CN107955225A - 一种用于天然乳胶文胸的乳胶制品及其制备方法 - Google Patents
一种用于天然乳胶文胸的乳胶制品及其制备方法 Download PDFInfo
- Publication number
- CN107955225A CN107955225A CN201610896588.2A CN201610896588A CN107955225A CN 107955225 A CN107955225 A CN 107955225A CN 201610896588 A CN201610896588 A CN 201610896588A CN 107955225 A CN107955225 A CN 107955225A
- Authority
- CN
- China
- Prior art keywords
- natural emulsion
- brassiere
- latex product
- acid
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种用于天然乳胶文胸的乳胶制品及其制备方法，所述乳胶制品包括以下质量百分比的组分制成：（A）材料85%－95%，（B）材料4%－8%，（C）材料3%－7%，（D）材料0.5%－3%，经过发泡、定型、蒸煮制得乳胶制品材料，然后经过加工、剪切和修整制成天然乳胶文胸。本发明在原有的水洗天然乳胶原料混合过程中，进行配方的改进以及材料的添加，从而在保证原本天然乳胶的特性的基础上，改善耐高温热压及耐黄性，使天然乳胶在应用上的范围更广。
Description
技术领域
本发明涉及水洗天然乳胶产品，尤其涉及一种用于天然乳胶文胸的乳胶制品及其制备方法。
背景技术
目前市场上所有销售的文胸（或称胸罩、乳罩、奶罩）基本上内置材料都是泡绵，而泡绵为聚醚或聚酯材料其环保性和抗菌性无法与天然乳胶本身的纯天然及抗菌功能相比。目前，由于乳胶制品具有超柔软、透气性好、高韧性、不变形、不硬化、无毒、物理性能稳定、能抑制病菌、螨虫滋生、无静电等优点，开始应用于纺织、医疗等行业。
天然乳胶是橡胶树的一种产物，取自于橡胶树汁液，极其珍贵，因为每天每棵橡胶树只能产 30ml 乳胶汁。一个乳胶产品至少需一天到一天半的时间完成制作，是相当费时且材料珍贵的一种产品。现有的天然乳胶的柔软性和稳定性等特性与泡绵相比，在制作文胸的过程中乳胶无法进行直接热压成型，且加热容易变黄色，因此现阶段没有文胸是内置材料是天然乳胶的，而市场上销售的所谓的天然乳胶文胸只是在两泡绵中间进行不热压的夹层方式进行。在制作文胸过程中，天然乳胶因无法直接热压且难以达到耐黄性（加热不易变成黄色）的要求，因而有待改进。
发明内容
本发明的目的是为了克服目前水洗天然乳胶经过高温一次成型制作天然乳胶文胸时，无法达到高温热压稳定及抗黄变的效果。本发明提供了一种用于天然乳胶文胸的乳胶制品及其制备方法，使得产品不仅可以经过高温热压并且不变黄。
为了实现上述发明目的，本发明所采用的技术方案是：
一种用于天然乳胶文胸的乳胶制品及其制备方法，所述乳胶制品材料包括以下质量百分比的组分制成：（A）材料85%－95%，（B）材料4%－8%，（C）材料3%－7%，（D）材料0.5%－3%。
所述（A）材料具体组分包括：天然乳胶、硫磺粉、催化剂 、分散剂 、促进剂、橡胶硫化促进剂、乳胶抗氧化剂、表面活性剂、乳化剂、植物油酸、胺、水、植物油酸、氢氧化钾、蓖麻油、纤维素钠、合成胶，其中天然乳胶质量百分比为70－95%，合成胶质量百分比为5－15%。
所述（B）材料具体组分包括：植物油酸、蓖麻油，其中植物油酸和蓖麻油的质量配比为6：4。
所述（C）材料具体组分包括：抗氧化剂、紫外线吸收剂的任一或混合组分。
所述（D）材料具体组分包括：光稳定剂。
所述（A）材料中天然乳胶进行抽胺处理使其PH值达到6.0－7.0，优选为pH=6.5。
所述用于天然乳胶文胸的乳胶制品及其制备方法，其特征在于：所述乳胶制品由以下各组分具体配比及混合方式制成：
①硫磺粉（20%－35%）加水（40%－60%）并加入DPG（3%－5%）、分散剂NF（2%－5%）、ZDC（5%－9%）、MZ（6.6%－9%）、KY-616（3%－7%）、洗衣粉（0.1%－2%）、洗洁精（0.1%－2%）、植物油酸（0.1%－2%）、胺（0.1%－2%）将此些物料混合进行充分碾磨。
②天然乳胶进行抽胺处理使其PH值达到6.5左右。
③氧化锌（60%－65%）、洗衣粉（5%）、水（25%－30%）进行充分搅拌混合。
④植物油酸（20%－25%）、水（70%－75%）、氢氧化钾（5%）进行充分搅拌混合。
⑤蓖麻油（30%－35%）、水（65%－70%）搅拌混合用明火将其煮沸腾。
⑥凝软固剂（40%－45%）、水（60%－65%）进行充分搅拌混合。
⑦纤维素钠（40%－45%）、水（60%－65%）进行充分搅拌混合。
⑧合成胶。
将以上①、②、④、⑤、⑦、⑧按7%－10%、70%－80%、2%－4%、 0.5%－1.5%、0.5%－1.5% 、10%－13%以此比例进行充分搅拌混合成（A）材料。
按（A）材料总量为标准加入（B）材料（植物油酸和蓖麻油以配比6：4搅拌混合成）4%－8%。
再加入以下（C）材料3%－7%以及（D）材料0.5%－3%后将此些物料搅拌混合均匀成（a）混合物。
其中，所述（C）材料包括以下质量百分比的组分：亚磷酸类抗氧化剂30－50%、受阻胺类抗氧化剂10－30%、苯基甲（乙）类紫外线吸收剂20－40%、受阻酚类抗氧化剂5－10%、苯并三氮类紫外线吸收剂4－10%。
所述（D）材料包括以下质量百分比的组分：双（1,2,2,6,6-五甲基-4-哌啶基）癸二酸75－85%，癸二酸甲基-1,2,2,6,6-五甲基-4-哌啶酯15－25%。
或者，所述（C）材料包括以下质量百分比的组分：亚磷酸三（2，4-二叔丁基苯基）酯（抗氧剂168 ）10－50%，四[β-（3，5-二叔丁基-4-羟基苯基）丙酸]季戊四醇酯（抗氧剂1010）10－50%， N,N'-双-(3-(3,5-二叔丁基-4-羟基苯基)丙酰基)己二胺（抗氧剂 1098）10－50%。
所述（D）材料中包括癸二酸双-2,2,6,6-四甲基哌啶醇酯（光稳定剂 770）。
所述（a）混合物在通过发泡设备进行发泡的过程中，即同时注入③和⑥（质量百分比以2%－4%和2%－4%计）进行发泡定型；待微有凝固现象即放入90℃－110℃蒸汽箱进行蒸40－45分钟，即可制得乳胶制品材料。
所述乳胶制品材料经加工、剪切、修整成文胸。
本发明中各组分为市售产品。
本发明的有益效果是：在原有的水洗天然乳胶原料混合过程中，进行配方的改进以及材料的添加，从而在保证原本天然乳胶的特性的基础上，改善耐高温热压及耐黄性。本发明不仅能方便制造出各种符合人体曲线美丽的造型文胸，并使天然乳胶在应用上范围更广。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例1
一种用于天然乳胶文胸的乳胶制品及其制备方法，所述乳胶制品材料包括以下质量百分比的组分制成：
①按照总质量100g，称取以下组分：硫磺粉（20%－35%）35 加水（40%－60%）50并加入DPG（3%－5%）、分散剂NF（2%－5%）、ZDC（5%－9%）、MZ（6.6%－9%）、KY-616（3%－7%）、洗衣粉（0.1%－2%）、洗洁精（0.1%－2%）、植物油酸（0.1%－2%）、胺（0.1%－2%）将此些物料混合进行充分碾磨。
②称取天然乳胶 750g，进行抽胺处理使其PH值达到6.5左右。
④称取植物油酸6g、水22.5g、氢氧化钾1.5g进行充分搅拌混合。
⑤称取蓖麻油3g、水7g搅拌混合用明火将其煮沸腾。
⑦称取纤维素钠4g、水6g进行充分搅拌混合。
⑧称取合成胶100g。
将以上①、②、④、⑤、⑦、⑧进行充分搅拌混合成（A）材料。
称取植物油酸24g和蓖麻油16g，搅拌混合成（B）材料，然后加入到（A）材料中。
然后再加入（C）材料30g以及（D）材料30g后将此些物料搅拌混合均匀成（a）混合物。
其中，（C）材料制备为称取亚磷酸类抗氧化剂9g、受阻胺类抗氧化剂9g、苯基甲（乙）类紫外线吸收剂6g、受阻酚类抗氧化剂3g、苯并三氮类紫外线吸收剂3g后搅拌混合制得。
（D）材料制备为称取双（1,2,2,6,6-五甲基-4-哌啶基）癸二酸22.5g，癸二酸甲基-1,2,2,6,6-五甲基-4-哌啶酯7.5g后搅拌混合制得。
称取氧化锌13g、洗衣粉1g、水6g进行充分搅拌混合，制得③。
称取凝软固剂8g、水12g进行充分搅拌混合，制得⑥。
将制得的（a）混合物在通过发泡设备进行发泡的过程中，即同时注入③和⑥进行发泡定型；待微有凝固现象即放入90℃－110℃蒸汽箱进行蒸40－45分钟，即可制得乳胶制品材料。
将制得乳胶制品材料进行拔模、脱水、烘干、剪切、修整等加工后，制得天然乳胶文胸。
本实施例中，所有的原材料都为市售产品。
实施例2
一种用于天然乳胶文胸的乳胶制品及其制备方法，所述乳胶制品材料包括以下质量百分比的组分制成：
①按照总质量100g，称取以下组分：硫磺粉（20%－35%）35 加水（40%－60%）50并加入DPG（3%－5%）、分散剂NF（2%－5%）、ZDC（5%－9%）、MZ（6.6%－9%）、KY-616（3%－7%）、洗衣粉（0.1%－2%）、洗洁精（0.1%－2%）、植物油酸（0.1%－2%）、胺（0.1%－2%）将此些物料混合进行充分碾磨。
②称取天然乳胶 750g，进行抽胺处理使其PH值达到6.5左右。
④称取植物油酸6g、水22.5g、氢氧化钾1.5g进行充分搅拌混合。
⑤称取蓖麻油3g、水7g搅拌混合用明火将其煮沸腾。
⑦称取纤维素钠4g、水6g进行充分搅拌混合。
⑧称取合成胶100g。
将以上①、②、④、⑤、⑦、⑧进行充分搅拌混合成（A）材料。
称取植物油酸24g和蓖麻油16g，搅拌混合成（B）材料，然后加入到（A）材料中。
然后再加入（C）材料30g以及（D）材料30g后将此些物料搅拌混合均匀成（a）混合物。
其中，（C）材料制备为亚磷酸三（2，4-二叔丁基苯基）酯 （抗氧剂168 ）12g，四[β-（3，5-二叔丁基-4-羟基苯基）丙酸]季戊四醇酯（抗氧剂1010）9g， N,N'-双-(3-(3,5-二叔丁基-4-羟基苯基)丙酰基)己二胺（抗氧剂 1098）9g后搅拌混合制得。
（D）材料制备为称取癸二酸双-2,2,6,6-四甲基哌啶醇酯（光稳定剂 770）30g制得。
称取氧化锌13g、洗衣粉1g、水6g进行充分搅拌混合，制得③。
称取凝软固剂8g、水12g进行充分搅拌混合，制得⑥。
将制得的（a）混合物在通过发泡设备进行发泡的过程中，即同时注入③和⑥进行发泡定型；待微有凝固现象即放入90℃－110℃蒸汽箱进行蒸40－45分钟，即可制得乳胶制品材料。
将制得乳胶制品材料进行拔模、脱水、烘干、剪切、修整等加工后，制得天然乳胶文胸。
本实施例中，所有的原材料都为市售产品。
以上所述仅为本发明的部分实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效配方或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (7)
1.一种用于天然乳胶文胸的乳胶制品及其制备方法，其特征在于：所述乳胶制品包括以下质量百分比的组分制成：（A）材料85%－95%，（B）材料4%－8%，（C）材料3%－7%，（D）材料0.5%－3%；
所述（A）材料具体组分包括：天然乳胶、硫磺粉、催化剂 、分散剂 、促进剂、橡胶硫化促进剂、乳胶抗氧化剂、表面活性剂、乳化剂、植物油酸、胺、水、植物油酸、氢氧化钾、蓖麻油、纤维素钠、合成胶，其中天然乳胶质量百分比为70－95%，合成胶质量百分比为5－15%；
所述（B）材料具体组分包括：植物油酸、蓖麻油，其中植物油酸和蓖麻油的质量配比为6：4；
所述（C）材料具体组分包括：抗氧化剂、紫外线吸收剂的任一或混合组分；
所述（D）材料具体组分包括：光稳定剂。
2.根据权利要求1所述的用于天然乳胶文胸的乳胶制品及其制备方法，其特征在于：所述（A）材料中天然乳胶进行抽胺处理使其PH值达到6.0－7.0，优选为pH=6.5。
3.根据权利要求1所述的用于天然乳胶文胸的乳胶制品及其制备方法，其特征在于：所述乳胶制品材料由以下各组分具体配比及混合方式制成：
①硫磺粉（20%－35%）加水（40%－60%）并加入DPG（3%－5%）、分散剂NF（2%－5%）、ZDC（5%－9%）、MZ（6.6%－9%）、KY-616（3%－7%）、洗衣粉（0.1%－2%）、洗洁精（0.1%－2%）、植物油酸（0.1%－2%）、胺（0.1%－2%）将此些物料混合进行充分碾磨；
②天然乳胶进行抽胺处理使其PH值达到6.5左右；
③氧化锌（60%－65%）、洗衣粉（5%）、水（25%－30%）进行充分搅拌混合；
④植物油酸（20%－25%）、水（70%－75%）、氢氧化钾（5%）进行充分搅拌混合；
⑤蓖麻油（30%－35%）、水（65%－70%）搅拌混合用明火将其煮沸腾；
⑥凝软固剂（40%－45%）、水（60%－65%）进行充分搅拌混合；
⑦纤维素钠（40%－45%）、水（60%－65%）进行充分搅拌混合，
⑧合成胶；
将以上①、②、④、⑤、⑦、⑧按7%－10%、70%－80%、2%－4%、0.5%－1.5%、0.5%－1.5% 、10%－13%以此比例进行充分搅拌混合成（A）材料；按（A）材料总量为标准加入（B）材料（植物油酸和蓖麻油以配比6：4搅拌混合成）4%－8%；再加入以下（C）材料3%－7%以及（D）材料0.5%－3%后将此些物料搅拌混合均匀成（a）混合物；
所述（a）混合物在通过发泡设备进行发泡的过程中，即同时注入③和⑥（质量百分比以2%－4%和2%－4%计）进行发泡定型；待微有凝固现象即放入90℃－110℃蒸汽箱进行蒸40－45分钟，即可制得乳胶制品材料。
4.根据权利要求3所述的用于天然乳胶文胸的乳胶制品及其制备方法，其特征在于：所述（C）材料包括以下质量百分比的组分：亚磷酸类抗氧化剂30－50%、受阻胺类抗氧化剂10－30%、苯基甲（乙）类紫外线吸收剂20－40%、受阻酚类抗氧化剂5－10%、苯并三氮类紫外线吸收剂4－10%。
5.根据权利要求3所述的用于天然乳胶文胸的乳胶制品及其制备方法，其特征在于：所述（D）材料包括以下质量百分比的组分：双（1,2,2,6,6-五甲基-4-哌啶基）癸二酸75－85%，癸二酸甲基-1,2,2,6,6-五甲基-4-哌啶酯15－25%。
6.根据权利要求3所述的用于天然乳胶文胸的乳胶制品及其制备方法，其特征在于：所述（C）材料包括以下质量百分比的组分：亚磷酸三（2，4-二叔丁基苯基）酯 （抗氧剂168 ）10－50%，四[β-（3，5-二叔丁基-4-羟基苯基）丙酸]季戊四醇酯（抗氧剂1010）10－50%， N,N'-双-(3-(3,5-二叔丁基-4-羟基苯基)丙酰基)己二胺（抗氧剂 1098）10－50%。
7.根据权利要求3所述的用于天然乳胶文胸的乳胶制品及其制备方法，其特征在于：所述（D）材料中包括癸二酸双-2,2,6,6-四甲基哌啶醇酯（光稳定剂 770）。