal fibre textile fabric cannot anti-plumage, it is impossible to as the fabric of eiderdown quilt etc., limit Modal fibre The application of dimension.
The content of the invention
In order to overcome the not anti-plumage of existing Modal fibre textile fabric, it is not used to need the natural feather with anti-plumage In bedding and clothing, the present invention provides a kind of anti-plumage fabric plus material producing method and anti-plumage face material.
A kind of anti-plumage fabric plus material producing method provided by the invention, the production method are more than using Modal fibre spinning For high grade cotton yarn equal to 60S as raw materials for production, the production method includes warping process, sizing operation and weaving process;
The control condition of the weaving process is clearly open for half, 80~84mm of amount of opening, warp tension≤1400N, after Beam is less than brest beams, 310~320 ° of opening time, 90~100 ° of Filling Insertion Time.
In one of the embodiments, the Modal fibre is the super fine denier Modal fibre of fineness 0.8dtex.
In one of the embodiments, the control condition of the weaving process is clearly open for half, amount of opening 82mm, upper machine Tension 1200N, the back rest are less than brest beams, 316 ° of opening time, 98 ° of Filling Insertion Time.
In one of the embodiments, the control condition of the warping process is 0.50~0.54g/cm3 of rolling density, whole Through 540~560m/min of speed.
In one of the embodiments, the warping process uses Switzerland's Benniger wide cut warping machine, total quantity of warps 21000 Root, 24 warp beams, rolling density 0.52g/cm3, speed of beaming 550m/min.
In one of the embodiments, the control condition of the sizing operation be regain 5.5~6%, the vehicle of sizing machine Speed 40~50m/min, 12~13KN of squeezing roller pressure, 78~82 DEG C of slurry groove temperature.
In one of the embodiments, the production method further includes dyeing and finishing technology, and the dyeing and finishing technology includes following place Manage step:Singe, concise desizing, bleaching, mercerising, Anti-Pilling Finishes, stentering forming and preshrunk.
In one of the embodiments, the workshop temperature of the production method is 23~27 DEG C, relative humidity for 68~ 74%.
The present invention also provides a kind of anti-plumage face material, the anti-plumage face material using production method as described above prepare and Into.
In one of the embodiments, the anti-plumage face material through close 787~1220/10cm, filling density 590~670/ 10cm。
Above-mentioned anti-plumage face material, it is former as production using the high grade cotton yarn more than or equal to 60S of super fine denier Modal fibre spinning Material can fully preserve the advantageous characteristic of Modal fibre, and have anti-plumage effect after weaving, can be used in eiderdown quilt In the fabric of clothes, the application range of Modal fibre is improved.
Specific embodiment
The invention will now be further described with reference to specific embodiments, but these embodiments are intended to be used to explain the present invention, And it is not considered as limiting the invention.It it should be appreciated that without departing from the spirit and scope of the invention can be to this The details and form of inventive technique scheme are modified and replaced, but these modifications and replacement each fall within protection scope of the present invention It is interior.
Modal (Modal) is the cellulose of the koplon of Austrian Lenzin (Lenzing) company exploitation Regenerated fiber has the characteristics that sucting wet air permeability is good, rigidity is low, soft, shape-retaining ability is poor.Although there are many excellent for Modal fibre Characteristic, but that dyeing defect, color spot, folding line, broken hole, fluffing, pilling etc. are susceptible to when for producing cloth is all for Modal fibre More problems.Common Modal fibre species is as shown in mark 1.
The species and its parameter of 1 Modal fibre of table
The anti-plumage fabric plus material producing method of an embodiment provided by the invention, using being more than for super fine denier Modal fibre spinning For high grade cotton yarn equal to 80S as raw materials for production, which includes warping process, sizing operation and weaving process.
Wherein, the control condition of weaving process is clearly open for half, 80~84mm of amount of opening, warp tension≤1400N, after Beam is less than brest beams, 310~320 ° of opening time, 90~100 ° of Filling Insertion Time.
Above-mentioned anti-plumage face material, it is former as production using the high grade cotton yarn more than or equal to 60S of super fine denier Modal fibre spinning Material can fully preserve the advantageous characteristic of Modal fibre, and have anti-plumage effect after weaving, can be used in eiderdown quilt In the fabric of clothes, the application range of Modal fibre is improved.
The present inventor is according to the characteristics of ultra-fine denier modal and the characteristic of anti-plumage face material, by repetition test, It was found that the control condition of weaving process is half clear opening, 80~84mm of amount of opening, warp tension≤1400N, the back rest is less than chest Beam, 310~320 ° of opening time, during 90~100 ° of Filling Insertion Time, the characteristics of Modal fibre stiffness can be overcome poor, and It can make woven anti-plumage face material softness, anti-plumage effect is good.
As a kind of optional embodiment, Modal fibre is the super fine denier Modal fibre of fineness 0.8dtex.The present invention Inventor by constantly attempting, find to weave anti-plumage face material compared to other kinds not using super fine denier Modal fibre Dai Er fibers have more excellent characteristic.Super fine denier Modal fibre is Modal most careful, most soft currently on the market Fiber, such Modal fibre use beech, have used green technology in production process, one generated in fiber production process Serial waste or substance can be not only recovered for re-use, and various useful byproduct can more be made.It can naturally be dropped Solution, it is last to revert to the Nature again from natural, it complies fully with the world today and is pursued to environmental protection, naturally.
Further, the control condition of weaving process is clearly open for half, amount of opening 82mm, warp tension 1200N, after Beam is less than brest beams, 316 ° of opening time, 98 ° of Filling Insertion Time.When manufacturing process selects the control condition, woven anti-plumage face material Anti- plumage effect is good and frivolous, fine and smooth, hygroscopicity number, particularly suitable for producing the fabric of eiderdown quilt.
As a kind of optional embodiment, the control condition of warping process is 0.50~0.54g/cm of rolling density3, warping 540~560m/min of speed.The characteristics of super fine denier Modal fibre rigidity is low, single fiber is thin, even if weaving is more than or equal to 60S's High grade cotton yarn may also be warp end break or float occur in weaving, therefore carry out warping processing to warp thread, by the control of warping process Condition setting processed is 0.50~0.54g/cm of rolling density3, 540~560m/min of speed of beaming can make during warping Power is uniform, improves warping effect, avoids occurring warp end break or float during weaving process.
Still optionally further, warping process uses Switzerland's Benniger wide cut warping machine, total quantity of warps 21000,24 warps Axis, rolling density 0.52g/cm3, speed of beaming 550m/min.
It is provided by the invention a kind of for the anti-plumage face material of super fine denier Modal fibre weaving as a kind of optional embodiment Slashing technique slurry, following raw material is included per 780L above-mentioned slurries:
Above-mentioned slashing size, by TM-8010, phosphate ester starch, tapioca and poly- allyl diethylene glycol (DEG) ester group Into the main component of slurry, so as to form the slurry of " highly concentrated, low viscous ", which has super fine denier Modal fibre excellent Good coherent and wearability, the rate of sizing is high, and the serous coat excellent spring formed, so as to improve the fibre of the Modal after sizing The intensity and wearability of dimension reduce its risk being broken in weaving.
Further, being applied in combination by phosphate ester starch and tapioca, can make the serous coat elasticity to be formed good, Wearability significantly improves, it is good to be bonded filoplume effect, effectively warp can be controlled to extend, and slurry in subsequent desizing process more Waste water that is disposable, generating is few.
It should be noted that the raw material type do not specifically noted in the present invention, such as antistatic agent, preservative, softening agent, The material for being commercially for textile industry can be selected.
Still optionally further, following raw material is included per 780L slurries:
As a kind of optional embodiment, the viscosity of slurry is 4.5~5.5s.The viscosity of slurry is controlled in 4.5~5.5s, It can make slurry and rapidly be infiltrated during yarn contacts, obvolvent yarn, and the rate of sizing is high.
As a kind of optional embodiment, the solid content of slurry is 15~25%.The solid content of slurry is limited, avoids it solid It is excessive that too high levels change the thickness of yarn after sizing, influences woven through close, reduces anti-plumage effect.
As a kind of optional embodiment, the modulator approach of slurry is in putting into suitable quantity of water in high pressure mixing cirtern, is being stirred Under the conditions of add in by several times TM-8010, phosphate ester starch, tapioca, poly- allyl diethylene glycol (DEG) ester, wax disk(-sc), antistatic agent, Preservative and softening agent simultaneously plus water constant volume, continue 30~40min of stirring, be steam heated to 105~108 DEG C continue stirring 10~ 15min, press-in supply bucket are spare.By the way that various raw materials is made to be pre-mixed 30~40min of stirring, starch etc. can be made fully to absorb water Expansion, is further heated by steam, can be made starch gelatinization and is uniformly mixed with antistatic agent etc., and slurry is more easily-controllable The viscosity of slurrying material is in 4.5~5.5s.
As a kind of optional embodiment, a kind of sizing method provided by the invention, using above-mentioned slurry.
As a kind of optional embodiment, the control condition of sizing operation is regain 5.5~6%, the speed of sizing machine 40~50m/min, 12~13KN of squeezing roller pressure, 78~82 DEG C of slurry groove temperature.Pass through the above-mentioned control of empty control sizing operation Condition can be matched with the property of slurry, and collaboration improves sizing effect, completes serous coat, yarn texture is even closer, yarn is straight Footpath reduces, and circularity increases.
As a kind of optional embodiment, the preliminary drying temperature of sizing is 115~120 DEG C, and it is 80~90 DEG C to dry temperature again.This Invention properly increases preliminary drying temperature using secondary drying, can dry yarn, and diameter reduces, and is more advantageous to being woven as The anti-plumage face material of high sley.
As a kind of optional embodiment, the rate of sizing of sizing is 25~30%, enhancing rate 20~30%.By in control Formula of size is stated, the rate of sizing of sizing can be made to control 25~30%, enhancing rate reaches 20~30%.
Usually, modal fabric surface is susceptible to the defects of generating filoplume, easy pilling, although can by sizing The low woven modal fabric of sinking to a certain degree generates drawbacks described above, but still can be further by adjusting dyeing and finishing technology into one Step overcomes the defect.Optionally, aforementioned production method further includes dyeing and finishing technology, and dyeing and finishing technology includes following processing step:Singe, Concise desizing, bleaching, mercerising, Anti-Pilling Finishes, stentering forming and preshrunk.By above-mentioned dyeing and finishing technology, can overcome completely Drawbacks described above, and excellent anti-plumage effect can be obtained without last phase tidying up effect not environmentally.
As a kind of optional embodiment, the workshop temperature of production method is 23~27 DEG C, and relative humidity is 68~74%. Under this condition, loom efficiency is stablized, and fabric quality is preferable.
The present invention also provides a kind of anti-plumage face material, anti-plumage face material is prepared using production method as described above.The face Expect soft, comfortable, water imbibition and anti-plumage effect are good, and green, environmental protection, harmless.
As a kind of optional embodiment, anti-plumage face material through close 787~1220/10cm, filling density 590~670/ 10cm。
Embodiment one
The raw material and trimmed size of the present embodiment are as follows:
Raw material specification:60S high grade cotton yarns (super fine denier Modal fibre is formed by weaving)
Fabric specification:The ultra-fine denier modal 80* of 105 〞 eight pieces of satin weaves of ultra-fine 80 200*250 of denier modal
Trimmed size:The ultra-fine denier modal 80* of 98.5 〞 eight pieces of satin weaves of ultra-fine 80 216*252 of denier modal
Production method includes warping process, sizing operation, weaving process, dyeing and finishing process.
Warping process:
Warp end break and float during in order to reduce later process processing, it is ensured that the uniformity of piece yarn tension.Before bobbin cradle, In, the tension of back zone unwinding the warp be inconsistent, back zone Yarn guide distance is long, and yarn tension is big, and proparea Yarn guide distance is short, yarn Power is small, and by adjusting yarn path with balance tension, middle back zone tension reaches unanimity before making.The present embodiment selects Switzerland's Benniger Wide cut beam warper, total quantity of warps 21000,24 warp beams, rolling density 0.52g/cm3, speed of beaming 550m/ min。
Further, warping process should also be noted that problems with:
(1) housekeeping of each Xelminator, each reed, each deflector roll is carried out before producing.
(2) tension in Warping is the key that each road, and monofilament tension must keep uniformity, this is the key that the process, Power will be detected progressively.Winding part requirement even tension could produce.Under the premise of ensuring normally to drive, tension can be small then small. Tension is uniform.Tension is irregular, and it is inconsistent to be easy to cause final finishing dyed color.
(3) processing of filoplume is the most important thing.The sensitivity of filoplume detection is improved, size filoplume will be handled.It is stringent whole Through improving quality.Warp beam winding is smooth during production.
Sizing operation:
Sizing operation is the key that warp beam processing, while suitable slurry is selected, it is necessary to work up rational slurry Yarn process.Formula of size is as shown in table 2.
2 formula of size of table
Using single slash-vat slasher or dual-box slasher, sizing machine sets regain as 5.5~6%, the vehicle of sizing machine Speed is 40~50m/min, and 12~13KN of squeezing roller pressure, slurry groove temperature is 78~82 DEG C, and preliminary drying temperature is 115~120 DEG C, multiple It is 80~90 DEG C to dry temperature, and the rate of sizing is 25~30%, enhancing rate 20~30%.
Weaving process:
This implementation selects Tianjin field coltfoal ZAX9100 air-jet looms to produce the anti-plumage face material.In weaving process, because through it is close compared with Greatly, single fiber is thin, easily breaks end, influences weaving efficiency.Therefore, suitably to reduce warp tension, also to reduce for weft yarn and move back solution Tension selects suitable storage latitude form.Because fabric looped weft is larger, the auxiliary appliances such as width support are chosen, ensure that weaving is smoothed out.
When air-jet loom produces, using half, clearly opening, 80~84mm of amount of opening, warp tension≤1400N, the back rest are low In brest beams, 310~320 ° of opening time, 90~100 ° of Filling Insertion Time.I.e. using half clear opening, amount of opening is small, and tension is small, after Beam is low, opening time evening, the weaving process in Filling Insertion Time evening.Therefore, the temperature in workshop is controlled at 23 DEG C~27 DEG C, it is relatively wet It spends for 68%~74%, loom efficiency and fabric quality are all relatively stablized.If relative humidity is too small, workshop drying, yarn passes through steel Reed, heald, menopause tablet friction easily fluffing, and easily being wound between yarn, influence the clear Xi degree that is open.
Dyeing and finishing technology:
Dyeing and finishing technology includes following processing step:Singe, concise desizing, bleaching, mercerising, Anti-Pilling Finishes, stentering forming And preshrunk
It singes
In order to reduce the filoplume of fabric surface and obtain a kind of clean and tidy fabric surface, by the woven super fine denier of the present embodiment The anti-plumage face material of Modal carries out processing of singing.After this processing, all pole in application in working process or afterwards Big avoids pilling.
Concise desizing
Refining desizing is slurry applied in finish and wax, the sizing technique removed in weaving and spinning process etc..This The anti-plumage face material of invention preferably use it is relatively mild refine desizing condition, replace sodium hydroxide with partial sodium carbonate in production process. Optionally, the auxiliary agent of anti pilling is added in concise desizing further to prevent fluffing, pilling.
Optionally, refining desizing is carried out using feed liquid as shown in table 3, refines the temperature of desizing as 80 DEG C, the time is 30min。
3 desizing feed liquid of table
Title Content
Sodium hydroxide 2g/L
Sodium carbonate 2g/L
Anti pilling auxiliary agent 0.3g/L
Remover 0.3g/L
Bleaching
In order to improve the whiteness of fabric, meet the processing request of bleaching fabric.Bleaching process flow:Bleaching liquor is padded (to roll remaining Rate 70%~75%), decatize (100 DEG C, 35~40min), washing drying.
Mercerising
Mercerization finish can be effectively improved pilling and obtain light rate, and can greatly reduce feel with high-temperature alkali mercerization finish What is be hardened is sorry.
Using mild mercerization, 30min is banked up at 60 DEG C after being padded with the NaOH solution of 100g/L, with hot water and Cold water is washed, and carries out washing neutralization with olefin(e) acid, and it is 7~7.5 to make cloth cover pH value.
Anti-Pilling Finishes
Using the enzyme agent of 0.5~1.0g/L, with acetic acid tune pH to 4.5~6, using bath raio as 1 under the conditions of 50~60 DEG C: 3~1:20 pairs of anti-plumage face material, which impregnate, carries out Anti-Pilling Finishes.
Anti-Pilling Finishes are a kind of cellulose crosslinked dose of arrangements, are a kind of resin finishings.On the one hand, because cellulose fibre Expansion factor during cold-heat treatment and fabric size is caused to change, can be in order to which size caused by reducing expansion changes It is solved by adding the method for fiber cross-linkers.On the other hand, the durability of fabric can be improved by crosslink finishing, improves hand Sense assigns that fabric smooth feeling is few and moistening feel without body bone, fabric is made to have the water imbibition and antistatic property of brilliance, so as to improve Pilling phenomenon during taking.
Ferment processing is to be removed the villus of fabric surface using auxiliary agent, the phenomenon that so as to reduce pilling.Ferment Element processing carries out before and after dyeing.
Stentering forming
Stentering forming is one of key point of finishing process quality.Tentering is carried out using cloth gripper formula hot flue stenter It arranges.
Preshrunk
Ensure that the warp-wise of fabric shrinks to require, the further feel for improving product.
By anti-plumage face material prepared by aforementioned production method, leading indicator detection is as follows:
Above-mentioned testing result meets GB18401-2010B classes, Grade A requirement as defined in FZ/T14013-2009 standards.It should Anti- plumage face material has good gas permeability, and soft-touch, anti-plumage effect is good.
Although the embodiment of the present invention has been shown and described above, it is to be understood that above-described embodiment is example Property, it is impossible to limitation of the present invention is interpreted as, those of ordinary skill in the art within the scope of the invention can be to above-mentioned Embodiment is changed, changes, replacing and modification.

Claims (10)

1. a kind of anti-plumage fabric plus material producing method, which is characterized in that the production method is using being more than for Modal fibre spinning etc. In 60S high grade cotton yarn as raw materials for production, the production method includes warping process, sizing operation and weaving process;
Clearly opening, 80~84mm of amount of opening, warp tension≤1400N, the back rest are low for half for the control condition of the weaving process In brest beams, 310~320 ° of opening time, 90~100 ° of Filling Insertion Time.
2. production method according to claim 1, which is characterized in that the Modal fibre is the super of fineness 0.8dtex Fine denier modal fiber.
3. production method according to claim 1, which is characterized in that the control condition of the weaving process is partly clearly to open Mouthful, amount of opening 82mm, warp tension 1200N, the back rest are less than brest beams, 316 ° of opening time, 98 ° of Filling Insertion Time.
4. production method according to claim 1, which is characterized in that the control condition of the warping process is rolling density 0.50~0.54g/cm3, 540~560m/min of speed of beaming.
5. production method according to claim 4, which is characterized in that the warping process is whole using Switzerland's Benniger wide cut Through machine, total quantity of warps 21000,24 warp beams, rolling density 0.52g/cm3, speed of beaming 550m/min.
6. production method according to claim 1, which is characterized in that the control condition of the sizing operation is regain 5.5~6%, 40~50m/min of speed of sizing machine, 12~13KN of squeezing roller pressure, 78~82 DEG C of slurry groove temperature.
7. production method according to claim 1, which is characterized in that the production method further includes dyeing and finishing technology, described Dyeing and finishing technology includes following processing step:Singe, concise desizing, bleaching, mercerising, Anti-Pilling Finishes, stentering forming and preshrunk.
8. production method according to claim 1, which is characterized in that the workshop temperature of the production method is 23~27 DEG C, relative humidity is 68~74%.
9. a kind of anti-plumage face material, which is characterized in that the anti-plumage face material is using the life as described in claim 1 to 8 any one Production method is prepared.
10. anti-plumage face material according to claim 9, which is characterized in that the anti-plumage face material through close 787~1220/ 10cm, 590~670/10cm of filling density.
CN201810011419.5A 2018-01-05 2018-01-05 Anti- plumage fabric plus material producing method and anti-plumage face material Pending CN108060496A (en)