CN103046194A - Dacron draped shading fabric and manufacturing method thereof - Google Patents

Dacron draped shading fabric and manufacturing method thereof Download PDF

Info

Publication number
CN103046194A
CN103046194A CN2012105881251A CN201210588125A CN103046194A CN 103046194 A CN103046194 A CN 103046194A CN 2012105881251 A CN2012105881251 A CN 2012105881251A CN 201210588125 A CN201210588125 A CN 201210588125A CN 103046194 A CN103046194 A CN 103046194A
Authority
CN
China
Prior art keywords
fabric
terylene
draped
fold
dacron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105881251A
Other languages
Chinese (zh)
Other versions
CN103046194B (en
Inventor
孙文浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANGZHOU MEIYUAN TEXTILE CO Ltd
Original Assignee
HANGZHOU MEIYUAN TEXTILE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANGZHOU MEIYUAN TEXTILE CO Ltd filed Critical HANGZHOU MEIYUAN TEXTILE CO Ltd
Priority to CN201210588125.1A priority Critical patent/CN103046194B/en
Publication of CN103046194A publication Critical patent/CN103046194A/en
Application granted granted Critical
Publication of CN103046194B publication Critical patent/CN103046194B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Disclosed is dacron draped shading fabric. The dacron draped shading fabric is a double-layer bag fabric formed by knitting a group of warps and two groups of wefts, and not the inner layer, but the surface layer of the double-layer bag fabric is of a draped structure. The draped structure of the surface layer is formed by raised lines and grooves distributed on the surface fabric. The dacron draped shading fabric is stable in drapes and free of deformation during stretching in use, is layering and stereoscopic in drape style, thick and good in drooping effect and has good shading effect. The manufacturing method of the dacron draped shading fabric includes steps of stretching the warps, weaving in a jacquard manner, preforming, washing, dyeing and finishing, and forming, and further includes steaming and boiling surface wefts before stretching the warps. The manufacturing method of the dacron draped shading fabric is simple and easy to control, high in efficiency and low in cost.

Description

A kind of terylene fold shade fabric and preparation method thereof
Technical field
The present invention relates to the production method of a kind of fabric and this fabric, relate in particular to a kind of terylene fold shade fabric and preparation method thereof.
Background technology
Fold has been given vision and the haptic effect of fabric uniqueness, is widely used in clothes and decorative fabric.The production method of existing double-deck crinkle fabric is mainly to be used the double ends axle to weave or makes, presses the rear arrangements such as pleat or chemical paste stamp to make to fabric, the double ends axle is weaved and is utilized two beams of a loom through the different concavo-convex folds that form the fabric surface of tension force, this method complex manufacturing, high to equipment requirement, difficult control; Fabric is made, pressed the post processings such as pleat or chemical paste stamp make double-deck crinkle fabric, its fold easily is stretched distortion and affects attractive in appearance and sense of touch in the fabric use procedure, and this method efficient is low, cost is high.
Summary of the invention
The technical problem to be solved in the present invention is, for above the deficiencies in the prior art, a kind of terylene fold shade fabric is provided, this fabric fold is stable, it is undeformed to stretch in the fabric use procedure, and the fold style has more stereovision, third dimension, and fabric is abundant, vertical sense and has good shaded effect well.
A kind of technical solution of the present invention is:
A kind of terylene fold shade fabric, it is by one group of warp thread and two groups of double-ply bag fabrics that weft yarn is interwoven, its top layer has by raised line and recessed fold that is staggered and forms, nexine corrugationless structure; Wherein, described raised line is to be interwoven by table warp and table latitude, and described recessed is through forming with the back weft access node by table.
Described one group of warp thread adopts the CATION terylene low-stretch yarn of 100D/48F; Described two groups of weft yarns adopt respectively the polyester filament of 300D/96F, the black silk of terylene of 300D/96F; Described organizine density is 65 pieces/centimetre; Described weft density is 50 pieces/centimetre; Described organizine adds up to 18360; Described table organization and inner tissue are plain weave, and table organization arranges than being 1:1 with the tram of inner tissue.
This fabric fold is stable, and is undeformed, and the fold style has more stereovision, third dimension.Double-layer fabric is abundant, and vertical sense and has good shaded effect well.
Another technical problem that the present invention will solve is, the preparation technology of this terylene fold shade fabric is provided, and this preparation technology is simple, easy to control, efficient is high, cost is low.
Another technical scheme of the present invention provides a kind of preparation technology of terylene fold shade fabric, comprise following technical process: skewer is through technique → jacquard weaving technique → presetting technology → washing dyeing and finishing technology → setting process, it also is included in the table latitude boiling treatment process of skewer before technique, described table latitude boiling treatment process is put into totally-enclosed boiler and is heated to 100 ℃ ~ 120 ℃ with the programming rate of 2 ℃ ~ 5 ℃/min by room temperature for showing latitude, and is incubated 10 ~ 20min under high temperature; Described skewer is common process through technique, jacquard weaving technique, presetting technology, washing dyeing and finishing technology and setting process, and wherein, the pre-setting temperature of described presetting technology is 150 ℃; Described washing dyeing and finishing technology temperature is 130 ℃; The setting temperature of described setting process is 160 ℃.
Terylene fold shade fabric of the present invention before looming weaving especially the his-and-hers watches latitude carried out the thermophilic digestion processing, reduce to 5 ~ 8% through the warp-wise dimensional stability to heating in house of table latitude in the time of 150 ℃ that thermophilic digestion is processed, and the warp-wise dimensional stability to heating in house of the back weft of processing without thermophilic digestion in the time of 150 ℃ is 10 ~ 15%.The table latitude dimensional stability to heating in house different from back weft causes double-layer fabric the nexine fabric to occur with respect to the broadwise contraction of top layer fabric under presetting technology is processed, and both there was the warp-wise projection in the top layer fabric with respect to the nexine material; Owing to the existence of table warp with the binding place of back weft, make fabric part, top layer still keep smooth, the top layer fabric convexes to form recessed relatively, recessed the projection with the top layer fabric is divided into many raised lines, the fold of top layer fabric has appearred consisting of in a certain way circulation of raised line and recessed, and the regularity of distribution that changes binding place can change the wrinkling style of top layer fabric.To have fold blank volume cloth after washing dyeing and finishing and setting process processing, the third dimension of superficial fold, stereovision strengthen, and pleated structure is more stable, full, and the nexine fabric is more smooth, abundant.Terylene fold shade fabric tool double-decker of the present invention, its nexine fabric parallel are selected the black silk of terylene, and the two combination can reach preferably shaded effect, and the pleated structure on top layer also plays certain auxiliary shade function.The production method of terylene fold shade fabric of the present invention is simple, efficient is high, cost is low, and unique fold style and good shading performance make it particularly have competitiveness in the shade curtain fabric market in fabric market.
Description of drawings
Below in conjunction with accompanying drawing the present invention is further Mi Ming:
The access node organization chart of Fig. 1 terylene fold of the present invention shade fabric;
Crunode among the figure represents through the riser on the table latitude; Round dot represents the riser of back warp on back weft; Triangle represents that through the riser on back weft the space is the latitude floating-point of tram on organizine, square expression binding place.
Specific implementation method
Below in conjunction with accompanying drawing the present invention is described further.
Adopt one group of warp thread and two groups of weft weavings, warp thread adopts the CATION terylene low-stretch yarn of 100D/48F; The table latitude adopts the terylene fullly drawn yarn (FDY) of 300D/96F, and back weft adopts the complete black silk that stretches of the terylene of 300D/96F; Organizine density is 65 pieces/centimetre; Weft density is 50 pieces/centimetre; Organizine adds up to 18360; As shown in Figure 1, table organization and inner organizing are all adopted plain weave structure, and table organization arranges than being 1:1 with the tram of inner tissue.
To show latitude puts into totally-enclosed boiler and is heated to 100 ℃~120 ℃ with the programming rate of 2 ℃~5 ℃/min by room temperature, and after being incubated 10~20min under the high temperature, take out, treat that temperature is down to about 50 ℃~80 ℃, then, with reference to shown in Figure 1, technique skewer warp and looming weaving obtain the top layer double-ply bag fabric cloth base consistent with the nexine outward appearance routinely; The cloth base is carried out pre-setting, and the pre-setting temperature is 150 ℃, and the door width of cloth is 290cm, and the speed of a motor vehicle is 50 yards, and this moment, top layer fabric fold blank formed; Technique is washed dyeing and finishing process to the cloth base routinely; At last the cloth base is finalized the design, setting temperature is 160 ℃, and the door width of cloth is 280cm, and the speed of a motor vehicle is 30 yards, obtains top layer warp-wise fold, and the closely knit smooth finished fabric of nexine detects the processing such as packing to finished fabric.

Claims (4)

1. terylene fold shade fabric, it is characterized in that: it is by one group of warp thread and two groups of double-ply bag fabrics that weft yarn is interwoven, and its top layer has by raised line and recessed fold that is staggered and forms, nexine corrugationless structure; Wherein, raised line is to be interwoven by table warp and table latitude, and described recessed is through forming with the back weft access node by table.
2. a kind of terylene fold shade fabric according to claim 1 is characterized in that: the CATION terylene low-stretch yarn of one group of warp thread employing 100D/48F; Two groups of weft yarns adopt respectively the polyester filament of 300D/96F, the black silk of terylene of 300D/96F.
3. the preparation method of terylene fold shade fabric as claimed in claim 1, comprise following technical process: skewer is through technique → jacquard weaving technique → presetting technology → washing dyeing and finishing technology → setting process, it is characterized in that: it also is included in the table latitude boiling treatment process of skewer before technique, described table latitude boiling treatment process is put into totally-enclosed boiler and is heated to 100 ℃ ~ 120 ℃ with the programming rate of 2 ℃ ~ 5 ℃/min by room temperature for showing latitude, and is incubated 10 ~ 20min under high temperature.
4. the production method of terylene fold shade fabric according to claim 3, it is characterized in that: the pre-setting temperature of described presetting technology is 150 ℃; Described washing dyeing and finishing technology temperature is 130 ℃; The setting temperature of described setting process is 160 ℃.
CN201210588125.1A 2012-12-31 2012-12-31 Dacron draped shading fabric and manufacturing method thereof Expired - Fee Related CN103046194B (en)