CN105776863A - Mild satin glaze and manufacturing method thereof - Google Patents

Mild satin glaze and manufacturing method thereof Download PDF

Info

Publication number
CN105776863A
CN105776863A CN201610181020.2A CN201610181020A CN105776863A CN 105776863 A CN105776863 A CN 105776863A CN 201610181020 A CN201610181020 A CN 201610181020A CN 105776863 A CN105776863 A CN 105776863A
Authority
CN
China
Prior art keywords
glaze
satin
profit
percent
satin glaze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610181020.2A
Other languages
Chinese (zh)
Inventor
叶德林
韦前
黄春林
韦守泉
朱光耀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG XINMINGZHU CERAMIC GROUP CO Ltd
Foshan Sanshui Newpearl Building Ceramics Industrial Co Ltd
Original Assignee
GUANGDONG XINMINGZHU CERAMIC GROUP CO Ltd
Foshan Sanshui Newpearl Building Ceramics Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG XINMINGZHU CERAMIC GROUP CO Ltd, Foshan Sanshui Newpearl Building Ceramics Industrial Co Ltd filed Critical GUANGDONG XINMINGZHU CERAMIC GROUP CO Ltd
Priority to CN201610181020.2A priority Critical patent/CN105776863A/en
Publication of CN105776863A publication Critical patent/CN105776863A/en
Pending legal-status Critical Current

Abstract

The invention relates to mild satin glaze, which is characterized by being prepared from the following raw materials in percentage by weight: 15 to 26 percent of potash feldspar, 20 to 22 percent of albite, 10 to 15 percent of kaoline, 5 to 10 percent of soapstone, 10 to 22 percent of calcite, 8 to 14 percent of tin oxide, 2 to 5 percent of wollastonite and 10 to 15 percent of sewage squeezed mud. Mineral raw materials and chemical engineering raw materials are matched to be used; a fire-new formula is used; a ceramic tile glaze surface which is flat, fine and pinhole-free and has satin luster can be obtained; the glaze surface does not have strong reflection; a soft, silent and comfortable feeling is given to people; good anti-staining and anti-slip performance is realized; the mild satin glaze belongs to building ceramic tile glaze with great market potentials.

Description

One accumulates profit satin glaze and manufacture method thereof
Technical field
The present invention relates to the glaze paint of a kind of architectural pottery and manufacture method thereof.
Background technology
Smooth satiny glaze paint, element is quiet and not delicate and charming, smooth and brightless, and finger touches like Adeps caprae seu ovis, light such as wax, like satin, like thin,tough silk, stain resistance, and in the same circumstances, heat stability and comprcssive strength are all good than common Transparent frlt, bright glaze.This matting glaze product can make people feel quiet, in detail and, body and mind is loosened, and tired out alleviates, happy.High-grade matting glaze product, has catered to the psychology of people, has increasingly been subject to the welcome of consumer with its distinctive effect.
But this almost Perfect accumulate profit glaze paint, current industrialization produce Building Ceramics Industry, become the problem of a kind of very difficult breakthrough.Especially for the low water absorption tile product of once-firing, the technical research of this glaze paint being also not bery short of, there is glaze paint out-of-flatness, have the shortcomings such as Pericarpium Citri Reticulatae glaze paint and tiny pin hole in such glaze kind at present in whole structure.
Summary of the invention
Technical problem solved by the invention is in that to overcome the existing deficiency accumulateing profit sheen glaze paint, it is provided that satin glaze and manufacture method thereof are moistened in a kind of brand-new accumulateing.
For achieving the above object, the technical scheme is that one accumulates profit satin glaze, the percentage by weight of the raw material of this satin glaze consists of: potash feldspar 15 ~ 26%, albite 20 ~ 22%, Kaolin 10 ~ 15%, Talcum 5 ~ 10%, calcite 10 ~ 22%, stannum oxide 8 ~ 14%, wollastonite 2 ~ 5%, sewage squeezing mud 10 ~ 15%.
The weight content of the chemical composition of this satin glaze is SiO2It is 38 ~ 50%;Al2O3It is 15 ~ 23%;Fe2O3It is 0.1 ~ 1%;TiO2It is 2 ~ 2.5%;CaO is 10 ~ 25%;MgO is 2 ~ 8;K2O is 3 ~ 10%;Na2O is 5 ~ 10%;SnO2It is 5 ~ 6%;ZrO2It is 0.2 ~ 0.5%.
This accumulates profit satin glaze surface gloss and is 10-15 DEG C.
A kind of manufacture method accumulateing profit satin glaze, step is as follows: a, consist of according to raw material weight percentage ratio: potash feldspar 15 ~ 26%, albite 20 ~ 22%, Kaolin 10 ~ 15%, Talcum 5 ~ 10%, calcite 10 ~ 22%, stannum oxide 8 ~ 14%, wollastonite 2 ~ 5%, sewage squeezing mud 10 ~ 15% chooses raw material, and adds the water of raw material gross weight 50%;B, ball milling more than 24 hours, obtains glaze slip, then by precipitating type partition method, coarse granule is separated, and controlling fineness 325 mesh screen residue is mass fraction 0.1 ~ 0.5%, older more than 48 hours afterwards;C, the method adopting straight line falling body type pouring glaze, be uniformly applied to billet surface by glaze slip;D, when firing temperature is 1200 DEG C calcine 1 hour, obtain accumulateing profit satin glaze.
The beneficial effects of the present invention is: by raw mineral materials and industrial chemicals with the use of, adopt brand-new formula, glaze paint can be obtained smooth, fine and smooth free of pinholes and there is the ceramic tile glaze paint of gloss as tiffany, glaze paint is without strongly reflective, to a kind of soft, quiet, comfortable impression of people, and there is well antifouling, non-skid property, be the architectural ceramics brick glaze kind of a kind of great market potential.
Detailed description of the invention
One accumulates profit satin glaze, the percentage by weight of the raw material of this satin glaze consists of: potash feldspar 15 ~ 26%, albite 20 ~ 22%, Kaolin 10 ~ 15%, Talcum 5 ~ 10%, calcite 10 ~ 22%, stannum oxide 8 ~ 14%, wollastonite 2 ~ 5%, sewage squeezing mud 10 ~ 15%.The weight content of the chemical composition of this satin glaze is SiO2It is 38 ~ 50%;Al2O3It is 15 ~ 23%;Fe2O3It is 0.1 ~ 1%;TiO2It is 2 ~ 2.5%;CaO is 10 ~ 25%;MgO is 2 ~ 8;K2O is 3 ~ 10%;Na2O is 5 ~ 10%;SnO2It is 5 ~ 6%;ZrO2It is 0.2 ~ 0.5%.Sewage squeezing mud can adopt the sewage sludge that building ceramic enterprises production process produces, and after precipitation purification process technique, the cycling and reutilization raw material of preparation, to save cost, it can also use common mud.
This accumulates the smooth exquisiteness in profit satin glaze surface, and feel is gentle, and surface gloss is 10-15 DEG C, is the glossiness to people's vision the most comfortable.
A kind of manufacture method accumulateing profit satin glaze, step is as follows.
A, consist of according to raw material weight percentage ratio: potash feldspar 15 ~ 26%, albite 20 ~ 22%, Kaolin 10 ~ 15%, Talcum 5 ~ 10%, calcite 10 ~ 22%, stannum oxide 8 ~ 14%, wollastonite 2 ~ 5%, sewage squeezing mud 10 ~ 15% chooses raw material, and adds the water of raw material gross weight 50%.
B, ball milling more than 24 hours, obtains glaze slip, then by precipitating type partition method, coarse granule is separated, and controlling fineness 325 mesh screen residue is mass fraction 0.1 ~ 0.5%, older more than 48 hours afterwards.
C, the method adopting straight line falling body type pouring glaze, be uniformly applied to billet surface by glaze slip.
D, when firing temperature is 1200 DEG C calcine 1 hour, obtain accumulateing profit satin glaze.
Embodiment 1: calculate by weight, takes potash feldspar 26%, albite 20%, Kaolin 10%, Talcum 8%, calcite 12%, stannum oxide 9%, wollastonite 3%, sewage squeezing mud 12%, mix homogeneously after pulverizing;Gross weight according to above raw material is benchmark, adds the water of 50% weight in load weighted raw material, after ball mill ball milling 24 hours, obtain glaze slip, by precipitating type partition method, coarse granule being separated, controlling fineness (325 mesh screen residue) is 0.4%, older 48 hours afterwards again;The method adopting straight line falling body type to drench glaze, is uniformly applied to billet surface by glaze slip;Calcine 1 hour when firing temperature is 1200 DEG C, obtain accumulateing profit satin glaze.
The glaze chemical composition (wt%) of this embodiment is: SiO2It is 42.7%;Al2O3It is 22%;Fe2O3It is 0.5%;TiO2It is 2.5%;CaO is 10%;MgO is 6%;K2O is 5%;Na2O is 5.8%;SnO2It is 5%;ZrO2It is 0.3%.
Embodiment 2: calculate by weight, takes potash feldspar 20%, albite 20%, Kaolin 12%, Talcum 5%, calcite 13%, stannum oxide 13%, wollastonite 2%, sewage squeezing mud 15%, mix homogeneously after pulverizing;Gross weight according to above raw material is benchmark, adds the water of 50% weight in load weighted raw material, after ball mill ball milling 24 hours, obtain glaze slip, by precipitating type partition method, coarse granule being separated, controlling fineness (325 mesh screen residue) is 0.5%, older 48 hours afterwards again;The method adopting straight line falling body type to drench glaze, is uniformly applied to billet surface by glaze slip;Calcine 1 hour when firing temperature is 1200 DEG C, obtain accumulateing profit satin glaze.
The chemical composition (wt%) of this embodiment is: SiO2It is 44.6%;Al2O3It is 15%;Fe2O3It is 0.6%;TiO2It is 2.3%;CaO is 10%;MgO is 6;K2O is 8%;Na2O is 7%;SnO2It is 6%;ZrO2It is 0.5%.

Claims (6)

1. one kind is accumulate profit satin glaze, it is characterised in that the percentage by weight of the raw material of this satin glaze consists of: potash feldspar 15 ~ 26%, albite 20 ~ 22%, Kaolin 10 ~ 15%, Talcum 5 ~ 10%, calcite 10 ~ 22%, stannum oxide 8 ~ 14%, wollastonite 2 ~ 5%, sewage squeezing mud 10 ~ 15%.
2. accumulate profit satin glaze as claimed in claim 1, it is characterised in that the weight content of the chemical composition of this satin glaze is SiO2It is 38 ~ 50%;Al2O3It is 15 ~ 23%;Fe2O3It is 0.1 ~ 1%;TiO2It is 2 ~ 2.5%;CaO is 10 ~ 25%;MgO is 2 ~ 8;K2O is 3 ~ 10%;Na2O is 5 ~ 10%;SnO2It is 5 ~ 6%;ZrO2It is 0.2 ~ 0.5%.
3. accumulate profit satin glaze as claimed in claim 1, it is characterised in that this accumulates profit satin glaze surface gloss and is 10-15 DEG C.
4. the manufacture method accumulateing profit satin glaze, it is characterised in that step is as follows:
A, consist of according to raw material weight percentage ratio: potash feldspar 15 ~ 26%, albite 20 ~ 22%, Kaolin 10 ~ 15%, Talcum 5 ~ 10%, calcite 10 ~ 22%, stannum oxide 8 ~ 14%, wollastonite 2 ~ 5%, sewage squeezing mud 10 ~ 15% chooses raw material, and adds the water of raw material gross weight 50%;
B, ball milling more than 24 hours, obtains glaze slip, then by precipitating type partition method, coarse granule is separated, and controlling fineness 325 mesh screen residue is mass fraction 0.1 ~ 0.5%, older more than 48 hours afterwards;
C, the method adopting straight line falling body type pouring glaze, be uniformly applied to billet surface by glaze slip;
D, when firing temperature is 1200 DEG C calcine 1 hour, obtain accumulateing profit satin glaze.
5. accumulate the manufacture method of profit satin glaze as claimed in claim 4, it is characterised in that the weight content of the chemical composition of this satin glaze is SiO2It is 38 ~ 50%;Al2O3It is 15 ~ 23%;Fe2O3It is 0.1 ~ 1%;TiO2It is 2 ~ 2.5%;CaO is 10 ~ 25%;MgO is 2 ~ 8;K2O is 3 ~ 10%;Na2O is 5 ~ 10%;SnO2It is 5 ~ 6%;ZrO2It is 0.2 ~ 0.5%.
6. accumulate the manufacture method of profit satin glaze as claimed in claim 4, it is characterised in that this accumulates profit satin glaze surface gloss and is 10-15 DEG C.
CN201610181020.2A 2016-03-28 2016-03-28 Mild satin glaze and manufacturing method thereof Pending CN105776863A (en)