CN107935629A - A kind of foamed ceramic embryo material - Google Patents
A kind of foamed ceramic embryo material Download PDFInfo
- Publication number
- CN107935629A CN107935629A CN201711383559.7A CN201711383559A CN107935629A CN 107935629 A CN107935629 A CN 107935629A CN 201711383559 A CN201711383559 A CN 201711383559A CN 107935629 A CN107935629 A CN 107935629A
- Authority
- CN
- China
- Prior art keywords
- parts
- foamed ceramic
- embryo material
- ceramic embryo
- suspending agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of foamed ceramic embryo material, each component and shared parts by weight are:15 20 parts of spodumene, 4 10 parts of subnar soil, 5 10 parts of clay, 15 20 parts of quartz, 5 11 parts of kaolin, 38 parts of suspending agent, 25 parts of reinforcing agent, 10 20 parts of flyash, 26 parts of zinc oxide, 6 13 parts of mullite.Gained foamed ceramic material of the invention, function admirable, has the function of very strong refractory heat-insulating, and safety and firmness is good, non-aging.
Description
Technical field
The present invention relates to a kind of ceramic material, is specifically a kind of foamed ceramic embryo material.
Background technology
Foamed ceramic is the closed pore of the high porosity formed using advanced production technology and foaming technique through high-temperature roasting
Ceramic material, there is product to be suitable for building exterior wall heat preserving, fire-blocking belt, the cold-heat bridge processing of building self-heat conserving etc..Product has
There is fire protection flame retarding, deformation coefficient is small, anti-aging, and performance is stablized, and eco-environmental prote is good, good with plinth course and float coat compatibility,
Safety and firmness is good, can be with the building same service life.More importantly material fire-protection rating is A1 grades, overcomes organic material to be afraid of bright
Fire, deadly defect easy to aging, has filled up the domestic blank of building inorganic heat insulation material.
The content of the invention
The present invention provides a kind of foamed ceramic embryo material, can significantly improve the performance of ceramic material.
To achieve the above object, the present invention provides following formula:
A kind of foamed ceramic embryo material, each component and shared parts by weight are:15-20 parts of spodumene, 4-10 parts of subnar soil,
5-10 parts of clay, 15-20 parts quartzy, 5-11 parts of kaolin, 3-8 parts of suspending agent, 2-5 parts of reinforcing agent, 10-20 parts of flyash, oxygen
Change 2-6 parts of zinc, 6-13 parts of mullite.
Preferably, the suspending agent is sodium carboxymethylcellulose.
Preferably, the reinforcing agent is etherified sour calcium for composite anion and receives.
Gained foamed ceramic material of the invention, function admirable, has the function of very strong refractory heat-insulating, and safety and firmness
It is good, it is non-aging.
Embodiment
A kind of foamed ceramic embryo material, each component and shared parts by weight are:15-20 parts of spodumene, 4-10 parts of subnar soil,
5-10 parts of clay, 15-20 parts quartzy, 5-11 parts of kaolin, 3-8 parts of suspending agent, 2-5 parts of reinforcing agent, 10-20 parts of flyash, oxygen
Change 2-6 parts of zinc, 6-13 parts of mullite.The suspending agent is sodium carboxymethylcellulose, and the reinforcing agent is etherified for composite anion
Sour calcium is received.
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated, it will be appreciated that the specific embodiments described herein are merely illustrative of the present invention, is not used to
Limit the present invention.
Embodiment 1:
A kind of foamed ceramic embryo material, each component and shared parts by weight are:15-20 parts of spodumene, 4-10 parts of subnar soil,
5-10 parts of clay, 15-20 parts quartzy, 5-11 parts of kaolin, 3-8 parts of suspending agent, 2-5 parts of reinforcing agent, 10-20 parts of flyash, oxygen
Change 2-6 parts of zinc, 6-13 parts of mullite.
Embodiment 2:
A kind of foamed ceramic embryo material, each component and shared parts by weight are:15-20 parts of spodumene, 4-10 parts of subnar soil,
5-10 parts of clay, 15-20 parts quartzy, 5-11 parts of kaolin, 3-8 parts of suspending agent, 2-5 parts of reinforcing agent, 10-20 parts of flyash, oxygen
Change 2-6 parts of zinc, 6-13 parts of mullite.
Embodiment 3:
A kind of foamed ceramic embryo material, each component and shared parts by weight are:15-20 parts of spodumene, 4-10 parts of subnar soil,
5-10 parts of clay, 15-20 parts quartzy, 5-11 parts of kaolin, 3-8 parts of suspending agent, 2-5 parts of reinforcing agent, 10-20 parts of flyash, oxygen
Change 2-6 parts of zinc, 6-13 parts of mullite.
Claims (3)
1. a kind of foamed ceramic embryo material, it is characterised in that each component and shared parts by weight are:15-20 parts of spodumene, subnar
4-10 parts native, 5-10 parts of clay is 15-20 parts quartzy, 5-11 parts of kaolin, 3-8 parts of suspending agent, 2-5 parts of reinforcing agent, flyash
10-20 parts, 2-6 parts of zinc oxide, 6-13 parts of mullite.
2. foamed ceramic embryo material according to claim 1, it is characterised in that the suspending agent is sodium carboxymethylcellulose.
3. foamed ceramic embryo material according to claim 1 or 2, it is characterised in that the reinforcing agent is composite anion ether
Change sour calcium to receive.