CN108035047A - A kind of preparation process for train fabric - Google Patents
A kind of preparation process for train fabric Download PDFInfo
- Publication number
- CN108035047A CN108035047A CN201711094839.6A CN201711094839A CN108035047A CN 108035047 A CN108035047 A CN 108035047A CN 201711094839 A CN201711094839 A CN 201711094839A CN 108035047 A CN108035047 A CN 108035047A
- Authority
- CN
- China
- Prior art keywords
- fabric
- chosen
- phosphorous flame
- raw material
- woven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation process for train fabric, comprise the following steps：Raw material is chosen：Phosphorous flame-retardant fiber and polyester industrial yarn are chosen as making raw material, wherein described phosphorous flame-retardant fibre number is 3.0dtex 4.0dtex, phosphorus content is 6500 7000PPM, the terylene industrial silk size is 800dtex 1000dtex, and polyester industrial yarn and the phosphorous flame-retardant fiber is chosen by 1: 1.8 2.0；It is woven：Choose woven rapier loom and carry out woven processing, the raw material of selection is uniformly used in mixed way, the 380 400/10cm of rapier loom warp count, 200 220/10cm of weft count, knits and take fabric；High-temperature shaping：The fabric that takes will be knitted it is put into eight section baking oven forming machines and carry out qualitative processing, it is 25 30m/min of speed control forming machine rotating speed, and temperature is 170 180 DEG C, and the time is 30 40min.The fabric of the present invention can effectively improve the intensity and fire resistance of fabric, improve the quality of fabric, and after tested, Tear strength can reach the requirement of 400N, and reach the beautiful perfect adaptation with performance.
Description
Technical field
The present invention relates to technical field prepared by fabric, more particularly to a kind of preparation process for train fabric.
Background technology
Weaving original meaning is taken from the general name of spinning and weaving, but with the continuous hair of weaving knowledge hierarchy and subject system
Exhibition and perfect, after particularly non-woven textile material and the technologies such as three-dimensional is composite braided produce, weaving is not only traditional spinning
And weaving, also including nonwoven fabric technology, three dimensional weaving technique, electrostatic nanometer net-forming technology etc., weaving is roughly divided into spinning with compiling
Two procedures are knitted, the foremost textile of China is no more than silk, and the transaction of silk has driven the exchange and friendship of oriental and occidental cultures
Logical development, also have impact on business and the military affairs in west, there are certain defect, the intensity of fabric for existing train fabric indirectly
All have much room for improvement with fire protecting performance.A kind of for this reason, it is proposed that preparation process for train fabric.
The content of the invention
It is a primary object of the present invention to provide a kind of preparation process for train fabric, background skill can be effectively solved
The problem of in art.
To achieve the above object, the technical solution taken of the present invention is：
A kind of preparation process for train fabric, comprises the following steps：
（1）, raw material choose：Phosphorous flame-retardant fiber and polyester industrial yarn are chosen as raw material is made, wherein the phosphorous flame-retardant is fine
Fibre number is 3.0dtex-4.0dtex, and phosphorus content 6500-7000PPM, the terylene industrial silk size is 800dtex-
1000dtex, polyester industrial yarn and the phosphorous flame-retardant fiber are chosen by 1: 1.8-2.0；
（2）, it is woven：Choose woven rapier loom and carry out woven processing, by step（1）The raw material of selection is uniformly used in mixed way, institute
Rapier loom warp count 380-400 roots/10cm is stated, weft count 200-220 roots/10cm, knit and take fabric；
（3）, high-temperature shaping：Will（2）Knit the fabric taken and be put into the qualitative processing of eight section baking oven forming machines progress, control forming machine rotating speed
For speed 25-30m/min, temperature is 170-180 DEG C, and time 30-40min, makes fabric dimensionally stable, is not contracted with reaching washing
The effect of water.
Further, the step（1）The phosphorous flame-retardant fibre number of selection is 3.0dtex, phosphorus content 6500PPM,
The terylene industrial silk size of selection is 800dtex, and polyester industrial yarn and the phosphorous flame-retardant fiber is chosen by 1: 1.8.
Compared with prior art, the present invention has the advantages that：The present invention is by choosing phosphorous flame-retardant fiber and washing
Synthetic fibre industrial yarn is as raw material is made, wherein the phosphorous flame-retardant fibre number is 3.0dtex-4.0dtex, phosphorus content 6500-
7000PPM, the terylene industrial silk size are 800dtex-1000dtex, and polyester industrial yarn and the phosphorous flame-retardant fiber presses 1:
1.8-2.0 chooses, and can effectively improve the intensity and fire resistance of fabric, improves the quality of fabric, after tested, Tear strength
The requirement of 400N can be reached, and reached the beautiful perfect adaptation with performance.
Embodiment
To make the technical means, the creative features, the aims and the efficiencies achieved by the present invention easy to understand, with reference to
Embodiment, the present invention is further explained.
Embodiment 1：
A kind of preparation process for train fabric, comprises the following steps：
（1）, raw material choose：Phosphorous flame-retardant fiber and polyester industrial yarn are chosen as raw material is made, wherein the phosphorous flame-retardant is fine
Fibre number is 3.0dtex, phosphorus content 6500PPM, and the terylene industrial silk size is 800dtex, the polyester industrial yarn and
Phosphorous flame-retardant fiber is chosen by 1: 1.8；
（2）, it is woven：Choose woven rapier loom and carry out woven processing, by step（1）The raw material of selection is uniformly used in mixed way, institute
380/10cm of rapier loom warp count is stated, 200/10cm of weft count, knits and take fabric；
（3）, high-temperature shaping：Will（2）Knit the fabric taken and be put into the qualitative processing of eight section baking oven forming machines progress, control forming machine rotating speed
For speed 25m/min, temperature is 170 DEG C, time 30min.
Embodiment 2：
A kind of preparation process for train fabric, comprises the following steps：
（1）, raw material choose：Phosphorous flame-retardant fiber and polyester industrial yarn are chosen as raw material is made, wherein the phosphorous flame-retardant is fine
Fibre number is 3.5dtex, phosphorus content 6800PPM, and the terylene industrial silk size is 900dtex, the polyester industrial yarn and
Phosphorous flame-retardant fiber is chosen by 1: 1.9；
（2）, it is woven：Choose woven rapier loom and carry out woven processing, by step（1）The raw material of selection is uniformly used in mixed way, institute
390/10cm of rapier loom warp count is stated, 210/10cm of weft count, knits and take fabric；
（3）, high-temperature shaping：Will（2）Knit the fabric taken and be put into the qualitative processing of eight section baking oven forming machines progress, control forming machine rotating speed
For speed 28m/min, temperature is 175 DEG C, time 35min.
Embodiment 3：
A kind of preparation process for train fabric, comprises the following steps：
（1）, raw material choose：Phosphorous flame-retardant fiber and polyester industrial yarn are chosen as raw material is made, wherein the phosphorous flame-retardant is fine
Fibre number is 4.0dtex, phosphorus content 7000PPM, and the terylene industrial silk size is 1000dtex, the polyester industrial yarn and
Phosphorous flame-retardant fiber is chosen by 1: 2.0；
（2）, it is woven：Choose woven rapier loom and carry out woven processing, by step（1）The raw material of selection is uniformly used in mixed way, institute
400/10cm of rapier loom warp count is stated, 220/10cm of weft count, knits and take fabric；
（3）, high-temperature shaping：Will（2）Knit the fabric taken and be put into the qualitative processing of eight section baking oven forming machines progress, control forming machine rotating speed
For speed 30m/min, temperature is 180 DEG C, time 40min.
The basic principles, main features and the advantages of the invention have been shown and described above.The technical staff of the industry
It should be appreciated that the present invention is not limited to the above embodiments, the above embodiments and description only describe the present invention
Principle, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these change and
Improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appended claims and its equivalent
Thing defines.
Claims (2)
- A kind of 1. preparation process for train fabric, it is characterised in that：Comprise the following steps：Raw material is chosen：Phosphorous flame-retardant fiber and polyester industrial yarn are chosen as raw material is made, wherein the phosphorous flame-retardant fiber is fine It is 800dtex- to spend for 3.0dtex-4.0dtex, phosphorus content 6500-7000PPM, the terylene industrial silk size 1000dtex, polyester industrial yarn and the phosphorous flame-retardant fiber are chosen by 1: 1.8-2.0；It is woven：Choose woven rapier loom and carry out woven processing, by step（1）The raw material of selection is uniformly used in mixed way, the sword Bar warp on loom density 380-400 roots/10cm, weft count 200-220 roots/10cm, knit and take fabric；High-temperature shaping：Will（2）Knit the fabric taken and be put into the qualitative processing of eight section baking oven forming machines progress, control forming machine rotating speed as speed 25-30m/min is spent, temperature is 170-180 DEG C, time 30-40min.
- A kind of 2. preparation process for train fabric according to claim 1, it is characterised in that：The step（1）Choosing The phosphorous flame-retardant fibre number taken is 3.0dtex, and phosphorus content 6500PPM, the terylene industrial silk size of selection is 800dtex, Polyester industrial yarn and the phosphorous flame-retardant fiber is chosen by 1: 1.8.