CN108298939A - A kind of thermal insulation material - Google Patents

A kind of thermal insulation material Download PDF

Info

Publication number
CN108298939A
CN108298939A CN201810357877.4A CN201810357877A CN108298939A CN 108298939 A CN108298939 A CN 108298939A CN 201810357877 A CN201810357877 A CN 201810357877A CN 108298939 A CN108298939 A CN 108298939A
Authority
CN
China
Prior art keywords
parts
thermal insulation
insulation material
flyash
kaolin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810357877.4A
Other languages
Chinese (zh)
Inventor
章志明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Informed Technology Service Co Ltd
Original Assignee
Huzhou Informed Technology Service Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huzhou Informed Technology Service Co Ltd filed Critical Huzhou Informed Technology Service Co Ltd
Priority to CN201810357877.4A priority Critical patent/CN108298939A/en
Publication of CN108298939A publication Critical patent/CN108298939A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of thermal insulation materials, which is characterized in that is made of the raw material of following parts by weight:30 50 parts of portland slag cement, 56 parts of polypropylene fibre, 13 parts of glass fibre, 10 20 parts of kaolin, 5 10 parts of flyash, 25 parts of polyacrylic acid, 13 parts of foaming agent, 0.1 0.5 parts of sodium metasilicate, 0.5 2 parts of early strength agent, 20 30 parts of water.The present invention provides a kind of thermal insulation material, can increase heat-resistant knocking stability and high-temperature behavior and of low cost, and has the characteristics that keep the temperature, heat-insulated, sound insulation.

Description

A kind of thermal insulation material
Technical field
The present invention relates to technical field of buildings more particularly to a kind of thermal insulation materials.
Background technology
Thermal insulation material is inorganic active thermal insulation material with ordinary cement, insulation stone, calcium powder, campanulaceae, etc. be used as primary raw material, Closed pore inorganic active thermal insulation material, inorganic active made of advanced production technology and Chemical Engineering Technology are studied through test of many times Thermal insulation material with ordinary cement, insulation stone, calcium powder, campanulaceae, etc. be used as primary raw material, using advanced production technology and chemical industry skill Closed pore inorganic active thermal insulation material made of art is studied through test of many times, product have fire protection flame retarding, and deformation coefficient is small, anti-ageing Change, performance is stablized, and eco-environmental prote is good, and good with plinth course and float coat compatibility, safety and firmness is good, can be with the building same longevity Life, existing fireproof and heat-insulating material heat-resistant knocking stability energy and high-temperature behavior is poor, cost is higher.
Invention content
The object of the present invention is to provide a kind of thermal insulation material, can increase heat-resistant knocking stability and high-temperature behavior and at This is cheap, and has the characteristics that heat preservation, heat-insulated, sound insulation.
Technical scheme of the present invention:A kind of thermal insulation material, which is characterized in that be made of the raw material of following parts by weight: 30-50 parts of portland slag cement, 5-6 parts of polypropylene fibre, 1-3 parts of glass fibre, 10-20 parts of kaolin, flyash 5-10 Part, 2-5 parts of polyacrylic acid, 1-3 parts of foaming agent, 0.1-0.5 parts of sodium metasilicate, 0.5-2 parts of early strength agent, 20-30 parts of water.
A kind of thermal insulation material above-mentioned, which is characterized in that be made of the raw material of following parts by weight:Slag silicate brine 30 parts of mud, 5 parts of polypropylene fibre, 1 part of glass fibre, 10 parts of kaolin, 5 parts of flyash, 2 parts of polyacrylic acid, 1 part of foaming agent, 0.1 part of sodium metasilicate, 0.5 part of early strength agent, 20 parts of water.
A kind of thermal insulation material above-mentioned, which is characterized in that be made of the raw material of following parts by weight:Slag silicate brine 50 parts of mud, 6 parts of polypropylene fibre, 3 parts of glass fibre, 20 parts of kaolin, 10 parts of flyash, 5 parts of polyacrylic acid, 3 parts of foaming agent, 0.5 part of sodium metasilicate, 2 parts of early strength agent, 30 parts of water.
A kind of thermal insulation material above-mentioned, which is characterized in that be made of the raw material of following parts by weight:Slag silicate brine 40 parts of mud, 5 parts of polypropylene fibre, 2 parts of glass fibre, 15 parts of kaolin, 8 parts of flyash, 4 parts of polyacrylic acid, 2 parts of foaming agent, 0.3 part of sodium metasilicate, 1 part of early strength agent, 25 parts of water.
Beneficial effects of the present invention:Heat-resistant knocking stability and high-temperature behavior and of low cost can be increased, and with protecting The characteristics of warm, heat-insulated, sound insulation.
Specific implementation mode
The present invention is further illustrated for following example, but is not intended as the foundation limited the present invention.
Embodiment 1:A kind of thermal insulation material is made of the raw material of following parts by weight:Portland slag cement 30-50 Part, 5-6 parts of polypropylene fibre, 1-3 parts of glass fibre, 10-20 parts of kaolin, 5-10 parts of flyash, 2-5 parts of polyacrylic acid, hair 1-3 parts of infusion, 0.1-0.5 parts of sodium metasilicate, 0.5-2 parts of early strength agent, 20-30 parts of water.
Embodiment 2:A kind of thermal insulation material is made of the raw material of following parts by weight:30 parts of portland slag cement gathers 5 parts of tacryl, 1 part of glass fibre, 10 parts of kaolin, 5 parts of flyash, 2 parts of polyacrylic acid, 1 part of foaming agent, sodium metasilicate 0.1 Part, 0.5 part of early strength agent, 20 parts of water.
Embodiment 3:A kind of thermal insulation material is made of the raw material of following parts by weight:50 parts of portland slag cement gathers 6 parts of tacryl, 3 parts of glass fibre, 20 parts of kaolin, 10 parts of flyash, 5 parts of polyacrylic acid, 3 parts of foaming agent, sodium metasilicate 0.5 Part, 2 parts of early strength agent, 30 parts of water.
Embodiment 4:A kind of thermal insulation material is made of the raw material of following parts by weight:40 parts of portland slag cement gathers 5 parts of tacryl, 2 parts of glass fibre, 15 parts of kaolin, 8 parts of flyash, 4 parts of polyacrylic acid, 2 parts of foaming agent, sodium metasilicate 0.3 Part, 1 part of early strength agent, 25 parts of water.

Claims (4)

1. a kind of thermal insulation material, which is characterized in that be made of the raw material of following parts by weight:Portland slag cement 30-50 Part, 5-6 parts of polypropylene fibre, 1-3 parts of glass fibre, 10-20 parts of kaolin, 5-10 parts of flyash, 2-5 parts of polyacrylic acid, hair 1-3 parts of infusion, 0.1-0.5 parts of sodium metasilicate, 0.5-2 parts of early strength agent, 20-30 parts of water.
2. a kind of thermal insulation material according to claim 1, which is characterized in that be made of the raw material of following parts by weight: 30 parts of portland slag cement, 5 parts of polypropylene fibre, 1 part of glass fibre, 10 parts of kaolin, 5 parts of flyash, polyacrylic acid 2 Part, 1 part of foaming agent, 0.1 part of sodium metasilicate, 0.5 part of early strength agent, 20 parts of water.
3. a kind of thermal insulation material according to claim 1, which is characterized in that be made of the raw material of following parts by weight: 50 parts of portland slag cement, 6 parts of polypropylene fibre, 3 parts of glass fibre, 20 parts of kaolin, 10 parts of flyash, polyacrylic acid 5 Part, 3 parts of foaming agent, 0.5 part of sodium metasilicate, 2 parts of early strength agent, 30 parts of water.
4. a kind of thermal insulation material according to claim 1, which is characterized in that be made of the raw material of following parts by weight: 40 parts of portland slag cement, 5 parts of polypropylene fibre, 2 parts of glass fibre, 15 parts of kaolin, 8 parts of flyash, polyacrylic acid 4 Part, 2 parts of foaming agent, 0.3 part of sodium metasilicate, 1 part of early strength agent, 25 parts of water.
CN201810357877.4A 2018-04-20 2018-04-20 A kind of thermal insulation material Withdrawn CN108298939A (en)