CN108033682A - The sheen glaze and glaze noodle producing method of glazed tile - Google Patents
The sheen glaze and glaze noodle producing method of glazed tile Download PDFInfo
- Publication number
- CN108033682A CN108033682A CN201711295044.1A CN201711295044A CN108033682A CN 108033682 A CN108033682 A CN 108033682A CN 201711295044 A CN201711295044 A CN 201711295044A CN 108033682 A CN108033682 A CN 108033682A
- Authority
- CN
- China
- Prior art keywords
- glaze
- paint
- glazed tile
- sheen
- glossiness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the sheen glaze and glaze noodle producing method of a kind of glazed tile, the chemical composition and mass percentage of its siccative are：SiO248~53%, Al2O311~15%, CaO 6~8%, MgO 0.5~1.5%, K2O 2~5%, Na2O 2~5%, B2O30.2~1%, BaO 5~8%, ZnO 10~13%, ZrO22~3%, Fe2O3≤0.2%、TiO2≤ 0.1%, surplus is impurity.This glaze adds suitable aluminium oxide, zinc oxide, calcic, baric raw material in formula, forms composite matt glaze agent；Zinc-aluminium high temperature forms spinelle, improves glaze paint opacity, adjusts glossiness, adjusts the high temperature levelability of glaze paint so that the more smooth exquisiteness of glaze paint.This glaze introduces suitable kaolin, and aluminium oxide, zinc oxide, adjusts glaze paint chemical composition, to adjust in glaze the mineral compositions such as calcium is unglazed, barium is unglazed and zinc is unglazed, composite matt glaze agent, reach the smooth exquisiteness of glaze paint, the low purpose of glossiness.
Description
Technical field
The present invention relates to a kind of Ceramic glaze and preparation method, prepared by the sheen glaze and glaze paint of especially a kind of glazed tile
Method.
Background technology
With the raising of present material and culture level and the popularization of environmental sanitation, requirement of the people to environment of living
A part higher and higher, that glazed tile is decorated as living environment, it is moist that people are more desirable to glazed tile surface more smooth, touches
Feel, easy cleaning, surface gloss is low, it is not easy to because light damages eyes, therefore, study surfacing exquisiteness light
Sliding and low glossiness sheen glaze is the inevitable requirement that people improve the quality of living.
Or existing common matting glaze rough surface glossiness is low, or the smooth glossiness of glaze paint is high, the two must not be simultaneous
One.Also there is the sheen glaze newly researched and developed currently on the market, but I develops different from their technique, and effect is also different, he
On the basis of former common dumb light glaze paint, by adding soft polissoir, by the soft throwing of glaze paint, although this soft throwing glossiness
It is low, but pin hole is more, and production production process is added into, production cost is considerably increased, and less than optimal sheen glaze paint is imitated
Fruit.Also there is the sheen glaze that low gloss ink is sprayed in highlighted glaze paint, though this technique is easy to operate, its glossiness also has
Between 30~70, gloss is too strong.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of sheen glaze of the high glazed tile of glossiness；The present invention also carries
A kind of glaze noodle producing method of glazed tile is supplied.
In order to solve the above technical problems, the technical solution used in the present invention is：The chemical composition and quality hundred of its siccative
Point content is：SiO248~53%, Al2O311~15%, CaO 6~8%, MgO 0.5~1.5%, K2O 2~5%, Na2O 2~
5%、B2O30.2~1%, BaO 5~8%, ZnO 10~13%, ZrO22~3%, Fe2O3≤0.2%、TiO2≤ 0.1%, surplus is
Impurity.
The raw material of siccative described in glaze of the present invention is using kaolin, zirconium silicate, aluminium oxide, burning talcum, albite, zinc oxide
And frit.
The method of the present invention uses above-mentioned glaze；The siccative adds water to be modulated into glaze slip, and glazing is behind the surface of brick, sintering
It can obtain the glaze paint.
325 purpose of glaze slip described in the method for the present invention is tailed over as 0.1~0.4g/100ml, flow velocity for 50 milliliters of current meters 25~
35 seconds, proportion was 1.85~1.90g/ml.
It is using beneficial effect caused by above-mentioned technical proposal：The present invention added in component suitable aluminium oxide,
Zinc oxide, calcium oxide, barium monoxide, form composite matt glaze agent；Zinc-aluminium high temperature forms spinelle, improves glaze paint opacity, adjusts light
Damp degree, adjusts the high temperature levelability of glaze paint so that the more smooth exquisiteness of glaze paint.Suitable kaolin, oxygen are introduced in raw material of the present invention
Change aluminium, zinc oxide, adjust glaze paint chemical composition, calcium is unglazed, barium is unglazed and zinc is unglazed adjusting in glaze, the mineral such as composite matt glaze agent
Composition, reaches the smooth exquisiteness of glaze paint, the low purpose of glossiness.
The method of the present invention products obtained therefrom is compared with the similar product mutually having, its glaze paint is more moist, and glossiness is low, slightly
Rugosity is in below 0.7um, and glossiness is between 10~20；Since glaze paint more flat smooth is fine and smooth, glossiness is low, and product glaze paint is high
The defects of warm flow leveling is more preferable, more difficult generation pin hole, glossiness is low, injury of the more difficult generation to human eye；
Gained sheen glaze product surface is more moist, and glossiness is low, is more suitable for the needs of modern people's consumption.
Embodiment
The present invention will be further described in detail with reference to the specific embodiments.
The sheen glaze of this glazed tile is using kaolin, zirconium silicate, aluminium oxide, burning talcum, albite, zinc oxide and melts
Block is configured to siccative, then adds water to be modulated into glaze slip by siccative；Glazing can obtain glaze paint behind the surface of brick, sintering.It is described dry
Material is matched by the mass percentage of following chemical compositions：SiO248~53%, Al2O311~15%, CaO 6~8%,
MgO 0.5~1.5%, K2O 2~5%, Na2O 2~5%, B2O30.2~1%, BaO 5~8%, ZnO 10~13%, ZrO22~
3%、Fe2O3≤0.2%、TiO2≤ 0.1%, surplus is impurity.325 purpose of glaze slip is tailed over as 0.1~0.4g/100ml, flow velocity
For 50 milliliters of current meters 25~35 seconds, proportion was 1.85~1.90g/ml.
Embodiment 1-7：The sheen glaze and glaze noodle producing method of this glazed tile are using following with when technique.
（1）Composition proportion：It is configured to using kaolin, zirconium silicate, aluminium oxide, burning talcum, albite, zinc oxide and frit
Siccative, the composition proportion of siccative is shown in Table 1 in each embodiment.
Table 1：The composition proportion of siccative in each embodiment（wt%）
In table 1, the surplus of each embodiment dry ingredients is impurity.
（2）Modulate glaze slip：Water is added to be modulated into glaze slip above-mentioned siccative.The index of glaze slip is shown in Table 2 obtained by each embodiment.
Table 2：The index of glaze slip obtained by each embodiment
The time that flow velocity described in table 2 flows to end for 50 milliliters of volumetric standards detection glaze slips.
（3）Glaze paint detects：Above-mentioned glaze slip glazing be can obtain into the glaze paint behind the surface of brick, sintering.To gained
Glaze paint carries out complete detection analysis and summary, obtains the every overall target of table 3.
Table 3：The Testing index of each embodiment glaze paint
The interpretation of result detected from table 3 goes out：Common matting glaze 1, glaze paint pin hole is less, and glossiness is higher more than 20, roughness
It is partially thick in more than 0.7um；Common matting glaze 2, glaze paint pin hole is less, and glossiness is below 20, but roughness is in more than 0.7um
It is partially thick.Glaze paint pin hole obtained by this glaze is seldom, is better than common matting glaze, glossiness is between 10~20, while surface roughness
In below 0.7um, it is better than common matting glaze；Seldom with glaze paint pin hole, glossiness is low, and surface roughness is low, and glaze paint is smooth thin
The features such as greasy.
Claims (4)
1. the sheen glaze of a kind of glazed tile, it is characterised in that the chemical composition and mass percentage of its siccative be：SiO2 48
~53%, Al2O311~15%, CaO 6~8%, MgO 0.5~1.5%, K2O 2~5%, Na2O 2~5%, B2O30.2~1%,
BaO 5~8%, ZnO 10~13%, ZrO22~3%, Fe2O3≤0.2%、TiO2≤ 0.1%, surplus is impurity.
2. the sheen glaze of glazed tile according to claim 1, it is characterised in that：The raw material of the siccative for kaolin,
Zirconium silicate, aluminium oxide, burn talcum, albite, zinc oxide and frit.
A kind of 3. glaze noodle producing method of glazed tile, using the glaze described in claim 1 or 2, it is characterised in that：The siccative
Water is added to be modulated into glaze slip, glazing can obtain the glaze paint behind the surface of brick, sintering.
4. the glaze noodle producing method of glazed tile according to claim 3, it is characterised in that：325 purpose of glaze slip tails over
For 0.1~0.4g/100ml, flow velocity is 50 milliliters of current meters 25~35 seconds, and proportion is 1.85~1.90g/ml.