CN108018720A - A kind of durable shiinkproof finish technique of wool fabric - Google Patents
A kind of durable shiinkproof finish technique of wool fabric Download PDFInfo
- Publication number
- CN108018720A CN108018720A CN201711350669.3A CN201711350669A CN108018720A CN 108018720 A CN108018720 A CN 108018720A CN 201711350669 A CN201711350669 A CN 201711350669A CN 108018720 A CN108018720 A CN 108018720A
- Authority
- CN
- China
- Prior art keywords
- wool fabric
- durable
- parts
- finishing liquid
- resin finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of durable shiinkproof finish technique of wool fabric, include the following steps：1）Pad resin finishing liquid：Qualified wool fabric will be examined to infiltrate into resin finishing liquid, two leachings two are carried out and roll processing, pick-up rate is 75 ~ 80%, wherein the resin finishing liquid includes the following ingredients formed by mass percentage：Waterborne polyurethane resin 30% 35%, softening agent 10% 15%, antiseptic 7% 10%, water 45% 55%；2）Preliminary drying；3）Bake；4）Washing.By the above-mentioned means, the present invention wool fabric is arranged using waterborne polyurethane resin dressing liquid, technique is simple and easy to control, during arrangement unharmful substance generation, safety and environmental protection, and it is collated after wool fabric there is durable anti-felting performance.
Description
Technical field
The present invention relates to fabric post-processing technology field, more particularly to a kind of durable shiinkproof finish work of wool fabric
Skill.
Background technology
Wool fabric has the advantages of other fabrics are incomparable, but the feltability of wool as a kind of expensive goods
Wool fabric is set easily to produce felting in washing, this has seriously affected the appearance and performance of wool fabric.For a long time,
Enterprise is mostly to carry out shiinkproof finish to wool fabric with oxidizer containing chlorine, still, oxidizer containing chlorine in process is arranged,
Substantial amounts of AOX can be produced（Adsorbable organic halogenes）, environment is seriously polluted, human body is damaged, while complex process,
Operating process is grown, and energy consumption is big, and wool fabric can be made to produce yellowing phenomenon.
The content of the invention
The invention mainly solves the technical problem of providing a kind of durable shiinkproof finish technique of wool fabric, can solve
Drawbacks described above existing for existing wool shrinkproof finishing technique.
In order to solve the above technical problems, one aspect of the present invention is：A kind of the durable of wool fabric is provided
Shiinkproof finish technique, includes the following steps：
1）Pad resin finishing liquid：Qualified wool fabric will be examined to infiltrate into resin finishing liquid, two leachings two are carried out and roll processing,
Pick-up rate is 75 ~ 80%, wherein the resin finishing liquid includes the following ingredients formed by mass percentage：Aqueous polyurethane tree
Fat 30%-35%, softening agent 10%-15%, antiseptic 7%-10%, water 45%-55%；
2）Preliminary drying：By step 1）Wool fabric after processing is dried to it and contains damp rate in advance at 70-75 DEG C<6%；
3）Bake：By step 2）Wool fabric after processing carries out baking 8-10min at 120-125 DEG C；
4）Washing：By step 3）Wool fabric after processing, which is infiltrated, carries out open width washing into clear water, then dries.
In a preferred embodiment of the present invention, the preparing raw material of the waterborne polyurethane resin includes：Isophorone two
40-45 parts of cyanate, polyethylene adjoin 12-18 parts of pyrrolidone, 10-15 parts of dibutyl tin, 8-12 parts of laurate, 20-25 parts of ethanol,
18-22 parts of sodium ethoxide.
In a preferred embodiment of the present invention, step 1）In, the bath raio of the wool fabric and resin finishing liquid is 1：
20。
In a preferred embodiment of the present invention, step 1）In, the temperature of the resin finishing liquid is 45-50 DEG C.
The beneficial effects of the invention are as follows：The present invention arranges wool fabric using waterborne polyurethane resin dressing liquid,
Technique is simple and easy to control, during arrangement unharmful substance produce, safety and environmental protection, and it is collated after wool fabric have it is durable
Anti- felting performance.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that so as to make a clearer definition of the protection scope of the present invention.
The embodiment of the present invention includes：
Embodiment one
A kind of durable shiinkproof finish technique of wool fabric, includes the following steps：
1）Pad resin finishing liquid：Qualified wool fabric will be examined to press bath raio 1：The resin finishing that temperature is 45 DEG C is arrived in 20 infiltrations
In liquid, carry out two leachings two and roll processing, pick-up rate 75%, wherein the resin finishing liquid includes forming down by mass percentage
Row component：Waterborne polyurethane resin 30%, softening agent 12%, antiseptic 8%, water 50%；
2）Preliminary drying：By step 1）Wool fabric after processing is dried to it and contains damp rate in advance at 70 DEG C<6%；
3）Bake：By step 2）Wool fabric after processing carries out baking 9min at 120 DEG C；
4）Washing：By step 3）Wool fabric after processing, which is infiltrated, carries out open width washing into clear water, then dries.
Wherein, the preparing raw material of the waterborne polyurethane resin includes：42 parts of isophorone dicyanate, polyethylene, which adjoin, to be coughed up
15 parts of alkanone, 12 parts of dibutyl tin, 9 parts of laurate, 22 parts of ethanol, 20 parts of sodium ethoxide.
Embodiment two
A kind of durable shiinkproof finish technique of wool fabric, includes the following steps：
1）Pad resin finishing liquid：Qualified wool fabric will be examined to press bath raio 1：The resin finishing that temperature is 45 DEG C is arrived in 20 infiltrations
In liquid, carry out two leachings two and roll processing, pick-up rate 78%, wherein the resin finishing liquid includes forming down by mass percentage
Row component：Waterborne polyurethane resin 32%, softening agent 14%, antiseptic 9%, water 45%；
2）Preliminary drying：By step 1）Wool fabric after processing is dried to it and contains damp rate in advance at 75 DEG C<6%；
3）Bake：By step 2）Wool fabric after processing carries out baking 10min at 125 DEG C；
4）Washing：By step 3）Wool fabric after processing, which is infiltrated, carries out open width washing into clear water, then dries.
Wherein, the preparing raw material of the waterborne polyurethane resin includes：45 parts of isophorone dicyanate, polyethylene, which adjoin, to be coughed up
16 parts of alkanone, 14 parts of dibutyl tin, 10 parts of laurate, 24 parts of ethanol, 18 parts of sodium ethoxide.
Present invention is disclosed a kind of durable shiinkproof finish technique of wool fabric, using waterborne polyurethane resin dressing liquid pair
Wool fabric is arranged, and technique is simple and easy to control, during arrangement unharmful substance produce, safety and environmental protection, and it is collated after
Wool fabric has durable anti-felting performance.
Upper described only the embodiment of the present invention, is not intended to limit the scope of the invention, every to utilize the present invention
The equivalent structure or equivalent flow shift that description is made, is directly or indirectly used in other related technical areas,
It is included within the scope of the present invention.
Claims (4)
1. the durable shiinkproof finish technique of a kind of wool fabric, it is characterised in that include the following steps：
1）Pad resin finishing liquid：Qualified wool fabric will be examined to infiltrate into resin finishing liquid, two leachings two are carried out and roll processing,
Pick-up rate is 75 ~ 80%, wherein the resin finishing liquid includes the following ingredients formed by mass percentage：Aqueous polyurethane tree
Fat 30%-35%, softening agent 10%-15%, antiseptic 7%-10%, water 45%-55%；
2）Preliminary drying：By step 1）Wool fabric after processing is dried to it and contains damp rate in advance at 70-75 DEG C<6%；
3）Bake：By step 2）Wool fabric after processing carries out baking 8-10min at 120-125 DEG C；
4）Washing：By step 3）Wool fabric after processing, which is infiltrated, carries out open width washing into clear water, then dries.
2. the durable shiinkproof finish technique of wool fabric according to claim 1, it is characterised in that the aqueous polyurethane
The preparing raw material of resin includes：40-45 parts of isophorone dicyanate, polyethylene adjoin 12-18 parts of pyrrolidone, dibutyl tin 10-
15 parts, 8-12 parts of laurate, 20-25 parts of ethanol, 18-22 parts of sodium ethoxide.
3. the durable shiinkproof finish technique of wool fabric according to claim 1, it is characterised in that step 1）In, it is described
The bath raio of wool fabric and resin finishing liquid is 1：20.
4. the durable shiinkproof finish technique of wool fabric according to claim 1, it is characterised in that step 1）In, it is described
The temperature of resin finishing liquid is 45-50 DEG C.